CN117816161A - 用于甘油氢解制备1,3-丙二醇催化剂的制备方法以及催化剂及应用 - Google Patents
用于甘油氢解制备1,3-丙二醇催化剂的制备方法以及催化剂及应用 Download PDFInfo
- Publication number
- CN117816161A CN117816161A CN202211182485.1A CN202211182485A CN117816161A CN 117816161 A CN117816161 A CN 117816161A CN 202211182485 A CN202211182485 A CN 202211182485A CN 117816161 A CN117816161 A CN 117816161A
- Authority
- CN
- China
- Prior art keywords
- catalyst
- glycerol
- tungsten
- propanediol
- roasting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及催化剂制备技术领域,公开了一种用于甘油氢解制备1,3‑丙二醇催化剂的制备方法以及催化剂及应用。用于甘油氢解制备1,3‑丙二醇催化剂的制备方法包括:(1)采用过量浸渍法将氧化钨前驱体、溶剂和γ‑Al2O3接触,经水浴蒸干、第一干燥和第一焙烧处理后,得到复合氧化物WO3/Al2O3;所述氧化钨前驱体为六氯化钨;(2)将所述复合氧化物WO3/Al2O3、水和Pt的前驱体接触,经水浴蒸干、第二干燥、第二焙烧、还原处理后,得到催化剂Pt/WO3/Al2O3。该制备方法能够在较低温度下将氧化物前驱体转变成WO3,降低催化剂制备过程中的能耗。
Description
技术领域
本发明涉及催化剂制备技术领域,具体地,涉及一种用于甘油氢解制备1,3-丙二醇催化剂的制备方法以及催化剂及应用。
背景技术
甘油氢解产物之一1,3-丙二醇是生产不饱和聚酯、增塑剂、表面活性剂、乳化剂和破乳剂的原料;在聚氨酯行业中,其常用作聚酯多元醇的原料、聚醚多元醇的起始剂和聚氨酯扩链剂等;在有机化工行业中,其也是重要的单体和中间体,最主要的用途是作为聚合物单体,合成聚对苯二甲酸丙二醇酯(PTT)。PTT作为一种生物可降解的新型聚酯,它克服了聚对苯二甲酸乙二醇酯(PET)太硬和聚对苯二甲酸丁二醇酯(PBT)太软的缺点,同时具有优异的回弹性、易染性和生物降解性,在地毯、纺织、工程塑料等行业具有巨大的发展潜力。合成PTT的经济性受限于1,3-丙二醇。
目前,1,3-丙二醇的生产方法有丙烯醛水合氢化法,环氧乙烷羰基化法,生物发酵法以及甘油氢解法等。
丙烯醛水合氢化法在丙烯醛水合过程中,产物3-羟基丙醛选择性较低,并且极不稳定,容易产生缩醛,不利于分离;而且,丙烯醛本身属剧毒、易燃、易爆化学品。环氧乙烷羰基化法设备投资大、反应压力高。生物发酵法缺点是原料的转换率和产物的浓度均较低,副产物多,产物和菌种的分离成本高。而甘油氢解法不仅工艺流程短,反应原料毒性低,反应条件温和,而且反应可以在水相中进行,对环境污染小,是一种绿色合成路线。
Pt-W系催化剂是甘油氢解反应研究较多的催化剂体系。
Pt-W可以单独存在,CN102728380A公开了一种甘油氢解制备1,3-丙二醇的催化剂及其制备和应用,该催化剂载体为介孔氧化钨载体,活性组分为金属铂、铑、钌、钇、钯、镍、铜中的一种或二种以上;CN113262783A公开了一种催化甘油定向氢解为丙二醇的催化剂及其制备方法,采用原子层沉积(ALD)技术,在富含氧空位的氧化钨载体上负载单原子Pt来制备催化剂。
Pt-W也可以负载于载体之上,常用载体包括氧化铝、氧化锆、二氧化硅等;CN112169795A公开了优化的多元醇氢解催化剂活化方法,制备了以氧化铝为载体的催化剂Pt/WO3/Al2O3。
