CN1273404C - 垃圾灰渣蒸养轻质砖的生产方法 - Google Patents

垃圾灰渣蒸养轻质砖的生产方法 Download PDF

Info

Publication number
CN1273404C
CN1273404C CNB2004100989161A CN200410098916A CN1273404C CN 1273404 C CN1273404 C CN 1273404C CN B2004100989161 A CNB2004100989161 A CN B2004100989161A CN 200410098916 A CN200410098916 A CN 200410098916A CN 1273404 C CN1273404 C CN 1273404C
Authority
CN
China
Prior art keywords
production
hours
steam
mnc
brick
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2004100989161A
Other languages
English (en)
Other versions
CN1636918A (zh
Inventor
李桓宇
Original Assignee
李桓宇
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 李桓宇 filed Critical 李桓宇
Priority to CNB2004100989161A priority Critical patent/CN1273404C/zh
Publication of CN1636918A publication Critical patent/CN1636918A/zh
Application granted granted Critical
Publication of CN1273404C publication Critical patent/CN1273404C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种垃圾灰渣蒸养轻质砖的生产方法,它以垃圾灰渣粉料、河沙或河沙、氧化钙、硫酸钙、水泥、氯化钙、MNC-A1早强剂、MNC-C防冻、硫酸亚铁、硫酸镁和水为原料,将上述原料混合后呈潮湿状用机械振动挤压成型,振动压力为25~30MPa,再将成型后轻质砖用蒸压釜进行蒸汽养护,先升温加热2~3小时后,在95~100℃再恒温5~8时,再自然降温1~2小时,制成蒸养轻质砖产品,该生产方法具有方法简单、可靠、生产过程无“三废”排放,节省能源,保护环境,减少占地面积,提高生产率,降低了生产成本,产品质量符合国家标准,重量轻,强度高,成本低,无污染的优点及效果。

