CN1254201C - Polypropylene fiber chemical treatment agont and its application in tobacco leaf feeding process - Google Patents
Polypropylene fiber chemical treatment agont and its application in tobacco leaf feeding process Download PDFInfo
- Publication number
- CN1254201C CN1254201C CN 200410040644 CN200410040644A CN1254201C CN 1254201 C CN1254201 C CN 1254201C CN 200410040644 CN200410040644 CN 200410040644 CN 200410040644 A CN200410040644 A CN 200410040644A CN 1254201 C CN1254201 C CN 1254201C
- Authority
- CN
- China
- Prior art keywords
- polypropylene fiber
- chemical treatments
- fiber chemical
- methyl
- cigarette
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses polypropylene fiber chemical treatment agent and thereof application in a tobacco leaf feeding technology. The polypropylene fiber chemical treatment agent contains natural isolate 5, methyl radical 2 and isopropyl cyclohexanol, which can effectively remove pungent irritation generated by heated polypropylene fiber filter tips for cigarettes. The present invention is applied in a way that the agent is firstly diluted and then uniformly sprayed on the surfaces of tobacco leaves, and conventional follow up cigarette processing procedures are subsequently carried out. The present invention is the chemical treatment agent which optimizes the combination of many kinds of sour agent, natural isolate and synthetic perfume. The present invention can effectively regulate the balance of chemical components in smoke gas, prevents the pungent irritation chemical components from generation, and changes the characteristic that the pungent irritation generated by heated polypropylene fiber filter tips through pH value regulation. The fullness of flue-cured tobacco aroma is increased, and the fragrance quality is improved. In addition, dopant gas is further covered effectively, aftertaste is improved, pungent taste and the irritation existing in the polypropylene fiber filter tips for cigarettes are remarkably removed, and the inner quality of the polypropylene fiber filter tips for cigarettes is improved.
Description
Technical field
The present invention relates to the chemical characteristic or the biochemical treatment of the filter tip and the tobacco leaf of cigarette, especially relate to a kind of polypropylene fiber chemical treatments and the application in tobacco feeding technology thereof.
Background technology
The cigarette commodity that cigarette industry requires to produce have full jealous, suitable strength, strong fragrance, the tar of low content.The chemical treatments that existing cigarette generally adopts generally contains 2 hydroxy propanoic acid, P-methoxybenzal-dehyde, 3-hydroxyl-2-ethyl-pyrokomane and solvent.2 hydroxy propanoic acid is a kind of acid, and it mainly acts on is to regulate acid-base value to reduce excitant and to cover assorted gas.P-methoxybenzal-dehyde is a kind of natural isolate, and main effect is to improve the cigarette pleasant impression.3-hydroxyl-2-ethyl-pyrokomane is a kind of synthetic perfume, and main effect is to increase the fragrance richness to improve flavouring essence quality and to cover assorted gas.Solvent is to adopt propane diols mostly.And generally adopt the cigarette of polypropylene fiber filter tip of the polypropylene fiber wire-beam forming of chemical synthesis, because polypropylene fiber tow smooth surface, the chemical composition of pungent stimulation in the flue gas can not be effectively filtered, and also pungent stimulation can be produced after the plastic properties of itself is heated when sucking cigarette.The chemical treatments that above-mentioned existing cigarette generally adopts can not be removed pungent and the stimulation that the polypropylene fiber filter tip cigarette exists significantly, directly influences the acceptability of these cigarette.Have not yet to see the pungent of desirable removal polypropylene fiber filter tip cigarette existence and the chemical treatments and the application in tobacco feeding technology thereof of stimulation.
Summary of the invention
The technical problem that the present invention will solve is, proposes a kind of polypropylene fiber chemical treatments, and it can effectively be removed the polypropylene fiber filter tip cigarette and be subjected to thermogenetic pungent stimulation.
