CN104177999A - Environmentally-friendly fast-drying paint - Google Patents
Environmentally-friendly fast-drying paint Download PDFInfo
- Publication number
- CN104177999A CN104177999A CN201310189285.3A CN201310189285A CN104177999A CN 104177999 A CN104177999 A CN 104177999A CN 201310189285 A CN201310189285 A CN 201310189285A CN 104177999 A CN104177999 A CN 104177999A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmentally
- acid
- drying paint
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses environmentally-friendly fast-drying paint. The environmentally-friendly fast-drying paint comprises, by weight, 10-15 parts of diglycollic acid resin, 8-10 parts of crystal titanium ion particles, 10-15 parts of eleostearic acid, 20-30 parts of xylenol sodium salt, 10-12 parts of linoleic acid, 4-6 parts of rosin water and 30-40 parts of soft solvent oil. The environmentally-friendly fast-drying paint has no color and no taste, is environmentally friendly and practical and greatly shortens paint curing time after use.
Description
Technical field
The present invention relates to a kind of coating, be specifically related to a kind of environmental protection Quick drying paint.
Background technology
Paint is being widely used in house ornamentation market at present, but contains a large amount of toxic substances in a lot of paint, very not environmental protection, simultaneously the dry solidifying time of existing paint longer, running into overcast and rainyly can affect finishing progress especially.
Summary of the invention
Goal of the invention: the present invention, in order to solve the deficiencies in the prior art, provides a kind of environmental protection Quick drying paint.
Technical scheme: a kind of environmental protection Quick drying paint, it is formulated by di-alcohol acid resin, crystal titanium ion particle, eleostearic acid, xylenol sodium, linolenic acid, rosin and water, the weight part of described each component is: di-alcohol acid resin: 10-15 part; Crystal titanium ion particle: 8-10 part; Eleostearic acid: 10-15 part; Xylenol sodium: 20-30 part; Linolenic acid: 10-12 part; Rosin: 4-6 part; Soft solvent oil: 30-40 part.
Beneficial effect: a kind of environmental protection Quick drying paint of the present invention, colorless and odorless, environmental protection is practical, and after using, the dry solidifying time of paint shortens greatly simultaneously.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment 1:
An environmental protection Quick drying paint, it is formulated by di-alcohol acid resin, crystal titanium ion particle, eleostearic acid, xylenol sodium, linolenic acid, rosin and water, the weight part of described each component is: di-alcohol acid resin: 10 parts; Crystal titanium ion particle: 8 parts; Eleostearic acid: 10 parts; Xylenol sodium: 20 parts; Linolenic acid: 10 parts; Rosin: 4 parts; Soft solvent oil: 30 parts.
The compound method of above-mentioned environment-friendly antirust paint: 8 parts of crystal titanium ion particles, 10 parts of eleostearic acids and 10 parts of linolenic acid mixtures are added to reactor heating, spray into successively 10 parts of di-alcohol acid resins, 20 parts of xylenol sodium, 4 parts of rosin and 30 parts of soft soluble oils and mix in the time of 200 ℃.
Embodiment 2:
An environmental protection Quick drying paint, it is formulated by di-alcohol acid resin, crystal titanium ion particle, eleostearic acid, xylenol sodium, linolenic acid, rosin and water, the weight part of described each component is: di-alcohol acid resin: 15 parts; Crystal titanium ion particle: 10 parts; Eleostearic acid: 15 parts; Xylenol sodium: 30 parts; Linolenic acid: 12 parts; Rosin: 6 parts; Soft soluble oil: 40 parts.
The compound method of above-mentioned environment-friendly antirust paint: 10 parts of crystal titanium ion particles, 15 parts of eleostearic acids and 12 parts of linolenic acid mixtures are added to reactor heating, spray into successively 15 parts of di-alcohol acid resins, 30 parts of xylenol sodium, 6 parts of rosin and 40 parts of soft soluble oils and mix in the time of 200 ℃.
Embodiment 3:
An environmental protection Quick drying paint, it is formulated by di-alcohol acid resin, crystal titanium ion particle, eleostearic acid, xylenol sodium, linolenic acid, rosin and water, the weight part of described each component is: di-alcohol acid resin: 12.5 parts; Crystal titanium ion particle: 9 parts; Eleostearic acid: 12.5 parts; Xylenol sodium: 25 parts; Linolenic acid: 11 parts; Rosin: 5 parts; Soft soluble oil: 35 parts.
The compound method of above-mentioned environment-friendly antirust paint: 9 parts of crystal titanium ion particles, 12.5 parts of eleostearic acids and 11 parts of linolenic acid mixtures are added to reactor heating, spray into successively 12.5 parts of di-alcohol acid resins, 25 parts of xylenol sodium, 5 parts of rosin and 35 parts of soft soluble oils and mix in the time of 200 ℃.
Claims (1)
1. an environmental protection Quick drying paint, is characterized in that: it is formulated by di-alcohol acid resin, crystal titanium ion particle, eleostearic acid, xylenol sodium, linolenic acid, rosin and water, and the weight part of described each component is: di-alcohol acid resin: 10-15 part; Crystal titanium ion particle: 8-10 part; Eleostearic acid: 10-15 part; Xylenol sodium: 20-30 part; Linolenic acid: 10-12 part; Rosin: 4-6 part; Soft solvent oil: 30-40 part.