CN1244656C - Composition of natural oil resin for reducing dry time and mfg. method of the same and composition of natural paint having the same - Google Patents
Composition of natural oil resin for reducing dry time and mfg. method of the same and composition of natural paint having the same Download PDFInfo
- Publication number
- CN1244656C CN1244656C CNB028056973A CN02805697A CN1244656C CN 1244656 C CN1244656 C CN 1244656C CN B028056973 A CNB028056973 A CN B028056973A CN 02805697 A CN02805697 A CN 02805697A CN 1244656 C CN1244656 C CN 1244656C
- Authority
- CN
- China
- Prior art keywords
- natural
- oil
- paint
- weight
- weight part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a natural, oily resin composition for reducing drying time of paint, a method for producing the same, and a natural paint containing the same as a main ingredient. The present invention provides a natural, oily resin composition which is produced by stepwise polymerizing natural raw materials consisting of 25 to 40 parts by weight of tung oil, 25 to 40 parts by weight of boiled linseed oil and 20 to 50 parts of rosin ester, and the adding citrus-turpentine oil to the polymerization product at the amount of 40 to 80 parts by weight relative to the weight of the polymerization product. Also, the present invention provides a natural paint composition, comprising 30 to 50 parts by weight of the natural, oily resin of Claim 1, 8 to 20 parts by weight of vegetable oils, 0.1 to 2 parts by weight of lecithin, and the remainder of assistant raw materials which are conventionally used in production of natural paints. According to the present invention, a natural paints can be produced, which is environment-friendly and excellent in workability and film-forming properties.
Description
Technical field
The present invention relates to a kind of be used to shorten paint natural, the oleoresin composition of time of drying, its manufacture method and a kind of with its natural paint as main component.The present invention be more particularly directed to a kind of at selected mixture ratio and the oleoresin composition that originates from the polymerization crude vegetal under the condition, and manufacture method.And, the present invention relates to originate from and mix above-mentioned natural, oleoresin as main component and in conjunction with the natural paint of conventional additive, it has the obvious time of drying that has shortened, and paint film stability and the workability improved.
Background technology
So far, normally used paint comprises chemistry paint with good drying property and the natural paint with relatively poor drying property.
Yet in the present normally used chemistry paint, siccative contains and is used in a large number guarantee that the heavy metal of drying property and homininoxious healthy volatile organic compounds (VOC) comprise benzene, toluene and dimethylbenzene.Therefore, the advantage of chemistry paint is its rapid drying.
Yet chemistry paint contains a large amount of deleterious heavy metals and volatile organic compounds, so that has kept toxic substance, comprises lead and chromium.And in the drying process of chemistry paint, except that toxic substance, volatile organic compound as aromatic hydrocarbon, halon and sulfur-bearing hydrocarbon, constantly outwards distributes, thereby causes serious environmental problem.
In addition, suppose that chemistry paint directly influence people's health, so that cause that respiratory disease, anaphylactia, pamplegia disease, cancer or the like cover disease among the people that contact paints in painter or nothing.Equally, move among the people in a new house with chemical whitewashing, some phenomenons often take place, comprise anaphylactia at those, eczema, diarrhoea, cough and having a headache, these phenomenons are called ill house syndromes widely.
In fact, according to studies show that Department of the Environment of Korea republic makes in April, 1996, volatile organic compounds (VOC) is the main cause of ozone generation and photo-chemical smog, and is the toxic substance fatal to human body, comprises the generation of cancer.Simultaneously, report claims the use of chemistry paint to account for 37% of volatile organic compounds generation factor, is the best part.
Simultaneously, according to the research that a U.S. is presided over, report claims to surpass 80% and has been poisoned in house or room by the people of heavy metal or chemical substance murder by poisoning.Consider this point, the room pollution that is caused by chemistry paint is a serious problem.For this reason, in the U.S. and some flourishing European countries, use the paint that contains volatile organic compounds that goes beyond the limit to be forbidden a very long time by according to law.Therefore, replace the research of chemistry paint just to be guided energetically with natural paint.
On the other hand, in order to produce natural paint, Synolac is synthetic, and wherein Synolac is by polyprotonic acid by generalization widely, phthalic acid for example, and with polyhydroxy-alcohol, for example the esterification of glycerol forms, and comes modification with oil.Developing this method is in order to solve the environment collapse and to the deleterious heavy metal problem of human body, to be to paint at chemistry in essence.