CN112044435A公开了甘油选择性氢解制1,3-丙二醇用Pt-W催化剂及其制备方法,制备了以氧化钛为载体的催化剂Pt/WO3/TiO2,将其用于甘油氢解反应时发现,以金红石相氧化钛为载体的催化剂无论是催化活性还是1,3-丙二醇选择性,均远远高于锐钛矿相氧化钛为载体的催化剂,目标产物1,3-丙二醇得率提高近38倍。由此可见,载体的作用除了分散活性组分以外,但是其物理性质和化学性质也会影响催化剂的活性。此外,在大多数专利或文献中,氧化钨前驱体大多选用偏钨酸铵或仲钨酸铵这类多酸盐,通常需要较高温度才能将多酸盐完全转变成WO3。
因此,研究和开发优化载体的性质具有重要意义。
发明内容
本发明的目的是为了克服现有技术用于甘油氢解制备1,3-丙二醇催化剂的制备方法中需要较高的温度才能将氧化物前驱体转变为WO3的问题,提供一种用于甘油氢解制备1,3-丙二醇催化剂的制备方法以及催化剂及应用,该制备方法能够在较低温度下将氧化物前驱体转变成WO3,降低催化剂制备过程中的能耗。
为了实现上述目的,本发明第一方面提供了一种用于甘油氢解制备1,3-丙二醇催化剂的制备方法,其中,所述的制备方法包括:
(1)采用过量浸渍法将氧化钨前驱体、溶剂和γ-Al2O3接触,经水浴蒸干、第一干燥和第一焙烧处理后,得到复合氧化物WO3/Al2O3;所述氧化钨前驱体为六氯化钨;
(2)将所述复合氧化物WO3/Al2O3、水和Pt的前驱体接触,经水浴蒸干、第二干燥、第二焙烧、还原处理后,得到催化剂Pt/WO3/Al2O3。
本发明第二方面提供了一种由前述所述的制备方法制备得到的用于甘油氢解制备1,3-丙二醇催化剂。
本发明第三方面提供了一种前述所述的用于甘油氢解制备1,3-丙二醇催化剂在甘油氢解制备1,3-丙二醇中的应用。
通过上述技术方案,本发明提供的甘油氢解制备1,3-丙二醇催化剂制备方法,以六氯化钨为氧化钨前驱体,可以在较低温度下转变成助剂WO3。通过选取具有合适物性γ-氧化铝为载体,可以提高氧化钨的分散性,进而提高对催化活性有贡献的氧化钨组分含量;优化铂钨原子比,提高催化剂活性。
具体实施方式
在本文中所披露的范围的端点和任何值都不限于该精确的范围或值,这些范围或值应当理解为包含接近这些范围或值的值。对于数值范围来说,各个范围的端点值之间、各个范围的端点值和单独的点值之间,以及单独的点值之间可以彼此组合而得到一个或多个新的数值范围,这些数值范围应被视为在本文中具体公开。
如前所述,本发明第一方面提供了一种用于甘油氢解制备1,3-丙二醇催化剂的制备方法,其中,所述的制备方法包括:
(1)采用过量浸渍法将氧化钨前驱体、溶剂和γ-Al2O3接触,经水浴蒸干、第一干燥和第一焙烧处理后,得到复合氧化物WO3/Al2O3;所述氧化钨前驱体为六氯化钨;
(2)将所述复合氧化物WO3/Al2O3、水和Pt的前驱体接触,经水浴蒸干、第二干燥、第二焙烧、还原处理后,得到催化剂Pt/WO3/Al2O3。
在本发明中,需要说明的是,所述的复合氧化物WO3/Al2O3中,Al2O3为载体,WO3为活性组分。
根据本发明,所述溶剂选自乙醚、乙醇、苯和四氯化碳中的一种或多种;优选为乙醇。在本发明中,选择本发明特定的溶剂,具有无毒,挥发性适中的优点。
根据本发明,所述接触的条件包括:室温至90℃搅拌2-8h;优选情况下,在室温条件下搅拌2-8h;优选情况下,所述接触在搅拌条件下进行,其中,所述搅拌条件包括:搅拌速率为100-600转/分钟。
根据本发明,所述水浴蒸干的条件包括:温度为40-90℃;优选情况下,温度为50-90℃。
根据本发明,所述第一干燥的条件包括:温度为60-100℃,时间为6-12h;优选情况下,温度为80-100℃,时间为8-12h。
