CN1306284A - 一种耐高温超薄导线的制造方法及产品 - Google Patents
一种耐高温超薄导线的制造方法及产品 Download PDFInfo
- Publication number
- CN1306284A CN1306284A CN 00100301 CN00100301A CN1306284A CN 1306284 A CN1306284 A CN 1306284A CN 00100301 CN00100301 CN 00100301 CN 00100301 A CN00100301 A CN 00100301A CN 1306284 A CN1306284 A CN 1306284A
- Authority
- CN
- China
- Prior art keywords
- high temperature
- temperature resistant
- thin
- ultra
- insulating barrier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种耐高温超薄导线的制造方法及产品,它是选用聚乙烯(100)、交联剂1,3-双(叔丁基过氧异丙基)苯(5-10)、阻燃剂(20-50)、抗氧剂(5-10),光稳定剂三(1,2,2’,6,6’-五甲基呱啶基)亚磷(5-20),经混合造粒制成导线的绝缘层,然后用电子加速器对导线的绝缘层进行辐照交联处理;用本发明方法制成的导线可在150℃的高温条件下长期工作,并且耐油、阻燃、耐磨、柔软。
Description
本发明涉及一种耐高温超薄导线的制造方法及产品。
目前,超薄导线的长期工作温度大都不超过130℃,超过这个温度导线的绝缘塑料层往往很快老化,甚至起火。从而限制了导线的负荷。如果想通过更大的负荷,那只有增加导线金属芯的横截面,这样将使导线外径增大及重量增加,从而导致布线空间增大及影响导线长期使用等。
本发明的目的在于改进现有技术的缺点,而提供一种耐高温超薄导线的制造方法及产品。
为实现上述发明目的本发明采用以下设计方法,首先它是选用下列组分(重量比)经混合造粒挤出制成导线的绝缘层,
聚乙烯 100 交联剂1,3-双(叔丁 5-10
基过氧异丙基)苯
阻燃剂 20-50 抗氧剂 5-10
光稳定剂三(1,2,2’,6,6’ 5-20
-五甲基呱啶基)亚磷
其次,把制线金属拨丝、绞线并与上述颗粒按超薄绝缘层挤出工艺制成导线;
第三步,用电子加速器对所述制成的导线绝缘层进行辐照交联处理,辐照剂量50-250kGy,辐照能量:0.5-3.0Mev,辐照方式:平行“8字”方式工艺或者交叉“8字”方式工艺。
用上述材料制成的导线绝缘层经电子加速器进行辐照交联处理后,其绝缘层分子结构发生了变化,可提高导线的长期工作温度在150℃。按上述方法制成的导线,如需要可在绝缘层外用超薄挤出工艺制一层与绝缘材料一样的护套层,其并与绝缘层一起进行电子加速器辐照交联处理。当然绝缘层用电子加速器进行辐照交联处理后,亦可用超薄挤出工艺制一层氟塑料护套层。在上述造粒组分中,交联剂选用的是1,3-双(叔丁基过氧异丙基)苯;阻燃剂可选用的是氢氧化铝、氢氧化镁或者十溴二苯醚;抗氧剂可选用的是:四-(4-羟基-3,5-特丁基苯基丙酸)季戊四醇酯(抗氧剂1010)、3,5-二特丁基-4-羟基苯丙酸十八酯(抗氧剂1076)、1,1,3-三(乙-甲基-4羟基-5-特丁基苯基)丁烷(抗氧剂CA);光稳定剂选用的是三(1,2,2’,6,6’-五甲基呱啶基)亚磷。
用本发明方法制出的导线绝缘层或者绝缘层与护套层一起构成的包复层的厚度在0.1mm-0.8mm之间,可长期工作在150℃的高温条件下,其机械性能为:
绝缘层老化前抗张强度≥10兆帕,
绝缘层老化前断裂伸长率≥150%。
经空气烘箱老化168小时,老化温度≥178℃±2℃,老化前后抗张强度变化率≤±30%,