Yet although the natural paint that uses this method to produce before is successful, it is friendly for environment, and does not harm human body, and they have serious drawback aspect the most important physical property of this paint time of drying relating to.That is, their beginning-tangible time of having is 10 hours and setting time is 24-48 hour.In addition, they have the moulding problem of relatively poor workability and paint film.
Therefore, though the most widely used at present chemistry paint has superiority aspect time of drying, they also have harmful and to the disagreeableness shortcoming of environment to human body.On the other hand, be advantage friendly and that do not harm human body though natural paint has for environment, they can not be widely used because long time of drying, relatively poor workability and relatively poor paint film moulding problem are still unresolved.
The inventor has done a lot of researchs attempting to solve in this practical problems, and therefore develops and a kind ofly produce the natural paint that natural paint is compared the uniqueness with excellent physical properties with existing Germany.This natural paint that has improved has been disclosed among Korean Patent Application No. 1998-40664 and the 1998-40665.Disclosed natural paint has had significant improvement in these patent applications aspect it shortens time of drying.Yet these natural paint are needing further to improve aspect workability and the paint film stability.
Disclosure of an invention
Therefore, an object of the present invention is to provide a kind of novel natural, oleoresin composition, it has a good drying property in workability that embodiment has improved and paint film stability, and provide that a kind of manufacturing is natural, oleoresin method for compositions and with its natural paint as main component.
In order to achieve the above object, to be to be selected from the vegetables oil of limited kinds be with polymeric under selected ratio and the polymerizing condition for characteristics of the present invention.
Natural, oleoresin composition according to the present invention has been eliminated the major defect of former chemistry paint toxic ingredient, can solve the problem of the time of drying of delay, relatively poor workability and relatively poor paint film stability simultaneously.
Simultaneously, another object of the present invention provides a kind of natural paint, and it is natural by using, the oleoresin composition is as main raw material, and other compositions are manufactured as less important raw material.
This purpose can by with natural, oleoresin composition and as the vegetables oil of main component together with traditional less important raw material, mix with selected mixture ratio and condition and to reach.
Realize best mode of the present invention
Below describe the present invention in detail.
The invention provides a kind of natural oiliness resin combination, it is used as main raw material when making natural paint, and makes the method for this natural oiliness resin combination.
The invention provides a kind of natural oiliness resin combination, it makes by polymerization natural matter progressively, this raw material is made up of tung oil, the Toenol 1140 that boils of 25-40 weight part and the rosin ester of 20-50 weight part with respect to the 25-40 weight part of the natural matter total amount of 100 weight parts, and the citrus-rosin oil with the 40-80 weight part joins in the polymerization product then.
The invention provides natural, the oleoresin method for compositions of a kind of manufacturing, may further comprise the steps, the natural matter of the rosin ester of the Toenol 1140 that boils of the tung oil that contains the 25-40 weight part, 25-40 weight part and 20-50 weight part is provided; Natural matter is weighed, is introduced in the reactor, at the rare gas element of an atmospheric pressure, for example under the existence of nitrogen under 200-300 ℃ temperature, the polymerization first time was carried out in reaction in 7-12 hour; The product of polymerization procedure carries out the polyase 13 second time-8 hour with the first time, is under the condition of V in the viscosity (Gardner's method (G#)) of the polymerisate first time, is that Z and acid number are less than 10 until reaching viscosity; Temperature in the reactor is reduced to 90 ℃, with respect to 100 weight parts the second time polymerisate 40-80 weight part citrus-rosin oil join for the second time in the polymerisate, will react the mixture cool to room temperature of generation then.
Provide step according to natural matter of the present invention to comprise from vegetables oil, to choose natural matter and selected natural matter is weighed according to estimated rate.
Preferred its state of tung oil that uses is for being purified fully at boiling point and therefore being presented a pure concentration.Owing to it has double covalent bonds and therefore has good drying property and high viscosity, thus tung oil selected for use, although it has a relatively low iodine number.And tung oil has this characteristic and is that it contains a kind of alpha-eleostearic acid as main component and have good alkali-resistivity.Simultaneously, it has the characteristic of fast dry doubling formation hard membrane layer in oil ﹠ fat.The consumption of this tung oil is approximately the weight of 25-40 part with respect to the total amount of the natural matter of 100 weight parts that use in first step.
