CN1229704A - 铜钨－铬铜整体触头立式烧结方法 - Google Patents

铜钨－铬铜整体触头立式烧结方法 Download PDF

Info

Publication number
CN1229704A
CN1229704A CN 98112840 CN98112840A CN1229704A CN 1229704 A CN1229704 A CN 1229704A CN 98112840 CN98112840 CN 98112840 CN 98112840 A CN98112840 A CN 98112840A CN 1229704 A CN1229704 A CN 1229704A
Authority
CN
China
Prior art keywords
copper
chromium
tungsten
sintering
tail
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 98112840
Other languages
English (en)
Other versions
CN1096322C (zh
Inventor
范志康
梁淑华
陈文革
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xian University of Technology
Original Assignee
Xian University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xian University of Technology filed Critical Xian University of Technology
Priority to CN98112840A priority Critical patent/CN1096322C/zh
Publication of CN1229704A publication Critical patent/CN1229704A/zh
Application granted granted Critical
Publication of CN1096322C publication Critical patent/CN1096322C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

铜钨－铬铜整体触头立式烧结方法,属于铜钨－铬铜整体触头烧结技术,解决已有技术中整体触头沿圆周方向组织、性能不均匀;触指变形不均匀,使用过程中电烧损大;毛坯缩孔较深,工艺出品率低;铜钨头与铬铜尾铜的结合强度低等技术问题。本发明将装有铜钨头与铬铜尾铜的成型模竖直放置于烧结装置的炉腔内进行整体烧结,并用还原气氛对铜钨头与铬铜尾铜的结合面进行有效地还原处理。本发明用于所有铜钨－铬铜整体触头的烧结。

Description

铜钨-铬铜整体触头立式烧结方法
本发明涉及一种铜钨-铬铜整体触头烧结方法，尤其是铜钨-铬铜整体触头立式烧结方法。
在本发明完成之前，本发明的发明人烧结铜钨-铬铜整体触头采用卧式烧结方法，成型模斜卧放置于卧式连续烧结炉内，导致整体触头沿圆周方向组织性能不均匀，如硬度不均匀，触指变形不均匀，即使能用，在使用过程中触头电烧损大；毛坯缩孔较深，工艺出品率低；在烧结过程中还原气氛不好控制，无法对铜钨头与铬铜尾铜的结合面进行有效的还原处理，导致结合强度低。
本发明的目的在于，提供一种铜钨-铬铜整体触头立式烧结方法。采用本烧结方法成形的铜钨-铬铜整体触头沿圆周方向组织、性能均匀性好，耗材少，并能在烧结过程中对铜钨头与铬铜尾铜的结合面进行有效还原处理，净化结合面，结合强度高。
本发明公开的烧结方法是将装有铜钨头与铬铜尾铜的成型模竖直放置于烧结装置炉腔内进行整体烧结成型。
具体步骤如下：
1．将铜钨头置于成型模底部，然后放入铬铜尾铜，再将成型模竖直放入烧结装置炉腔内，后在惰性气氛保护下，用感应加热或电阻加热方式加热
2．待炉温升至950～980℃时，用还原气氛对铜钨头与铬铜尾铜的结合面进行还原处理10～30分钟；
3．在惰性气氛保护下，将炉温升至1250～1280℃烧结1～2小时；
4．将炉温冷却至250～300℃，将铜钨-铬铜整体触头取出。
本发明与已有技术相比具有如下优点：
1．因将成型模竖直放置于烧结装置炉腔内，所以铜钨头与铬铜尾铜沿圆周组织、性能分布均匀性好；触指变形小，使用过程中触头电烧损小；毛坯缩孔小，工艺出品率高，减少了材料消耗；
2．因采用还原气氛对铜钨头与铬铜尾铜结合面进行有效还原，将结合面净化，提高了结合强度。
附图是铜钨-铬铜整体触头立式烧结装置的结构示意图。其中1为炉体，2为感应加热线圈，3为铜钨头，4为铬铜尾铜，5为成型模，6为缩孔，7为炉盖。
本发明的具体实施方案结合附图叙述如下：
实施例1
CuW70-QCr0.5整体触头按下列工艺烧结：
1．将CuW70铜钨头置于成型模底部，然后放入QCr0.5铬铜尾铜，再将成型模竖直放入烧结炉腔内，并在氮气气氛保护下用感应加热；
2．待炉温升至980℃，用氢气对CuW70铜钨头与QCr0.5铬铜尾铜的结合面进行还原处理20分钟；
3．在氮气气氛保护下将炉温升至1250℃烧结1.5小时；
4．将炉温冷却至300℃，把CuW70-QCr0.5整体触头取出。
实施例2
CuW80-QCr0.5整体触头按下列工艺烧结：
1．将CuW80铜钨头置于成型模底部，然后放入QCr0.5铬铜尾铜，再将成型模竖直放入烧结炉腔内，后在氮气气氛保护下用感应加热；
2．待炉温升至960℃，用氢气对CuW80铜钨头与QCr0.5铬铜尾铜的结合面进行还原处理30分钟；
3．在氮气气氛保护下将炉温升至1260℃，烧结1.5小时；
4．将炉温冷却至300℃，把CuW80-QCr0.5整体触头取出。

Claims (4)

  1. 一种铜钨-铬铜整体触头的烧结方法，其特征是，将装有铜钨头和铬铜尾铜的成型模竖直放置于烧结装置的炉腔内进行整体烧结成型；
    具体步骤如下：
    1．将铜钨头置于成型模〔5〕的底部，然后放入铬铜尾铜〔4〕，再将成型模〔5〕竖直放入烧结装置炉腔内，后在惰性气氛保护下，用感应加热或电阻电热方式加热；
  2. 2．待炉温升至950～980℃时，用还原气氛对铜钨头〔3〕与铬铜尾铜〔4〕的结合面进行还原处理10～30分钟；
  3. 3．在惰性气氛保护下，将炉温升至1250～1280℃，烧结1～2小时；
  4. 4．将炉温冷却至250～300℃，将铜钨-铬铜整体触头取出。
CN98112840A 1998-03-23 1998-03-23 铜钨——铬铜整体触头立式烧结方法 Expired - Fee Related CN1096322C (zh)