老化前后断裂伸长率变化率≤±30%。
本发明产品还耐油、阻燃、耐磨、柔软。
实施例1
首先选用下列组份(重量比)经混合造粒挤出制成导线的绝缘层
聚乙烯 100 1,3-双(叔丁基过氧异 5
丙基)苯
氢氧化铝 35 抗氧剂1010 10
三(1,2,2’,6,6’-五甲 5
基呱啶基)亚磷
其次,把制线金属拔丝、绞线并与上述颗粒按照超薄绝缘层挤出工艺制成导线;
第三步用电子加速器对所述的导线绝缘层进行辐照交联处理;其辐照剂量是50KGy,辐照能量3.0Mev,采用平行“8字”辐照方式工艺。
实施例2
首先选用下列组份(重量比)经混合造粒挤出制成导线的绝缘层
聚乙烯 100 1,3-双(叔丁基过 8
氧异丙基)苯
氢氧化镁 50 抗氧剂1076 5
三(1,2,2’,6,6’-五甲 10
基呱啶基)亚磷
其次,把制线金属拔丝、绞线并与上述颗粒按照超薄绝缘层挤出工艺制成导线;然后在绝缘层外再用超薄挤出工艺制一层与绝缘材料一样的护套层。
第三步用电子加速器对所述的导线绝缘层和护套层进行辐照交联处理;其辐照剂量是150KGy,辐照能量2.0Mev,采用交叉“8字”辐照方式工艺。
实施例3
首先选用下列组份(重量比)经混合造粒挤出制成导线的绝缘层
聚乙烯 100 1,3-双(叔丁基过氧 10
异丙基)苯
十溴二苯醚 20 抗氧剂CA 8
三(1,2,2’,6,6’-五 20
甲基呱啶基)亚磷
其次,把制线金属拔丝、绞线并与上述颗粒按照超薄绝缘层挤出工艺制成导线;
第三步用电子加速器对所述的导线绝缘层进行辐照交联处理;其辐照剂量是250KGy,辐照能量0.5Mev,采用平行“8字”辐照方式工艺。
第四步在绝缘层外再用超薄挤出工艺制一层氟塑料护套层。
Claims (10)
1、一种耐高温超薄导线的制造方法,其特征在于:
(1)它是由下列组分(重量比)混合造粒挤出制成导线的绝缘层,
聚乙烯 100 1,3-双(叔丁基过 5-10
氧异丙基)苯
阻燃剂 20-50 抗氧剂 5-10
三(1,2,2’,6,6’-五 5-20
甲基呱啶基)亚磷
(2)制线金属经拔丝、绞线并与上述颗粒按超薄绝缘层挤出工艺制成导线;
(3)用电子加速器对导线绝缘层进行辐照交联处理,辐照剂量50-250kGy,辐照能量:0.5-3.0Mev,辐照方式:平行“8字”方式工艺或者交叉“8字”方式工艺。
2、根据权利要求1所述的一种耐高温超薄导线的制造方法,其特征在于:所述的交联剂量是1,3-双(叔丁基过氧异丙基)苯。
3、根据权利要求1所述的一种耐高温超薄导线的制造方法,其特征在于:所述的阻燃剂量是氢氧化铝、氢氧化镁或者十溴二苯醚。
4、根据权利要求1所述的一种耐高温超薄导线的制造方法,其特征在于:所述的抗氧剂量是四-(4-羟基-3,5-特丁基苯基丙酸)季戊四醇酯(抗氧剂1010)、3,5-二特丁基-4-羟基苯丙酸十八酯(抗氧剂1076)、1,1,3-三(乙-甲基-4羟基-5-特丁基苯基)丁烷(抗氧剂CA)。
5、根据权利要求1所述的一种耐高温超薄导线的制造方法,其特征在于:所述的光稳定剂量是三(1,2,2’,6,6’-五甲基呱啶基)亚磷。
6、根据权利要求1所述的一种耐高温超薄导线的制造方法,其特征在于:在导线绝缘层外用超薄挤出工艺在绝缘层外制一层与绝缘层材料一样的护套层,其并与绝缘层一起进行电子加速器辐照交联处理。
7、根据权利要求1所述的一种耐高温超薄导线的制造方法,其特征在于:导线绝缘层外用超薄挤出工艺制一层氟塑料护套层。
8、一种耐高温超薄导线,其特征在于:由聚乙烯、交联剂、阻燃剂、抗氧剂、光稳定剂制成的绝缘层是经电子加速器进行辐照交联处理而成的。
9、根据权利要求8所述的一种耐高温超薄导线,其特征在于:导线的绝缘层外有一与绝缘层材料一样的用电子加速器进行辐照交联处理的护套层。
10、根据权利要求8所述的一种耐高温超薄导线,其特征在于:在导线的绝缘层外有一氟塑料制成的护套层。