CN1282796A - 金属陶瓷复合材料制造方法 - Google Patents

金属陶瓷复合材料制造方法 Download PDF

Info

Publication number
CN1282796A
CN1282796A CN 00105257 CN00105257A CN1282796A CN 1282796 A CN1282796 A CN 1282796A CN 00105257 CN00105257 CN 00105257 CN 00105257 A CN00105257 A CN 00105257A CN 1282796 A CN1282796 A CN 1282796A
Authority
CN
China
Prior art keywords
metal
pottery
ceramic
hour
hour speed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 00105257
Other languages
English (en)
Inventor
王晏晨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 00105257 priority Critical patent/CN1282796A/zh
Publication of CN1282796A publication Critical patent/CN1282796A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种金属与陶瓷的复合方法,它把素烧陶瓷和金属一起进行二次烧制而成。金属陶瓷复合材料,具有陶瓷材料的坚硬、耐磨、耐腐蚀之特性,又比普通陶瓷的延展性能好,更易进行机械加工;并且,金属陶瓷复合材料热稳定性能优良,热膨胀系数小。它可以在机械、建筑、化工等领域替代特殊金属材料,取得良好的经济效益。本发明方法与陶瓷烧制工艺基本相同,有成熟的工业化生产基础。

Description

金属陶瓷复合材料制造方法
本发明涉及金属与陶瓷合成为金属陶瓷复合材料的制造方法，尤其是熔点比陶瓷烧结温度低的金属与陶瓷的合成之制造方法。
陶瓷材料硬度高、耐磨、耐腐蚀，但延展性能差，不易进行机械加工。而金属材料具有良好的延展性能和机械加工性能。将陶瓷与金属材料复合，使之兼备两者的优点：具有比陶瓷的机械加工性能好，又比普通金属硬度高、更耐磨的良好特性。
本发明的目的就是，提供一种金属陶瓷复合材料的制造方法，使这种材料既有陶瓷般硬度与耐磨性能，又比陶瓷更易进行机械加工。
本发明采用的方法是，先将瓷土制成工件，素烧成陶瓷，(素烧是指陶瓷不施釉烧制)，然后将陶瓷工件与金属一起再次装进匣钵进行二次烧制。烧制时，先以100～150℃／小时的速度升温至950℃左右；再以80～120℃／小时的升温速度加热，达到陶瓷的烧成温度1100～1400℃后，保温几个小时，让熔解后的高温金属分子，向陶瓷内部扩散。扩散结束后，以150～300℃／小时的速度降温，在冷却至接近金属熔点时，排出匣钵中的残余金属溶液，再以40～100℃／小时的速度降至室温，即成金属陶瓷复合材料。
本发明方法实施的金属陶瓷复合材料，其内部晶粒被金属氧化，晶粒之间的联系既有陶瓷又有金属。因而它既有陶瓷材料硬度高、耐磨、耐腐蚀的特性；又比陶瓷更易进行机械加工，比金属材料的热形变小。本发明方法与陶瓷烧制工艺相似，无特殊技术要求，便于工业化。金属陶瓷复合材料能在机械、建筑、化工等许多领域推广应用。
本发明方法的一种以铝与长石质瓷合成为铝陶瓷复合材料的具体实施方案如下：先将瓷土制成工件，(假定工件厚度在10mm以下)，素烧成瓷，然后再将瓷工件装进匣钵，并在匣钵中加入铝碎沫，进行二次烧制。瓷工件要与钵底固定，使在铝熔解后瓷工件不会浮出金属溶液表面。在隧道窖中烧制时，先以100～150℃／小时的速度升温，950℃以后，以80～120℃／小时速度升温，达到陶瓷烧成温度1250～1400℃后，保温1～3小时，让金属分子充分向瓷体内部扩散。对于厚度大的工件，高温持续时间要长些。950℃以上的铝溶液分子，每小时可以向陶瓷深度扩散1～2毫米左右。扩散完成后，以150～300℃／小时的速度冷却至800℃左右，(铝熔点660℃)，排出匣钵中残余的铝溶液，最后以40～100℃／小时的速度降至室温，即成铝陶瓷复合材料工件。

Claims (3)

  1. (1)，一种将金属与陶瓷合成为金属陶瓷复合材料的制造方法，其特征在于：它将陶瓷与金属一起装钵进行二次烧制，使陶瓷浸在金属溶液中，让金属分子向陶瓷内部热扩散而成金属陶瓷复合材料。
  2. (2)，根据权利要求(1)所述的发明方法，其特征在于：将金属与陶瓷一起加热时，先以100～150℃／小时的速度升温至950℃左右，再以80～120℃／小时的速度升温至陶瓷烧成温度1100～1400℃；保温几个小时后，再以150～300℃／小时的降温速度冷却至接近金属熔点，排出金属残液，然后以40～100℃／小时的速度降至室温。
  3. (3)，根据权利要求(2)所述的发明方法，其特征在于：先将瓷土制成工件，素烧成陶瓷，再与金属一起进行二次烧制。
CN 00105257 2000-04-23 2000-04-23 金属陶瓷复合材料制造方法 Pending CN1282796A (zh)