根据本发明,所述第二干燥的条件包括:温度为80-120℃,时间为6-12h;优选情况下,温度为100-120℃,时间为8-12h。
根据本发明,所述第一焙烧的条件包括:温度为250-450℃焙烧4-10h;优选地,温度为250-350℃焙烧6-10h。
根据本发明,所述第二焙烧的条件包括:温度为250-400℃焙烧2-8h;优选地,温度为250-350℃焙烧4-8h。
本发明提供的甘油氢解制备1,3-丙二醇催化剂制备方法,以六氯化钨为氧化钨前驱体,可以在较低温度下转变成助剂WO3。
根据本发明,所述还原的条件包括:温度为200-400℃,时间为1-4h;优选情况下,温度为250-300℃,时间为2-3h。
在本发明中,所述还原条件为气相还原,还原性气体为氢气,氢气含量为1-100%,优选为10-100%,其余为氮气。还原气体流速为10-100ml/min,优选为10-50ml/min。优选为常压还原。
根据本发明,所述γ-Al2O3的比表面积≥50m2/g,优选为50-500m2/g,更优选为100-400m2/g,更进一步优选为150-300m2/g。
根据本发明,所述γ-Al2O3的孔径≥5nm,优选为5-30nm,更优选为6-15nm。
根据本发明,所述Pt前驱体包括氯铂酸、四氨合氯化铂、四氨合硝酸铂和硝酸铂中的一种或多种,优选为氯铂酸。
根据本发明,在步骤(1)中,相对于3g所述γ-Al2O3,所述氧化钨前驱体的用量为0.5-1.5g;优选情况下,相对于3g所述γ-Al2O3,所述氧化钨前驱体的用量为0.5-1.3g。
根据本发明,在步骤(2)中,相对于3g所述WO3/Al2O3,所述Pt的前驱体的用量为0.24-0.4g;优选情况下,相对于3g所述WO3/Al2O3,所述Pt的前驱体的用量为0.24-0.32g。
本发明第二方面提了一种由前述所述的制备方法制备得到的用于甘油氢解制备1,3-丙二醇催化剂。
根据本发明,所述催化剂包括复合氧化物WO3/Al2O3以及负载在所述复合氧化物WO3/Al2O3上的活性组分Pt,且钨原子的表面密度为1-5个/nm2,优选为1-3个/nm2,更优选为1.5-2.5个/nm2,更进一步优选为1.73-2.57个/nm2;在本发明中,如果钨原子的表面密度过高,则会形成对催化剂活性没有贡献的晶相WO3,且降低对催化剂活性有贡献的多钨酸物种;如果钨原子的表面密度过低,则会使得Pt与氧化钨不能有效接触,降低催化剂活性。
根据本发明,铂钨原子比为0.01-1,优选为0.05-0.8,更优选为0.16-0.67。在本发明中,如果铂钨原子比过高,则会降低铂分散性,不仅不利于催化剂活性提高,还会增加催化剂成本;如果铂钨原子比过低,则会降低活性位的数量。
在本发明中,需要说明的是,“钨原子的表面密度”是指载体表面每平方纳米的区域内钨原子的个数。
“铂钨原子比”是指铂钨摩尔比。
根据本发明,以所述催化剂的总重量为基准,所述WO3的含量为8-25重量%,所述Pt的含量为2.9-5重量%;优选地,以所述催化剂的总重量为基准,所述WO3的含量为8.5-21.7重量%,所述Pt的含量为2.9-4.8重量%;更优选地,以所述催化剂的总重量为基准,所述WO3的含量为9-20重量%,所述Pt的含量为3-4重量%。
根据本发明,所述催化剂的比表面积为110-230m2/g,孔体积为0.4-1.1ml/g,最可几孔径为7-16nm;优选地,所述催化剂的比表面积为113-225m2/g,孔体积为0.4-1ml/g,最可几孔径为7.9-15.4nm。
本发明第三方面提供了一种前述所述的用于甘油氢解制备1,3-丙二醇催化剂在甘油氢解制备1,3-丙二醇中的应用。
根据本发明,所述催化剂用于甘油氢解制备1,3-丙二醇反应,反应在高压反应釜中进行,原料为甘油水溶液和氢气,先用纯氢置换反应釜内空气后,充入氢气,在一定温度下搅拌反应。
根据本发明,所述甘油水溶液质量分数为1-50%,优选为3-30%。
