CN117757177A - Xlpo护套料及其制备方法、护套 - Google Patents
Xlpo护套料及其制备方法、护套 Download PDFInfo
- Publication number
- CN117757177A CN117757177A CN202311871864.6A CN202311871864A CN117757177A CN 117757177 A CN117757177 A CN 117757177A CN 202311871864 A CN202311871864 A CN 202311871864A CN 117757177 A CN117757177 A CN 117757177A
- Authority
- CN
- China
- Prior art keywords
- parts
- xlpo
- flame retardant
- antioxidant
- poe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种XLPO护套料及其制备方法、护套。所述XLPO护套料的配料以重量份计，包括：EVA35‑55份，PE5‑10份，POE10‑15份，磷酸酯改性POSS阻燃剂5‑30份，相容剂3‑8份，阻燃剂20‑100份。本发明提供的高阻燃XLPO护套料具有优异的阻燃性和物理机械性能。
Description
技术领域
本发明涉及护套料领域，具体涉及一种XLPO护套料及其制备方法及护套。
背景技术
XLPO电缆料有很多种可以满足UL电线阻燃要求的低烟、无卤阻燃电缆料，无卤高阻燃电缆料是通过添加大量的氢氧化铝、二乙基次磷酸铝、MCA等阻燃剂改性，大量阻燃剂的添加导致了材料的物理性能的下降，不能满足标准要求，XLPO材料柔性较好，绝缘性好，结构轻便，成本低廉，具有优异的抗开裂，耐低温，耐磨，机械性能等，在鞋材，管材，注塑及电缆料中有着大量的应用，因此开发一款高阻燃，性能优的XLPO材料十分必要。
发明内容
鉴于上述现有技术的不足，本发明提出一种XLPO护套料及其制备方法及护套，旨在解决目前XLPO材料阻燃性和物理机械性能较差的问题。
为实现上述目的，本发明提出一种XLPO护套料，所述XLPO护套料的配料以重量份计，包括：EVA35-55份，PE5-10份，POE10-15份，磷酸酯改性POSS阻燃剂5-30份，相容剂3-8份，阻燃剂20-100份。
可选地，所述PE包括低密度PE、中密度PE、高密度PE、线性低密度PE和茂金属PE中的一种或多种；所述POE为四碳POE或八碳POE中的一种或多种。
可选地，所述阻燃剂包括P系阻燃剂0-10、N系阻燃剂0-20份和无机阻燃剂20-60份。
可选地，所述XLPO护套料的配料还包括润滑剂0.2-1份、抗氧剂0.5-2和光稳定剂0.2-1份；所述润滑剂为硬脂酸、硬脂酸钙、硬脂酸镁、聚乙烯蜡、石蜡、硅酮中一种或多种的组合；所述抗氧剂包括抗氧剂1035、抗氧剂168、抗氧剂TH-412S、抗氧剂1098、抗氧剂1010中的至少一种；所述光稳定剂包括氧化锌，二氧化钛，二苯甲酮，水杨酸，苯并三唑中的一种或几种。
可选地，所述磷酸酯改性POSS阻燃剂由缩水甘油醚氧丙基笼状聚倍半硅氧烷、2-胺乙基-2,3-二羟丙基-羟基磷酸酯与催化剂添加于有机溶液中反应得到。
可选地，所述相容剂为PE接枝马来酸酐、POE接枝马来酸酐、PP接枝马来酸酐、EMA接枝马来酸酐中的一种或多种。
为了实现上述目的，本发明还提出一种XLPO护套料的制备方法，包括以下步骤：催化反应得到磷酸酯改性POSS阻燃剂；将EVA、PE、POE、相容剂、磷酸酯改性POSS阻燃剂、阻燃剂、润滑剂混合均匀，进行密炼挤出造粒，得到颗粒料；将所述颗粒料通过干燥得到所述XLPO护套料。
可选地，催化反应得到磷酸酯改性POSS阻燃剂，包括以下步骤：将缩水甘油醚氧丙基笼状聚倍半硅氧烷溶于有机溶剂溶液中，在催化剂的作用下，加入2-胺乙基-2,3-二羟丙基-羟基磷酸酯，进行催化反应后清洁干燥，得到磷酸酯改性POSS阻燃剂。
