CN1244516C - Special tourmaline ceramic product - Google Patents
Special tourmaline ceramic product Download PDFInfo
- Publication number
- CN1244516C CN1244516C CN 00126626 CN00126626A CN1244516C CN 1244516 C CN1244516 C CN 1244516C CN 00126626 CN00126626 CN 00126626 CN 00126626 A CN00126626 A CN 00126626A CN 1244516 C CN1244516 C CN 1244516C
- Authority
- CN
- China
- Prior art keywords
- ceramic product
- tourmalinite
- tourmaline ceramic
- special
- clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a special tourmaline ceramic product, which comprises the raw materials that tourmaline is used as a main material, and crystal quartz, clay soil, zeolite, zirconia, titanium oxide, bismuth trioxide, silver oxide, nickel powder and borax powder are used as auxiliary materials. The present invention is characterized in that the content of the tourmaline is 10 to 60%, and the content of a mixture of the auxiliary materials of the rest is 40 to 90%. The ceramic product is formed by a conventional ceramic product technology, and the ceramic product is fired into a finished product at the flame temperature of 600 DEG C to 1300 DEG C.
Description
Technical field
The present invention relates to a kind of special tourmaline ceramic product, belong to the ceramic preparation method class.
Background technology
Tourmalinite is unique a kind of mineral that have electric property in the mineral on the earth, as a kind of silicate minerals that contains Mg, Fe, Li, AL and Mn, studies show that through modern science: little powdered tourmalinite exists positive pole and negative pole, after the solar radiation, wherein contain magnesium and surpass 10% dravite, radiate to breed light maximum, this light plays optimum effect to blood of human body circulation and metabolism.Some researchs also show: tourmalinite is once contact water, moment just can be in water release current, this electric current is best suited for 0.06 milliampere weak current of human body, and when water contacts with above-mentioned weak current, the hydrogen ion during moisture on every side gives just separates with hydroxide ion; Hydrogen ion and electronics are combined into hydrogen on the one hand: hydroxide ion and water molecules on every side become interfacial activity material and the negative ion that can produce more than 300 times, measuring at this moment by ultrasonic wave, hydrogen is 1.32PPM, the reduction potential of this explanation water this moment is fine, and the pH value of water is the weak base ionized water about 7.4 under this environment.Because this alkalescent water is unfavorable for the breeding of algae, thereby occurred adopting this method to eliminate the report of algae to water pollution.
In addition, also find through expert's research: tourmalinite has life energy, can discharge negative electrode negative ion greatly, the performance of its pyroelectricity, piezoelectricity and frictional electricity is all very remarkable, itself also has reductive action, can suppress the corruption of food, deodorizing effect is 6 times of gac, and its far infrared and the effect that enhances metabolism are semi-permanent.
As fully visible, tourmalinite is people living in faraway places as a kind of DEVELOPMENT PROSPECT of silicic acid mineral, and is unpredictalbe.But the very regrettably above-mentioned effect of tourmalinite can not be used with the performance of monomer composition, can only adopt the material acting in conjunction relevant with other to realize according to purposes.
Summary of the invention
The objective of the invention is: the tourmalinite that can realize above-mentioned functions composite product is provided.
This special tourmaline ceramic product contains the major ingredient tourmalinite, reaches the mixture of auxiliary material crystal quartz, clay, zirconium white, titanium oxide, borax powder etc.; It is characterized in that: the incorporation of tourmalinite is 10-60%; And the incorporation of crystal quartz, clay, zirconium white, titanium oxide, borax powder mixture is 40-90%.
Described various main materials and auxiliary materials particle fineness is between 200～order, 1400 orders.
Described this special tourmaline ceramic product is fired under 600 ℃～1300 ℃ flame temperatures and is formed.
Embodiment
Special tourmaline ceramic product according to above scheme is mixed with not only can become the ceramic health-care product, also can become the water body purification agent simultaneously, to the pollution of water body, can also be used as uses such as anticorrosion reodorant simultaneously when effectively suppressing the algae growth.
Below provide embodiments of the invention, and further provide the enforcement embodiments of the invention.
| Major ingredient | Incorporation | Auxiliary material | Incorporation | |
| Embodiment 1 | Tourmalinite | 10％ | Kaolin (clay class) | 90％ |
| Embodiment 2 | Tourmalinite | 60％ | Kaolin (clay class)+zirconium white | 40％ |
| Embodiment 3 | Tourmalinite | 35％ | Kaolin+nickel powder | 65％ |
| Embodiment 4 | Tourmalinite | 40％ | Clay+zirconium white+nickel powder | 60％ |
| Embodiment 5 | Tourmalinite | 25％ | Crystal quartz+clay+zirconium white+titanium oxide+borax powder | 75％ |
| Embodiment 6 | Tourmalinite | 50％ | Silver suboxide+zeolite | 50％ |
| Embodiment 7 | Tourmalinite | 60％ | Zeolite | 40％ |
| Embodiment 8 | Tourmalinite | 20％ | Clay+zeolite+titanium oxide+bismuthous oxide bismuth trioxide+silver suboxide+nickel powder+borax powder | 80％ |
In the above-described embodiments, each embodiment that is provided, according to the difference of its constituent,
Its effect separately also is not quite similar.Its actual manufacture craft route is as follows:
The all mixing mud of material apolegamy → pulverizing → slight adjustments → moulding → drying machine that is shaped grinds shaping → burn till processing → finished product.Specific practice promptly is: at first according to the function and usage of being drafted, choose a certain proportion of tourmalinite and supplementary product kind and proportioning; Next is that above-mentioned compound is carried out efflorescence, be ground into 200-1400 purpose fine powder according to processing requirement, and uniform mixing is smelt moulded pottery not yet put in a kiln to bake; It three is slight shapings, adjusts granularity, the 4th, and dry rounding shaping, it five is the blank after being shaped to be allowed to condition under 600 ℃～1300 ℃ the flame burn till, and becomes product.
In this tourmaline ceramic goods, as the tourmalinite raw material that is suitable for, each major ingredient SiO in itself main chemical
2Content is at 35-75%; AL
2O
3Content at 12-35%, MgO content at 1-23%, Fe
2O
3Content is between 2-5.5%.
The clay that is adopted can be a kaolin, also can be that other contains magnesium at the general clay more than 10%.Also can mix zeolite, bismuthous oxide bismuth trioxide, silver suboxide, nickel powder in the auxiliary material that is adopted.
This special cermacis goods are mainly used in the algal grown that suppresses in lake, marsh, the fishing ground, purify water, also can be used for anticorrosion, antibiotic, the health care etc. under some environment.
Claims (3)
1, a kind of special tourmaline ceramic product contains the major ingredient tourmalinite, reaches auxiliary material crystal quartz, clay, zirconium white, titanium oxide, borax powder, and it is characterized in that: the incorporation of tourmalinite is 10-60%; And the incorporation of the mixture of crystal quartz, clay, zirconium white, titanium oxide, borax powder is 40-90%.
2, a kind of special tourmaline ceramic product according to claim 1, the particle fineness that it is characterized in that the various main materials and auxiliary materials that adopted is between 200～1400 orders.
3, a kind of special tourmaline ceramic product according to claim 1 burns till under 600 ℃ of-1300 ℃ of temperature.