CN1275887C - 石英玻璃管的制造方法 - Google Patents

石英玻璃管的制造方法 Download PDF

Info

Publication number
CN1275887C
CN1275887C CNB028212274A CN02821227A CN1275887C CN 1275887 C CN1275887 C CN 1275887C CN B028212274 A CNB028212274 A CN B028212274A CN 02821227 A CN02821227 A CN 02821227A CN 1275887 C CN1275887 C CN 1275887C
Authority
CN
China
Prior art keywords
density
soot
quartz glass
tube
region
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CNB028212274A
Other languages
English (en)
Chinese (zh)
Other versions
CN1575261A (zh
Inventor
O·洪巴赫
F·根西克
D·克鲁伯
M·迪特里希
R·萨特曼
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Heraeus Quarzglas GmbH and Co KG
Original Assignee
Heraeus Tenevo GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Heraeus Tenevo GmbH filed Critical Heraeus Tenevo GmbH
Publication of CN1575261A publication Critical patent/CN1575261A/zh
Application granted granted Critical
Publication of CN1275887C publication Critical patent/CN1275887C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B37/00—Manufacture or treatment of flakes, fibres, or filaments from softened glass, minerals, or slags
    • C03B37/01—Manufacture of glass fibres or filaments
    • C03B37/012—Manufacture of preforms for drawing fibres or filaments
    • C03B37/014—Manufacture of preforms for drawing fibres or filaments made entirely or partially by chemical means, e.g. vapour phase deposition of bulk porous glass either by outside vapour deposition [OVD], or by outside vapour phase oxidation [OVPO] or by vapour axial deposition [VAD]
    • C03B37/01413—Reactant delivery systems
    • C03B37/0142—Reactant deposition burners
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B19/00—Other methods of shaping glass
    • C03B19/14—Other methods of shaping glass by gas- or vapour- phase reaction processes
    • C03B19/1415—Reactant delivery systems
    • C03B19/1423—Reactant deposition burners
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B2207/00—Glass deposition burners
    • C03B2207/36—Fuel or oxidant details, e.g. flow rate, flow rate ratio, fuel additives
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B2207/00—Glass deposition burners
    • C03B2207/60—Relationship between burner and deposit, e.g. position
    • C03B2207/62—Distance
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B2207/00—Glass deposition burners
    • C03B2207/60—Relationship between burner and deposit, e.g. position
    • C03B2207/66—Relative motion

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Manufacturing & Machinery (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • General Life Sciences & Earth Sciences (AREA)
  • Geochemistry & Mineralogy (AREA)
  • Glass Melting And Manufacturing (AREA)
  • Glass Compositions (AREA)
  • Manufacture, Treatment Of Glass Fibers (AREA)
CNB028212274A 2001-10-26 2002-10-09 石英玻璃管的制造方法 Expired - Lifetime CN1275887C (zh)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE10152328.9 2001-10-26
DE10152328A DE10152328B4 (de) 2001-10-26 2001-10-26 Verfahren zur Herstellung eines Rohres aus Quarzglas, rohrförmiges Halbzeug aus porösem Quarzglas u. Verwendung desselben

Publications (2)

Publication Number Publication Date
CN1575261A CN1575261A (zh) 2005-02-02
CN1275887C true CN1275887C (zh) 2006-09-20

Family

ID=7703476

Family Applications (1)

Application Number Title Priority Date Filing Date
CNB028212274A Expired - Lifetime CN1275887C (zh) 2001-10-26 2002-10-09 石英玻璃管的制造方法

Country Status (5)

Country Link
US (1) US20050000250A1 (enExample)
JP (1) JP4229442B2 (enExample)
CN (1) CN1275887C (enExample)
DE (1) DE10152328B4 (enExample)
WO (1) WO2003037808A1 (enExample)

