CN104479525A - Water-based antirust paint for multiple device shells and preparation method thereof - Google Patents
Water-based antirust paint for multiple device shells and preparation method thereof Download PDFInfo
- Publication number
- CN104479525A CN104479525A CN201410711563.1A CN201410711563A CN104479525A CN 104479525 A CN104479525 A CN 104479525A CN 201410711563 A CN201410711563 A CN 201410711563A CN 104479525 A CN104479525 A CN 104479525A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- mixture
- minute
- antirust paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-based antirust paint for multiple device shells. The invention is characterized in that the water-based antirust paint is prepared from the following raw materials in parts by weight: 2-3 parts of linoleic acid, 3-5 parts of zinc yellow, 2-3 parts of sodium dihydrogen phosphate, 3-4 parts of mica ferric oxide, 0.2-0.3 part of BYK-011, 2-3 parts of paraffin emulsion, 33-36 parts of water-based alkyd resin, 0.4-0.6 part of alkylphenol polyoxyethylene, 16-20 parts of deionized water, 2-3 parts of water-based polyamide, 1-2 parts of water-based anti-skinning agent, 1-2 parts of silane coupling agent KH550, 1-2 parts of sodium dodecylsulfate, 0.3-0.4 part of polydimethylsiloxane, 25-28 parts of acrylic acid emulsion, 2-4 parts of 2,2,4-trimethyl-1,3-pentadiol monoisobutyrate and 4-7 parts of assistant. The water-based antirust paint has the advantages of low production cost, environment friendliness and high safety, is convenient for application and harmless to health of the human body, has obvious antirust effect, greatly prolongs the service life of the device shell, reduces the cost on latter maintenance, and has wide application range. The added assistants have the functions of shock absorption and noise reduction, thereby greatly reducing the hazards of noise to people.
Description
Technical field
The present invention relates to a kind of paint and preparation method thereof, particularly one kind of multiple apparatus casing use rust-inhibiting paints and preparation method thereof.
Background technology
Every coating using water as solvent or make dispersion medium, all can be described as water-borne coatings.Water-borne coatings comprises water soluble paint, water-reducible coatings, water-dispersible paint 3 kinds.Water-borne coatings, with water as solvent, saves ample resources, and fire hazard when water-borne coatings eliminates construction, reduces topsoil; Water-borne coatings only adopts a small amount of hypotoxicity alcohol ether organic solvent, improves operating environmental condition; Water-borne coatings directly can apply construction in wet structure and wet environment; It is good to material surface adaptability, strong adhesion.
The rust corrosion of metallic substance has become a catastrophe in national economy; rust corrosion causes the waste of material; not only bring serious financial loss; and also can bring great social danger as the material of apparatus casing; therefore protect the material such as metal not got rusty, making it play effect, the slow corrosion of resistance, increase the service life is an important task.Traditional solvent-borne type rust-inhibiting paint is in manufacture, construction, drying, solidification, film process, a large amount of VOC (volatile organic compounds) is distributed in air, serious pollution and threat are caused to human ecological environment, therefore aqueous antirust paint is more and more subject to the favor of people.
Summary of the invention
The object of this invention is to provide one kind of multiple apparatus casing use rust-inhibiting paints and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
One kind of multiple apparatus casing use rust-inhibiting paints, are made up of the raw material of following weight part: linolenic acid 2-3, zinc network yellow 3-5, SODIUM PHOSPHATE, MONOBASIC 2-3, iron mica 3-4, BYK-0110.2-0.3, paraffin wax emulsions 2-3, aqueous alkide resin 33-36, alkylphenol polyoxyethylene 0.4-0.6, deionized water 16-20, aqueous polyamide 2-3, water-based anti skinning agent 1-2, Silane coupling agent KH550 1-2, sodium laurylsulfonate 1-2, polydimethylsiloxane 0.3-0.4, ACRYLIC EMULSION 25-28, alcohol ester 12 2-4, auxiliary agent 4-7;
Described auxiliary agent is made up of the raw material of following weight part: tripoly phosphate sodium STPP 2-4, alkylphenol polyoxyethylene 1-2, polyvinyl alcohol 2-3, urea 6-8, nanometer silver 4-5, titanate coupling agent 1-2, methyl methacrylate 10-15, ethyl propenoate 3-5, Potassium Persulphate 1-2, water 8-11, hollow glass micropearl 6-8, fly ash micro-sphere 4-6, sepiolite powder 3-5,1.2% chitosan-acetic acid solution 3-5, ammonium molybdate 2-4, polyvinyl acetate emulsion 5-8; Preparation method is that methyl methacrylate, ethyl propenoate, polyvinyl acetate emulsion and water mix by (1), passes into fluidized-bed and makes its fluidisation; (2) hollow glass micropearl, fly ash micro-sphere, sepiolite powder and Potassium Persulphate are mixed, passing into fluidized-bed is boiling state; (3) mixture of step (1) is sprayed on the mixture of step (2) on the surface, under 60-80 ° of C, reacts 1-2 hour, add titanate coupling agent again and remaining surplus materials stirs after reaction terminates, then add rubber mill grinding distribution evenly.
