CN1186725A - 超薄切割砂轮片及其生产工艺 - Google Patents

超薄切割砂轮片及其生产工艺 Download PDF

Info

Publication number
CN1186725A
CN1186725A CN98113101A CN98113101A CN1186725A CN 1186725 A CN1186725 A CN 1186725A CN 98113101 A CN98113101 A CN 98113101A CN 98113101 A CN98113101 A CN 98113101A CN 1186725 A CN1186725 A CN 1186725A
Authority
CN
China
Prior art keywords
grinding wheel
super thin
thin cutting
layer
product
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN98113101A
Other languages
English (en)
Other versions
CN1061285C (zh
Inventor
梁永辉
李广棋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN98113101A priority Critical patent/CN1061285C/zh
Publication of CN1186725A publication Critical patent/CN1186725A/zh
Application granted granted Critical
Publication of CN1061285C publication Critical patent/CN1061285C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种超薄切割砂轮片及其生产工艺,在砂轮片中增加一层玻璃纤维网格布层,采用碳化硅、酚醛树脂、高强度炭黑作磨料,以四氧化三铁作填料。经混合,加料入模具中,加压制成制件,固化即得。本发明大大提高了砂轮片的硬度,工作速度,切割效率,抗冲击能力,承受侧压能力,降低了材料损耗,降低了环境污染,减少了尘土飞扬。本发明生产工艺简单。

Description

超薄切割砂轮片及其生产工艺
本发明涉及一种切割工具及其生产工艺，特别是一种适合于切割各种高硬度、低损耗的金属材料的砂轮片及其生产工艺。
现有的各种超薄型切割砂轮片(厚度≤1.3mm)均没有增强结构，抗冲击能力差，不能承受侧压，使用速度低(≤35m/s)，且采用的无机填充物颗粒在每平方厘米15.5～31孔范围内(即100～200目)，比重在1.3～3.9g/cm3之间，由于粒度细、比重小，在切割过程中随磨料剥落时而四处飞扬，造成工作面粉尘大、空气污染严重、工效低，使用过程中易破裂、事故率高，不安全等缺点，综合性能欠佳。
本发明的目的就在于克服目前超薄切割砂轮片的上述缺点，提供一种抗冲击性能好，强度高，切割效率高，在使用中不破裂，极少粉尘飞扬、空气污染少、安全可靠的超薄切割砂轮片及其生产工艺。
本发明是这样实现的。
在砂轮片中间增加一层玻璃纤维网格布，使得超薄切割砂轮片的结构分为三层，即上、下为砂轮层，中间为玻璃纤维网格布层。
其中，砂轮层磨料一改传统的超薄型切割砂轮片的刚玉磨料，而用碳化硅磨料(α-SiC)，配以粉状酚醛树脂(分子量小于1000)，高强度碳黑(C)，采用在磨具行业未使用过的四氧化三铁(Fe3O4)作填料。该四种成分的比例和粒径如下：
碳化硅α-SiC     粒径300～400μm  用量70～80重量份
 酚醛树脂         80～100μm       10～20重量份
高强度碳黑C        80～100μm      0.2～1.0重量份
四氧化三铁Fe3O43～5μm         5～15重量份
玻璃纤维网格布的成分是无碱玻璃纤维，厚度为不大于300μm，每平方米重量不大于80克。
以上材料，经加工制成厚度不大于1.2mm、比重为2.30～2.48g/cm3的砂轮片。
填料当然也可以采用本领域普通技术人员熟知的技术加入其它填料，如石膏粉等。
本发明的生产工艺是将碳化硅、酚醛树脂、高强度碳里、四氧化三铁按比例搅拌成既松散又具可塑性的混合料，置于-5°～-10℃低温中，使之成松散状成型料，取半量成型料放入模具内，摊平后放上玻璃纤维网格布，以48～196KPa(0.5～2kg/cm2)压力压平后，将余下的半量成型料倒入摊平，加上盖板，将模具放入油压机内采用70～90℃温度，施以25MPa压力保持0.5～2分钟。卸下模具，制件放入固化炉固化，即得成品。
固化可采用本技术领域普通技术人员熟知的技术。
固化也可以采用先用10小时时间将固化炉内的制件由35℃逐渐升温至于120℃，继用6小时时间将制件由120℃升至180℃，再用20小时时间将制件由180℃降至常温，即得。
本发明超薄切割砂轮片具有以下优点和积极效果：
1.砂轮片的硬度提高，被加工材料可以从洛氐硬度HRC50°提高HRC60°～65°。
2.砂轮片的工作速度提高，从最高速度35m/s提高至72m/s。
3.抗冲击能力、承受侧压能力提高，实验证明无增强网的超薄切割砂轮片从1.5m高度呈自由落体状下落至水泥地面无一不破裂，而本发明的砂轮片从10m处沿任何方向落下无一破裂。
4.减少材料损耗，并达到开料、精磨一次完成，提高了工效。
5.改变了常用的树脂砂轮的无机填料，降低了环境污染，减少了尘土飞扬，本发明采用Fe3O4填料，由于比重大，随磨料剥落时下沉快，飞扬性大为减少，同时由于Fe3O4具有磁性，一剥落即被工作台磁性吸盘吸往，不至于飞出。
下面结合实施例对本明作进一步说明。
实施例1，采用以下原料：
碳化硅        粒径300～400μm    用量70重量份
酚醛树脂          80～100μm     用量10重量份
高强度碳黑        80～100μm     用量0.2重量份
四氧化三铁        3～5μm        用量5重量份
无碱玻璃纤维  厚度200μm         重量60g/m2
以上材料，经加工制成厚度为1.1 mm，比重为2.30g/cm3的砂轮片。
生产工艺同上，固化采用本技术领域普通技术人员熟知的技术。
实施例2，采用以下原料：
碳化硅        粒径300～400μm    用量80重量份
酚醛树脂          80～100μm     用量20重量份
高强度碳黑        80～100μm     用量1.0重量份
四氧化三铁        3～5μm        用量15重量份
无碱玻璃纤维  厚度250μm         重量75g/m2
以上材料，经加工制成厚度为1.18mm，比重为2.45g/m3的砂轮片。
生产工艺同上，固化采用先用10小时将制件由35℃逐渐升温至120℃，继用6小时将制件由120℃升至180℃，再用20小时将制件由180℃降至常温，即可。
实施例3，原料用量：高强度碳黑1.0重量份，其余同实施例1，生产工艺同实施例2。
实施例4，原料用量：酚醛树脂为20重量份，其余同实施例1，生产工艺同实施例2。
实施例5，原料用量：四氧化三铁为15重量份，其余同实施例1，生产工艺同实施例2。
实施例6，原料用量：碳化硅为70重量份，高强度碳黑为0.2重量份，其余同实施例2，生产工艺同实施例1。
本发明大大提高了砂轮片的硬度，工作速度抗冲击能力，承受侧压能力，降低了材料损耗，降低了环境污染，减少了尘土飞扬。
本发明生产工艺简单。

