CN1297620C - 光滑砖石表面防滑增强剂及其制备方法 - Google Patents
光滑砖石表面防滑增强剂及其制备方法 Download PDFInfo
- Publication number
- CN1297620C CN1297620C CNB2005100434660A CN200510043466A CN1297620C CN 1297620 C CN1297620 C CN 1297620C CN B2005100434660 A CNB2005100434660 A CN B2005100434660A CN 200510043466 A CN200510043466 A CN 200510043466A CN 1297620 C CN1297620 C CN 1297620C
- Authority
- CN
- China
- Prior art keywords
- skid
- intensifier
- brick masonry
- masonry surface
- smooth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供一种光滑砖石表面防滑增强剂,该防滑增强剂含有如下按质量份配比的组分:有机硅10-20、渗透剂0.2-0.6、表面活性剂0.1-0.4、PF阳离子聚电解质0.4-0.8、水79-89。该防滑增强剂的制备方法是在合成釜中加入有机硅、渗透剂、表面活性剂并拌匀,后加入纯净水,继续搅拌至无色透明时再加入PF阳离子聚电解质,混匀静放而成。经过使用本发明所述的防滑增强剂之后,在不改变光滑外观的前提下不仅透气、憎水、防渗、抗冻融增强,而且还具有明显的防滑效果。
Description
技术领域
本发明涉及一种用于光滑砖石表面防滑、增强反应型有机硅复合处理剂及其制备方法。
技术背景
在现代建筑工程、市政建设和室内装修中,由于光滑的建筑材料的美观、耐用被广泛用于道路、室内路面装修等各种建设领域的地面铺设。但是由于光滑的表面见水后表面摩擦阻力减小,人容易被滑倒,由于滑倒受伤而引起的诉讼、纠纷、赔偿和损失每年也在不断增加。决定防滑程度的指标为摩擦系数(COF),这个指标的范围是从0至1。根据美国ASTM和UL、OSHA标准,地板表面的摩擦系数0.5以上为安全系数,低于0.5的,将有引致滑倒摔伤的危险。一般的未处理的瓷砖或大理石花岗岩等材料干燥表面摩擦系数在0.3-0.4之间,沾水后的潮湿表面则低至0.2,在这样未处理材料的湿表面上行走是极度危险的。
本发明利用有机硅、PF阳离子聚电解质、渗透剂、表面活性剂,使有机硅单体吸附在聚合物表面,使极性基的Si-O-键吸附在水中,而R-键伸向憎水表面,首先在砖石表面形成一种物理吸附,经过24小时,逐渐形成一种网状的具有刚性的化学吸附膜。这种膜是反应型的,抗水透气、耐侯耐老化,改善了砖石原有的表面物理性质,而且由于有机硅和阳离子电解质的共同作用,改变了砖石表面的电负性。见水不滑,而且吸水率降低,因此抗冻融性能变好,强度增加。
光滑的粘土砖石表面的防滑处理一般是通过烧制的办法,中国专利89103796,公开了“防滑耐磨陶瓷及模具的烧制”它是用烧制的方法解决防滑问题,对花岗岩这种自然形成的岩石无能为力。
对砖石表面的下雨天防滑的处理,中国专利99124995.X是由塑性化天然橡胶、合成橡胶、酯化松香、石油树脂制成喷雾剂,在冬季及雨雪天气喷洒在路面上以备防滑。
中国专利01111447.9和93110910.8使用无机酸和有机酸及表面活性剂等物质处理表面,使表面强度增加。
以上专利提供的技术,没有采用相应措施使光滑砖石表面通过化学反应改变砖石表面电负性,在砖石表面不改变外观的前提下,见水时不滑并使砖石表面的抗冻融性能变好。
发明内容:
本发明的目的之一是克服上述现有技术存在的缺陷,提供一种可使光滑砖石表面通过化学反应改变砖石表面电负性,在砖石表面不改变外观的前提下,见水时不滑并使砖石表面的抗冻融性能变好的光滑砖石表面防滑增强剂;目的之二是提供该光滑砖石表面防滑增强剂的制备方法。
本发明的目的之一可通过以下技术措施来实现:
该光滑砖石表面防滑增强剂含有如下按质量份配比的组分
有机硅 10-20
渗透剂 0.2-0.6
表面活性剂 0.1-0.4
PF阳离子聚电解质 0.4-0.8
水 79-89。
本发明的目的之一还可以通过如下技术措施来实现:
所述的有机硅是二甲基硅醇盐、甲基硅醇盐、二乙基硅醇盐或乙基硅醇盐;所述的硅醇盐是钠盐或钾盐;所述的渗透剂是磺化琥珀酸二辛酯钠盐或脂肪醇聚氧乙烯醚磷酸酯;所述的表面活性剂是聚氧乙烯失水山梨醇酐油酸酯、聚氧乙烯失水山梨醇酐棕榈酸酯或全氟醇聚氧乙烯醚;所述的水是纯净水。所述的PF阳离子聚电解质是指按照由山东省技术监督局批准备案的标准(标准号Q/SYZ003-93,备案号3700G285-93)进行生产和销售的市销品。所述的水是纯净水。
本发明的目的之二可通过以下技术措施来实现:
该光滑砖石表面防滑增强剂的制备方法是在合成釜中加入有机硅、渗透剂、表面活性剂并拌匀,后加入纯净水,继续搅拌至无色透明时再加入PF阳离子聚电解质,混匀静放而成。
根据需要把光滑砖石表面防滑增强处理剂配成5%、10%的水溶液使用,也可以直接刷涂表面或用喷雾器直接喷洒。
化学反应型的有机硅,PF阳离子聚电解质,渗透剂,表面活性剂和水组成的无色透明的水溶液,使用方便,可以做成喷剂使用,直接喷到需处理的光滑表面,24小时之后便可使用。由于防渗水,所以在冬天不会因为水的结冰而冻融影响光滑表面的强度。
本发明用于光滑的花岗岩表面,烧制的光滑的粘土硅表面,经过使用本发明的防滑增强剂之后,在不改变光滑外观的前提下不仅透气、憎水、防渗、抗冻融增强,而且还具有明显的防滑效果。
该发明具有如下优点:
1.该剂形成的表面是均匀的表面且渗透至砖石表面1-2mm处,24小时后且可使用。
2.由于本发明应用的砖、石表面主要是带负电的,所用的有机硅、PF阳离子聚电解质、表面活性剂、渗透剂与砖石表面形成化学吸附层,经过24小时逐渐形成一种网状的具有刚性的化学吸附膜,该种膜是反应型的。透气、防渗,防滑。所以在冬季不会因水渗到砖石里后冻融引起的强度降低。经过济南大学建筑材料质量检测中心检测(检测号:NO.A30-FHJ-001)依据标准GB/T9966.1.2.3.-2001、Q/syH001-2003.对花岗岩检测。
性能 | 未经处理 | 处理后 | 注明 |
摩擦系数 | -0.23 | >0.78 | 小于0.5滑大于0.5不滑 |
吸水率(%) | - | 降低30% | |
冻融强度(Mpa) | - | 124.6 |
具体实施方式:
实施例1:
组分 配比
二甲基硅醇钠 15
磺化琥珀酸二辛酯钠盐 0.3
聚氧乙烯失水山梨醇酐油酸酯 0.2
PF阳离子聚电解质 0.5
水 84。
实施例2:
组分 配比
甲基硅醇钠 10
脂肪醇聚氧乙烯醚磷酸酯 0.6
聚氧乙烯失水山梨醇酐油酸酯 0.1
PF阳离子聚电解质 0.8
纯净水 79。
实施例3、
组分 配比
二乙基硅醇钠 20
磺化琥珀酸二辛酯钠盐 0.2
聚氧乙烯失水山梨醇酐油酸酯 0.4
PF阳离子聚电解质 0.4
纯净水 89。
实施例4:
组分 配比
乙基硅醇钾 12
磺化琥珀酸二辛酯钠盐 0.5
聚氧乙烯失水山梨醇酐棕榈酸酯 0.3
PF阳离子聚电解质 0.6
纯净水 80。
实施例5:
组分 配比
二甲基硅醇钾 18
磺化琥珀酸二辛酯钠盐 0.4
聚氧乙烯失水山梨醇酐油酸酯 0.1
PF阳离子聚电解质 0.7
水 85。
实施例6:
组分 配比
甲基硅醇钾 16
磺化琥珀酸二辛酯钠盐 0.6
聚氧乙烯失水山梨醇酐棕榈酸酯 0.2
PF阳离子聚电解质 0.5
纯净水 82。
实施例7:
组分 配比
二乙基硅醇钠 13
脂肪醇聚氧乙烯醚磷酸酯 0.3
全氟醇聚氧乙烯醚 0.1
PF阳离子聚电解质 0.4
纯净水 81。
实施例8:
组分 配比
乙基硅醇钾 17
磺化琥珀酸二辛酯钠盐 0.5
全氟醇聚氧乙烯醚 0.4
PF阳离子聚电解质 0.7
纯净水 84。
实施例9:
组分 配比
甲基硅醇钾 11
脂肪醇聚氧乙烯醚磷酸酯 0.5
全氟醇聚氧乙烯醚 0.3
PF阳离子聚电解质 0.6
水 87。
Claims (6)
1、光滑砖石表面防滑增强剂,其特征在于它含有如下按质量份配比的组分:
有机硅 10-20
渗透剂 0.2-0.6
表面活性剂 0.1-0.4
PF阳离子聚电解质 0.4-0.8
水 79-89
所述的有机硅是二甲基硅醇盐、甲基硅醇盐、二乙基硅醇盐或乙基硅醇盐。
2、根据权利要求1所述的光滑砖石表面防滑增强剂,其特征在于所述的硅醇盐是钠盐或钾盐。
3、根据权利要求1所述的光滑砖石表面防滑增强剂,其特征在于所述的渗透剂是磺化琥珀酸二辛酯钠盐或脂肪醇聚氧乙烯醚磷酸酯。
4、根据权利要求1所述的光滑砖石表面防滑增强剂,其特征在于所述的表面活性剂是聚氧乙烯失水山梨醇酐油酸酯、聚氧乙烯失水山梨醇酐棕榈酸酯或全氟醇聚氧乙烯醚。
5、根据权利要求1所述的光滑砖石表面防滑增强剂,其特征在于所述的水是纯净水。
6、权利要求1的光滑砖石表面防滑增强剂的制备方法,其特征在于在合成釜中加入有机硅、渗透剂、表面活性剂并拌匀,后加入纯净水,继续搅拌至无色透明时再加入PF阳离子聚电解质,混匀静放而成。