CN1210830A - Beili art stone and its forming technology - Google Patents
Beili art stone and its forming technology Download PDFInfo
- Publication number
- CN1210830A CN1210830A CN98111434A CN98111434A CN1210830A CN 1210830 A CN1210830 A CN 1210830A CN 98111434 A CN98111434 A CN 98111434A CN 98111434 A CN98111434 A CN 98111434A CN 1210830 A CN1210830 A CN 1210830A
- Authority
- CN
- China
- Prior art keywords
- natural
- stone
- hours
- artificial
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Beili art stone is an artificial stone with color hue and sense similar to natural stone, high strength, water resistance and fire resistance, and excellent weather resistance, and it is suitable for used as artistic arts, ornament and others. It consists of natural or artificial stone powder and color sand, cement, mineral pigment and other additive, and it is produced through material weighing, mixing, moulding through tamping, demolding after solidification, steam curing, trimming, painting surface treating agent, painting methyl silicone resin solution and full drying.
Description
What power up process stone of the present invention and moulding process thereof related to is a kind of have lithotome tone, texture, the intensity height, and waterproof is not fired, and weathering resistance is good, is suitable for doing the artificial art stone material and the forming process thereof of artistic moulding, ornament.
Existing processes is decorated building stones, stone material, and three classes are arranged, and a class is to adopt lithotome, through cutting, chisel shaping, be subjected to limitation of size complete processing complexity, time-consuming, cost is high, be difficult to produce in batches, the quality instability.Second class is to utilize mineral-type materials such as cement, magnesium oxide, magnesium chlorides etc. add stone flour stone grain mineral fibre or vegetable fibre as agglutinate, make aggregate or reinforcement material, model forming, this based article outward appearance is texture and the tone that cement or plastering outward appearance prior art can't show lithotome, the 3rd class is to utilize organic polymer resin to make agglutinate, admixture stone flour stone grain, mill base, solidifying agent, model formings such as promotor, this type of technology products made thereby surface compact light, no lithotome chisel texture, and cost is higher, goods are subjected to the influence of sunshine and difference variation yielding out of doors, loss of gloss, the surface efflorescence, the processing shrinkage coefficient should not be made big product of view picture greatly.
The objective of the invention is the weak point at above-mentioned Handicraft decorative stone material existence, a kind of power up process stone and moulding process thereof are provided, power up process stone has lithotome tone texture, be rich in artistic appeal, the intensity height, carrying capacity is big, water-tolerant, contamination resistance is strong, has certain ventilation, water-absorbent, weathering resistance is good, is a kind of good artistic design, ornament Artistic stone material, its forming process novelty, it is convenient to make, and cost is low pollution-free.
Power up process stone and moulding process thereof take following scheme to realize: power up process stone is by various chromatic natural or artificial stone flours, natural or artificial color sand, and cement, water mineral color additive composition is formed.Power up process stone composition scope is:
Natural or artificial stone flour 20%～40% (weight)
Natural or artificial color sand 20%～65% (weight)
Cement 10%～30% (weight)
Water 5%～20% (weight)
Mineral color 0%～5% (weight)
Additive 0%～5% (weight)
The each component summation is 100% (weight)
Wherein additive can adopt acrylic ester emulsion, phenylpropyl alcohol carboxyl emulsion.
Power up process stone forming process:
1, weighing composition raw material according to a certain ratio: the natural or artificial color sand of various chromatic natural or artificial stone flours, cement, water, mineral color, additive are standby,
2, earlier chromatic natural the or artificial stone flour of siccative, natural or artificial color sand, cement, mineral color are stirred,
3, water and additive are added in the above-mentioned siccative that stirs slowly further stir again, make blank,
4, with the mould coated releasing agent of cleaning out, the above-mentioned blank of mixing thoroughly is added in the die cavity in batches, mechanical pudding,
5, the ambient cure demoulding in 24～48 hours,
6, normal temperature or vapor cure, vapor cure 24～48 hours, normal temperature maintenance 72～168 hours requires heat and moisture preserving, 15 ℃～40 ℃ of holding temperatures.
7, air-dry, 48 hours～72 hours time, finishing, polishing, cleaning,
8, coated surface treatment agent: optional unsaturated polyester resin solution, a kind of or compound coated in polyurethane resin solution, benzene emulsion, the acrylic ester emulsion 1～3 time, drying.
9, coated methyl silicon resin solution is 1～3 time.
10, promptly make power up process stone finished product after the thorough drying.
Power up process stone has lithotome color harmony texture, rich color, be rich in artistic appeal, the high carrying capacity of intensity is big, and contamination resistance is strong, good waterproof performance, have certain ventilation, water-absorbent is not fired, and is not afraid of sunshine, weathering resistance is good, can be used as a kind of good permanent molding artistic design stone material, building, ornament material, applied range.Power up process novel unique, the making facility of technology of doing made of stones, cost is low, pollution-free generation in the making processes.Can be made into dead front type and air-permeable product.