If the consumption of tung oil is less than 25 parts weight, it does not almost have effect on drying property, yet when its consumption is 40 parts weight, can cause relatively poor paint film.This tung oil has double covalent bonds.Therefore, in polymerization procedure, oxygen in the atmosphere and double covalent bonds reaction produce superoxide, and produce hydroxyl and oxo bridge, like this with the tung oil polymerization.
The another kind of vegetables oil that the present invention uses is the Toenol 1140 that boils.The Toenol 1140 that has boiled is to obtain by heating Toenol 1140 under about 250-300 ℃ the temperature.This time of drying that adds the final painting of the further shortening of heat energy.
The use of the Toenol 1140 that therefore, boils is vital for the present invention.The consumption of the Toenol 1140 that boils is approximately the weight of 25-40 part with respect to the total amount of the natural matter of 100 weight parts that use in first step.Its consumption will produce inadequately workability and relatively poor paint film moulding phenomenon fully during less than 25 parts weight in the paint that makes, yet prolongs drying and relatively poor paint film moulding phenomenon if its consumption greater than 40 parts weight, will produce in paint.
In polymerization procedure, methylene group adjacent with two keys in the Toenol 1140 that boils is oxidized to produce unsettled hydroperoxide, and it is dissociated into radical at once.Lipid acid acts on radical to produce peroxide bond, ether key, C-C key or the like, the Toenol 1140 polymerization that will boil like this.
The another kind of vegetables oil that uses among the present invention is according to the rosin fat of traditional method with rosin and glycerine reaction acquisition.Abietinic consumption is approximately the weight of 25-50 part with respect to the total amount of the natural matter of 100 weight parts.If its consumption is during less than 20 parts weight, the elasticity of paint film will be relatively poor, yet if its consumption greater than 50 parts weight, paint film will have strong elasticity and therefore become fragile.
In the present invention, above-mentioned various natural matters are incorporated in the reactor, and first polymerization procedure that continues 7-12 hour under 200-300 ℃ temperature.
The rare gas element that uses in first polymerization procedure comprises nitrogen and helium, is not react with natural matter.Consider that economic benefit preferably uses nitrogen as rare gas element.
In the present invention, if first polymerization procedure is 200 ℃ or following carrying out, polymerization can not carried out finely.On the other hand, if first polymerization procedure will produce excessive polymerism and cause natural matter to be tending towards gel 300 ℃ or above carrying out.
Usually, in low temperature range, natural matter should be aggregated in a relatively long time, but in high temperature range, they should be aggregated within a short period of time.
In the present invention, second polymerization procedure carries out after first polymerization procedure.In second polymerization procedure, the product of first polymerization procedure is by further polyase 13-7 hour in the viscosity (G#) of first polymerisate under the condition of V.It is that Z and acid number are less than 10 that second polymerization procedure carries out up to reaching viscosity.Since first polymerisate along with the time through gradually from solid-state liquefy, the reformed time point of viscosity and acid number is very important.
If the step of adding solvent before condition described above arrives, paint film will reduce gluing intensity and workability, and unsettled resin state occurs.On the other hand, if viscosity and acid number have surpassed above-mentioned condition, natural matter will cause producing relatively poor paint film phenomenon by gel and by excessively polymerization.
In the present invention, after second polymerization procedure carries out, the step of adding solvent.In the step of adding solvent, the heating in the reactor is stopped to reduce temperature.When the temperature in the reactor had arrived about 90 ℃, the citrus-rosin oil that is approximately 40-80 part consumption with respect to second polymerisate, 100 weight parts was added in second polymerisate.The mixture that produces is cooled to room temperature, to finish reaction.
Citrus-rosin oil among the present invention uses as natural solvent.Be preferably based on the D-lemonine that surpasses 99% purity, it can be by mixing the same eucalyptus-rosin oil of tangerine oil with 3: 1 to 5: 1 weight ratio, and purifying above 4 hours by heated mixt under 80-250 ℃ temperature then obtains.