根据本发明,所述Pt与甘油质量比为0.001-0.015,优选为0.005-0.01。
根据本发明,所述氢气初始压力为1-8MPa,优选为2-6MPa。
根据本发明,所述反应温度为100-200℃,优选为120-180℃,更优选为150-180℃。
根据本发明,优选情况下,所述反应温度150-180℃,1,3-丙二醇收率高。
根据本发明,所述反应时间为3-24h,优选为6-24h。
以下将通过实施例对本发明进行详细描述。
以下实施例和对比例中:
比表面积,孔体积和孔径分布用Autosorb-iQ(美国康塔公司)气体吸附仪测得;
产物及原料含量用气相色谱(安捷伦,7890A)测得;
原料甘油为伊诺凯公司牌号为innochem的市售品。
实施例1
本实施例在于说明采用本发明的方法制备的用于甘油氢解制备1,3-丙二醇催化剂及其应用。
(1)将1.02g WCl6溶于50ml乙醇中,加入3g氧化铝(比表面积:222.5m2/g,孔体积:0.54ml/g,最可几孔径:7.4nm),室温,在搅拌速率为450转/分钟条件下,搅拌5h后,50℃水浴蒸干,100℃烘箱干燥8h,250℃焙烧10h,得到WO3/Al2O3;
(2)将0.32g氯铂酸溶于10ml水中,加入3g上述WO3/Al2O3,室温搅拌5h后,80℃水浴蒸干,120℃烘箱干燥8h,350℃焙烧3h,氢气(100%)250℃还原2h,得到催化剂Pt/WO3/Al2O3。
经测定:钨原子的表面密度为2.32个/nm2,铂钨原子比为0.29;
以所述催化剂的总重量为基准,所述WO3的含量为16重量%,所述Pt的含量为3.9重量%。
所述催化剂Pt/WO3/Al2O3比表面积为162m2/g,孔体积为0.49ml/g,最可几孔径为7.9nm。
(3)取0.5g上述催化剂Pt/WO3/Al2O3,分散于30g甘油水溶液(10%)中,将催化剂和反应液一并转移至100mL高压釜中。在室温条件下H2压力3MPa置换5次后,充入氢气至5MPa,搅拌速度650转/min,反应温度为180℃,反应12h后停止搅拌。冷却至室温后,离心分离,用0.25μm滤膜过滤后收集水相样品,用气相色谱分析产物组成。
甘油转化率69.8%;1,3-丙二醇选择性:51.1%;1,3-丙二醇收率:35.7%。
实施例2
本实施例在于说明采用本发明的方法制备的用于甘油氢解制备1,3-丙二醇催化剂及其应用。
(1)将0.51g WCl6溶于50ml乙醇中,加入3g氧化铝(比表面积:146.5m2/g,孔体积:0.43ml/g,最可几孔径:8.7nm),室温,在搅拌速率为150转/分钟条件下,搅拌8h后,70℃水浴蒸干,80℃烘箱干燥10h,350℃焙烧4h,得到WO3/Al2O3;
(2)将0.28g氯铂酸溶于10ml水中,加入3g上述WO3/Al2O3,室温搅拌8h后,60℃水浴蒸干,80℃烘箱干燥10h,250℃焙烧8h,氢气(10%)250℃还原2h,得到催化剂Pt/WO3/Al2O3。
经测定:钨原子的表面密度为1.76个/nm2,铂钨原子比为0.46;
以所述催化剂的总重量为基准,所述WO3的含量为8.7重量%,所述Pt的含量为3.4重量%。
所述催化剂Pt/WO3/Al2O3比表面积为120m2/g,孔体积为0.41ml/g,最可几孔径为9.2nm。
(3)取0.65g上述催化剂Pt/WO3/Al2O3,分散于15g甘油水溶液(3%)中,将催化剂和反应液一并转移至100mL高压釜中。在室温条件下H2压力3MPa置换5次后,充入氢气至4MPa,搅拌速度650转/min,反应温度为155℃,反应6h后停止搅拌。冷却至室温后,离心分离,用0.25μm滤膜过滤后收集水相样品,用气相色谱分析产物组成。
甘油转化率:70.1%;1,3-丙二醇选择性:50.3%;1,3-丙二醇收率:35.3%。