Embodiment 1: make power up process stone 100kg
It is 1, by proportioning weighing composition raw material: chromatic natural or artificial stone flour 20kg (weight proportion 20%), natural or artificial color sand 50kg (weight proportion 50%), cement 20kg (weight proportion 20%), water 10kg, standby,
2, earlier chromatic natural the or artificial stone flour of siccative, natural or artificial color sand, cement are stirred,
3, water is added slowly further to stir in the above-mentioned siccative that stirs again and makes blank,
4, with the mould coated releasing agent of cleaning out, the above-mentioned blank of mixing thoroughly is added in the die cavity in batches, mechanical pudding,
5, the ambient cure demoulding in 24 hours,
6, the normal temperature maintenance is 120 hours, requires heat and moisture preserving, holding temperature about 25 ℃,
7, finishing in air-dry 48 hours, polishing, cleaning,
8, coated acrylic ester emulsion, coated is 3 times continuously, drying,
9, coated first machine silicone resin is 1 time,
10, promptly make power up process stone finished product after the thorough drying.
Embodiment 2: make power up process stone 100kg
1, by proportioning weighing composition raw material: chromatic natural or artificial stone flour 30kg (weight proportion 30%), natural or artificial color sand 40kg (weight proportion 40%), cement 17kg (weight proportion 17%), water 5kg (weight proportion 5%), mineral color 5kg (weight proportion 5%), ACRYLIC EMULSION (additive) 3kg (weight proportion 3%), standby
2, earlier chromatic natural the or artificial stone flour of siccative, natural or artificial color sand, cement, pigment are stirred,
3, water, acrylic ester emulsion are added slowly further to stir in the above-mentioned siccative that stirs again and make blank,
4, with the mould coated releasing agent of cleaning out, the above-mentioned blank of mixing thoroughly is added in the die cavity in batches, mechanical pudding,
5, the ambient cure demoulding in 36 hours,
6, vapor cure is 48 hours,
7, air-dry, 48 hours time, finishing, polishing, cleaning,
8, coated polyurethane resin solution, coated is 2 times continuously, drying,
9, coated methyl silicon resin solution is 2 times,
10, promptly make power up process stone finished product after the thorough drying.
Embodiment 3: make power up process stone 100kg
1, by proportioning weighing composition raw material: chromatic natural or artificial stone flour 40kg (weight proportion 40%), natural or artificial color sand 22kg (weight proportion 22%), cement 25kg (weight proportion 25%), water 8kg (weight proportion 8%), mineral color 1kg (weight proportion 1%), phenylpropyl alcohol carboxyl emulsion 4kg (weight proportion 4%), standby
2, earlier natural the or artificial stone flour of siccative, natural or artificial color sand, cement, pigment are stirred,
3, again water, phenylpropyl alcohol carboxyl emulsion are added further to stir in the above-mentioned siccative that stirs slowly and make blank,
4, with the mould coated releasing agent of cleaning out, the above-mentioned blank of mixing thoroughly is added in the die cavity in batches, mechanical pudding,
5, the ambient cure demoulding in 48 hours,
6, vapor cure is 30 hours,
7, air-dry, 36 hours, finishing, polishing, cleaning,
8, coated unsaturated polyester resin solution, coated is 3 times continuously, drying,
9, coated methyl silicon resin solution is 1 time,
10, promptly make power up process stone finished product after the thorough drying.
Claims (4)
1, a kind of power up process stone is characterized in that by natural or artificial stone flour, natural or artificial color sand, and cement, water, mineral color, additive composition are formed.
2, power up process stone according to claim 1 is characterized in that craft stone composition scope is:
Natural or artificial stone flour 20%～40% (weight)
Natural or artificial color sand 20%～65% (weight)
Cement 10%～30% (weight)
Water 5%～20% (weight)
Mineral color 0%～5% (weight)
Additive 0%～5% (weight)
The each component summation is 100% (weight).
3, a kind of power up process stone moulding process is characterized in that:
(1), weighing composition raw material according to a certain ratio: the natural or artificial color sand of various chromatic natural or artificial stone flours, cement, water, mineral color, additive are standby,
Siccative chromatic natural or artificial stone flour, natural or artificial color sand, cement, mineral color stirred (2), earlier,
(3), again water and additive are added in the above-mentioned siccative that stirs slowly and further stir, make blank,
(4), with the mould coated releasing agent of cleaning out, the above-mentioned blank of mixing thoroughly is added in the die cavity in batches, mechanical pudding,
(5), the ambient cure demoulding in 24 hours～48 hours,
(6), normal temperature maintenance or vapor cure, vapor cure 24 hours～48 hours, normal temperature maintenance 72 hours～168 hours requires heat and moisture preserving, 15 ℃～40 ℃ of holding temperatures,
(7), air-dry, 48 hours～72 hours time, the finishing, the polishing, the cleaning,
(8), the coated surface treatment agent: optional unsaturated polyester resin solution, a kind of or compound coated in polyurethane resin solution, benzene emulsion, the acrylic ester emulsion 1～3 time, drying,
(9), coated methyl silicon resin solution 1～3 time,
(10), promptly make power up process stone finished product after the thorough drying.
4, power up process stone according to claim 1 is characterized in that additive can adopt acrylic ester emulsion, phenylpropyl alcohol carboxyl emulsion.