CN1193801A - 单组分有机硅绝缘液 - Google Patents

单组分有机硅绝缘液 Download PDF

Info

Publication number
CN1193801A
CN1193801A CN97108446A CN97108446A CN1193801A CN 1193801 A CN1193801 A CN 1193801A CN 97108446 A CN97108446 A CN 97108446A CN 97108446 A CN97108446 A CN 97108446A CN 1193801 A CN1193801 A CN 1193801A
Authority
CN
China
Prior art keywords
insulating liquid
mono
organic silicone
component organic
silicone insulating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN97108446A
Other languages
English (en)
Other versions
CN1077718C (zh
Inventor
王鹏
李志英
张天礼
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Irico Display Devices Co Ltd
Original Assignee
Caihong Color CRT General Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Caihong Color CRT General Factory filed Critical Caihong Color CRT General Factory
Priority to CN 97108446 priority Critical patent/CN1077718C/zh
Publication of CN1193801A publication Critical patent/CN1193801A/zh
Application granted granted Critical
Publication of CN1077718C publication Critical patent/CN1077718C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

单组分有机硅绝缘液系用于彩色显像管阳极端子绝缘的特种绝缘材料。该材料用纯有机硅作为主成膜物,在室温下加入环氧树脂对硅树脂进行改性以增加附着力,同时又采用混合溶剂以调整固化速度。通过各组分的优良复配使得该材料具有优良的耐电性,常态电击穿强度为81KV/MM,95±3%湿度下电击穿强度为69KV/MM,好的涂布性和好的贴附性,完全可以满足彩色显像管生产的要求。

Description

单组分有机硅绝缘液
本发明涉及一种专用于彩色显像管阳极端子绝缘的特种绝缘材料。
由于单组分绝缘液克服了双组分绝缘液有效期短，使用不便等缺点，所以比较受欢迎，目前国内彩色显像管生产厂家所用的单组分绝缘液全部依赖进口。在实际使用上仍存在着一些问题。如：国内一些厂家现用的SPA-32E单组分有机硅绝缘液，贴附性不稳定；潮湿状态(95±3％湿度)下阳极端子在加高电压(25KV)时有打火现象发生等。
本发明的目的是自行设计一种单组分绝缘液，并使其满足以下要求：优良的耐电性能；好的粘接性；好的工艺性和足够的有效期。从而较好的用于彩色显像管生产。
本发明的技术解决方案是：一种单组分有机硅绝缘液，由下述部分组成：
聚甲基苯基硅氧烷        18～33％
环氧乙烷                0～8％
白云母                  7～17％
铁红                    2～5％
酯类交联固化剂          1～8％
硅烷偶联剂              1～5％
溶剂                    40～60％
以上单位为重量百分比。
本发明选用聚甲基苯基硅氧烷为主成膜树脂，保证基本的绝缘性，在室温下加入环氧乙烷树脂对硅树脂进行冷改性以增加附着力，加入白云母粉可以提高绝缘性，降低成本，交联剂和硅烷偶联剂起交联固化和提高附着力的作用，溶剂中有少部分乙二醇以调节挥发速度并可提高流平性，从而以利于涂布，对无机填料进行超气流粉碎并严格分级以提高绝缘膜的致密性和憎水性。本发明填补了国内空白，绝缘液使用效果如下表所示：(在彩色显像管阳极端子周围使用)
项  目 工艺要求 使用情况
贴附性 涂敷后2小时胶带粘贴无脱落 合格
涂布性 涂布均匀、流利     合格
电性能 常态：＜25℃，湿度为60±20％，加压至40KV不打火 合格
潮湿状态下：湿度为95±2％，加压至25KV不打火 合格
我们在陕西省电工产品质量监督检验总站对进口的SPA-32E及我们设计的QJY-Z两种绝缘液的击穿强度作了检测，其结果见下表：
产品型号名称     击穿强度(KV)
  常态    受潮
QJY-Z(01)硅绝缘液    81     69
SPA-32E硅绝缘液    95     59
经长期实验和使用证明产品的各项性能及指标均可以满足彩色显像管生产的要求。
以下详细说明本发明实施例：
例1：1995年1月至11月我们按照下面的配方先后生产绝缘液50公斤，生产37cm彩色显像管10余万只，使用效果良好。
  项    目 材    料 用量(W/W％)
主成模树脂 2#硅树脂     33.0
增粘树脂 环氧634     5.0
颜料 铁红     2.0
无机填料 白云母粉     13.0
交联剂 正硅酸乙酯     1.5
偶联剂 KH-560     1.0
溶剂 醋酸丁酯     10.0
乙二醇     2.5
甲苯     32.0
例2：1994年10月至1995年12月我们按照以下配方先后生产绝缘液100公斤用于47cm和54cm彩色显像管的生产，生产彩色显像管20余万只，使用效果良好。
  项    目 材    料 用量(W/W％)
主成模树脂 2#硅树脂     28.5
无机填料 白云母粉     10.0
颜料 铁红     2.5
交联剂 正硅酸乙酯     2.5
硅烷偶联剂 KH-560     1.5
溶剂 乙二醇     4.0
醋酸丁酯     15.0
甲苯     36.0
例3：1995年4月至1996年6月我们按照以下配方先后生产绝缘液80余公斤，生产64cm彩色显像管近20万只，使用效果良好。
  项    目 材    料 用量(W/W％)
主成模树脂 2#硅树脂     22.8
无机填料 白云母粉     11.2
颜料 铁红     3.0
交联剂 钛酸正丁酯     2.0
硅烷偶联剂 KH-550     2.0
溶剂 乙二醇     3.0
醋酸丁酯     12.0
甲苯     44.0
其中2#硅树脂为聚甲基苯基硅氧烷，KH-560为γ-环氧丙基醚丙基三甲氧基硅烷，KH-550为γ-氨丙基三乙氧基硅烷。以上各例加料顺序为：无机填料、颜料、溶剂、主成膜树脂、交联剂、偶联剂。采用5L反应器，环境温度25℃，滚瓶160转/分6～12小时，以10小时为佳，得成品。

Claims (2)

1、一种单组分有机硅绝缘液，其特征在于：由下述部分组成：
    聚甲基苯基硅氧烷    18～33％
    环氧乙烷            0～8％
    白云母              7～17％
    铁红                2～5％
    酯类交联固化剂      1～8％
    硅烷偶联剂          1～5％
    溶剂                40～60％
    以上单位为重量百分比。
2、如权利要求1所述的单组分有机硅绝缘液，其特征在于：所说的溶剂由苯、二甲苯、甲苯中任一种或几种，醋酸丁酯、醋酸乙酯中任一种和正丁醇、乙二醇中任一种混合而成，其重量百分比为：
    芳香烃及衍生物      65～75％
    酯类                20～30％
    醇类                5～10％
CN 97108446 1997-03-13 1997-03-13 单组分有机硅绝缘液 Expired - Fee Related CN1077718C (zh)