Description

垃圾灰渣蒸养轻质砖的生产文法
技术领域
本发明涉及一种垃圾灰渣蒸养轻质砖的生产方法,属建筑材料。
背景技术
目前用垃圾灰渣制造轻质免烧砖,它解决了城市垃圾的污染问题,同时变废为宝,为建筑业提供了合格的建材,但它的制造方法有一定的不足,占地面积大、生产周期长、生产率低、在下雨的时候,气温低,靠自然条件很难固化,因此不利于生产。
发明内容
本发明的目的正是为了克服上述已有技术存在的缺点与不足而提供一种用蒸气养护的垃圾灰渣蒸养轻质砖的生产方法,从而缩短了生产周期,提高了产量,降低了生产成本,不受天气的影响。
本发明的目的是通过下列技术方案实现的:垃圾灰渣蒸养轻质砖的生产方法,采用下述重量配比的原料:垃圾焚烧灰渣粉料        450-650份河沙或石粉              250-400份氧化钙                  150-200份硫酸钙                  30-50份水泥                    90-120份氯化钙                  5-18份MNC-A1早强剂           1.0-2.6份MNC-C防冻剂             2.0-6.0份硫酸亚铁                5-12份硫酸镁                  50-80份水                      80-140份,其特征在于它按下述方法进行的:将上述原料混合呈潮湿状后用机械振动挤压成型,振动压力为25~30MPa,再将成型后轻质砖用蒸压釜进行蒸汽养护,先升温加热2~3小时后,在95~100℃再恒温5~8小时,然后自然降温1~2小时,制成蒸养轻质砖产品。
本发明的方法是对垃圾灰渣免烧砖的方法改进,采用相同的原料,垃圾经焚烧后的灰渣为主要原料,它为城市的生活垃圾经过发电焚烧后的炉渣及飞灰,经分选除去废金属再粉碎,其粉碎粒径为-15mm,再经除臭、灭害、灭菌、消毒的粉料,它含有大量的二氧化硅和三氧化二铝及铁、钙,具有稳定性好、密度低,性质与天然骨料,与河沙或石粉、氧化钙、硫酸钙、氯化钙、水泥、早强剂和防冻剂化学物质混合制造轻质砖,其中河沙或石粉粒径为-15mm,氧化钙和硫酸钙粒径为-0.2mm,它用蒸压釜的蒸汽对成型的轻质砖进行养护与免烧砖的自然养护时间相比大大减少,而且不受天气影响,大大提高产量,降低了生产成本,缩短了生产周期,也减少占地面积。
按着本发明的方法生产和原料也可生产不同规格的蒸养空心砌块。
按着本发明的方法的生产的蒸养轻质砖经深圳市建材科学研究院质量检测,蒸养轻质砖检测依据jc525标淮,蒸养轻质砖规格40mm×115mm×53mm,其结果如下:1、抗压强度:平均值为9~10MPa,2、抗折强度:平均值为2~2.5MPa,3、吸水率:17%,4、体积密度:1500kg/m3。
蒸养空心砌块检测依据为GB15229-2002标准,蒸养空心砌块规格为390mm×190mm×190mm,检测结果平均值为5.6MPa,结论评定为5级。
放射性物质检测依据为GB6566-2001标淮。
检测结果:放射性物质低于国家规定标淮98%,基本上属于无放射性物质产品,使用范围不受限制。
由于采取上述技术方案使本发明技术与已有技术相比具有生产方法简单、可靠、生产过程无“三废”排放,节省能源,保护环境,减少占地面积,提高生产率,降低了生产成本,产品质量符合国家标准,重量轻,强度高,成本低,无污染的优点及效果。
具体实施方式
实施例1将城市的生活垃圾经过发电焚烧后的炉渣及飞灰,经分选除去废金属再粉碎,其粉碎粒径为-15mm,再经除臭、灭害、灭菌、消毒的粉料,取垃圾灰渣粉料450kg、粒径为-15mm的河沙400kg、粒径为-0.2mm的氧化钙150kg和硫酸钙50kg、水泥90kg、氯化钙18kg、MNC-A1早强剂1.0kg、MNC-C防冻6kg、硫酸亚铁5kg、硫酸镁80kg和水80kg,将上述原料混合呈潮湿状后用机械振动挤压成型,振动压力为25MPa,再将成型后轻质砖用蒸压釜进行蒸汽养护,先升温加热2小时后,在95~100℃再恒温8小时,再自然降温1小时,制成蒸养轻质砖产品,经检测平均抗压强度为9.0MPa,抗折强度为2.0MPa。
实施例2将城市的生活垃圾经过发电焚烧后的炉渣及飞灰,经分选除去废金属再粉碎,其粉碎粒径为-15mm,再经除臭、灭害、灭菌、消毒的粉料,取垃圾灰渣粉料550kg、粒径为-15mm的石粉300kg、粒径为-0.2mm的氧化钙180kg和硫酸钙40kg、水泥110kg、氯化钙10kg、MNC-A1早强剂1.5kg、MNC-C防冻4kg、硫酸亚铁8kg、硫酸镁65k和水120kg,将上述原料混合呈潮湿后用机械振动挤压成型,振动压力为28MPa,再将成型后轻质砖用蒸压釜进行蒸汽养护,先升温加热2.5小时后,在95~100℃再恒温6小时,再自然降温1.5小时,制成蒸养轻质砖产品,经检测平均抗压强度为9.5MPa,抗折强度为2.3MPa。
实施例3将城市的生活垃圾经过发电焚烧后的炉渣及飞灰,经分选除去废金属再粉碎,其粉碎粒径为-15mm,再经除臭、灭害、灭菌、消毒的粉料,取垃圾灰渣粉料650kg、粒径为-15mm的河沙250kg、粒径为-0.2mm的氧化钙200kg和硫酸钙30kg、水泥120kg、氯化钙5kg、MNC-A1早强剂2.6kg、MNC-C防冻2kg、硫酸亚铁12kg、硫酸镁50kg和水140kg,本将上述原料混合呈潮湿状后用机械振动挤压成型,振动压力为30MPa,再将成型后轻质砖用蒸压釜进行蒸汽养护,先升温加热3小时后,在95~100℃再恒温5小时,再自然降温2小时,制成蒸养轻质砖产品,经检测平均抗压强度为10.0MPa,抗折强度为2.5MPa。

Claims (1)

1.垃圾灰渣蒸养轻质砖的生产方法,采用下述重量配比的原料:垃圾焚烧灰渣粉料                  450-650份河沙或石粉                        250-400份氧化钙                            150-200份硫酸钙                            30-50份水泥                              90-120份氯化钙                            5-18份MNC-A1早强剂                    1.0-2.6份MNC-C防冻剂                       2.0-6.0份硫酸亚铁                          5-12份硫酸镁                            50-80份水                                80-140份,其特征在于它按下述方法进行的:将上述原料混合呈潮湿状后用机械振动挤压成型,振动压力为25~30MPa,再将成型后轻质砖用蒸压釜进行蒸汽养护,先升温加热2~3小时后,在95~100℃再恒温5~8小时,然后自然降温1~2小时,制成蒸养轻质砖产品。
CNB2004100989161A 2004-12-15 2004-12-15 垃圾灰渣蒸养轻质砖的生产方法 Expired - Fee Related CN1273404C (zh)