CN1613812A - 城市垃圾焚烧灰渣轻质免烧砖 - Google Patents

城市垃圾焚烧灰渣轻质免烧砖 Download PDF

Info

Publication number
CN1613812A
CN1613812A CNA200410009708XA CN200410009708A CN1613812A CN 1613812 A CN1613812 A CN 1613812A CN A200410009708X A CNA200410009708X A CN A200410009708XA CN 200410009708 A CN200410009708 A CN 200410009708A CN 1613812 A CN1613812 A CN 1613812A
Authority
CN
China
Prior art keywords
ash
mnc
light
powder
particle diameter
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA200410009708XA
Other languages
English (en)
Inventor
李桓宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNA200410009708XA priority Critical patent/CN1613812A/zh
Publication of CN1613812A publication Critical patent/CN1613812A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种城市垃圾焚烧灰渣轻质免烧砖，其特征在于它是由400－600份城市垃圾焚烧灰渣粉料、200－400份河沙或石粉、110－150份氧化钙、30－50份硫酸钙、80－120份水泥、5－18份氯化钙、1.0－2.6份MNC－AI早强剂、2－6份MNC－C防冻剂、5－12份硫酸亚铁、50－80份硫酸镁和80－140份水混合呈潮湿状后用机械振动挤压成型，在25－30Mpa的压力下制成轻质免烧砖，它具有密度小，体轻、制作方法简单，无三废排放，解决了环境污染，又减少土地占用量，节省能源的优点及效果。

