CN1330387C - 磁性复合颗粒型血管栓塞材料 - Google Patents

磁性复合颗粒型血管栓塞材料 Download PDF

Info

Publication number
CN1330387C
CN1330387C CNB2005100182655A CN200510018265A CN1330387C CN 1330387 C CN1330387 C CN 1330387C CN B2005100182655 A CNB2005100182655 A CN B2005100182655A CN 200510018265 A CN200510018265 A CN 200510018265A CN 1330387 C CN1330387 C CN 1330387C
Authority
CN
China
Prior art keywords
magnetic
powder type
type vessel
embolizing material
shape memory
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2005100182655A
Other languages
English (en)
Other versions
CN1654090A (zh
Inventor
李世普
戴红莲
黄健
曹献英
黄福龙
王欣宇
韩颖超
贾莉
邵海成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan University of Technology WUT
Original Assignee
Wuhan University of Technology WUT
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan University of Technology WUT filed Critical Wuhan University of Technology WUT
Priority to CNB2005100182655A priority Critical patent/CN1330387C/zh
Publication of CN1654090A publication Critical patent/CN1654090A/zh
Application granted granted Critical
Publication of CN1330387C publication Critical patent/CN1330387C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种介入用血管栓塞材料。磁性复合颗粒型血管栓塞材料，其特征是它包括磁性颗粒(1)和形状记忆高分子材料(2)，各组份所占质量比为：20-40%磁性颗粒(1)、60-80%形状记忆高分子材料(2)，磁性颗粒(1)均匀分布在形状记忆高分子材料(2)中。本发明在血液中有良好的悬浮性；能方便观察栓塞部位；能有效的避免误栓；能进入病变部位能回复病变形状，达到紧密填塞，是一种使用效果理想的介入用血管栓塞材料。