Another technical problem that the present invention will solve is to propose the application of a kind of polypropylene fiber chemical treatments in tobacco feeding technology, to increase flue-cured tobacco fragrance richness, the raising flavouring essence quality.
For polypropylene fiber chemical treatments of the present invention, above-mentioned technical problem is solved like this:
Polypropylene fiber chemical treatments of the present invention is characterized in that: contain and can effectively remove natural isolate 5-methyl-2-isopropyl cyclohexanol that the polypropylene fiber filter tip cigarette is subjected to thermogenetic pungent stimulation.
For polypropylene fiber chemical treatments of the present invention, above-mentioned technical problem can further be solved like this:
Polypropylene fiber chemical treatments of the present invention also contains acid, and described acid is a kind of or two or more arbitrarily in acetate, 2 hydroxy propanoic acid and the 2 methyl valeric acid.They can effectively regulate the balance of chemical composition in the flue gas, and part stops the generation of pungent stimulation chemical composition, and the adjusting by acid-base value, to reduce excitant and to cover assorted gas.
Polypropylene fiber chemical treatments of the present invention also contains synthetic perfume, described synthetic perfume is 3-hydroxyl-2-ethyl-pyrokomane, γ-Ji Neizhi, 3,5,5-trimethyl-2-cyclohexanone, 3,7,11-trimethyl-2,6, a kind of or two or more arbitrarily in the pure and mild benzyl carbinol of 10-12 carbon triolefin-1-.They can increase the fragrance richness or improve flavouring essence quality and cover assorted gas.
Described natural isolate also comprises one or both in P-methoxybenzal-dehyde, the 1-methyl-4-isopropyl-1-cyclohexene-8-alcohol.They can improve flavouring essence quality, improve the cigarette pleasant impression.
Polypropylene fiber chemical treatments of the present invention also contains solvent, and described solvent is a propane diols.
For polypropylene fiber chemical treatments of the present invention, above-mentioned technical problem can preferably like this be solved:
Polypropylene fiber chemical treatments of the present invention is characterized in that: each component and weight percent content are respectively:
5-methyl-2-isopropyl cyclohexanone 1.34～3.69%;
Acetate 5.86～10.50%;
2 hydroxy propanoic acid 1.84～7.80%;
2 methyl valeric acid 0.45～2.96%;
3-hydroxyl-2-ethyl pyrokomane 0.98～2.98%;
γ-Ji Neizhi 0.44～1.44%;
3,5,5-trimethyl-2-cyclohexanone 0.53～1.21%;
3,7,11-trimethyl-2,6,10-12 carbon triolefin-1-alcohol 0.71～3.32%;
Benzyl carbinol 7.32～13.89%;
P-methoxybenzal-dehyde 0.71～2.63%;
1-methyl-4-isopropyl-1-cyclohexene-8-alcohol 0.09～0.36%;
Propane diols 64.31～68.36%.
For the application of polypropylene fiber chemical treatments of the present invention in tobacco feeding technology, above-mentioned technical problem is solved like this:
The polypropylene fiber chemical treatments is diluted earlier, evenly be sprayed at tobacco leaf surface then, carry out conventional follow-up cigarette manufacturing procedure again.
For the application of polypropylene fiber chemical treatments of the present invention in tobacco feeding technology, above-mentioned technical problem can further be solved like this:
Described dilution is with 50～70% ethanol dilution polypropylene fiber chemical treatments.
The amount of described sprinkling is looked the cigarette tobacco leaf formulation quality and is regulated, the cigarette leaf group that prescription quality is high, and corresponding sprinkling amount is just few.
Described cigarette tobacco leaf formulation quality is divided into the upper, middle and lower Three Estate, corresponding sprinkling amount is respectively less, in, many.
Before the described sprinkling polypropylene fiber chemical treatments, conventional vacuum conditioning, leaves moisting cigarette manufacturing procedure are arranged successively also.
