CN1051502C - Embossing stainless starlight panel having a colored and topographical and a fabricating method thereof - Google Patents
Embossing stainless starlight panel having a colored and topographical and a fabricating method thereof Download PDFInfo
- Publication number
- CN1051502C CN1051502C CN95115966A CN95115966A CN1051502C CN 1051502 C CN1051502 C CN 1051502C CN 95115966 A CN95115966 A CN 95115966A CN 95115966 A CN95115966 A CN 95115966A CN 1051502 C CN1051502 C CN 1051502C
- Authority
- CN
- China
- Prior art keywords
- starlight
- plate
- stainless
- embossing
- colored
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
An embossed stainless steel panel with designs thereon is produced by (a) photomechanically obtaining two silk screens having a portion wherein the photoresist is removed and a hardened portion, (b) applying the first screen have a topographical surface, in which a gold-plated and electrolytically formed a black pattern in the unmasked areas, (c) applying the second screen and forming bright-etched portion in the unmasked areas and then gold plating (11) the bright-etched portion.
Description
The present invention relates to a kind of embossing stainless starlight plate with landform (Topographical) face, in detail, it is a kind of embossing stainless starlight plate and preparation method thereof with colored landform face, wherein, the Gold plated Layer that has pre-determined pattern forms according to the bright etching part (bright-etching portion) of embossing program on starlight plate surface, other parts form black, so that this two parts color presents the arrangement of coordination.
At present, by various patterns and shape being produced on the stainless steel starlight plate face that designs as the elevator decoration such as drawing, coating embedding, serigraphy and etching technique.Wherein, etching technique has obtained using the most widely.
Etching is to finish according to the step of Fig. 1 a to 1d.At first, a black as shown in Figure 1a movably pattern film is placed in has a screen frame frame 2 shown in Fig. 1 b, scribbles all the time on the silk screen 1 of negative photoresist, by pressurization their is closely connected mutually.To removing the pattern film after this combining structure exposure.Then, silk screen 1 is cleaned, obtain owing to do not receive illumination cause photoresist dissolving not with the zone 3 of photoresist layer with owing to receiving the zone that has the photoresist layer 4 that illumination causes the photoresist hardening.
As above the silk screen of Chu Liing is placed on the stainless steel starlight plate, coats propylene urine gastral cavity resinoid printing ink on its whole.After removing silk screen, just having formed on the stainless steel starlight plate shown in Fig. 1 c has part 5 that printing ink covers and the part 6 of not covered by printing ink.
Then this combining structure is immersed the part 6 that the ferric chloride solution etching does not have printing ink, then to its carry out drying, peel off, clean, processing such as neutralization, like this, the etching part 7 of a mattness has just formed on the smooth and bright like a mirror stainless steel starlight plate shown in Fig. 1 d.
But when using the chemical attack of one dimension, be not enough to obtain the grade of the landform of a protuberance of demonstration plane effect on the degree of depth.In addition, if foreign matter has been sneaked into described etching part, then foreign matter is not easy to remove, and causes the design's effect to reduce greatly.
On the other hand, giving the colouring of embossing stainless starlight plate is known prior art, and therefore this technology lacks the whole structure on how much by carry out single paintedly can obtaining single color intuitively on embossing face.
The present invention addresses the above problem.Therefore, one object of the present invention just provides a kind of by coordinating the embossing stainless starlight plate material that has the landform face that color is smeared, wherein, the Gold plated Layer that has pre-determined pattern is formed on bright etching part, and other parts allow painted black, and gold changes as requested so that these are matching in color.
For realizing above-mentioned purpose of the present invention, one aspect of the present invention provides a kind of embossing stainless starlight plate that has colored landform face, and it comprises: the bright etching face with predetermined pattern that forms on described embossing stainless starlight plate; A Gold plated Layer that on described bright etching face, forms; With a black part that on the residual surface of described embossing stainless starlight plate, forms.
