CN1177619C - 一种医疗外科用固定材料及其制备方法 - Google Patents

一种医疗外科用固定材料及其制备方法 Download PDF

Info

Publication number
CN1177619C
CN1177619C CNB991171713A CN99117171A CN1177619C CN 1177619 C CN1177619 C CN 1177619C CN B991171713 A CNB991171713 A CN B991171713A CN 99117171 A CN99117171 A CN 99117171A CN 1177619 C CN1177619 C CN 1177619C
Authority
CN
China
Prior art keywords
parts
fixing material
tert
butyl
surgery
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB991171713A
Other languages
English (en)
Other versions
CN1294021A (zh
Inventor
闵拥军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB991171713A priority Critical patent/CN1177619C/zh
Publication of CN1294021A publication Critical patent/CN1294021A/zh
Application granted granted Critical
Publication of CN1177619C publication Critical patent/CN1177619C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开了一种医疗外科用固定材料，它含有30～100份反式聚异戊二烯和0.05～1.0份防老剂。本发明还公开了该固定材料的制备方法。本发明的医疗外科用固定材料不仅克服了现有石膏固定材料缺点，而且与以聚己酸内酯为主要原料合成的固定材料相比，原料便宜易得，成本低，可实际推广使用。

Description

一种医疗外科用固定材料及其制备方法
本发明涉及一种医疗外科用固定材料及其制备方法。
目前医院中通用的医疗外科用固定材料为石膏，用它来制作各种固定夹板、放疗定位板等。但是用这种材料制成的固定夹板、放疗定位板具有很多不足之处：1、适用范围一定的有局限性：手指、腕、肘关节、肩关节、鼻骨、脚、踝、膝关节、下肢、头部、颈部、肋骨、脊柱、骨盆各种静态固定及关节炎、烧伤伴骨折、开放性骨折等全固定或半固定、放射治疗模型、矫形模型定位等不规则部位难以使用；2、不透气：导致皮肤红肿、搔痒等现象；3、缺乏韧性，易断裂；4、笨重，体积大：患者生活不便；5、缺乏可塑性：不能使用于形状复杂的部位；6、使用不便：往往需要用纱布绷带配合缠绕固定；7、X射线难以穿过：不便于随时作放射检查及治疗；8、怕水：病人不能洗澡和接受水疗；9、不容易储存：必须保存在干燥的环境，保存时间短。鉴于传统的石膏材料具有如此多的不足之处，人们开始研究新型的固定材料，陈慧敏等人在《医疗卫生装备》1992年第一期《新型医用固定材料---PCL塑性夹板》一文中报导了以聚己酸内酯为主要原料合成的固定材料，虽然部分解决了原有石膏材料存在的问题，但由于聚己酸内酯市场供应极少，且价格昂贵，无法工业化大生产，无法取代原有的石膏材料。
本发明的目的在于提供一种克服了石膏固定材料缺点且原料便宜易得，成本低的医疗外科用固定材料。
本发明的医疗外科用固定材料，含有30～100份反式聚异戊二烯和0.05～1.0份防老剂，还可以在其中加入5～30份SBS(苯乙烯-丁二烯-苯乙烯嵌段共聚物)、SIS(苯乙烯-异戊二烯-苯乙烯嵌段共聚物)、聚氨酯弹性体中的一种、两种或三种，另外还可以加入5～30份顺式聚异戊二烯、3～8份硫化剂和0.1～0.8份硫化促进剂。在此基础上还可以继续添加8～20份补强剂和/或5～15份软化剂。所述的防老剂为2，6-二叔丁基-4-甲基苯酚、亚磷酸三(壬基苯酯)、β-(4-羟基-3，5-二叔丁基苯基)丙酸正十八碳醇酯、硫代二丙酸二月桂酯或1，1，3-三(二-甲基-4-羟基-5-叔丁基苯基)丁烷；硫化剂为硫磺、过氧化苯甲酰或二叔丁基过氧化异丙苯；硫化促进剂为胍类、硫脲类、磺盐酸类或醛胺类，尤其为二苯胍、四甲基秋兰姆一硫化合物、四甲基秋兰姆二硫化合物或四乙基秋兰姆二硫化合物；软化剂为古马隆茚树脂、煤焦油、煤沥青、苯二甲酸酯或环烷油；补强剂为白碳黑、轻质碳酸钙或滑石粉。
本发明的医疗外科用固定材料的制备方法，由以下步骤组成：
(1)将30～100份反式聚异戊二烯和0.05～1.0份防老剂和/或5～30份SBS和/或SIS和/或聚氨酯弹性体和/或5～30份顺式聚异戊二烯、3～8份硫化剂和0.1～0.8份硫化促进剂和/或8～20份补强剂和/或5～15份软化剂混合；
(2)60～90℃下塑炼15～20分钟。当含有5～30份顺式聚异戊二烯、3～8份硫化剂和0.1～0.8份硫化促进剂时，还需在135℃下塑炼15～25分钟；
(3)造粒，然后20兆拉德Co60辐照；
(4)80～90℃，800～1500公斤/厘米2下注射成型。
本发明的医疗外科用固定材料与石膏材料相比，具有以下优点：
(1)具有记忆功能，可以重复使用；
(2)具有透气功能，不会引起皮肤红肿、搔痒等现象；
(3)具有一定的韧性，不易断裂；
(4)重量轻；
(5)具有可塑性，可使用在肩关节、鼻骨等不规则的部位；
(6)安装及拆卸方便，不需要用纱布绷带配合缠绕固定；
(7)X射线100％可透过，可以随时作放射检查及治疗；
(8)不透水，不溶于水，病人可以洗澡和接受水疗；
(9)储存时间长。
本发明的医疗外科用固定材料与聚己酸内酯为主要原料合成的固定材料相比，具有以下优点：(1)原材料价格便宜，市场供应丰富；(2)成本低，可实际推广使用。
下面的实施例可以使本专业技术人员更好地理解本发明，但不以任何方式限制本发明。
实施例1
(1)将100份反式聚异戊二烯和0.08份2，6-二叔丁基-4-甲基苯酚混合；
(2)85℃下塑炼10分钟；
(3)造粒，然后20兆拉德Co60辐照；
(4)90℃，900公斤/厘米2下注射成型。
实施例2
(1)将80份反式聚异戊二烯、0..05份硫代二丙酸二月桂酯、20份SBS混合；
(2)90℃下塑炼15分钟；
(3)造粒，然后20兆拉德Co60辐照；
(4)85℃，1200公斤/厘米2下注射成型。
实施例3
(1)将90份反式聚异戊二烯、8份硫磺、0.5份四甲基秋兰姆一硫化合物、0.3份1，1，3-三(二-甲基-4-羟基-5-叔丁基苯基)丁烷混合；
(2)75℃下塑炼20分钟，然后135℃塑炼15分钟；
(3)造粒，然后20兆拉德Co60辐照；
(4)87℃，1000公斤/厘米2下注射成型。
实施例4
(1)将50份反式聚异戊二烯、0..6份β-(4-羟基-3，5-二叔丁基苯基)丙酸正十八碳醇酯、25份顺式聚异戊二烯、0.4份四甲基秋兰姆二硫化合物、7份过氧化苯甲酰、6份古马隆茚树脂、5份SIS、15份白碳黑混合。
(2)65℃下塑炼20分钟，然后135℃塑炼20分钟；
(3)造粒，然后20兆拉德Co60辐照；
(4)80℃，800公斤/厘米2下注射成型。