The follow-up cigarette manufacturing procedure of described routine has storage leaf, chopping, baking silk successively, adds table perfume, stores silk, cigarette and packing.
Polypropylene fiber chemical treatments of the present invention is a kind of chemical treatments that is applied to tobacco feeding technology, with the essence and flavoring agent that generally in cigarette is made, adds tangible difference is arranged, under the prerequisite that reaches the equal quality requirement, can increase flue-cured tobacco fragrance richness, improve flavouring essence quality.Especially polypropylene fiber chemical treatments of the present invention be according to the polypropylene fiber filter tip physics, chemical property and to the filtering feature of flue gas, the chemical treatments of the multiple acid of a kind of optimum organization, natural isolate and the synthetic perfume that proposes contains and can effectively remove natural isolate 5-methyl-2-isopropyl cyclohexanol that the polypropylene fiber filter tip cigarette is subjected to thermogenetic pungent stimulation.Can effectively regulate the balance of chemical composition in the flue gas, stop the generation of pungent stimulation chemical composition, and the adjusting by acid-base value, polypropylene fiber filter tip itself changed because the characteristic of the pungent stimulation of generation of being heated.Not only increase flue-cured tobacco fragrance richness, improved flavouring essence quality, also further effectively covered assorted gas, improved pleasant impression, removed pungent and stimulation that the polypropylene fiber filter tip cigarette exists significantly, improved the interior quality of polypropylene fiber filter tip cigarette.
The specific embodiment
Below in conjunction with the specific embodiment the present invention is described in further detail:
One one kinds of polypropylene fiber chemical treatments of the specific embodiment
Each component and the weight percent content of this polypropylene fiber chemical treatments are respectively:
5-methyl-2-isopropyl cyclohexanone 1.5%;
Acetate 7.5%;
2 hydroxy propanoic acid 3.8%;
2 methyl valeric acid 1.2%;
3-hydroxyl-2-ethyl-pyrokomane 2.0%;
γ-Ji Neizhi 1.1%;
3,5,5-trimethyl-2-cyclohexanone 0.6%;
3,7,11-trimethyl-2,6,10-12 carbon triolefin-1-alcohol 2.5%;
Benzyl carbinol 10.0%;
P-methoxybenzal-dehyde 1.5%;
1-methyl-4-isopropyl-1-cyclohexene-8-alcohol 0.1%;
Propane diols 68.2%.
As required, be mixed with the polypropylene fiber chemical treatments by above component and weight percent content, use the 50% ethanol dilution of equivalent before using earlier, evenly be sprayed at tobacco leaf surface then, the sprinkling amount is looked the cigarette tobacco leaf formulation quality and is regulated, the cigarette tobacco leaf formulation quality is divided into the upper, middle and lower Three Estate, and every 100Kg tobacco leaf sprinkling amount accordingly is respectively 0.05Kg, 0.08Kg, 0.12Kg.Subsequent treatment cigarette processing technology is routinely carried out.
21 kinds of polypropylene fiber chemical treatments of the specific embodiment
Each component and the weight percent content of this polypropylene fiber chemical treatments are respectively:
5-methyl-2-isopropyl cyclohexanone 1.5%;
Acetate 7.0%;
2 hydroxy propanoic acid 4.8%;
2 methyl valeric acid 1.0%;
3-hydroxyl-2-ethyl-pyrokomane 2.5%;
γ-Ji Neizhi 0.8%;
3,5,5-trimethyl-2-cyclohexanone 0.8%;
3,7,11-trimethyl-2,6,10-12 carbon triolefin-1-alcohol 2.1%;
Benzyl carbinol 12.0%;
P-methoxybenzal-dehyde 1.2%;
1-methyl-4-isopropyl-1-cyclohexene-8-alcohol 0.2%;
Propane diols 66.1%.