In addition, the present invention also provides the method for the embossing stainless starlight plate that a kind of making has colored landform face, it comprises the following steps: first step, after the original film that will have a plurality of patterns is placed on the silk screen that scribbles photoresist respectively, expose and clean, form the silk screen of the part that has the dissolved part of photoresist and hardened; Second step, a silk screen be placed on the embossing stainless starlight plate cover with smoke agent for shielding after, carry out painted with black to the whole surface of shaded portions or described embossing stainless starlight plate not; Third step, another silk screen is placed on cover on the stainless steel starlight plate of described second step after, shaded portions is not carried out bright etching, and removes smoke agent for shielding; The 4th step is placed on described another silk screen on the surface through the described stainless steel starlight plate of third step and covers, and uncovered bright etching position is carried out gold-plated, removes smoke agent for shielding then.
Above-mentioned purpose of the present invention and other advantage will become more obvious to the description of most preferred embodiment by the reference accompanying drawing:
Fig. 1 a to 1d shows the etching step of a routine, wherein:
Fig. 1 a shows a black and white pattern film,
Fig. 1 b shows through overexposure and cleaned silk screen,
Fig. 1 c shows a state of the photoresist that covers on the stainless steel starlight plate,
Fig. 1 d shows through removing the state of the photoresist that covers after being etched with;
Fig. 2 a to 2g shows the step of making the stainless steel starlight plate that has colored landform face according to the present invention, wherein:
Fig. 2 a shows the pattern film,
Fig. 2 b shows through overexposure and the silk screen after cleaning,
Fig. 2 c shows the plane of an embossing stainless starlight plate,
Fig. 2 d shows the state that forms black after covering,
Fig. 2 e shows the state that carries out after the bright etching,
Fig. 2 f shows the state after the bright etching part plating,
Stainless steel starlight plate after Fig. 2 g shows and completes according to the present invention.
A kind of stainless steel starlight plate according to the present invention is to form like this, promptly, make have the bright etching part that pre-determines pattern be formed on through embossing handle stainless steel starlight plate material on, to form a Gold plated Layer at bright etching part, remainder then forms black.
Make Gold plated Layer 11 in electrolyte solvent, make intrinsic gold of gold and brown or green coupling with the known method in present technique field through decolorization.
As mentioned above, obtain smooth mirror surface by an embossed portion being divided bright etching, bright thorough gold has shown painted effect in the part of corresponding embossing, and it only is different from embossing face gold-plated and do not carry out bright etched regular situation.In addition, this painted the black with formation on this embossing part cooperates, thereby produces a tangible orographic effect.
If make when needed and golden in electrolyte, handle, have so the gold of gold inherent colour and black match become brown or green, to obtain a tangible visual illusion effect.(decolorization is a technology well-known in the art here, therefore is not described in detail).
With reference to Fig. 2 a to 2g, will the embodiment according to an embossing stainless starlight plate of the present invention be described in detail.
Among Fig. 2 a, pattern film A and B with some landform are placed on respectively on the silk screen that always scribbles photoresist, then to this combining structure exposure, take film away, cleaning web, like this, shown in Fig. 2 b, obtain because dissolving and do not have the part 3 of photoresist layer and have the silk screen A ' and the B ' of part 4 of the photoresist layer of hardening.
The masking process of the stainless steel starlight plate material that will describe below silk screen A ' that is obtained by above-mentioned steps and B ' are used in.
At first, the silk screen A ' that gets ready is placed on the embossing face 8 of this stainless steel starlight plate and with acid-proof ink and covers, then in case remove silk screen A ', shown in Fig. 2 d, form crested face 5 and do not cover face 6 as figure A "; then crested face 6 usefulness black are not handled, and remove acid-proof ink formation black side 9 as figure A .
The condition that forms this black requirement is: with the CrO of 110～150 grams per liters
3H with 580～700 grams per liters
2SO
4, and the electrolyte solution of the water of surplus handled 3.5～5 hours object construction under 70～80 ℃ temperature, to make it painted with black pigment.
The deep or light of black changes along with the variation of electrolyte temperature.
The silk screen B ' that another has same pattern is placed on the stainless steel starlight plate A , uses method as hereinbefore to make it to cover, and then shown in Fig. 2 e, removes silk screen B ' formation and covers face 5 and do not cover face 6, as figure B ".
