CN1210434C - 带有保护层系的刀具 - Google Patents
带有保护层系的刀具 Download PDFInfo
- Publication number
- CN1210434C CN1210434C CN 97182439 CN97182439A CN1210434C CN 1210434 C CN1210434 C CN 1210434C CN 97182439 CN97182439 CN 97182439 CN 97182439 A CN97182439 A CN 97182439A CN 1210434 C CN1210434 C CN 1210434C
- Authority
- CN
- China
- Prior art keywords
- cutter
- workpiece
- value
- mex
- arc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
样品编号 | 涂覆情况 | 层 | x | y | QI=I(200)/I(111) | 残余应力GPa | 可达到的切削距离(m)(直到分层的距离) | 附注 | |||
偏电压(负) | 氮气压力(毫巴) | 弧电流(A) | |||||||||
本发明 | 1 | 60 | 2.0×10-2 | 150 | (TixAly)N | 0.5 | 0.5 | 1.5 | 5.2 | 2.2m(2.1m) | |
2 | 60 | 8.0×10-2 | 150 | (TixAly)N | 0.5 | 0.5 | 6.7 | 4.8 | 2.8m(2.5m) | ||
3 | 40 | 2.0×10-2 | 150 | (TixAly)N | 0.5 | 0.5 | 8.1 | 4.2 | 8.8m(8.5m) | 表面精研 | |
4 | 40 | 3.0×10-2 | 150 | (TixAly)N | 0.4 | 0.6 | 10.2 | 3.9 | 3.9m(3.5m) | ||
5 | 40 | 0.5×10-2 | 150 | (TixAly)N | 0.5 | 0.5 | 6.0 | 5.8 | 2.0m(1.7m) | ||
6 | 30 | 2.0×10-2 | 150 | (TixAly)N | 0.5 | 0.5 | 15.4 | 2.5 | 4.2m(4.0m) | ||
7 | 20 | 2.0×10-2 | 150 | (TixAly)N | 0.5 | 0.5 | 22.5 | 1.2 | 3.3m(3.3m) | ||
对比例 | 8 | 60 | 0.5×10-2 | 150 | (TixAly)N | 0.5 | 0.5 | 0.8 | 6.1 | 1.0m(0.8m) | |
9 | 100 | 2.0×10-2 | 150 | (TixAly)N | 0.5 | 0.5 | 0.7 | 5.5 | 0.9m(0.9m) | ||
10 | 100 | 3.0×10-2 | 150 | (TixAly)N | 0.5 | 0.5 | 0.9 | 4.8 | 0.8m(0.7m) | ||
11 | 150 | 2.0×10-2 | 150 | (TixAly)N | 0.5 | 0.5 | 0.2 | 7.2 | 0.1m(0.1m) | ||
12 | 100 | 0.5×10-2 | 150 | (TixAly)N | 0.4 | 0.6 | 0.1 | 6.8 | 0.2m(0.1m) |
样品编号 | 中间层(微米) | 钛铝层 | x | y | 最外层 | QI=I(200)/I(111) | 可达到的切削距离(m)(直到分层的距离) | |
本发明 | 13 | TiN(0.4μm) | (TiXAlY)N(4.6μm) | 0.5 | 0.5 | - | 1.5 | 4.5m(4.2) |
14 | TiN(0.4μm) | (TiXAlY)N(4.1μm) | 0.5 | 0.5 | TiCN(0.5μm) | 7.2 | 7.8(7.6m) | |
15 | TiN(0.4μm) | (TiXAlY)N(4.4μm) | 0.5 | 0.5 | TiCN(0.5μm) | 6.8 | 6.0m(5.5m) | |
16 | TiCN(0.4μm) | (TiXAlY)N(4.1μm) | 0.5 | 0.5 | (TiAl)NO(0.5μm) | 5.2 | 6.2m(6.0m) | |
17 | TiN(0.4μm) | (TiXAlY)N(4.1μm) | 0.5 | 0.5 | Al2O3(0.5μm) | 12.5 | 10.1m(9.8m) | |
18 | TiN(0.4μm) | (TiXAlY)N(4.1μm) | 0.5 | 0.5 | Al2O3(0.5μm) | 7.0 | 9.8m(9.5m) | |
对比例 | 19 | TiN | (TiXAlY)N | 0.5 | 0.5 | - | 0.8 | 1.5m(1.2m) |
20 | TiN | (TiXAlY)N | 0.5 | 0.5 | TiCN | 0.8 | 1.9m(1.5m) | |