实施例3
本实施例在于说明采用本发明的方法制备的用于甘油氢解制备1,3-丙二醇催化剂及其应用。
(1)将1.28g WCl6溶于50ml乙醇中,加入3g氧化铝(比表面积:286.3m2/g,孔体积:0.78ml/g,最可几孔径:7.6nm),室温,在搅拌速率为600转/分钟条件下,搅拌2h后,55℃水浴蒸干,120℃烘箱干燥12h,300℃焙烧8h,得到WO3/Al2O3;
(2)将0.24g氯铂酸溶于10ml水中,加入3g上述WO3/Al2O3,室温搅拌2h后,90℃水浴蒸干,100℃烘箱干燥12h,300℃焙烧5h,氢气(50%)250℃还原2h,得到催化剂Pt/WO3/Al2O3。
经测定:钨原子的表面密度为2.26个/nm2,铂钨原子比为0.18;
以所述催化剂的总重量为基准,所述WO3的含量为19.4重量%,所述Pt的含量为2.9重量%。
所述催化剂Pt/WO3/Al2O3比表面积为219m2/g,孔体积为0.71ml/g,最可几孔径为8.2nm。
(3)取0.5g上述催化剂Pt/WO3/Al2O3,分散于10g甘油水溶液(30%)中,将催化剂和反应液一并转移至100mL高压釜中。在室温条件下H2压力3MPa置换5次后,充入氢气至6MPa,搅拌速度650转/min,反应温度为180℃,反应24h后停止搅拌。冷却至室温后,离心分离,用0.25μm滤膜过滤后收集水相样品,用气相色谱分析产物组成。
甘油转化率:67.5%;1,3-丙二醇选择性:49.8%;1,3-丙二醇收率:33.6%。
实施例4
本实施例在于说明采用本发明的方法制备的用于甘油氢解制备1,3-丙二醇催化剂及其应用。
(1)将0.50g WCl6溶于50ml乙醇中,加入3g氧化铝(比表面积:146.5m2/g,孔体积:0.43ml/g,最可几孔径:8.7nm),室温,在搅拌速率为250转/分钟条件下,搅拌5h后,55℃旋蒸至干,80℃烘箱干燥12h,400℃焙烧6h,得到WO3/Al2O3;
(2)将0.40g氯铂酸溶于10ml水中,加入3g上述WO3/Al2O3,室温搅拌5h后,90℃水浴蒸干,100℃烘箱干燥12h,300℃焙烧5h,氢气(100%)250℃还原2h,得到催化剂Pt/WO3/Al2O3。
经测定:钨原子的表面密度为1.73个/nm2,铂钨原子比为0.67;
以所述催化剂的总重量为基准,所述WO3的含量为8.5重量%,所述Pt的含量为4.8重量%。
所述催化剂Pt/WO3/Al2O3比表面积为113m2/g,孔体积为0.4ml/g,最可几孔径为9.5nm。
(3)取0.6g上述催化剂Pt/WO3/Al2O3,分散于30g甘油水溶液(12%)中,将催化剂和反应液一并转移至100mL高压釜中。在室温条件下H2压力3MPa置换5次后,充入氢气至4MPa,搅拌速度650转/min,反应温度为180℃,反应10h后停止搅拌。冷却至室温后,离心分离,用0.25μm滤膜过滤后收集水相样品,用气相色谱分析产物组成。
甘油转化率:66.4%;1,3-丙二醇选择性:48.8%;1,3-丙二醇收率:32.4%。
实施例5
本实施例在于说明采用本发明的方法制备的用于甘油氢解制备1,3-丙二醇催化剂及其应用。
(1)将1.48g WCl6溶于50ml乙醇中,加入3g氧化铝(比表面积:291.5m2/g,孔体积:1.18ml/g,最可几孔径:14.6nm),室温,在搅拌速率为500转/分钟条件下,搅拌5h后,50℃水浴蒸干,100℃烘箱干燥8h,450℃焙烧4h,得到WO3/Al2O3;
(2)将0.24g氯铂酸溶于10ml水中,加入3g上述WO3/Al2O3,室温搅拌5h后,80℃水浴蒸干,120℃烘箱干燥8h,400℃焙烧3h,氢气(100%)250℃还原2h,得到催化剂Pt/WO3/Al2O3。
经测定:钨原子的表面密度为2.57个/nm2,铂钨原子比为0.16;