Description

磁性复合颗粒型血管栓塞材料
技术领域
本发明涉及一种介入用血管栓塞材料，特别是微血管或末梢血管栓塞材料。
背景技术
现有技术中，已经有多种介入用血管栓塞材料，主要有固体栓塞材料，如自体血块、明胶海绵、止血剂和闭塞胶等可吸收性固体栓塞材料和微弹簧圈、可脱性球囊和微粒等不可吸收性固体栓塞材料；液态栓塞材料，如α-氰基丙烯酸正丁酯(NBCA)、次乙烯醇异分子聚合物(EVAL)、醋酸纤维素聚合物(CAP)。可吸收性固体栓塞材料一般只被用作术前栓塞和短期栓塞治疗，而且由于其本身透X线，需与造影剂混用，目前应用范围越来越小；弹簧圈昂贵的价格制约了使用；可脱性球囊置位的技术较为复杂，而且球囊充盈度难于控制；常用的PVA微粒在X光下不可见且易粘结微导管；液态栓塞材料操作难度大，易发生误栓。
发明内容
本发明的目的在于提供一种具有定向性、栓塞效果好、能在X光下显影的的磁性复合颗粒型血管栓塞材料。
为实现上述目的，本发明的技术方案是：磁性复合颗粒型血管栓塞材料，其特征是它包括磁性颗粒1和形状记忆高分子材料2，各组份所占质量比为：20-40％磁性颗粒1、60-80％形状记忆高分子材料2，磁性颗粒1均匀分布在形状记忆高分子材料2中。
所述的磁性颗粒1为钡铁氧体BaFe12O19、四氧化三铁Fe3O4、钴铁氧体CoxFe2-xO4、γ-三氧化二铁γ-Fe2O3等无机材料粉末造粒而成，能够在X光下显影。
所述的形状记忆高分子材料2为具有形状记忆功能的聚氨酯、交联聚乙烯、反式聚异戊二烯、聚苯乙烯等，其形状回复温度为体温接近(为36℃-38℃)。
本发明采用磁性颗粒均匀分布在形状记忆高分子材料中，通过调整磁性材料与形状记忆高分子材料的质量比，使比重可调，其比重和人体血液的比重接近(为1.1-1.5)，或磁性复合颗粒型血管栓塞材料的比重与微导管注射用生理盐水或葡萄糖的比重接近(1.1-1.5)，从而使其在血液中有良好的悬浮性；磁性材料不透X光，能方便观察栓塞部位；能在一定强度外加磁场作用下定向运动，通过控制外加磁场，可以更好的导向栓塞材料，有效的避免误栓；所选取的高分子材料具有形状记忆功能，结合血管造影技术根据病灶在体外预制出合适大小和形状的记忆体，进入病变部位能回复病变形状，达到紧密填塞，是一种使用效果理想的介入用血管栓塞材料。
附图说明
图1是本发明的结构示意图；
图2是本发明的工作原理图；
图中：1为磁性颗粒，2为形状记忆高分子材料，3为磁性复合颗粒型血管栓塞材料，4为微导管，5为血管。
具体实施方式
实施例1：
磁性复合颗粒型血管栓塞材料，由钡铁氧体(BaFe12O19)颗粒和颗粒直径为1～100μm的聚氨酯组成，各组份所占质量比为：钡铁氧体(BaFe12O19)颗粒30％、聚氨酯70％，钡铁氧体颗粒均匀分布在聚氨酯中；磁性复合颗粒型血管栓塞材料的比重为1.35。
上述磁性复合颗粒型血管栓塞材料的制备方法：选用颗粒直径为1～100μm的聚氨酯，掺入占质量比30％的钡铁氧体颗粒，混合搅拌后，在模具中冷压，烧结后形成能在血液中悬浮的颗粒状结构，颗粒的直径为100μm～1000μm，根据临床的不同要求，筛分成不同规格，即得到磁性复合颗粒型血管栓塞材料。
临床使用时，根据要堵塞的血管大小及病变部位，选择颗粒直径合适的本发明磁性复合颗粒型血管栓塞材料。在介入手术中，通过微导管4将本发明之磁性复合颗粒型血管栓塞材料3注入要堵塞的血管5中，诱导血栓形成最终堵住目标血管。
实施例2：
磁性复合颗粒型血管栓塞材料，由四氧化三铁颗粒和颗粒直径为1～100μm的聚氨酯组成，各组份所占质量比为：四氧化三铁颗粒20％、聚氨酯80％，四氧化三铁颗粒均匀分布在聚氨酯中；磁性复合颗粒型血管栓塞材料的比重为1.1。
上述磁性复合颗粒型血管栓塞材料的制备方法：选用颗粒直径为1～100μm的聚氨酯，掺入占质量比20％的四氧化三铁颗粒，混合搅拌后，在模具中冷压，烧结后形成能在血液中悬浮的颗粒状结构，颗粒的直径为100μm～1000μm，根据临床的不同要求，筛分成不同规格，即得到磁性复合颗粒型血管栓塞材料。
实例3：
磁性复合颗粒型血管栓塞材料，由钡铁氧体颗粒和颗粒直径为1～100μm的反式聚异戊二烯组成，各组份所占质量比为：钡铁氧体颗粒40％、反式聚异戊二烯60％，钡铁氧体颗粒均匀分布在反式聚异戊二烯中；磁性复合颗粒型血管栓塞材料的比重为1.26。
上述磁性复合颗粒型血管栓塞材料的制备方法：选用颗粒直径为1～100μm的反式聚异戊二烯，掺入占质量比40％的钡铁氧体颗粒，混合搅拌后，在模具中冷压，烧结后形成能在血液中悬浮的颗粒状结构，颗粒的直径为100μm～1000μm，根据临床的不同要求，筛分成不同规格，即得到磁性复合颗粒型血管栓塞材料。
实例4：
磁性复合颗粒型血管栓塞材料，由钴铁氧体颗粒和颗粒直径为1～100μm的交联聚乙烯组成，各组份所占质量比为：钴铁氧体颗粒25％、交联聚乙烯75％，钴铁氧体颗粒均匀分布在交联聚乙烯中。
上述磁性复合颗粒型血管栓塞材料的制备方法：选用颗粒直径为1～100μm的交联聚乙烯，掺入占质量比25％的钴铁氧体颗粒，混合搅拌后，在模具中冷压，烧结后形成能在血液中悬浮的颗粒状结构，颗粒的直径为100μm～1000μm，根据临床的不同要求，筛分成不同规格，即得到磁性复合颗粒型血管栓塞材料。
实例5：
磁性复合颗粒型血管栓塞材料，由γ-三氧化二铁颗粒和颗粒直径为1～100μm的聚苯乙烯组成，各组份所占质量比为：γ-三氧化二铁颗粒35％、聚苯乙烯65％，γ-三氧化二铁颗粒均匀分布在聚苯乙烯中。
上述磁性复合颗粒型血管栓塞材料的制备方法：选用颗粒直径为1～100μm的聚苯乙烯，掺入占质量比35％的γ-三氧化二铁颗粒，混合搅拌后，在模具中冷压，烧结后形成能在血液中悬浮的颗粒状结构，颗粒的直径为100μm～1000μm，根据临床的不同要求，筛分成不同规格，即得到磁性复合颗粒型血管栓塞材料。

Claims (3)

1.磁性复合颗粒型血管栓塞材料，其特征是它包括磁性颗粒(1)和形状记忆高分子材料(2)，各组份所占质量比为：20-40％磁性颗粒(1)、60-80％形状记忆高分子材料(2)，磁性颗粒(1)均匀分布在形状记忆高分子材料(2)中。
2.根据权利要求1所述磁性复合颗粒型血管栓塞材料，其特征是：所述的磁性颗粒(1)为钡铁氧体、四氧化三铁、钴铁氧体或γ-三氧化二铁颗粒。
3.根据权利要求1所述磁性复合颗粒型血管栓塞材料，其特征是：所述的形状记忆高分子材料(2)为具有形状记忆功能的聚氨酯、交联聚乙烯、反式聚异戊二烯或聚苯乙烯，其形状回复温度为36℃-38℃。
CNB2005100182655A 2005-02-07 2005-02-07 磁性复合颗粒型血管栓塞材料 Expired - Fee Related CN1330387C (zh)