CN1314634C - 单质炸药降静电处理方法 - Google Patents
单质炸药降静电处理方法 Download PDFInfo
- Publication number
- CN1314634C CN1314634C CNB200410064666XA CN200410064666A CN1314634C CN 1314634 C CN1314634 C CN 1314634C CN B200410064666X A CNB200410064666X A CN B200410064666XA CN 200410064666 A CN200410064666 A CN 200410064666A CN 1314634 C CN1314634 C CN 1314634C
- Authority
- CN
- China
- Prior art keywords
- explosive
- static electricity
- processing method
- compound explosive
- reducing processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种单质炸药降静电处理方法。其步骤是将溶剂与衣物柔顺剂BKD或HKD系列抗静电剂混合形成稀溶液，并将此溶液加入到单质炸药中，单质炸药在溶液中经历悬浮浸润过程，达到充分浸润吸附后，经抽滤除去多余溶液，形成的湿态炸药经干燥即得在颗粒表面具有包覆层的抗静电炸药。本发明可使单质炸药静电积累显著降低，流散性提高，有助于提高炸药抵抗外界危害的能力，保证产品质量和提高生产效率，在导爆索的生产中，可克服装药的不稳定性，避免以往时常发生的断药、少药、下药难等问题；而在雷管的生产中，能消除浮药和保证定容装药精度，产品性能和质量也将进一步提高。
Description
一技术领域
本发明涉及一种单质炸药表面处理方法，特别是一种单质炸药降静电处理方法。
二背景技术
单质炸药以其特有作功能力和猛度，广泛应用于军民领域。但是，炸药又是一类不导电物质，电阻率范围在4×1010～5×1013Ω·cm，因而在运动摩擦过程中易产生静电和积累静电，尤其在其干燥、筛选和包装工序，其静电电压可高达5～6万伏，而静电放电火花将会引起炸药的燃烧和爆炸，显然这是重大恶性事故的隐患之一，是潜在的危险因素。同时，单质炸药中存在有一定量的粉尘，致使颗粒间阻力增大，外界的机械挤压、摩擦、碰撞作用很容易引发爆炸反应。历年来由这类危害而导致爆破器材厂的技安事故屡见不鲜。因此，消除静电危害和改善药剂表面性能的措施是当前一项刻不容缓的重要课题。
三发明内容
本发明的目的在于提供一种能显著降低炸药的静电积累，提高炸药流散性及稳定性以及安全性的单质炸药降静电处理方法。
实现本发明目的的技术解决方案为：一种单质炸药降静电处理方法，其步骤是：将溶剂与衣物柔顺剂BKD或HKD系列抗静电剂混合形成稀溶液，并将此溶液加入到单质炸药中，单质炸药在溶液中经历悬浮浸润过程，达到充分浸润吸附后，经抽滤除去多余溶液，形成的湿态炸药经干燥即得在颗粒表面具有包覆层的抗静电炸药。
本发明利用静电剂所含基团的自身离子化传导表面电荷，来降低处理后炸药的表面电阻和体积电阻，并适度增加导电性，从而防止静电积累而发挥抗静电效能；同时，依靠吸附包覆和团聚作用，能促使微小颗粒间的相互团聚而减少药剂微粉度。选用的抗静电剂是外部型抗静电剂BKD或HKD，一般用水或乙醇作溶剂配成质量浓度为3‰～5‰的溶液，按液料质量比1～2.5∶1的量，利用炸药制备工艺中的抽滤器，对炸药进行浸润，温度为室温，浸润时间为10分钟～15分钟。随后真空抽滤，并干燥脱离除去溶剂，干燥条件：真空度0.06MPa以上、柜温50℃～70℃、时间5h～9h。
本发明与现有技术相比，其显著优点是：静电积累显著降低，流散性提高，有助于提高炸药抵抗外界危害的能力，保证产品质量和提高生产效率，在导爆索的生产中，可克服装药的不稳定性，避免以往时常发生的断药、少药、下药难等问题；而在雷管的生产中，能消除浮药和保证定容装药精度。
典型处理样品的性能改善实测值列于下表：
经表面处理后，太安的静电积累下降了83％，流散性则有所提高。其它的理化性能均符合GJB552-88《太安》的要求。经拉制导爆索和装配工程雷管，产品性能分别符合GB9786-88《普通导爆索》和GB13230-91《工业火雷管》标准。
四附图说明
附图为本发明的单质炸药降静电处理方法的流程图示意图。
五具体实施方式
实施例1：利用干净的结晶机准确计量400L水，加入2000mL BKD搅拌3分钟，配制成质量浓度为5‰的抗静电剂水溶液。把称量好的200kg的干品太安，加入过滤器内并扒平，然后缓慢放入质量浓度为5‰的抗静电剂水溶液，边放边搅拌，保证水溶液浸过干品药10cm，浸泡10～12分钟后，用真空抽滤除去水溶液，出料送往干燥工房，进行干燥，即得在颗粒表面具有包覆层的抗静电太安炸药。
实施例2：将过滤器内洗涤抽滤过两次的湿品精制太安(含水量15％以下)的，用预先配制好的质量浓度为5‰的降静电剂BKD水溶液浸泡10～12分钟后，溶液量按太安制备产量(理论)的2倍投入。期间要拉动滤布，使原先的湿品太安疏松分散，再抽滤至含水量15％以下即可送往干燥工房进行干燥，即得在颗粒表面具有包覆层的抗静电太安炸药。
实施例3：在铝制水槽内铺设好滤布，再将100kg纯水倒入水槽；同时称300gHKD抗静电剂，溶解于纯水中，形成质量浓度为3‰的处理液。称取干品太安40kg，缓缓倒入处理液中，并施以必要的搅拌，保证药剂全部浸润湿透；12分钟后提出滤袋和药剂，置于抽滤器内，真空下抽干；最后送入烘房干燥。
Claims (7)
1.一种单质炸药降静电处理方法，其特征在于：将溶剂与衣物柔顺剂BKD或HKD系列抗静电剂混合形成稀溶液，并将此溶液加入到单质炸药中，单质炸药在溶液中经历悬浮浸润过程，达到充分浸润吸附后，经抽滤除去多余溶液，形成的湿态炸药经干燥即得在颗粒表面具有包覆层的抗静电炸药。
2.根据权利要求1所述的单质炸药降静电处理方法，其特征在于：所述的单质炸药为太安、黑索今、奥克托今。
3.根据权利要求1或2所述的单质炸药降静电处理方法，其特征在于：单质炸药与溶液得料液比按质量计为1～2.5∶1。
4.根据权利要求1或2所述的单质炸药降静电处理方法，其特征在于：抗静电剂为与单质炸药不发生化学反应的水溶性或醇溶性抗静电剂，pH值近于中性。
5.根据权利要求1所述的单质炸药降静电处理方法，其特征在于：药剂浸润溶液中所用抗静电剂质量浓度小于8‰。
6.根据权利要求1或2所述的单质炸药降静电处理方法，其特征在于：溶剂为水或乙醇溶液。
7.根据权利要求1或6所述的单质炸药降静电处理方法，其特征在于：浸润温度为室温，浸润时间不超过20分钟。