CN106808877A - A kind of production method of light-transmitting three-D patterned glass - Google Patents
A kind of production method of light-transmitting three-D patterned glass Download PDFInfo
- Publication number
- CN106808877A CN106808877A CN201510857516.2A CN201510857516A CN106808877A CN 106808877 A CN106808877 A CN 106808877A CN 201510857516 A CN201510857516 A CN 201510857516A CN 106808877 A CN106808877 A CN 106808877A
- Authority
- CN
- China
- Prior art keywords
- glass
- ink
- plate glass
- corrosion
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to glass post-processing technical field, more particularly to a kind of method using chemical acid corrosion produces the production method of light-transmitting three-D patterned glass, first transparent plate glass is cleaned up, the silk screen for designing pattern in advance printed patterns on glass are used after drying, printing-ink uses corrosion-resistanting ink, glass back is covered with anti-corrosion material after drying, carries out one side emulsification, after the plate glass cleaning after treatment（Retain ink logo）Put into the corrosion case for fill corrosive liquid and soak 10-20 minutes, the composition and weight proportion of corrosive liquid are：Water 65-72 parts, sulfuric acid 5-10 parts, hydrofluoric acid 21-26 parts, plate glass after treatment is rinsed with water, the covering material of ink and glass back is removed, finished product is made after drying, the glass pattern produced is dim, printing opacity and mutually intersperse, production technology is unique, transparent pattern, artistic effect is good, can be used for indoor and outdoor decoration, the fields such as car and boat furniture engineering, with very strong artistic effect.
Description
Technical field
The invention belongs to glass post-processing technical field, more particularly to a kind of method using chemical acid corrosion produces the production method of light-transmitting three-D patterned glass, and the glass pattern produced is dim, printing opacity and mutually intersperse.
Background technology
At present, the technique that glass with craft pattern is processed on plate glass with the method combination silk-screen printing drawing of acid corrosion is ripe, but their effect is small opinion pattern part or plane pattern-free part, it is opaque, it is do not have level third dimension, by taking emulsifying glass as an example, emulsifying glass is to print out pattern with silk screen and ink on plate glass, acid corrosion is carried out again, but the pattern that it is etched has two kinds of effects, one is that the back side of the figuratum one side of print and pattern-free is all emulsified, opaque；Though two is that pattern part is transparent, without raised third dimension and stereovision, artistry is poor, and effect is bad for pattern.Also although the production method of concave convered glass solves pattern without the relief shortcoming of level, but " in the production method of 1 convered glass; what the first step was taken is that plate glass is carried out into comprehensive one side emulsification; and then impressing pattern; carry out acid corrosion again afterwards, because glass surface has been emulsified in its first step, so the pattern part of printing will not printing opacity; pattern part and pattern-free part all opaque dim effects of foot, therefore same third dimension, artistry and effect are bad in Shu.
The content of the invention
There is provided to plant it is an object of the invention to overcome the deficiencies in the prior art and adopt river
Silk-screen patterns are printed and the protection of strong corrosion resistant ink, then chemical etching, produce the production method of the raised light-transmitting three-D patterned glass of printing opacity, and its production technology is unique, and transparent pattern, artistic effect is good.
The object of the present invention is achieved like this：The technical method and step of use are as follows：
First transparent plate glass is cleaned up, with the silk screen of the pattern printed patterns on glass are designed in advance after airing, printing-ink uses corrosion-resistanting ink, after dry in the air thousand.
Being printed after drying after the figuratum plate glass back side is covered with anti-corrosion material carries out one side emulsification.
After plate glass simply cleaning after being processed by step 2（Retain ink logo）Put into the corrosion case for fill corrosive liquid and soak 10-20 minutes, the composition and weight proportion of corrosive liquid are：Water 65-72 parts, 5-10 parts of sulfuric acid, 21-26 parts of hydrofluoric acid.
Plate glass after being processed by step 3 is rinsed with water, removes the covering material of ink and glass back.
Plate glass water after being processed by step 4 rushes Xian totally, and finished product is made after drying.