If the temperature in the reactor surpasses 90 ℃, citrus-rosin oil seethes with excitement easily and volatilizees and converts coagulated state to.Therefore, the step of interpolation citrus-rosin oil should be 90 ℃ or following carrying out, preferably about 70 ℃.
By carrying out above-mentioned steps, make natural, oleoresin composition of the present invention.
Found that natural oiliness resin combination of the present invention has following physical property.
That is, the non-performance composition that comprises of natural oiliness resin combination is measured by KSM5000 testing method (2013) and is about 60-70%.Simultaneously, viscosity (G#, the 25 ℃) O-R that measures by the gastner viscometer.In addition, it has the proportion of 0.85-0.95 and when bore hole is observed, presents the state as jelly of millet.
The main component that natural oiliness resin combination according to the present invention can be used as natural paint, enamel, priming paint, varnish etc. is used.
And, the invention provides a kind of natural oil coating compositions, it has good drying property, workability and paint film shaping characteristic, it contains natural, oleoresin composition as main raw material.
Natural oil coating compositions characteristics according to the present invention are that the weight in the natural oil coating compositions is 100 parts, it contains natural, the oleoresin composition of 30-50 weight part as main raw material, the vegetables oil of 8-20 weight part, 0.1-2 the Yelkin TTS of weight part and be used in residue auxiliary material in the natural paint production usually.
Can believe when above-mentioned natural, when oleoresin is used to paint, with the polymerization of airborne oxygen with easily a kind of and fast mode carry out, so obviously shorten its time of drying.Yet, have been found that if the consumption of natural, oleoresin during less than 30 weight parts, the paint adhesive strength that the result obtains is lowered, if but when its consumption surpassed 50 weight parts, the paint that the result obtains was extended time of drying.In natural oil coating compositions of the present invention, above-mentioned vegetables oil uses and passes through the volatilization formation paint film of air as solvent.In these vegetables oil, preferably use citrus-rosin oil.
Simultaneously, in natural oil coating compositions of the present invention, Yelkin TTS is a kind of natural additive, and it uses as dispersion agent, and low dose of the use to realize the effect of its dispersion agent.If the consumption of Yelkin TTS is less than 0.1 weight part, its dissemination is not enough, if but its consumption surpasses 2 weight parts, and it will cause the prolongation of time of drying.
The auxiliary material that uses among the present invention comprises pigment, siccative, the weighting agent that tradition is used.Application target according to natural paint of the present invention is selected.
Natural oil coating compositions according to the present invention can make according to traditional method.If it is natural that natural paint is oiliness, then should be natural, the same vegetables oil of oleoresin, Yelkin TTS and pigment mix with suitable ratio.Then mixture is ground three or four times up to the granularity that is less than 10 μ m with three-stage roll mill.Next, siccative and other auxiliary material are joined in the resultant particle, mixture is filtered fill and packing again, make final natural painting like this.
Natural oil coating compositions of the present invention is found has following physical property.That is, it begins-and the tangible time of touching is 2 hours, and setting time is 10 hours, and the content of involatile constituent is 68.0 ± 2%, and viscosity is 70-80Ku, and proportion is the contrast ratio of 1.2 ± 0.20G/L and 0.93 ± 0.3.
And, according to three kinds of samples (white, red and green) their different physicalies of measurement in chemical Industry in South Korea test and EASD of natural, oil-based paints of the present invention.The result is displayed in the following table 1.
Industrial application
Therefore, because natural, oleoresin composition according to the present invention does not contain just like the used siccative that is made of plurality of heavy metal and volatile organic compounds in the former chemistry paint, in the product of final natural oil coating compositions, detect less than to environment and deleterious heavy metal of human body and volatile organic compounds.Like this, natural, oleoresin composition of the present invention is useful raw material as environment amenable product.
And the total solids level in the natural paint is in the scope of natural, oleoresin 55-66% of the present invention.Like this, natural paint has remarkable workability of having improved and good film forming characteristics.