Description

城市垃圾焚烧灰渣轻质免烧砖
技术领域
本发明涉及一种城市垃圾焚烧灰渣轻质免烧砖，具体地说它是以垃圾焚烧灰渣为主要原料在常温条件下用机械振动挤压成型的轻质免烧砖，属制砖技术。
技术背景
目前城市垃圾的焚烧灰渣与固体废弃物都是由国家投资采用填埋方法进行处理以减少对环境的污染。但随着我国经济的快速发展和城市规模的不断扩大，人口的高度集中，生活水平不断的提高，城市垃圾日益增加，由城市固体废弃物所造成的环境污染也越来越严重，如长期采用填埋方法处理，不仅需要占用大量的土地资源，而且会造成二次污染，对地下水资源污染更大，也造成了资源的浪费。
发明内容
本发明的目的正是为了解决上述存在的问题而提供一种将城市垃圾焚烧灰渣为主要原料制成的城市垃圾焚烧灰渣轻质免烧砖，从而使城市垃圾焚烧灰渣得到了再利用并变废为宝。
本发明的目的是通过下列技术方案实现的：
城市垃圾焚烧灰渣轻质免烧砖，其特征在于它是由下述重量配比为原料按常规方法用机械挤压成型经养护而成：
          城市垃圾焚烧灰渣粉料         400-600份
          河沙或石粉                   200-400份
          氧化钙                       110-150份
          硫酸钙                       30-50份
          水泥                         80-120份
          氯化钙                       5-18份
          MNC-AI早强剂                 1.0-2.6份
          MNC-C防冻剂                  2-6份
          硫酸亚铁                     5-12份
          硫酸镁          50-80份
          水              80-140份。
所述的城市垃圾焚烧灰渣粉料为城市的生活垃圾和工业垃圾的可燃垃圾经过发电焚烧后的炉渣及飞灰，经分选除去废金属再粉碎，其粉碎粒径为-15mm，再经除臭、灭害、灭菌，消毒的粉料。
所述的氧化钙、硫酸钙粒径为-0.2mm，河沙或石粉粒径为-15mm。
本发明采用城市垃圾焚烧灰渣粉料为原料，因为垃圾焚烧后的灰渣内含有大量的二氧化硅和三氧化二铝及铁、钙等多种化学成分组成，稳定性好、密度低，其物理性质和工程性质与天然骨料相似，并且容易进行粒径分配，是免烧砖的好原料，与氧化钙、硫酸钙、水泥、氯化钙、MNC-AI早强剂和MNC-C防冻剂的化学原料和骨料河沙或石粉混合反应制成免烧砖，不需高温培烧和蒸气养护，而利用化学反应在常温下固化，不产生“三废”，节省能源，保护环境，硫酸亚铁为还原剂、硫酸镁为硫酸亚铁的保持剂可使垃圾灰渣中的气味充分分解，达到迅速除臭的作用。
本发明免烧砖是按常规方法制作的，即将400-600份城市垃圾焚烧灰渣粉料、200-400份河沙或石粉、110-150份氧化钙、30-50份硫酸钙、80-120份水泥、5-18氯化钙、1.0-2.6份MNC-AI早强剂、2.0-6.0份MNC-C防冻剂、5-12份硫酸亚铁、50-80份硫酸镁和80-140份水混合呈潮湿状后用机械振动挤压成型，在25-30Mpa的压力下制成轻质免烧砖，再用喷水法在常温下自然干燥养护28天。
用本发明的原料也可制造不同规格的空心砌块。
本发明的产品经过质量检测结果如下：依据jc525-93标淮
        抗压强度：平均值9.0-10.5Mpa
        抗折强度：2-2.5Mpa
        体积密度：1503kg/m3
        吸水率：17.1％。
放射性物质检测依据GB6566-2001标准，
检测结果为放射性水平符合中华人民共和国国家标准《建筑材料放射性防护标准》规定的要求，其产销与使用范围不受限制。
空心砌块按GB15229-2002标准，检测结果评定为5级。
由于采取上述技术方案，本发明与已有技术相比具有如下优点及效果：
(a)本发明的轻质免烧砖，由于密度小，每立方米轻质免烧砖比粘土实心砖轻500kg以上，可减轻建筑物的自重和延长建筑物使用寿命；
(b)制作方法简单，无三废排放，符合国务院66文电“关于大力发展节能、节地、节水、利废保温隔热等新型墙体材料”精神要求，且投资少、见效快、成本低、效益好，适用各级办厂生产；
(c)变废为宝，解决了环境污染，又减少土地占用量，节省能源。
具体实施方式
实施例1
取城市的生活垃圾和工业垃圾的可燃垃圾经过发电焚烧后的炉渣及飞灰，经过分选除去废金属再粉碎，其粉碎粒径为-15mm，除臭、灭害、灭菌和消毒处理的城市垃圾焚烧灰渣粉料400kg、粒径为-15mm的河沙400kg、粒径为-0.2mm的氧化钙110kg和硫酸钙50kg、水泥80kg、氯化钙18kg、MNC-AI早强剂1kg、MNC-C防冻剂6kg、硫酸亚铁5kg、硫酸镁80kg和水140kg混合呈潮湿状后用机械振动挤压成型，在30Mpa的压力下制成轻质免烧砖，再用喷水法在常温下自然干燥养护28天，制成产品，经检测10块平均抗压强度为10.5Mpa，抗折强度为2.5Mpa。
实施例2
取城市的生活垃圾和工业垃圾的可燃垃圾经过发电焚烧后的炉渣及飞灰，经过分选除去废金属再粉碎，其粉碎粒径为-15mm，除臭、灭害、灭菌和消毒处理的城市垃圾焚烧灰渣粉料500kg、粒径为-15mm的河沙300kg、粒径为-0.2mm的氧化钙130kg和硫酸钙40kg、水泥100kg、氯化钙10kg、MNC-AI早强剂1.8kg、MNC-C防冻剂4kg、硫酸亚铁8kg、硫酸镁65kg和水110kg混合呈潮湿状后用机械振动挤压成型，在25Mpa的压力下制成轻质免烧砖，再用喷水法在常温下自然干燥养护28天，制成产品，经检测10块平均抗压强度为9Mpa，抗折强度为2.0Mpa。
实施例3
取城市的生活垃圾和工业垃圾的可燃垃圾经过发电焚烧后的炉渣及飞灰，经过分选除去废金属再粉碎，其粉碎粒径为-15mm，除臭、灭害、灭菌和消毒处理的城市垃圾焚烧灰渣粉料600kg、粒径为-15mm的石粉200kg、粒径为-0.2mm的氧化钙150kg和硫酸钙30kg、水泥120kg、氯化钙5kg、MNC-AI早强剂2.6kg、MNC-C防冻剂2kg、硫酸亚铁12kg、硫酸镁50kg和水80kg混合呈潮湿状后用机械振动挤压成型，在28Mpa的压力下制成轻质免烧砖，再用喷水法在常温下自然干燥养护28天，制成产品，经检测10块平均抗压强度为10Mpa，抗折强度为2.3Mpa。

Claims (3)

1、城市垃圾焚烧灰渣轻质免烧砖，其特征在于它是由下述重量配比的原料按常规方法用机械挤压成型经养护而成，
      城市垃圾焚烧灰渣粉料      400-600份
      河沙或石粉                200-400份
      氧化钙                    110-150份
      硫酸钙                    30-50份
      水泥                      80-120份
      氯化钙                    5-18份
      MNC-AI早强剂              1.0-2.6份
      MNC-C防冻剂               2.0-6.0份
      硫酸亚铁                  5-12份
      硫酸镁                    50-80份
      水                        80-140份。
2、根据权利要求1所述的轻质免烧砖，其特征在于所述的城市垃圾焚烧灰渣粉料为城市的生活垃圾和工业垃圾的可燃垃圾经过发电焚烧后的炉渣及飞灰，经分选除去废金属再粉碎，其粉碎粒径为-15mm，再经除臭、灭害、灭菌、消毒的粉料。
3、根据权利要求1所述的轻质免烧砖，其特征在于所述的氧化钙、硫酸钙粒径为-0.2mm，河沙或石粉粒径为-15mm。
CNA200410009708XA 2004-10-26 2004-10-26 城市垃圾焚烧灰渣轻质免烧砖 Pending CN1613812A (zh)