The positive effect of the present invention is as follows：
1st, pattern is directly printed on transparent plate glass, after patterned plate glass is carried out into first time emulsification, second acid etching is carried out again, and maintain ink logo do not fall off it is indeformable, the pattern for being processed is raised transparence, stereoeffect is very strong, and the height that pattern A rises is the height between 0.03-0.08 millimeter；
2nd, raised pattern is transparent, and the glass planar beyond pattern is emulsification, and its product effect is：Full wafer glass pattern is transparent, and non-pattern portion is dim, and transparent pattern third dimension is strong, and well arranged, the emulsifying effectiveness with pattern-free part forms striking contrast, by its river in indoor and outdoor decoration, the field such as car and boat furniture engineering, with very strong artistic effect.Specific embodiment embodiment 1
The production method of light-transmitting three-D patterned glass is that step is carried out by the following method：
Transparent plate glass is cleaned up, with the silk screen of the pattern printed patterns on glass are designed in advance after airing, printing-ink uses corrosion-resistanting ink, after dry in the air ten.
Figuratum plate glass is printed after drying to carry out single and emulsifies.
After the plate glass cleaning that will be processed by step 2（Retain ink logo）Put into the corrosion case for fill corrosive liquid and soak 10 minutes, the composition and weight proportion of corrosive liquid are prepared, 65 parts of water, 5 parts of sulfuric acid, 21 parts of hydrofluoric acid.
Plate glass after being processed by step 3 is rinsed with water, removes ink.
Plate glass after being processed by step 4 is rinsed well with water, and finished product is made after drying.
Embodiment 2
The production method of light-transmitting three-D patterned glass is that step is carried out by the following method：
Transparent plate glass is cleaned up, with the silk screen of the pattern printed patterns on glass are designed in advance after airing, printing-ink uses corrosion-resistanting ink, after dry in the air thousand.
Being printed after drying after the figuratum plate glass back side is covered with anti-corrosion material carries out one side emulsification.
After the plate glass cleaning that will be processed by step 2（Retain ink logo）Put into and soak 15 minutes in the rotten candle case for fill rotten candle liquid, the composition and weight proportion of corruption candle liquid are prepared, 67 parts of water, 8 parts of sulfuric acid, 25 parts of hydrofluoric acid.
Plate glass after being processed by step 3 is rinsed with water, removes the covering material of ink and glass back.
Plate glass after being processed by step 4 is rinsed well with water, and finished product is made after drying.
Embodiment 3
The production method of light-transmitting three-D patterned glass is that step is carried out by the following method：
Transparent plate glass is cleaned up, the silk screen of the good pattern printed patterns on glass are designed in state in advance after airing, printing-ink uses corrosion-resistanting ink, after dry.
Being printed after drying after the figuratum plate glass back side is covered with anti-corrosion material carries out one side emulsification.
After the plate glass cleaning that will be processed by step 2（Retain ink logo）Put into the corrosion case for fill corrosive liquid and soak 20 minutes, the composition and weight proportion of corrosive liquid are prepared, 72 parts of water, 10 parts of sulfuric acid, 26 parts of Gas fluoric acids.
Plate glass after being processed by step 3 is rinsed with water, removes the anti-corrosion material of ink and glass back.
Plate glass water after being processed by step 4 rushes Xian totally, and finished product is made after drying.
Claims (2)
1. a kind of production method of light-transmitting three-D patterned glass, it is characterised in that：The method and step of rice are as follows.
2. the first step：First transparent plate glass is cleaned up, with the silk screen of the pattern printed patterns on glass are designed in advance after airing, printing-ink uses corrosion-resistanting ink, after dry, second step：Printed after drying after figuratum plate glass back side anti-corrosion material covers
Carry out one side emulsification, the 3rd step：After the plate glass cleaning that will be processed by step 2（Retain ink logo）Put and soak 10 in the corrosion case for fill corrosive liquid ... that 20 minutes, the composition and weight proportion of corrosive liquid were into：Water 65-72 parts, 5-10 parts of sulfuric acid, 21-26 parts of hydrofluoric acid, the 4th step：The covering material of the plate glass water flushing after being processed by step 3, removing ink, and glass back, the 5th step：Plate glass after being processed by step 4 is rinsed well with water, and finished product is made after drying.