CN107042722A - A kind of preparation method of glass cameo - Google Patents
A kind of preparation method of glass cameo Download PDFInfo
- Publication number
- CN107042722A CN107042722A CN201710286518.XA CN201710286518A CN107042722A CN 107042722 A CN107042722 A CN 107042722A CN 201710286518 A CN201710286518 A CN 201710286518A CN 107042722 A CN107042722 A CN 107042722A
- Authority
- CN
- China
- Prior art keywords
- parts
- glass
- acid
- etching solution
- silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Present invention system provides a kind of preparation method of glass cameo, comprises the following steps：The pattern of silk-screen plate is designed on demand, is stamped acid-proof ink toward glass with silk-screen plate, is then dried or dry, acid-proof ink includes the component of following parts by weight：32 60 parts of epoxy resin, 12 24 parts of ethylene glycol monobutyl ether, 38 parts of cyclohexanone, 7 16 parts of aromatic hydrocarbon, take the glass of acquisition, are put into the etch bath equipped with etching solution and are etched, and etching period is 20 50 minutes, and etching solution includes the component of volumes below part：25 35 parts of hydrofluoric acid, 38 parts of sulfuric acid, 60 75 parts of water, take the glass of acquisition, the etching solution remained with caustic dip glass, take the glass of acquisition, remove the acid-proof ink on glass with cleaning agent, then dry or dry.Present invention design depiction makes the pattern to be formed be more prone to control on silk-screen plate, and the degree of accuracy is high, is carved using etching solution, disposal molding, and process is simple, easy to operate, and producing efficiency is high.
Description
Technical field
The present invention relates to glass processing field, a kind of preparation method of glass cameo is specifically disclosed.
Background technology
With the development of science and technology, the process technology of glass is more and more ripe, while people's spiritual pursuit is also improved constantly, it is right
The appearance requirement of glass also more and more higher, then people's depiction on glass, makes glass more attractive in appearance, and purposes is wider, most
Common glass-engraving is glass cameo, and glass cameo refers to carve various patterns in glass surface, glass is showed bumps
Uneven stereoeffect.
Traditional glass cameo is that artificial hand carves sand carving, and carving efficiency is low, and the working strength of workman is high, and cost of manufacture is high,
Pneumatic engraving machine was occurred in that later, and rough stereoeffect is formed by air pressure shock surface, but such method is still
Time-consuming longer, process is numerous and diverse, and producing efficiency is not high enough.
The content of the invention
Based on this, it is necessary to which for prior art problem, there is provided a kind of preparation method of glass cameo, production process letter
Single, producing efficiency is high.
To solve prior art problem, the present invention discloses a kind of preparation method of glass cameo, comprised the following steps：
(1) pattern of silk-screen plate is designed on demand；
(2) acid-proof ink is stamped toward glass with silk-screen plate, then dries or dry, acid-proof ink includes the group of following parts by weight
Point：32-60 parts of epoxy resin, 12-24 parts of ethylene glycol monobutyl ether, 3-8 parts of cyclohexanone, 7-16 parts of aromatic hydrocarbon；
(3) glass for taking step (2) to obtain, is put into the etch bath equipped with etching solution and is etched, and etching period is 20-50 points
Clock, etching solution includes the component of volumes below part：25-35 parts of hydrofluoric acid, 3-8 parts of sulfuric acid, 60-75 parts of water；
(4) glass for taking step (3) to obtain, the etching solution remained with caustic dip glass；
(5) glass for taking step (4) to obtain, removes the acid-proof ink on glass with cleaning agent, then dries or dry.
Further, etching period is 30 minutes.
Further, etching solution includes the component of volumes below part：65 parts of 30 parts of hydrofluoric acid, 5 parts of sulfuric acid and water.
Beneficial effects of the present invention are：The present invention discloses a kind of preparation method of glass cameo, and design depiction is in silk
On half tone, the pattern to be formed is set to be more prone to control, the degree of accuracy is high, is carved using etching solution, disposal molding, process letter
Single, easy to operate, producing efficiency is high.