Claims (2)

1、一种医疗外科用固定材料，由30～100份反式聚异戊二烯和0.05～1.0份防老剂、5～30份SBS和/或SIS和/或聚氨酯弹性体、5～30份顺式聚异戊二烯、3～8份硫化剂、0.1～0.8份硫化促进剂、8～20份补强剂和/或5～15份软化剂制成；其中防老剂为2，6-二叔丁基-4-甲基苯酚、亚磷酸三(壬基苯酯)、β-(4-羟基-3，5-二叔丁基苯基)丙酸正十八碳醇酯、硫代二丙酸二月桂酯或1，1，3-三(二-甲基-4-羟基-5-叔丁基苯基)丁烷，硫化剂为硫磺、过氧化苯甲酰或二叔丁基过氧化异丙苯，硫化促进剂为胍类、硫脲类、磺盐酸类或醛胺类，软化剂为古马隆茚树脂或煤焦油、煤沥青、苯二甲酸酯或环烷油，补强剂为白碳黑、轻质碳酸钙或滑石粉。
2、如权利要求1所述的固定材料，其特征在于硫化促进剂为二苯胍、四甲基秋兰姆一硫化合物、四甲基秋兰姆二硫化合物或四乙基秋兰姆二硫化合物。
CNB991171713A 1999-10-29 1999-10-29 一种医疗外科用固定材料及其制备方法 Expired - Fee Related CN1177619C (zh)