CN1236142C - 轻量涂布印刷纸及其制造方法 - Google Patents
轻量涂布印刷纸及其制造方法 Download PDFInfo
- Publication number
- CN1236142C CN1236142C CN 03118027 CN03118027A CN1236142C CN 1236142 C CN1236142 C CN 1236142C CN 03118027 CN03118027 CN 03118027 CN 03118027 A CN03118027 A CN 03118027A CN 1236142 C CN1236142 C CN 1236142C
- Authority
- CN
- China
- Prior art keywords
- pulp
- paper
- bleached
- printing paper
- coated printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种轻量涂布印刷纸及其制造方法,包括用漂白硫酸盐针叶木浆(BKP)、意大利杨碱性过氧化氢热磨机械浆(APMP)、漂白硫酸盐苇浆(BKP)或商品漂白阔叶木浆,经分别打浆后配比调制成混合浆,加入辅料配制成纸料,再抄造,其特征在于:采用AKD中性施胶、机内涂布,软辊压光等先进的抄造工艺,制得的轻量涂布印刷纸纸张表面强度好、纸张松厚度、透气度优于全化学浆配抄的轻涂纸,纸张平整光滑,适用于高档杂志、宣传材料等的彩色印刷,印刷色彩饱满鲜艳,图像网点清晰,可以代替进口产品,对我国造纸原料结构调整,对保护生态环境,都会产生积极的影响和极大的示范作用。
Description
技术领域
本发明涉及一种轻量涂布印刷纸及其制造工艺。
背景技术
轻量涂布纸是80年代由日本、欧美等国率先开发出来的新产品,是指在原纸每面涂布量低于12g/m2的一种印刷纸。通过对纸页的表面涂布处理,机械整饰,改善纸页的表面性能,广泛用于高档杂志、广告、画刊、课本的彩色印刷,发展十分迅速,是市场增长率最快的纸种。
国内生产轻涂纸的厂家主要有晨鸣、高唐等少数几家,所使用的原料大多数为化学浆,在纸张松厚度、透气度等技术指标方面与国外产品有一定的差距,尤其是机内涂布、压光装备水平不是很高,产品质量无法与国外同类产品相比。
发明内容
为克服一般不含化学机械浆的轻量涂布印刷纸的缺陷,本发明的目的是提供一种轻量涂布印刷纸及其制造方法。纸张具有表面强度好、松厚度、透气度优于全化学浆配抄的轻涂纸,纸张平整光滑、适用于高档杂志、宣传材料等的彩色印刷,印刷色彩饱满鲜艳,图像网点清晰的特点。为实现上述目的,本发明的技术方案如下:一种轻量涂布印刷纸,其特征在于:(1)浆料为漂白硫酸盐针叶木浆(BKP)、意大利杨碱性过氧化氢热磨机械浆(APMP)、漂白硫酸盐苇浆(BKP)或商品漂白阔叶木浆;浆料重量配比为化学木浆BKP:化学苇浆BKP或商品漂白阔叶木浆:意杨APMP浆为24~30∶30~35∶30~45;(2)辅料用量为;(A)AKD(烷基烯酮二聚体)用量0.1~0.25%(对绝干浆);(B)PAM(聚丙烯酰胺)用量:0.02~0.05%(对绝干浆);(C)阳离子淀粉用量:1.0~1.5%(对绝干浆);(D)染料用量:70~80g/t(对绝干浆);(E)填料用量:8~14%(对绝干浆);(3)涂料配方:瓷土50~80pph,重质碳酸钙(GCC)20~50pph,有机颜料5~10pph,以上三种原料配比为颜料总计100份;改性淀粉相对以上100份颜料为5~8pph(其中PPh为每100份中的份数);经分别打浆后配用抄造,制得的轻量涂布印刷纸定量为50~90g/m2,水分为5.5~7.0%,白度(ISO)75~90%,不透明度大于82%,表面吸收重量小于35g/m2;裂断长(纵向)大于4200m;横向耐折度大于12次,平滑度正、反两面平均大于500S,平滑度两面差小于20%,横向伸缩率小于3.5%;印刷表面强度不低于2.0m/s;灰分15~30%;光泽度大于35%,印刷光泽度大于65%。
所述的轻量涂布印刷纸的制造方法,包括用漂白硫酸盐针叶木浆(BKP)、意大利杨碱性过氧化氢热磨机械浆(APMP)、漂白硫酸盐苇浆(BKP)或商品漂白阔叶木浆,经分别打浆后配比调制成混合浆,加入辅料配制成纸料,再抄造,其特征在于:采用AKD中性施胶、机内膜涂布、软辊压光整饰,工艺技术参数如下:(1)浆料叩解度:漂白硫酸盐针叶木浆BKP:26~30°SR;漂白硫酸盐苇浆BKP:26~30°SR;商品漂白阔叶木浆:26~32°SR;意大利杨碱性过氧化氢热磨机械浆APMP:50~60°SR;(2)上网工艺条件:(A)上网浆浓度:0.5-0.75%;(B)上网浆pH值:7.5~8.5;(C)上网浆叩解度:50-60°SR;(3)涂布工艺条件:涂料粘度:800~1200mpa.s,pH:8.5~9.0;固含量:52~60%;涂布量8~20g/m2;进施胶前纸页干度92~95%;出施胶后纸页干度68~70%。(4)软压光工艺条件:一压区压力200~250kg/cm;二压区压力200~280kg/cm;一压光温度120℃~150℃;二压光温度120℃~150℃;进压光前纸页水份6~8%。