Embodiment
For the feature, technological means and the specific purposes reached, function of the present invention can be further appreciated that, with reference to
Embodiment is described in further detail to the present invention.
The present invention discloses a kind of embodiment for a kind of preparation method of glass cameo, comprises the following steps：
(1) pattern of silk-screen plate is designed on demand；
(2) acid-proof ink is stamped toward glass with silk-screen plate, then dries or dry, acid-proof ink includes the group of following parts by weight
Point：32-60 parts of epoxy resin, 12-24 parts of ethylene glycol monobutyl ether, 3-8 parts of cyclohexanone, 7-16 parts of aromatic hydrocarbon；
(3) glass for taking step (2) to obtain, is put into the etch bath equipped with etching solution and is etched, and etching period is 20-50 points
Clock, etching solution includes the component of volumes below part：25-35 parts of hydrofluoric acid, 3-8 parts of sulfuric acid, 60-75 parts of water；
(4) glass for taking step (3) to obtain, the etching solution remained with caustic dip glass；
(5) glass for taking step (4) to obtain, removes the acid-proof ink on glass with cleaning agent, then dries or dry.
The pattern of engraving is designed, depiction is presented on silk-screen plate, acid-proof ink is printed on by glass by silk-screen plate
On glass, then dry or dry, form one layer of antiacid corrosion layer, exposed glass shape is needs the pattern carved, by glass
Glass is put into acid etching pond and etched, and exposed glass is etched liquid erosion, and the pattern required for disposable formation is simple to operate
Convenient, processing and fabricating efficiency high, the etching solution for finally remaining glass surface and useless acid-proof ink are removed, and are dried, i.e.,
Form glass cameo.
A kind of preparation method of glass cameo of above-described embodiment, by designing the shape of silk-screen plate, makes depiction more
Plus be easily controlled, the different demand in market can be effectively met, unique etching solution makes etch effect more complete, the figure of formation
Case third dimension is stronger, has card-cut aesthetic feeling, and disposable etch-forming, process is simple, and producing efficiency is high.
For removing the cleaning agent of acid-proof ink typically using cyclohexanone and the solvent of arene.
Based on above-described embodiment, acid-proof ink is printed, glass is put into etch bath, etching solution includes volumes below part
Component：65 parts of 30 parts of hydrofluoric acid, 5 parts of sulfuric acid and water, etching took out glass after 30 minutes, then by the residual of glass surface
Etching solution and acid-proof ink are removed, and the glass with plastic relief is obtained after drying.
Embodiment described above only expresses the several embodiments of the present invention, and it describes more specific and detailed, but simultaneously
Therefore the limitation to the scope of the claims of the present invention can not be interpreted as.It should be pointed out that for one of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the guarantor of the present invention
Protect scope.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (3)
1. a kind of preparation method of glass cameo, it is characterised in that comprise the following steps：
(1) pattern of silk-screen plate is designed on demand；
(2) acid-proof ink is stamped toward glass with silk-screen plate, then dries or dry, the acid-proof ink includes following parts by weight
Component：32-60 parts of epoxy resin, 12-24 parts of ethylene glycol monobutyl ether, 3-8 parts of cyclohexanone, 7-16 parts of aromatic hydrocarbon；
(3) glass for taking step (2) to obtain, is put into the etch bath equipped with etching solution and is etched, and etching period is 20-50 points
Clock, the etching solution includes the component of volumes below part：25-35 parts of hydrofluoric acid, 3-8 parts of sulfuric acid, 60-75 parts of water；
(4) glass for taking step (3) to obtain, the etching solution remained with caustic dip glass；
(5) glass for taking step (4) to obtain, removes the acid-proof ink on glass with cleaning agent, then dries or dry.
2. the preparation method of a kind of glass cameo according to claim 1, it is characterised in that the etching period is 30 points
Clock.
3. the preparation method of a kind of glass cameo according to claim 1, it is characterised in that the etching solution includes following
The component of parts by volume：65 parts of 30 parts of hydrofluoric acid, 5 parts of sulfuric acid and water.