以所述催化剂的总重量为基准,所述WO3的含量为21.7重量%,所述Pt的含量为2.9重量%。
所述催化剂Pt/WO3/Al2O3比表面积为225m2/g,孔体积为1ml/g,最可几孔径为15.4nm。
(3)取1.0g上述催化剂Pt/WO3/Al2O3,分散于15g甘油水溶液(30%)中,将催化剂和反应液一并转移至100mL高压釜中。在室温条件下H2压力3MPa置换5次后,充入氢气至6MPa,搅拌速度650转/min,反应温度为170℃,反应20h后停止搅拌。冷却至室温后,离心分离,用0.25μm滤膜过滤后收集水相样品,用气相色谱分析产物组成。
甘油转化率:65.9%;1,3-丙二醇选择性:47.7%;1,3-丙二醇收率:31.4%。
实施例6
本实施例在于说明采用本发明的方法制备的用于甘油氢解制备1,3-丙二醇催化剂及其应用。
(1)将1.02g WCl6溶于50ml乙醇中,加入3g氧化铝(比表面积:222.5m2/g,孔体积:0.54ml/g,最可几孔径:7.4nm),室温,在搅拌速率为400转/分钟条件下,搅拌5h后,50℃水浴蒸干,100℃烘箱干燥8h,250℃焙烧10h,得到WO3/Al2O3;
(2)将0.32g氯铂酸溶于10ml水中,加入3g上述WO3/Al2O3,室温搅拌5h后,80℃水浴蒸干,120℃烘箱干燥8h,400℃焙烧3h,氢气(100%)250℃还原2h,得到催化剂Pt/WO3/Al2O3。
经测定:钨原子的表面密度为2.32个/nm2,铂钨原子比为0.29;
以所述催化剂的总重量为基准,所述WO3的含量为15.9重量%,所述Pt的含量为3.8重量%。
所述催化剂Pt/WO3/Al2O3比表面积为165m2/g,孔体积为0.48ml/g,最可几孔径为8.1nm。
(3)取1.5g上述催化剂Pt/WO3/Al2O3,分散于20g甘油水溶液(10%)中,将催化剂和反应液一并转移至100mL高压釜中。在室温条件下H2压力3MPa置换5次后,充入氢气至4MPa,搅拌速度650转/min,反应温度为160℃,反应8h后停止搅拌。冷却至室温后,离心分离,用0.25μm滤膜过滤后收集水相样品,用气相色谱分析产物组成。
甘油转化率:64.3%;1,3-丙二醇选择性:48.0%;1,3-丙二醇收率:30.9%。
对比例1
(1)将0.64g偏钨酸铵溶于10g水中,加入3gγ-Al2O3(比表面积:222.5m2/g,孔体积:0.54ml/g,最可几孔径:7.4nm),室温,在搅拌速率为600转/分钟条件下,搅拌5h后,60℃水浴蒸干,120℃烘箱干燥8h,550℃焙烧4h,得到WO3/Al2O3;
(2)将0.32g氯铂酸溶于10ml水中,加入3g上述WO3/Al2O3,室温搅拌5h后,80℃水浴蒸干,120℃烘箱干燥8h,400℃焙烧3h,氢气(100%)250℃还原3h,得到催化剂Pt/WO3/Al2O3。
经测定:钨原子的表面密度为2.32个/nm2,铂钨原子比为0.29;
以所述催化剂的总重量为基准,所述WO3的含量为15.9重量%,所述Pt的含量为3.9重量%。
所述催化剂Pt/WO3/Al2O3比表面积为167m2/g,孔体积为0.48ml/g,最可几孔径为8.1nm。
(3)取0.5g上述催化剂,分散于30g甘油水溶液(10%)中,将催化剂和反应液一并转移至100mL高压釜中。在室温条件下H2压力3MPa置换5次后,充入氢气至5MPa,搅拌速度650转/min,反应温度为180℃,反应12h后停止搅拌。冷却至室温后,离心分离,用0.25μm滤膜过滤后收集水相样品,用气相色谱分析产物组成。
甘油转化率:67.2%;1,3-丙二醇选择性:50.2%;1,3-丙二醇收率:33.7%。
对比例2