21 | TiN | (TiXAlY)N | 0.5 | 0.5 | TiCN | 0.7 | 1.8m(1.5m) | |
22 | TiN | (TiXAlY)N | 0.5 | 0.5 | (TiAl)NO | 0.1 | 0.6m(0.4m) |
样品编号 | 层组份 | w | x | y | z | 氧化膜的厚度(微米) | |
本发明 | 23 | (TiXAlYYZ)N | 0.48 | 0.5 | 0.02 | 0.7 | |
24 | (TiXAlYCrZ)N | 0.48 | 0.5 | 0.02 | 0.9 | ||
25 | (TiXAlYZrZ)N | 0.48 | 0.5 | 0.02 | 0.7 | ||
26 | (TiXAlYYZ)N | 0.25 | 0.5 | 0.25 | 0.1 | ||
27 | (TiXAlYZrZ)N | 0.25 | 0.5 | 0.25 | 0.5 | ||
28 | (TiXAlYWZ)N | 0.4 | 0.5 | 0.1 | 0.8 | ||
29 | (TiXAlYSiZ)N | 0.4 | 0.5 | 0.1 | 0.1 | ||
30 | (TiXAlYSiZ)N | 0.48 | 0.5 | 0.02 | 0.2 | ||
31 | (TiXAlYHfZ)N | 0.4 | 0.5 | 0.1 | 0.9 | ||
32 | (TiXAlYYZSiW)N | 0.1 | 0.3 | 0.5 | 0.1 | 0.05 | |
对比例 | 33 | (TiXAlY)N | 0.4 | 0.6 | 1.8 | ||
34 | (TiXAlYNbZ)N | 0.4 | 0.5 | 0.1 | 2.5 | ||
35 | (TiXAlYTaZ)N | 0.4 | 0.5 | 0.1 | 3.3 |
偏电压(负) | 氮气压力(毫巴) | 弧电流(A) | 中间层 | 层 | x | y | z | QI | 残余应力(GPa) | 钻孔编号 | ||
本发明 | 36 | 40 | 3.0×10-2 | 200 | TiN0.1μm | (TixAly)N | 0.6 | 0.4 | 5.4 | 2.1 | 210 | |
37 | 40 | 3.0×10-2 | 200 | TiN0.1μm | (TixAlyBz)N | 0.58 | 0.4 | 0.02 | 3.8 | 2.3 | 190 | |
对比例 | 38 | 150 | 1.0×10-2 | 200 | TiN0.1μm | (TixAly)N | 0.6 | 0.4 | 0.03 | 4.5 | 30 | |
39 | 150 | 1.0×10-2 | 200 | TiN0.1μm | (TixAlyBz)N | 0.58 | 0.4 | 0.02 | 0.1 | 4.8 | 38 |
偏电压(负) | 氮气压力(毫巴) | 弧电流(A) | 中间层 | 层 | x | y | QI | 残余应力(GPa) | 切削距离(m) | ||
本发明 | 40 | 40 | 3.0×10-2 | 200 | TiN0.1μm | (TixAly)N | 0.6 | 0.4 | 5.4 | 2.1 | 35m |
对比例 | 41 | 150 | 1.0×10-2 | 200 | TiN0.1μm | (TixAly)N | 0.6 | 0.4 | 0.03 | 4.5 | 11m(剥落) |
偏电压(负) | 氮气压力(毫巴) | 弧电流(A) | 中间层 | 层 | x | y | QI | 残留应力(GPa) | 切削距离(m) | ||
本发明 | 42 | 40 | 3.0×10-2 | 200 | TiN0.08μm | (TixAly)N | 0.6 | 0.4 | 5.0 | 2.2 | 17m |
对比例 | 43 | 150 | 1.0×10-2 | 200 | TiN0.08μm | (TixAly)N | 0.6 | 0.4 | 0.05 | 4.7 | 32m |
偏电压(负) | 氮气压力(毫巴) | 弧电流(A) | 中间层 | 层 | x | y | QI | 残留应力(GPa) | 钻削距离(m) | ||
本发明 | 44 | 40 | 3.0×10-2 | 200 | TiN0.1μm | (TixAly)N | 0.6 | 0.4 | 5.4 | 2.1 | 95m |
对比例 | 45 | 150 | 1.0×10-2 | 200 | TiN0.1μm | (TixAly)N | 0.6 | 0.4 | 0.03 | 4.5 | 48.5m |
偏电压(负) | 氮气压力(毫巴) | 弧电流(A) | 中间层 | 层 | x | y | QI | 残留应力(GPa) | 刀具寿命(分) | ||
本发明 | 46 | 40 | 3.0×10-2 | 200 | TiN0.12μm | (TixAly)N | 0.6 | 0.4 | 5.0 | 1.9 | 18.1分 |
对比例 | 47 | 150 | 1.0×10-2 | 200 | TiN0.12μm | (TixAly)N | 0.6 | 0.4 | 0.04 | 4.9 | 5.5分 |
Claims (23)