Claims (5)

1.一种超薄切割砂轮片，采用碳化硅磨料，其特征在于：在砂轮片中间增加一层玻璃纤维网格布层，砂轮片结构分为上砂轮层，中玻璃纤维网格布层、下砂轮层。
2.根据权利要求1所述的超薄切割砂轮片，其特征在于：砂轮层采用碳化硅、酚醛树脂、高强度碳黑作磨料，三者的粒径和用量是：
碳化硅    粒径300～400μm     用量70～80重量份
酚醛树脂       80～100μm     用量10～20重量份
高强度碳黑     80～100μm   用量0.2～1.0重量份
配以厚度不大于300μm，每平方米重量不大于80克的玻璃纤维网格布，加工成厚度不大于1.2mm、比重为2.30～2.48g/cm3的砂轮片。
3.根据权利要求1或2所述的超薄切割砂轮片，其特征在于加入四氧化三铁作填料，粒径为3～5μm，在碳化硅用量为70～80重量份时，四氧化三铁用量为5～15重量份。
4.一种权利要求1所述的超薄切割砂轮片的生产工艺，包括以下步骤：将碳化硅、酚醛树脂、高强度碳黑、四氧化三铁按比例搅拌成既松散又具可塑性的混合料，置于-5°～-10℃低温中，使之成松散状成型料，取半量成型料放入模具内，摊平后放上玻璃纤维网格布，以48～196KPa压力压平后，将余下的半量成型料倒入摊平，加上盖板，将模具放入油压机内采用70～90℃温度，施以25MPa压力保持0.5～2分钟，卸下模具，制件放入固化炉固化，即得成品。
5.根据权利要求4所述的超薄切割砂轮片的生产工艺，其特征在于固化采用先用10小时时间将固化炉内的制件由35℃逐渐升温至120℃，继用6小时时间将制件由120℃升至180℃，再用20小时时间将制件由180℃降至常温，即得。
CN98113101A 1998-01-06 1998-01-06 超薄切割砂轮片及其生产工艺 Expired - Fee Related CN1061285C (zh)