(1)将1.54g WCl6溶于50ml乙醇中,加入3g氧化铝(比表面积:222.5m2/g,孔体积:0.54ml/g,最可几孔径:7.4nm),室温,在搅拌速率为500转/分钟条件下,搅拌5h后,50℃水浴蒸干,100℃烘箱干燥8h,250℃焙烧10h,得到WO3/Al2O3;
(2)将0.16g氯铂酸溶于10ml水中,加入3g上述WO3/Al2O3,室温搅拌5h后,80℃水浴蒸干,120℃烘箱干燥8h,400℃焙烧3h,氢气(100%)250℃还原2h,得到催化剂Pt/WO3/Al2O3。
经测定:钨原子的表面密度为3.5个/nm2,铂钨原子比为0.1;
以所述催化剂的总重量为基准,所述WO3的含量为22.6重量%,所述Pt的含量为2重量%。
所述催化剂Pt/WO3/Al2O3比表面积为134m2/g,孔体积为0.39ml/g,最可几孔径为9nm。
(3)取0.5g上述催化剂,分散于30g甘油水溶液(10%)中,将催化剂和反应液一并转移至100mL高压釜中。在室温条件下H2压力3MPa置换5次后,充入氢气至5MPa,搅拌速度650转/min,反应温度为180℃,反应12h后停止搅拌。冷却至室温后,离心分离,用0.25μm滤膜过滤后收集水相样品,用气相色谱分析产物组成。
甘油转化率:43.7%;1,3-丙二醇选择性:45.9%;1,3-丙二醇收率:20.1%。
对比例3
0.26WCl6溶于35ml乙醇中,加入3g氧化铝(比表面积:146.5m2/g,孔体积:0.43ml/g,最可几孔径:8.7nm),室温,在搅拌速率为600转/分钟条件下,边搅拌边以0.12ml/分钟的滴加速率边滴加水乙醇溶液(0.24g水+15ml乙醇)滴加完成后继续搅拌5h,40℃水浴蒸干,100℃烘箱干燥8h,250℃焙烧10h,得到WO3/Al2O3;
(2)将0.24g氯铂酸溶于10ml水中,加入3g上述WO3/Al2O3,室温搅拌5h后,80℃水浴蒸干,120℃烘箱干燥8h,400℃焙烧3h,氢气(100%)250℃还原2h,得到催化剂Pt/WO3/Al2O3。
经测定:钨原子的表面密度为0.9个/nm2,铂钨原子比为0.74;
以所述催化剂的总重量为基准,所述WO3的含量为4.7重量%,所述Pt的含量为2.9重量%。
所述催化剂Pt/WO3/Al2O3比表面积为124m2/g,孔体积为0.41ml/g,最可几孔径为8.8nm。
(3)取0.5g上述催化剂Pt/WO3/Al2O3,分散于30g甘油水溶液(10%)中,将催化剂和反应液一并转移至100mL高压釜中。在室温条件下H2压力3MPa置换5次后,充入氢气至5MPa,搅拌速度650转/min,反应温度为180℃,反应12h后停止搅拌。冷却至室温后,离心分离,用0.25μm滤膜过滤后收集水相样品,用气相色谱分析产物组成。
甘油转化率:34.6%;1,3-丙二醇选择性:47.7%;1,3-丙二醇收率:16.5%。
对比例4
(1)0.32g氯铂酸溶于10ml水中,加入3g氧化铝(比表面积:286.3m2/g,孔体积:0.78ml/g,最可几孔径:7.6nm),室温搅拌5h后,80℃水浴蒸干,120℃烘箱干燥8h,350℃焙烧3h,氢气(100%)250℃还原2h,得到催化剂Pt/Al2O3。
(2)取0.5g上述催化剂Pt/WO3/Al2O3,分散于30g甘油水溶液(10%)中,将催化剂和反应液一并转移至100mL高压釜中。在室温条件下H2压力3MPa置换5次后,充入氢气至5MPa,搅拌速度650转/min,反应温度为180℃,反应12h后停止搅拌。冷却至室温后,离心分离,用0.25μm滤膜过滤后收集水相样品,用气相色谱分析产物组成。
甘油转化率:5.9%;1,3-丙二醇选择性:95.3%;1,3-丙二醇收率:5.6%。
