CN1186399C - 钒锆兰颜料制造方法 - Google Patents
钒锆兰颜料制造方法 Download PDFInfo
- Publication number
- CN1186399C CN1186399C CN 03131530 CN03131530A CN1186399C CN 1186399 C CN1186399 C CN 1186399C CN 03131530 CN03131530 CN 03131530 CN 03131530 A CN03131530 A CN 03131530A CN 1186399 C CN1186399 C CN 1186399C
- Authority
- CN
- China
- Prior art keywords
- blue pigment
- vanadium
- zirconium blue
- manufacture method
- vanadium zirconium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
钒锆兰颜料制造方法，尤其是指利用锆英砂为原料制造钒锆兰颜料的新方法，以锆英砂、纯碱、钒化合物、卤化物为原料，经球磨、培烧、球磨、水洗、烘干制得，原料中添加有磷酸盐，焙烧后依次通入氟化氢和三氧化硫气体，本方法使制造钒锆兰颜料的原料达到更加均匀和理想的混合状态，制造的钒锆兰颜料的着色强度和颜色鲜艳度更好，且整个工艺简洁，能耗少，生产成本低。
Description
技术领域
本发明涉及钒锆兰颜料的制造方法，尤其是指利用锆英砂为原料制造钒锆兰颜料的新方法。
技术背景
目前，钒锆兰颜料的制造方法有二种工艺，一是以二氧化锆为原料制造，二是以锆英砂为原料制造，由于第二种工艺是以二氧化锆的原料---锆英砂来制造钒锆兰颜料的，更具有竞争优势，以锆英砂制造钒锆兰颜料的工艺流程见附图1。这种工艺存在的不足是：1，发色不鲜艳，色调偏绿；2，发色不深，不如二氧化锆为原料的生产工艺；3，制造工艺流程长，且其中的酸介工段难以控制；4，二次培烧增加了能耗和生产成本。
发明内容
本发明正是为了克服上述不足，提供一种改进的锆英砂制钒锆兰颜料新方法，改进之处在原料中采用磷酸盐作色调改进剂，解决钒锆兰颜料发色不鲜艳、明快、色调偏绿的缺点，明显提高了钒锆兰颜料的产品质量，工艺中减少了背景技术中的酸介工段及其后的烘干、焙烧工段，酸介工段的酸碱中和过程通过在焙烧过程中通氟化氢和三氧化硫气体来完成，从而优化了合成流程，降低能耗和生产成本。具体是这样实施的：钒锆兰颜料制造方法，以锆英砂、纯碱、钒化合物、卤化物为原料，经球磨、培烧、球磨、水洗、烘干制得，其特征在于原料中添加有磷酸盐，焙烧后依次通入氟化氢和三氧化硫气体。其工艺流程图见附图2。
为了明显提高产品的发色强度，卤化物原料选择氟化镁和氯化钠，结合焙烧过程中通入的氟化氢气体，它们作为矿化剂和助色剂成份，显著地提高了产品的发色强度，其着色强度不仅优于报导的锆英砂(硅酸锆)合成工艺，而且优于传统的二氧化锆生产工艺。
通常状况下，100克锆英砂配入0.2-2％的磷酸盐，1-10％的氟化镁、2-10％的钒化合物，2-20％的氯化钠，55-95％的碳酸钠以及0.5-8％的氟化氢和42-75％的三氧化硫。
配入的磷酸盐是磷酸三钠、磷酸二氢钠、磷酸氢二钠、磷酸铵、磷酸氢二铵、磷酸二氢铵、磷酸镁的一种或几种混合物。
配入的钒化合物为五氧化二钒、偏钒酸铵、偏钒酸钠、钒酸钠的一种或几种混合物。
100克锆英砂配入的最佳原料比为：0.2-0.8％的磷酸盐，3-6％的氟化镁、2-10％的钒化合物，4-8％的氯化钠，60-70％的碳酸钠以及2-4％的氟化氢和48-56％的三氧化硫。
焙烧后，因先期物料碱性较强，易吸收三氧化硫，后期焙烧物料因碱性较弱，交换三氧化硫的能力下降，通入三氧化硫气体时速度逐步递减。
本发明所述的制造方法使制造钒锆兰颜料的原料达到更加均匀和理想的混合状态，制造的钒锆兰颜料的着色强度和颜色鲜艳度更好，且整个工艺简洁，能耗少，生产成本低。
附图说明
图1为技术背景的工艺流程图。
图2为本发明的工艺流程图。
具体实施方式
实施例1，将粒径＜47μm的100克锆英砂粉，5克石英粉，70克纯碱，0.5克磷酸氢二铵，5克五氧化二钒，4克氟化镁，6克氯化钠球磨1小时，然后放入隔焰加热的电炉中1100焙烧2小时，将温度降至1000，此时先用10分钟时间通入氟化氢气体3.5克，再用3小时通入三氧化硫气体55克，三氧化硫气体通入时先期流速是后期流速的五倍。
实施例2，将325目细的100克锆英砂粉，65克纯碱，0.8克磷酸二氢铵，6克偏钒酸铵，5克氟化镁，8克氯化钠球磨混合1小时，然后放入隔焰加热的反射炉中1050焙烧3小时，将炉温降至950，先用30分钟时间通入氟化氢气体2.5克，再用5小时通入三氧化硫气体50克，控制通入三氧化硫气体时先期流速是后期流速的四倍。
Claims (8)
1.钒锆兰颜料制造方法，以锆英砂、纯碱、钒化合物、卤化物为原料，经球磨、培烧、球磨、水洗、烘干制得，其特征在于原料中添加有磷酸盐，焙烧后依次通入氟化氢和三氧化硫气体。
2.根据权利要求1所述的钒锆兰颜料制造方法，其特征在于卤化物原料为氟化镁和氯化钠。
3.根据权利要求1所述的钒锆兰颜料制造方法，其特征在于锆英砂的粒径＜47μm。
4.根据权利要求2所述的钒锆兰颜料制造方法，其特征在于100克锆英砂配入0.2-2％的磷酸盐，1-10％的氟化镁、2-10％的钒化合物，2-20％的氯化钠，55-95％的碳酸钠以及0.5-8％的氟化氢和42-75％的三氧化硫。
5.根据权利要求4所述的钒锆兰颜料制造方法，其特征在于100克锆英砂配入的原料比为：0.2-0.8％的磷酸盐，3-6％的氟化镁、2-10％的钒化合物，4-8％的氯化钠，60-70％的碳酸钠以及2-4％的氟化氢和48-56％的三氧化硫。
6.根据权利要求1、4、5之一所述的钒锆兰颜料制造方法，其特征在于磷酸盐是磷酸三钠、磷酸二氢钠、磷酸氢二钠、磷酸铵、磷酸氢二铵、磷酸二氢铵、磷酸镁的一种或几种混合物。
7.根据权利要求1、4、5之一所述的钒锆兰颜料制造方法，其特征在于钒化合物为五氧化二钒、偏钒酸铵、偏钒酸钠、钒酸钠的一种或几种混合物。
8.根据权利要求7所述的钒锆兰颜料制造方法，其特征在于通入三氧化硫气体时速度逐步递减。