One kind of multiple apparatus casing use rust-inhibiting paints of the present invention, be made up of following concrete steps:
(1) polydimethylsiloxane, sodium laurylsulfonate, alkylphenol polyoxyethylene, BYK-011 and deionized water are mixed, 7-9 minute is stirred under 400-600 rev/min, add zinc network Huang, SODIUM PHOSPHATE, MONOBASIC, iron mica, auxiliary agent ultrasonic disperse 15-25 minute again, obtain mixture A;
(2) be added in Scattered Kettle by aqueous alkide resin, ACRYLIC EMULSION, alcohol ester 12, aqueous polyamide, 1200-1400 rev/min of lower high-speed mixing stirs 20-40 minute, obtains mixture B;
(3) mixture A is added in mixture B, then adds all the other surplus materialss, disperse 10-20 minute under the rotating speed of 800-1000 rev/min after, forward in shredder, obtain the material of 20-40 μm, to obtain final product.
Advantage of the present invention is: aqueous antirust paint productive expense of the present invention is low, green, environmental protection, safety, application is convenient, harmless to the health of human body, rust-proof effect is remarkable, substantially prolongs the working life of apparatus casing, reduce the expense of later maintenance, and applied widely, the auxiliary agent of interpolation also has the function of damping noise reduction, substantially reduces the harm of noise to people.
specific embodiments
Below by specific examples, the present invention is described in detail.
One kind of multiple apparatus casing use rust-inhibiting paints, are made up of the raw material of following weight part (kilogram): linolenic acid 3, zinc network Huang 4, SODIUM PHOSPHATE, MONOBASIC 2, iron mica 3, BYK-0110.2, paraffin wax emulsions 2, aqueous alkide resin 35, alkylphenol polyoxyethylene 0.5, deionized water 19, aqueous polyamide 3, water-based anti skinning agent 1, Silane coupling agent KH550 1, sodium laurylsulfonate 1, polydimethylsiloxane 0.3, ACRYLIC EMULSION 27, alcohol ester 12, auxiliary agent 6;
Described auxiliary agent is made up of the raw material of following weight part (kilogram): tripoly phosphate sodium STPP 3, alkylphenol polyoxyethylene 1, polyvinyl alcohol 3, urea 6, nanometer silver 4, titanate coupling agent 2, methyl methacrylate 13, ethyl propenoate 4, Potassium Persulphate 2, water 8, hollow glass micropearl 6, fly ash micro-sphere 5, the chitosan-acetic acid solution 4 of sepiolite powder 3,1.2%, ammonium molybdate 3, polyvinyl acetate emulsion 7; Preparation method is that methyl methacrylate, ethyl propenoate, polyvinyl acetate emulsion and water mix by (1), passes into fluidized-bed and makes its fluidisation; (2) hollow glass micropearl, fly ash micro-sphere, sepiolite powder and Potassium Persulphate are mixed, passing into fluidized-bed is boiling state; (3) mixture of step (1) is sprayed on the mixture of step (2) on the surface, under 60-80 ° of C, reacts 1-2 hour, add titanate coupling agent again and remaining surplus materials stirs after reaction terminates, then add rubber mill grinding distribution evenly.
