CN1331965C - 改性废旧聚苯乙烯泡沫塑料涂料 - Google Patents
改性废旧聚苯乙烯泡沫塑料涂料 Download PDFInfo
- Publication number
- CN1331965C CN1331965C CNB2005100459935A CN200510045993A CN1331965C CN 1331965 C CN1331965 C CN 1331965C CN B2005100459935 A CNB2005100459935 A CN B2005100459935A CN 200510045993 A CN200510045993 A CN 200510045993A CN 1331965 C CN1331965 C CN 1331965C
- Authority
- CN
- China
- Prior art keywords
- pigment
- foamed plastic
- waste old
- polystyrene foamed
- old polystyrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
改性废旧聚苯乙烯泡沫塑料涂料,采用低毒、价廉工业级溶剂在常温下对废旧聚苯乙烯泡沫塑料充分溶解后做为基料,再加入乳化、分散剂,固体填料,体质颜料,增塑剂,防冻剂及颜料。其中废旧聚苯乙烯泡沫塑料14-20;环己烯60-80;乳化、分散剂十二烷基苯磺酸钠0.1-0.3及OP-100.1-0.3;固体填料碳酸钙10-20,滑石粉4-8;体质颜料钛白粉1-3;增塑剂邻苯二甲酸二丁酯1-3;防冻剂乙二醇或丙三醇2-3;颜料适量。本发明由于原料的选择为废旧聚苯乙烯泡沫塑料,使用的环己烯是一种低毒、价廉工业级溶剂,其原料来源广泛,具有制备工艺简单、价格低廉、附着力好、耐酸碱、不易退色及不污染环境的优点,是一种较理想的外墙涂料。
Description
技术领域:本发明涉及一种改性废旧聚苯乙烯泡沫塑料涂料,具体地说是一种建筑装修外墙用涂料。
背景技术:聚苯乙烯泡沫塑料(FPS)因质轻(0.01-0.05g/cm3)、无毒、低吸水性、耐酸碱、耐侯、绝热、防音、防震、容易成型而在仪器仪表、工业品、易损建材、食品包装等方面应用十分广泛,全球年消耗量达数百万吨。但由于这类材料质轻、体积大,在自然条件下一、二百年也不降解,造成严重的白色污染,破坏生态环境。目前其替代品由于生产工艺复杂、成本高等因素尚未得到广泛应用,
发明内容:本发明的目的是针对上述现有技术的不足,而提供一种利用废旧聚苯乙烯泡沫塑料改性加工而得到用于外墙的涂料。可有效解决废旧聚苯乙烯泡沫塑料的污染问题及可获得可观的经济效益。为实现上述目的,本发明采用下述技术方案:改性废旧聚苯乙烯泡沫塑料涂料,采用低毒、价廉工业级溶剂在常温下对废旧聚苯乙烯泡沫塑料充分溶解后做为基料,再加入乳化、分散剂,固体填料,体质颜料,增塑剂,防冻剂及颜料。本发明是由下述组分并按重量份额制得:其中废旧聚苯乙烯泡沫塑料14-20;环己烯60-80;乳化、分散剂十二烷基苯磺酸钠0.1-0.3及OP-10(化学纯)0.1-0.3;固体填料碳酸钙(工业品)10-20,滑石粉(工业品)4-8;体质颜料钛白粉(工业品)1-3;增塑剂邻苯二甲酸二丁酯(化学纯)1-3;防冻剂乙二醇或丙三醇(工业品)2-3;颜料(工业品)适量。
制备方法:
(1)将废旧聚苯乙烯泡沫塑料置于容器中,在常温下按上述比例加入环己烯溶剂,经充分溶解并搅拌均匀。
(2)在溶有废旧聚苯乙烯泡沫塑料的基料中按上述比例依次加入乳化、分散剂十二烷基苯磺酸钠及OP-10,固体填料碳酸钙、滑石粉,体质颜料钛白粉,增塑剂邻苯二甲酸二丁酯搅拌混合均匀。
(3)按上述比例加入防冻剂乙二醇或丙三醇及颜料搅拌混合均匀,制得涂料。
本发明由于原料的选择为废旧聚苯乙烯泡沫塑料,使用的环己烯是一种低毒、价廉工业级溶剂,其原料来源广泛,制备工艺简单,可有效解决废旧聚苯乙烯泡沫塑料对环境污染的问题,社会效益及经济效益十分可观。该涂料具有价格低廉、附着力好、耐酸碱、不易退色及不污染环境的优点,是一种较理想的外墙涂料。