As required, be mixed with the polypropylene fiber chemical treatments by above component and weight percent content, use the 70% ethanol dilution of equivalent before using earlier, evenly be sprayed at tobacco leaf surface then, the sprinkling amount is looked the cigarette tobacco leaf formulation quality and is regulated, the cigarette tobacco leaf formulation quality is divided into the upper, middle and lower Three Estate, and every 100Kg tobacco leaf sprinkling amount accordingly is respectively 0.05Kg, 0.08Kg, 0.12Kg.Subsequent treatment cigarette processing technology is routinely carried out.
Above content be in conjunction with concrete preferred implementation to further describing that the present invention did, can not assert that concrete enforcement of the present invention is confined to these explanations.For this person of an ordinary skill in the technical field, without departing from the inventive concept of the premise, can also make some simple deduction or replace, all should be considered as belonging to the scope of patent protection that the present invention is determined by claims of being submitted to.
Claims (8)
1. a polypropylene fiber chemical treatments is characterized in that: contain and can effectively remove natural isolate 5-methyl-2-isopropyl cyclohexanol that the polypropylene fiber filter tip cigarette is subjected to thermogenetic pungent stimulation.
2. according to the described polypropylene fiber chemical treatments of claim 1, it is characterized in that: also contain acid, described acid is a kind of or two or more arbitrarily in acetate, 2 hydroxy propanoic acid and the 2 methyl valeric acid, they can effectively regulate the balance of chemical composition in the flue gas, part stops the generation of pungent stimulation chemical composition, and the adjusting by acid-base value, to reduce excitant and to cover assorted gas.
3. according to the described polypropylene fiber chemical treatments of claim 2, it is characterized in that: also contain synthetic perfume, described synthetic perfume is 3-hydroxyl-2-ethyl-pyrokomane, γ-Ji Neizhi, 3,5,5-trimethyl-2-cyclohexanone, 3,7,11-trimethyl-2,6, a kind of or two or more arbitrarily in the pure and mild benzyl carbinol of 10-12 carbon triolefin-1-, they can increase the fragrance richness or improve flavouring essence quality and cover assorted gas.
4. according to the described polypropylene fiber chemical treatments of claim 3, it is characterized in that: described natural isolate also comprises one or both in P-methoxybenzal-dehyde, the 1-methyl-4-isopropyl-1-cyclohexene-8-alcohol, they can improve flavouring essence quality, improve the cigarette pleasant impression.
5. according to the described polypropylene fiber chemical treatments of claim 4, it is characterized in that: also contain solvent, described solvent is a propane diols.
6. according to the described polypropylene fiber chemical treatments of claim 5, it is characterized in that: each component and weight percent content are respectively:
5-methyl-2-isopropyl cyclohexanone 1.34～3.69%;
Acetate 5.86～10.50%;
2 hydroxy propanoic acid 1.84～7.80%;
2 methyl valeric acid 0.45～2.96%;
3-hydroxyl-2-ethyl-pyrokomane 0.98～2.98%;
γ-Ji Neizhi 0.44～1.44%;
3,5,5-trimethyl-2-cyclohexanone 0.53～1.21%;
3,7,11-trimethyl-2,6,10-12 carbon triolefin-1-alcohol 0.71～3.32%;
Benzyl carbinol 7.32～13.89%;
P-methoxybenzal-dehyde 0.71～2.63%;
1-methyl-4-isopropyl-1-cyclohexene-8-alcohol 0.09～0.36%;
Propane diols 64.31～68.36%.
7. as the application of the described polypropylene fiber chemical treatments of one of claim 1 to 6 in tobacco feeding technology, it is characterized in that: be that the polypropylene fiber chemical treatments is diluted earlier, evenly be sprayed at tobacco leaf surface then, carry out conventional follow-up cigarette manufacturing procedure again.
8. according to the application of the described polypropylene fiber chemical treatments of claim 7 in tobacco feeding technology, it is characterized in that: described dilution is with 50～70% ethanol dilution polypropylene fiber chemical treatments.