所述意大利杨包括欧美黑杨72#、美洲黑杨63#、美洲黑杨69#等。
本发明制造工艺简单,产品配用了我公司自主知识产权的意杨APMP浆,采用AKD中性施胶、机内膜涂布、软辊压光等先进的抄造工艺。该产品具有表面强度好、松厚度、透气度优于全化学浆配抄的轻涂纸,纸张平整光滑、适用于高档杂志、宣传材料等的彩色印刷,印刷色彩饱满鲜艳,图像网点清晰的特点。岳阳纸业股份有限公司是国内首家开发配用部分以意大利杨APMP化机浆生产的轻量涂布印刷纸的厂家。生产的轻量涂布印刷纸填补国内空白,对国内轻量涂布纸市场有着重要的影响。本发明的产品经国家纸张质量检测中心检测达到参照日本等国质量指标制定的企业标准。产品投放市场,深受用户欢迎。开发意杨APMP配抄轻量涂布印刷纸新工艺,利用速生阔叶木资源,采用无污染工艺制备高得率浆,缓解了我国木材资源紧张局面,不仅对我国造纸原料结构调整,而且对保护生态环境,都会产生积极的影响和极大的示范作用。
具体实施方式
实施例:将分别打至适当叩解度的针叶木BKP浆、芦苇BKP浆、意杨APMP浆按28∶35∶37配比调制成600kg混合浆,加入67kg轻质碳酸钙填料及其适当的其它化学助剂配制成纸料,纸料经网部成形、复合压榨、前干燥;经膜涂布(涂料量333kg)、红外干燥、后干燥、软压光整饰、卷取、复卷得到用户要求规格尺寸的轻量涂布印刷纸1000kg。抄造上网浆浓度0.75%、pH值8.2、叩解度55°SR;涂布工艺条件:涂料粘度1000mpa.s、pH值8.5、固含量:55%,涂布量15g/m2,进施胶前纸页干度93%,出施胶后纸页干度68%;软压光工艺条件:一压区压力220kg/cm,二压区压力250kg/cm,一压光温度130℃,二压光温度130℃,进压光前纸页水份7%。成纸卷取水分6.5%;制得的轻量涂布纸定量为65g/m2,水分为6.5%,白度(ISO)85%,不透明度85%,表面吸收重量30g/m2;裂断长(纵向)4200m;横向耐折度20次,平滑度正/反500S/550S,平滑度两面差15%,横向伸缩率3.0%;印刷表面强度2.0m/s;灰分30%;光泽度30%,印刷光泽度65%。
Claims (2)
1、一种轻量涂布印刷纸,其特征在于:(1)浆料为漂白硫酸盐针叶木浆、意大利杨碱性过氧化氢热磨机械浆、漂白硫酸盐苇浆或商品漂白阔叶木浆;浆料重量配比为漂白硫酸盐针叶木浆∶漂白硫酸盐苇浆或商品漂白阔叶木浆∶意大利杨碱性过氧化氢热磨机械浆为24~30∶30~35∶30~45;(2)辅料对绝干浆用量为:(A)烷基烯酮二聚体用量0.1~0.25%;(B)聚丙烯酰胺用量:0.02~0.05%;(C)阳离子淀粉用量:1.0~1.5%;(D)染料用量:70~80g/t;(E)填料用量:8~14%;(3)涂料配方:瓷土50~80pph,重质碳酸钙20~50pph,有机颜料5~10pph,以上三种原料配比为颜料总计100份;改性淀粉相对以上100份颜料为5~8pph;经分别打浆后配用抄造,制得的轻量涂布印刷纸定量为50~90g/m2,水分为5.5~7.0%,白度75~90%,不透明度大于82%,表面吸收重量小于35g/m2;裂断长大于4200m;横向耐折度大于12次,平滑度正、反两面平均大于500S,平滑度两面差小于20%,横向伸缩率小于3.5%;印刷表面强度不低于2.0m/s;灰分15~30%;光泽度大于35%,印刷光泽度大于65%。
2、权利要求1所述的轻量涂布印刷纸的制造方法,包括用漂白硫酸盐针叶木浆、意大利杨碱性过氧化氢热磨机械浆、漂白硫酸盐苇浆或商品漂白阔叶木浆,经分别打浆后配比调制成混合浆,加入辅料配制成纸料,再抄造,其特征在于:采用烷基烯酮二聚体中性施胶、机内膜涂布、软辊压光整饰工艺,技术参数如下:(1)浆料叩解度:漂白硫酸盐针叶木浆:26~30°SR;漂白硫酸盐苇浆:26~30°SR;商品漂白阔叶木浆:26~32°SR;意大利杨碱性过氧化氢热磨机械浆:50~60°SR;(2)上网工艺条件:(A)上网浆浓度:0.5-0.75%;(B)上网浆pH值:7.5~8.5;(C)上网浆叩解度:50~60°SR;(3)涂布工艺条件:涂料粘度:800~1200mpa.s,pH:8.5~9.0;固含量:52~60%;涂布量8~20g/m2;进施胶前纸页干度92~95%;出施胶后纸页干度68~70%。(4)软压光工艺条件:一压区压力200~250Kg/cm;二压区压力200~280Kg/cm;一压光温度120℃~150℃;二压光温度120℃~150℃;进压光前纸页水份6~8%。