具体实施方式:
实施例一
改性废旧聚苯乙烯泡沫塑料涂料,是由下述组分并按重量份额制得:废旧聚苯乙烯泡沫塑料14;环己烯(工业品)60;乳化、分散剂十二烷基苯磺酸钠(化学纯)0.1及OP-10(化学纯)0.1;固体填料碳酸钙(工业品)10,滑石粉(工业品)4;体质颜料钛白粉(工业品)1;增塑剂邻苯二甲酸二丁酯(化学纯)1;防冻剂乙二醇或丙三醇(工业品)2;颜料(工业品)适量。
制备方法:
(1)将废旧聚苯乙烯泡沫塑料置于容器中,在常温下按上述比例加入环己烯溶剂,经充分溶解并搅拌均匀。
(2)在溶有废旧聚苯乙烯泡沫塑料的基料中按上述比例依次加入乳化、分散剂十二烷基苯磺酸钠及OP-10,固体填料碳酸钙、滑石粉,体质颜料钛白粉,增塑剂邻苯二甲酸二丁酯搅拌混合均匀。
(3)上述比例加入防冻剂乙二醇或丙三醇及颜料搅拌混合均匀,制得涂料。
实施例二
改性废旧聚苯乙烯泡沫塑料涂料,是由下述组分并按重量份额制得:废旧聚苯乙烯泡沫塑料20;环己烯80;乳化、分散剂十二烷基苯磺酸钠0.3及OP-10(化学纯)0.3;固体填料碳酸钙(工业品)20,滑石粉(工业品)8;体质颜料钛白粉(工业品)3;增塑剂邻苯二甲酸二丁酯(化学纯)3;防冻剂乙二醇或丙三醇(工业品)3;颜料(工业品)适量。
其制备方法与实施例一相同。
实施例三
改性废旧聚苯乙烯泡沫塑料涂料,是由下述组分并按重量份额制得:废旧聚苯乙烯泡沫塑料17;环己烯70;乳化、分散剂十二烷基苯磺酸钠0.2及OP-10(化学纯)0.2;固体填料碳酸钙(工业品)15,滑石粉(工业品)6;体质颜料钛白粉(工业品)2;增塑剂邻苯二甲酸二丁酯(化学纯)2;防冻剂乙二醇或丙三醇(工业品)2.5;颜料(工业品)适量。
其制备方法与实施例一相同。
本发明可根据实际需要加入不同色彩的颜料,直接涂于建筑物的外墙。
Claims (5)
1、一种改性废旧聚苯乙烯泡沫塑料涂料,其特征在于:采用工业级环己烯为溶剂,在常温下对废旧聚苯乙烯泡沫塑料充分溶解后做为基料,再加入乳化、分散剂,固体填料,体质颜料,增塑剂,防冻剂及颜料,上述各组分按重量份额配制,废旧聚苯乙烯泡沫塑料14-20;环己烯60-80;乳化、分散剂十二烷基苯磺酸钠0.1-0.3及OP-10 0.1-0.3;固体填料碳酸钙10-20,滑石粉4-8;体质颜料钛白粉1-3;增塑剂邻苯二甲酸二丁酯1-3;防冻剂乙二醇或丙三醇2-3;颜料适量。
2、根据权利要求1所述的改性废旧聚苯乙烯泡沫塑料涂料,其特征在于:它是由下述组分并按重量份额制得,废旧聚苯乙烯泡沫塑料14;环己烯60;乳化、分散剂十二烷基苯磺酸钠0.1及OP-10 0.1;固体填料碳酸钙10,滑石粉4;体质颜料钛白粉1;增塑剂邻苯二甲酸二丁酯1;防冻剂乙二醇或丙三醇2;颜料适量。
3、根据权利要求1所述的改性废旧聚苯乙烯泡沫塑料涂料,其特征在于:它是由下述组分并按重量份额制得,废旧聚苯乙烯泡沫塑料20;环己烯80;乳化、分散剂十二烷基苯磺酸钠0.3及OP-10 0.3;固体填料碳酸钙20,滑石粉8;体质颜料钛白粉3;增塑剂邻苯二甲酸二丁酯3;防冻剂乙二醇或丙三醇3;颜料适量。
4、根据权利要求1所述的改性废旧聚苯乙烯泡沫塑料涂料,其特征在于:它是由下述组分并按重量份额制得,废旧聚苯乙烯泡沫塑料17;环己烯70;乳化、分散剂十二烷基苯磺酸钠0.2及OP-10 0.2;固体填料碳酸钙15,滑石粉6;体质颜料钛白粉2;增塑剂邻苯二甲酸二丁酯2;防冻剂乙二醇或丙三醇2.5;颜料适量。
5、制备如权利要求1-4中任意一项所述的改性废旧聚苯乙烯泡沫塑料涂料的方法,其特征在于:
(1)将废旧聚苯乙烯泡沫塑料置于容器中,在常温下按上述比例加入环己烯溶剂,经充分溶解并搅拌均匀;
(2)在溶有废旧聚苯乙烯泡沫塑料的基料中按上述比例依次加入乳化、分散剂十二烷基苯磺酸钠及OP-10,固体填料碳酸钙、滑石粉,体质颜料钛白粉,增塑剂邻苯二甲酸二丁酯搅拌混合均匀;
(3)按上述比例加入防冻剂乙二醇或丙三醇及颜料搅拌混合均匀,制得涂料。