Families Citing this family (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102006024831B4 (de) * 2006-05-24 2008-03-27 Heraeus Quarzglas Gmbh & Co. Kg Verfahren zur Herstellung eines Halbzeugs aus synthetischem Quarzglas
DE102010005954B4 (de) 2010-01-27 2020-11-19 Heraeus Quarzglas Gmbh & Co. Kg Poröses Kohlenstofferzeugnis
JP5695025B2 (ja) * 2010-03-03 2015-04-01 株式会社フジクラ 光ファイバ母材の製造方法
DE102012013134B4 (de) * 2012-07-03 2014-04-03 Heraeus Quarzglas Gmbh & Co. Kg Verfahren zur Herstellung von Zylindern aus Quarzglas
WO2014099645A1 (en) * 2012-12-20 2014-06-26 Corning Incorporated Methods for forming optical fiber preforms with selective diffusion layers
DE102013107435B4 (de) * 2013-07-12 2015-01-29 Heraeus Quarzglas Gmbh & Co. Kg Verfahren zur Herstellung eines Quarzglas-Großrohres
JP6097892B2 (ja) * 2015-03-31 2017-03-15 古河電気工業株式会社 光ファイバ用多孔質ガラス母材の製造方法
EP3088370B1 (de) * 2015-04-28 2018-09-26 Heraeus Quarzglas GmbH & Co. KG Verfahren und vorrichtung zur herstellung eines rohres aus glas
WO2017103153A1 (de) 2015-12-18 2017-06-22 Heraeus Quarzglas Gmbh & Co. Kg Glasfasern und vorformen aus quarzglas mit geringem oh-, cl- und al-gehalt
TWI808933B (zh) 2015-12-18 2023-07-21 德商何瑞斯廓格拉斯公司 石英玻璃體、二氧化矽顆粒、光導、施照體、及成型體及其製備方法
TWI733723B (zh) 2015-12-18 2021-07-21 德商何瑞斯廓格拉斯公司 不透明石英玻璃體的製備
US11299417B2 (en) 2015-12-18 2022-04-12 Heraeus Quarzglas Gmbh & Co. Kg Preparation of a quartz glass body in a melting crucible of refractory metal
CN108698892A (zh) 2015-12-18 2018-10-23 贺利氏石英玻璃有限两合公司 从二氧化硅颗粒制备石英玻璃体
CN108698888A (zh) 2015-12-18 2018-10-23 贺利氏石英玻璃有限两合公司 在石英玻璃制备中作为中间物的经碳掺杂的二氧化硅颗粒的制备
KR20180095880A (ko) 2015-12-18 2018-08-28 헤래우스 크바르츠글라스 게엠베하 ＆ 컴파니 케이지 합성 석영 유리 결정립의 제조
CN108698890A (zh) 2015-12-18 2018-10-23 贺利氏石英玻璃有限两合公司 利用在熔融烘箱中的露点监测制备石英玻璃体
CN108698894A (zh) 2015-12-18 2018-10-23 贺利氏石英玻璃有限两合公司 在多腔式烘箱中制备石英玻璃体
KR20180095619A (ko) 2015-12-18 2018-08-27 헤래우스 크바르츠글라스 게엠베하 ＆ 컴파니 케이지 실리카 유리 제조 동안 규소 함량의 증가
CN109791250B (zh) * 2016-09-21 2021-03-12 康宁股份有限公司 包覆物折射率变化的光纤及其形成方法
EP4186873B1 (en) * 2021-11-29 2024-05-08 Schott Ag Glass tube for pharmaceutical containers and manufacturing process for a glass tube

Family Cites Families (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS60161347A (ja) * 1984-01-24 1985-08-23 Sumitomo Electric Ind Ltd 光フアイバ用ガラス母材の製造方法
JPS60186429A (ja) * 1984-03-01 1985-09-21 Sumitomo Electric Ind Ltd 光フアイバ用母材の製造方法
DE3422997A1 (de) * 1984-06-22 1986-01-02 Standard Elektrik Lorenz Ag, 7000 Stuttgart Verfahren zur herstellung von lichtwellenleitern
JPS61201637A (ja) * 1985-03-01 1986-09-06 Sumitomo Electric Ind Ltd 光フアイバ用母材の製造方法
US4810276A (en) * 1987-08-05 1989-03-07 Corning Glass Works Forming optical fiber having abrupt index change
JPH01160839A (ja) * 1987-12-18 1989-06-23 Nippon Telegr & Teleph Corp <Ntt> 光ファイバ用母材の製造方法
EP0611732B1 (en) * 1989-10-31 1997-10-08 Fujitsu Limited Process for fabricating an optical fiber preform
US5278931A (en) * 1992-12-31 1994-01-11 Corning Incorporated Low bend loss singlemode optical waveguide fiber
US6376401B1 (en) * 1998-09-07 2002-04-23 Tosoh Corporation Ultraviolet ray-transparent optical glass material and method of producing same
JP2000264647A (ja) * 1999-03-12 2000-09-26 Shin Etsu Chem Co Ltd 多孔質ガラス母材
JP2000272930A (ja) * 1999-03-26 2000-10-03 Mitsubishi Cable Ind Ltd 光ファイバ母材の製造方法
DE10050324C1 (de) * 2000-10-10 2001-12-13 Heraeus Quarzglas Verfahren zur Herstellung eines Rohres aus dotiertem Quarzglas, rohrförmiges Halbzeug aus porösem Quarzglas, daraus hergestelltes Quarzglasrohr und Verwendung desselben
WO2002090276A1 (en) * 2001-04-27 2002-11-14 Pirelli & C. S.P.A. Method for producing an optical fiber preform
US8516855B2 (en) * 2001-04-27 2013-08-27 Prysmian Cavi E Sistemi Energia S.R.L. Method for producing an optical fiber preform

