CN1181987C - Method for producing light-transmitting three-D patterned glass - Google Patents
Method for producing light-transmitting three-D patterned glass Download PDFInfo
- Publication number
- CN1181987C CN1181987C CNB031197086A CN03119708A CN1181987C CN 1181987 C CN1181987 C CN 1181987C CN B031197086 A CNB031197086 A CN B031197086A CN 03119708 A CN03119708 A CN 03119708A CN 1181987 C CN1181987 C CN 1181987C
- Authority
- CN
- China
- Prior art keywords
- glass
- plate glass
- ink
- patterns
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention belongs to the technical field of glass deep processing, particularly relates to a method for producing light transmitting 3D pattern glass by using a chemical producing method of acid corrosion. Firstly, transparent plate glass is cleaned, a wire mesh with designed patterns is used for printing the patterns on the glass after the glass is dried, and printing ink adopts anti-corrosive ink; the back surface of the glass is covered by an anti-corrosive material after dried and then is carried out single-surface emulsification; after cleaned (retaining ink patterns), the treated plate glass is put into a corrosion tank with corrosive solution for soaking 10 to 20 minutes; the corrosive solution has the proportion of components and weights: 65 to 72 shares of water, 5 to 10 shares of sulfuric acid and 21 to 26 shares of hydrofluoric acid; the treated plate glass is cleaned by water, the ink and covering materials at the back surfaces of the glass are cleared, and the plate glass is made into a finished produce after dried, manufactured glass patterns have the advantages of obscuration, light transmission, mutual interspersion, peculiar production process, transparent patterns and good artistic effect, can be used for fields, such as indoor and outdoor decoration, vehicle, ship and furniture engineering, etc. and has strong artistic effect.
Description
Technical field:
The invention belongs to glass deep process technology field, relate in particular to a kind of production method that adopts the method production light-penetration solid figured plate glass of chemical acid corrosion, the glass pattern of producing is dim, printing opacity is also interspersed mutually.
Background technology:
At present, the technology that processes glass with craft pattern with the drawing of the method zygomite reticulated printing of acid corrosion on plate glass is ripe, no matter but their effect is pattern part or plane pattern-free part, be opaque, be not have the level third dimension, with the emulsifying glass is example, emulsifying glass is to go out pattern with silk screen and ink printing on plate glass, carry out acid corrosion again, but the pattern that it etches has two kinds of effects, the one, emulsification has all been carried out at the one side and the patternless back side that are printed on pattern, and is opaque; The 2nd, though pattern part is transparent, pattern does not have protruding third dimension and stereovision, and artistry is poor, and effect is bad.There is not the relief shortcoming of level though also have the production method of concave convered glass to solve pattern, but in the production method of concave convered glass, what the first step was taked is that plate glass is carried out comprehensive single face emulsification, impressing pattern then, carry out acid corrosion afterwards again, because of glass surface in its first step emulsified, so the pattern part of printing can printing opacity, pattern part and pattern-free part all are opaque dim effects, and therefore same third dimension, artistry and effect are bad.
Summary of the invention:
The objective of the invention is to overcome the deficiencies in the prior art and provide printing of a kind of employing silk-screen patterns and strong corrosion resistant printing ink to protect; the production method of the light-penetration solid figured plate glass of printing opacity projection, its production technology uniqueness are produced in chemical etching again; pattern is transparent, and artistic effect is good.
The object of the present invention is achieved like this: the technical method and the step of employing are as follows:
(1) earlier transparent plate glass is cleaned up, behind the airing with the silk screen that designs pattern in advance at printed patterns on glass, printing-ink employing corrosion-resistanting ink, after dry.
(2) carry out single face emulsification after the plate glass back side that is printed on pattern after will drying covers with anti-corrosion material.
(3) will be set by step 2 plate glass after handling simply clean back (reservation ink logo) and put in the corrosion case that fills corrosive liquid and soaked 10---20 minute, the composition of corrosive liquid and weight proportion are: water 65--72 part, sulfuric acid 5-10 part, hydrofluoric acid 21-26 part.
(4) will be set by step 3 plate glass water flushings after handling, remove the cladding material of printing ink and glass back.
(5) will be set by step 4 plate glass waters after handling rinse well, make finished product after the drying.