Then, do not carry out light and be etched with and remove printing ink, thus, divide in this embossed portion to form the bright etching part shown in the figure B covering face 6.
On the other hand, the light etching part forms in such a way, promptly except the part that the process of being described by Fig. 2 d forms, this stainless steel starlight plate all is formed black, by using before silk screen B ' prior to bright etching, make the whole surface of the embossing starlight plate shown in Fig. 2 c use the black pigment all coloring under these conditions, and be shown in to finish on this surface as Fig. 2 e and cover operation.
When carrying out bright etching, add 1～5% Nicotinicum Acidum acid amides and surfactant to containing 5～10% glycerine, 30～50% phosphoric acid, 35～50% sulfuric acid and 1～5% chromic anhydride CrO
3In the electrolytic solution, this process is temperature and the 50～70A/m at 70～80 ℃
2Current density under electrolysis, etching part just becomes smooth (minute surface) like this.
Another silk screen B ' is placed in and covers through on the starlight plate B of above-mentioned operation, and is removed.
Utilize typical method gold-plated, thereby form Gold plated Layer shown in Fig. 2 f at bright etching part to combining structure.
Remove printing ink, obtain the starlight plate that completes of the present invention shown in Fig. 2 g.
On stainless steel starlight plate according to the present invention, embossing part by with the mass colour pigment coloring to produce a kind of and the different visual effect of conventional stainless steel starlight plate of in one plane coating black.
Form the bright etching part with certain depth by dividing in the embossed portion of black colorant of no use, this light etching part just becomes smooth.Equally, further the Gold plated Layer that forms at bright etching part has tangible characteristic with gold-plated comparing on a kind of common material.
As a result, the configuration of Gold plated Layer on the color coordination that seems, the variation according to manufacturing process simultaneously shows relief visual effect.
In addition, can make Gold plated Layer fading and go up can with gold coordinate to arrange in pairs or groups brown or green.
When utilizing special embodiment in addition special displaying and when describing of the present invention, knowing those skilled in the art should be appreciated that, under the prerequisite of the spirit and scope that do not depart from claim of the present invention and limited, it can be effective carrying out various variations in form and details.
Claims (5)
1. embossing stainless starlight plate that has colored landform face, it is held to levy and is that it comprises:
Bright etching face that on described embossing stainless starlight plate, forms with predetermined pattern;
A Gold plated Layer that on described bright etching face, forms; With
A black part that on the residual surface of described embossing stainless starlight plate, forms.
2. the embossing stainless starlight plate that has colored landform face according to claim 1 is characterized in that described Gold plated Layer forms with brown or green mutual coordination.
3. a making has the method for the embossing stainless starlight plate of colored landform face, it is characterized in that it comprises the following steps:
First step after the original film that will have a plurality of patterns is placed on the silk screen that scribbles photoresist respectively, exposes and cleans, and forms the silk screen (A ', B ') of the part that has the dissolved part of photoresist and hardened;
Second step, a silk screen A ' be placed on the embossing stainless starlight plate cover with smoke agent for shielding after, carry out painted with black to the whole surface of shaded portions or described embossing stainless starlight plate not;
Third step, another silk screen B ' is placed on cover on the stainless steel starlight plate of described second step after, shaded portions is not carried out bright etching, and removes smoke agent for shielding;
The 4th step is placed on described another silk screen B ' on the surface through the described stainless steel starlight plate of third step and covers, and uncovered bright etching position is carried out gold-plated, removes smoke agent for shielding then.
4. making according to claim 3 has the method for the embossing stainless starlight plate of colored landform face, it is characterized in that, above-mentioned Gold plated Layer is handled with electrolyte, and it is brown or green making its variable color.
5. making according to claim 3 has the method for the embossing stainless starlight plate of colored landform face, it is characterized in that, in third step, uses by 5～10% glycerine, 30～50% phosphoric acid, 35～50% sulfuric acid and 1～5% CrO
3, the mixed liquor that constitutes of 1～5% Nicotinicum Acidum acid amides and surfactant, with 70～80 ℃ temperature and 50～70A/m
2Current density stainless steel starlight plate is carried out electrolytic treatments.