通过对比例1可知,在Pt-W催化剂体系中,偏钨酸铵是常用的钨源,由偏钨酸铵为钨源得到的催化剂,在甘油氢解反应中转化率为67.2%,1,3-丙二醇选择性为50.2%,收率为33.7%;由六氯化钨为钨源得到的催化剂,甘油转化率为69.8%,1,3-丙二醇选择性为51.1%,收率为35.7%。两个催化剂的活性相比,后者略高于前者,而且以偏钨酸铵为钨源,其分解温度要高于以六氯化钨为钨源。
通过对比例2和对比例3可知,Pt的含量过低,或者表面钨原子密度过低,均不利于1,3-丙二醇收率提高。
通过对比例4可知,没有WO3,催化剂对甘油氢解反应活性很低,说明WO3是高活性甘油氢解反应催化剂必不可少的组分,其含量对催化剂活性至关重要。
以上详细描述了本发明的优选实施方式,但是,本发明并不限于此。在本发明的技术构思范围内,可以对本发明的技术方案进行多种简单变型,包括各个技术特征以任何其它的合适方式进行组合,这些简单变型和组合同样应当视为本发明所公开的内容,均属于本发明的保护范围。
Claims (10)
1.一种用于甘油氢解制备1,3-丙二醇催化剂的制备方法,其特征在于,所述的制备方法包括:
(1)采用过量浸渍法将氧化钨前驱体、溶剂和γ-Al2O3接触,经水浴蒸干、第一干燥和第一焙烧处理后,得到复合氧化物WO3/Al2O3;所述氧化钨前驱体为六氯化钨;
(2)将所述复合氧化物WO3/Al2O3、水和Pt的前驱体接触,经水浴蒸干、第二干燥、第二焙烧、还原处理后,得到催化剂Pt/WO3/Al2O3。
2.根据权利要求1所述的制备方法,其中,所述溶剂选自乙醚、乙醇、苯和四氯化碳中的一种或多种;优选为乙醇。
3.根据权利要求1所述的制备方法,其中,所述第一干燥的条件包括:温度为60-100℃,时间为6-12h;
和/或,所述第二干燥的条件包括:温度为80-120℃,时间为6-12h;
和/或,所述第一焙烧的条件包括:温度为250-450℃焙烧4-10h;优选地,温度为250-350℃焙烧6-10h;
和/或,所述第二焙烧的条件包括:温度为250-400℃焙烧2-8h;优选地,温度为250-350℃焙烧4-8h;
和/或,所述还原的条件包括:温度为200-400℃,时间为1-4h;
优选地,所述还原条件为气相还原,还原性气体为氢气,氢气含量为1-100%,优选为10-100%,其余为氮气;还原气体流速为10-100ml/min,优选为10-50ml/min。
4.根据权利要求1所述的制备方法,其中,所述γ-Al2O3的比表面积≥50m2/g,优选为50-500m2/g,更优选为100-400m2/g,更进一步优选为150-300m2/g;
优选地,所述γ-Al2O3的孔径≥5nm,优选为5-30nm,更优选为6-15nm。
5.根据权利要求1所述的制备方法,其中,所述Pt前驱体包括氯铂酸、四氨合氯化铂、四氨合硝酸铂和硝酸铂中的一种或多种,优选为氯铂酸。
6.一种由权利要求1-5中任意一项所述的制备方法制备得到的用于甘油氢解制备1,3-丙二醇催化剂。
7.根据权利要求6所述的催化剂,其中,所述催化剂包括复合氧化物WO3/Al2O3以及负载在所述复合氧化物WO3/Al2O3上的活性组分Pt,且钨原子的表面密度为1-5个/nm2,优选为1-3个/nm2,优选为1.5-2.5个/nm2;铂钨原子比为0.01-1,优选为0.05-0.8,更优选为0.16-0.67。
8.根据权利要求6或7所述的催化剂,其中,以所述催化剂的总重量为基准,所述WO3的含量为8-25重量%,所述Pt的含量为2.9-5重量%;
优选地,以所述催化剂的总重量为基准,所述WO3的含量为8.5-21.7重量%,所述Pt的含量为2.9-4.8重量%。
9.根据权利要求6所述的催化剂,其中,所述催化剂的比表面积为110-230m2/g,孔体积为0.4-1.1ml/g,最可几孔径为7-16nm。
10.一种权利要求6-9中任意一项所述的用于甘油氢解制备1,3-丙二醇催化剂在甘油氢解制备1,3-丙二醇中的应用。