Good effect of the present invention is as follows:
1, direct printed patterns on transparent plate glass, after patterned plate glass carried out the emulsification first time, carry out the acid etching second time again, and it is indeformable to have kept ink logo not come off, the pattern that is processed is protruding transparence, stereoeffect is very strong, and the height of pattern projection is the height between the 0.03-0.08 millimeter;
2, Tu Qi pattern is transparent, and the glass planar beyond the pattern is emulsification, its product effect is: the full wafer glass pattern is transparent, non-pattern part is dim, and the transparent pattern third dimension is strong, and is well arranged, formed striking contrast with the emulsifying effectiveness of pattern-free part, use it for indoor and outdoor decoration, fields such as car and boat furniture engineering have very strong artistic effect.
The specific embodiment:
Embodiment 1:
The production method of light-penetration solid figured plate glass is to carry out according to following method step:
(1) transparent plate glass is cleaned up, behind the airing with the silk screen that designs pattern in advance at printed patterns on glass, printing-ink adopts corrosion-resistanting ink, after dry.
(2) plate glass that is printed on pattern after will drying carries out single face emulsification.
(3) (reservation ink logo) put in the corrosion case that fills corrosive liquid and soaked 10 minutes after the plate glass of 2 processing cleaned set by step, the composition of corrosive liquid and weight proportion preparation, 65 parts in water, 5 parts in sulfuric acid, 21 parts in hydrofluoric acid.
(4) will be set by step 3 plate glass water flushings after handling, remove printing ink.
(5) will be set by step 4 plate glass waters after handling rinse well, make finished product after the drying.
Embodiment 2:
The production method of light-penetration solid figured plate glass is to carry out according to following method step:
(1) transparent plate glass is cleaned up, behind the airing with the silk screen that designs pattern in advance at printed patterns on glass, printing-ink adopts corrosion-resistanting ink, after dry.
(2) carry out single face emulsification after the plate glass back side that is printed on pattern after will drying covers with anti-corrosion material.
(3) (reservation ink logo) put in the corrosion case that fills corrosive liquid and soaked 15 minutes after the plate glass of 2 processing cleaned set by step, the composition of corrosive liquid and weight proportion preparation, 67 parts in water, 8 parts in sulfuric acid, 25 parts in hydrofluoric acid.
(4) will be set by step 3 plate glass water flushings after handling, remove the cladding material of printing ink and glass back.
(5) will be set by step 4 plate glass waters after handling rinse well, make finished product after the drying.
Embodiment 3:
The production method of light-penetration solid figured plate glass is to carry out according to following method step:
(1) transparent plate glass is cleaned up, behind the airing with the silk screen that designs pattern in advance at printed patterns on glass, printing-ink adopts corrosion-resistanting ink, after dry.
(2) carry out single face emulsification after the plate glass back side that is printed on pattern after drying covers with anti-corrosion material.
(3) (reservation ink logo) put in the corrosion case that fills corrosive liquid and soaked 20 minutes after the plate glass of 2 processing cleaned set by step, the composition of corrosive liquid and weight proportion preparation, 72 parts in water, 10 parts in sulfuric acid, 26 parts in hydrofluoric acid.
(4) will be set by step 3 plate glass water flushings after handling, remove the anti-corrosion material of printing ink and glass back.
(5) will be set by step 4 plate glass waters after handling rinse well, make finished product after the drying.
Claims (1)
1, a kind of production method of light-penetration solid figured plate glass is characterized in that: the method and the step of employing are as follows:
The first step: earlier transparent plate glass is cleaned up, behind the airing with the silk screen that designs pattern in advance at printed patterns on glass, printing-ink employing corrosion-resistanting ink, after dry,
Second step: after covering with anti-corrosion material, the plate glass back side that will be printed on pattern after will drying carries out single face emulsification,
The 3rd step: after the 2 plate glass cleanings of handling, the reservation ink logo is put in the corrosion case that fills corrosive liquid and was soaked 10---20 minute set by step, and the composition of corrosive liquid and weight proportion are: water 65--72 part, and sulfuric acid 5-10 part, hydrofluoric acid 21-26 part,
The 4th step: the plate glass water flushing after 3 processing set by step, the cladding material of removing printing ink and glass back,
The 5th step: the plate glass water after 4 processing is rinsed well set by step, makes finished product after the drying.