Also Published As

Publication number Publication date
DE10152328B4 (de) 2004-09-30
US20050000250A1 (en) 2005-01-06
CN1575261A (zh) 2005-02-02
WO2003037808A1 (de) 2003-05-08
JP4229442B2 (ja) 2009-02-25
JP2005507358A (ja) 2005-03-17
DE10152328A1 (de) 2003-05-22

Similar Documents

Publication Publication Date Title
CN1575261A (zh) 石英玻璃管的制造方法、由多孔石英玻璃构成的管状半成品及其用途
CN1129558C (zh) 采用等离子外部汽相沉积法制造用于光纤生产的管状件的方法
CN102089687B (zh) 弯曲不敏感型光纤，作为生产它的半成品的石英玻璃管，和用于生产所述纤维的方法
CN1298646C (zh) 制造光纤的方法和光纤毛坯
CN1345295A (zh) 在粉末预制棒中控制氟掺杂的方法
CN1246838A (zh) 具有折射率凹陷纤芯区的光纤制造方法
JP7555208B2 (ja) 大型中空状多孔質石英ガラス母材及びその製造方法
CN1849270A (zh) 光纤预制件的制造方法、光纤的制造方法以及光纤
US8516855B2 (en) Method for producing an optical fiber preform
CN1295169C (zh) 制造光纤预型件的方法
CN1282619C (zh) 由人造石英玻璃制造的套管和由该套管制造的光纤
EP3041801A2 (en) Method of making updoped cladding by using silicon tertrachloride as the dopant
AU716134B2 (en) Heat treatment of silica based glasses
CN111615499B (zh) 光纤母材的制造方法、光纤母材以及光纤的制造方法、光纤
CN100335430C (zh) 借助保持装置生产用合成石英玻璃制成的中空筒的方法和实施所述方法的保持装置
CN85104563A (zh) 生产含氟覆层光导纤维玻璃坯的方法
CN1305791C (zh) 低羟基含量圆柱形石英玻璃体的制造方法
CN1293008C (zh) 用来生产用于光纤的预成型坯件的基底管和过程
CN1262501C (zh) 在mcvd法中使用双喷灯制备光纤预制棒的方法和设备
US20090260400A1 (en) Method for Producing a Tubular Semifinished Product From Fluorine-Doped Quartz Glass
CN114262148B (zh) 光纤用玻璃基材的制造方法
CN1458099A (zh) 低水峰光纤预制件的制造方法
CN1281986C (zh) 通过椭圆度的改善最终具有低pmd的光纤预制棒的制造方法
CN1784360A (zh) 光纤母材及其制造方法
JP2022148517A (ja) 光ファイバ母材の製造方法、及び光ファイバ母材の製造装置

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
ASS Succession or assignment of patent right

Owner name: HEROEASY QUARTZ GLASS CO. KG

Free format text: FORMER OWNER: HERAEUS TENEVO AG

Effective date: 20080229

C41 Transfer of patent application or patent right or utility model
TR01 Transfer of patent right

Effective date of registration: 20080229

Address after: Hanau

Patentee after: HERAEUS QUARZGLAS GmbH & Co.KG

Address before: Hanau

Patentee before: HERAEUS TENEVO GmbH

CX01 Expiry of patent term

Granted publication date: 20060920

CX01 Expiry of patent term