One kind of multiple apparatus casing use rust-inhibiting paints of the present invention, be made up of following concrete steps:
(1) polydimethylsiloxane, sodium laurylsulfonate, alkylphenol polyoxyethylene, BYK-011 and deionized water are mixed, 7-9 minute is stirred under 400-600 rev/min, add zinc network Huang, SODIUM PHOSPHATE, MONOBASIC, iron mica, auxiliary agent ultrasonic disperse 15-25 minute again, obtain mixture A;
(2) be added in Scattered Kettle by aqueous alkide resin, ACRYLIC EMULSION, alcohol ester 12, aqueous polyamide, 1200-1400 rev/min of lower high-speed mixing stirs 20-40 minute, obtains mixture B;
(3) mixture A is added in mixture B, then adds all the other surplus materialss, disperse 10-20 minute under the rotating speed of 800-1000 rev/min after, forward in shredder, obtain the material of 20-40 μm, to obtain final product.
Paint flat appearance of the present invention is smooth, without lump, and snappiness mm≤2, hardness: 3H, shock-resistance: 50, water tolerance experiment (29 ± 1 ° of C, 36h): non-foaming, do not come off, thermotolerance experiment (100 ± 2 DEG C, 5h): non-foaming wrinkling, without cracking, resistance to artificial weathering experiment: by 500 hours, cold-hot is experiment (5 cycle) alternately: without bubbling, without cracking, without coming off, recombination loss Factor Experiment: 10 ° of C:0.129,30 ° of C:0.116.
Claims (2)
1. one kind of multiple apparatus casing use rust-inhibiting paints, it is characterized in that, be made up of the raw material of following weight part: linolenic acid 2-3, zinc network yellow 3-5, SODIUM PHOSPHATE, MONOBASIC 2-3, iron mica 3-4, BYK-0110.2-0.3, paraffin wax emulsions 2-3, aqueous alkide resin 33-36, alkylphenol polyoxyethylene 0.4-0.6, deionized water 16-20, aqueous polyamide 2-3, water-based anti skinning agent 1-2, Silane coupling agent KH550 1-2, sodium laurylsulfonate 1-2, polydimethylsiloxane 0.3-0.4, ACRYLIC EMULSION 25-28, alcohol ester 12 2-4, auxiliary agent 4-7;
Described auxiliary agent is made up of the raw material of following weight part: tripoly phosphate sodium STPP 2-4, alkylphenol polyoxyethylene 1-2, polyvinyl alcohol 2-3, urea 6-8, nanometer silver 4-5, titanate coupling agent 1-2, methyl methacrylate 10-15, ethyl propenoate 3-5, Potassium Persulphate 1-2, water 8-11, hollow glass micropearl 6-8, fly ash micro-sphere 4-6, sepiolite powder 3-5,1.2% chitosan-acetic acid solution 3-5, ammonium molybdate 2-4, polyvinyl acetate emulsion 5-8; Preparation method is that methyl methacrylate, ethyl propenoate, polyvinyl acetate emulsion and water mix by (1), passes into fluidized-bed and makes its fluidisation; (2) hollow glass micropearl, fly ash micro-sphere, sepiolite powder and Potassium Persulphate are mixed, passing into fluidized-bed is boiling state; (3) mixture of step (1) is sprayed on the mixture of step (2) on the surface, under 60-80 ° of C, reacts 1-2 hour, add titanate coupling agent again and remaining surplus materials stirs after reaction terminates, then add rubber mill grinding distribution evenly.
2. one kind of multiple apparatus casing use rust-inhibiting paints according to claim 1, is characterized in that, be made up of following concrete steps:
(1) polydimethylsiloxane, sodium laurylsulfonate, alkylphenol polyoxyethylene, BYK-011 and deionized water are mixed, 7-9 minute is stirred under 400-600 rev/min, add zinc network Huang, SODIUM PHOSPHATE, MONOBASIC, iron mica, auxiliary agent ultrasonic disperse 15-25 minute again, obtain mixture A;
(2) be added in Scattered Kettle by aqueous alkide resin, ACRYLIC EMULSION, alcohol ester 12, aqueous polyamide, 1200-1400 rev/min of lower high-speed mixing stirs 20-40 minute, obtains mixture B;
(3) mixture A is added in mixture B, then adds all the other surplus materialss, disperse 10-20 minute under the rotating speed of 800-1000 rev/min after, forward in shredder, obtain the material of 20-40 μm, to obtain final product.