Table 1: by the sample physicals result of chemical Industry in South Korea test and EASD's measurement
Test event | Unit | The result | Testing method |
Total solids level | % | 55-56 | K SM-5701-96 |
Pigment content | % | 9-33 | K SM-5701-96 |
Non-volatile extender content | % | 33-46 | K SM-5701-96 |
Water-content | % | 0.5-0.1 | KSM-5701-96 (Karl Fischer method) |
Denseness | K.U. * | 71-75 | K SM-5701-96 |
Gloss (60 °) | % | 94-96 | K SM-5701-96 |
Pliability | N.S. | 5 | K SM-5701-96 |
Begin the touch time | Hour | 2-3 | K SM-5701-96 |
Dry setting time | Hour | 10 | K SM-5701-96 |
Contrast ratio | - | 0.96-0.98 | K SM-5701-96 |
Hg | ppm | Do not detect | I.C.P. analyze |
As | ppm | Do not detect | I.C.P. analyze |
Organo-tin compound | ppm | Do not detect | Korea S's technology and Bureau of Standards announcement number: 1997-390 |
Sb | ppm | 2-4 | I.C.P. analyze |
Cr | ppm | 0.5-3 | I.C.P. analyze |
Pb | ppm | 1-5 | I.C.P. analyze |
Cd | ppm | 0-0.02 | I.C.P. analyze |
Co | ppm | 0.0003-0.03 | I.C.P. analyze |
Pb (content in non-volatile matter) | % | 0.0002-0.001 | I.C.P. analyze |
Cd (content in non-volatile matter) | % | Do not detect | I.C.P. analyze |
Cr (content in non-volatile matter) | % | Do not detect | I.C.P. analyze |
Sb (content in non-volatile matter) | % | 0.0003-0.001 | I.C.P. analyze |
Formaldehyde | ppm | Do not detect | Korea S's technology and Bureau of Standards announcement number: 1997-390 |
*The conversion relation of Ku of viscosity unit and the international PaS of viscosity unit following (25 ℃):
(1) 200-2100mPaS scope
Ln (Ku)=1.1187+0.8542*ln (0.1938v+36)-0.0443 (ln (0.1938v+36)
2Or
(e=2.718281828…)
(2) 2100-5000mPaS scope
Ln (Ku)=1.8118+0.596*ln (0.1938v+36)-0.0206 (ln (0.1938v+36)
2Wherein, v is the international mPaS of viscosity unit.
In addition, in the occasion of using according to natural paint of the present invention, they present highly improved economic performance and workability, have splendid solid volume content and consistency properties because they were compared with former chemistry paint.
Although describe preceding that this is natural in detail, oleoresin composition, its manufacture method and, be appreciated that they are the preferred embodiments of the present invention, do not do any qualification to the present invention with its natural oil coating compositions as main component.
Similarly, those those of skill in the art can make various modification, interpolation and replacement, and not depart from disclosed scope and spirit of the present invention in the appended claims.
Claims (3)
1. method of making natural oiliness resin combination may further comprise the steps:
A) provide the natural matter of the rosin ester of the tung oil that contains the 25-40 weight part, Toenol 1140 that the 25-40 weight part boils and 25-50 weight part;
B) described natural matter is weighed, and be introduced in the reactor, in the presence of an atmospheric rare gas element, the polymerization first time was carried out in reaction in 7-12 hour under 200-300 ℃ temperature;
C) for the first time the product of polymerization procedure carries out polyase 13 second time-8 hour, and the viscosity that polymerisate is measured by Gardner's method in the first time is under the state of V, is that Z and acid number are less than 10 until reaching viscosity by Gardner's method mensuration; With
D) temperature in the reactor is reduced to the highest 90 ℃, and add with respect to 100 weight parts the second time polymerisate 40-80 weight part citrus-rosin oil, to react the mixture cool to room temperature that produces then, described citrus-rosin oil is based on the D-lemonine that surpasses 99% purity, by the same eucalyptus-rosin oil of tangerine oil is mixed with 3: 1 to 5: 1 weight ratio, then mixture is heated purification and obtain under 80-250 ℃ temperature above 4 hours.
2. the natural oiliness resin combination that makes with the method for claim 1.
3. natural oil coating compositions, the natural oiliness resin combination that contains 30-50 weight part as claimed in claim 2 in its 100 weight part, the vegetables oil of 8-20 weight part, the Yelkin TTS of 0.1-2 weight part, and be used in residue auxiliary material in the natural paint production usually.