可选地，所述所述催化剂包括有机酸和/或无机酸的一种或几种；和/或，所述有机溶剂包括醇类、芳香烃类、脂肪烃类、脂环烃类、醚类、酮类及二醇衍生物中的至少一种。
为了实现上述目的，本发明还提出一种护套，应用于充电电缆，包括上述的护套料。
本发明的有益效果：在本发明中，通过将EVA、PE、POE、磷酸酯改性POSS阻燃剂和其他阻燃剂共同作为XLPO护套料的主要组分，各组分间相互配合、协同作用，使得电缆护套料可以保持交联聚烯烃原有的良好加工性能和弹性的同时，提升了XLPO护套料的阻燃性及物理机械性能，也解决了磷酸酯容易析出的问题，磷酸酯改性POSS状态为无色粘稠液体，加入到XLPO护套料中对XLPO护套料的性能影响较小，且不需要很高的添加量即可获得具有优异阻燃性的XLPO护套料。
附图说明
图1为本发明磷酸酯改性POSS阻燃剂的分子结构图。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将对本发明实施例中的技术方案进行清楚、完整地描述，应当理解，以下实施例仅仅用以解释本发明，并不用于限定本发明。
除非另有规定，本文使用的所有技术术语和科学术语具有要求保护主题所属领域的通常含义。
为了便于理解本实施例，以下对符号、仪器及术语作出解释：
XLPO：交联聚烯烃，是一种专门用在光伏电缆绝缘体的绝缘材料，特点之一是不含卤素，遇火时不会释放有毒气体，XLPO电缆具有阻燃性，还可以抵抗紫外线、水和臭氧，易于剥离且高度灵活。是一类具有优良综合性能的高分子合成材料。
EVA：Ethylene Vinyl Acetate Copolymer，是乙烯-醋酸乙烯共聚物，广泛用于发泡鞋材、功能性棚膜、包装模、热熔胶、电线电缆及玩具等领域。
PE：Polyethylene，是乙烯单体经聚合反应制得的一种热塑性树脂，无臭，无毒，手感似蜡，具有优良的耐低温性能，化学稳定性好，能耐大多数酸碱的侵蚀，电绝缘性优良。
POE：Polyolyaltha Olfin，是一种弹性复合材料。POE是乙烯和辛烯的共聚物，其中共聚单体辛烯的含量为20％～30％。
P系阻燃剂：磷系阻燃剂包括无机磷系阻燃剂和有机磷系阻燃剂。
N系阻燃剂：氮系阻燃剂。
XLPO电缆料有很多种可以满足UL电线阻燃要求的低烟、无卤阻燃电缆料，无卤高阻燃电缆料是通过添加大量的氢氧化铝、二乙基次磷酸铝、MCA等阻燃剂改性，大量阻燃剂的添加导致了材料的物理性能的下降，不能满足标准要求，XLPO材料柔性较好，绝缘性好，结构轻便，成本低廉，具有优异的抗开裂，耐低温，耐磨，机械性能等，在鞋材，管材，注塑及电缆料中有着大量的应用，因此开发一款高阻燃，性能优的XLPO材料十分必要。
为解决上述问题，本发明提出一种XLPO护套料，所述XLPO护套料的配料以重量份计，包括：EVA35-55份，PE5-10份，POE10-15份，磷酸酯改性POSS阻燃剂5-30份，相容剂3-8份，阻燃剂20-100份。
在本方案中，通过将EVA、PE、POE、磷酸酯改性POSS阻燃剂和其他阻燃剂共同作为XLPO护套料的主要组分，各组分间相互配合、协同作用，使得电缆护套料可以保持交联聚烯烃原有良好加工性能和弹性的同时，提升了XLPO护套料的阻燃性及物理机械性能，也解决了磷酸酯容易析出的问题，磷酸酯改性POSS状态为无色粘稠液体，加入到XLPO护套料中对XLPO护套料的性能影响较小，且不需要很高的添加量即可获得具有优异阻燃性的XLPO护套料。
在一些实施例中，所述XLPO护套料的配料以重量份计，优选为包括：EVA35-55份，PE5-10份，POE10-15份，磷酸酯改性POSS阻燃剂5-30份，相容剂3-8份，阻燃剂20-100份。
进一步地，所述PE包括低密度PE、中密度PE、高密度PE、线性低密度PE和茂金属PE中的一种或多种；所述POE为四碳POE或八碳POE中的一种或多种。
在一些实施例中，所述PE包括低密度PE和中密度PE。
在一些实施例中，所述POE包括四碳POE。
在一些实施例中，所述POE包括八碳POE。
进一步地，所述阻燃剂包括P系阻燃剂0-10、N系阻燃剂0-20份和无机阻燃剂20-60份。
磷-氮协效阻燃剂的阻燃机理为凝聚相阻燃和气相阻燃的综合作用，阻燃剂在燃烧受热过程中会分解生成磷酸、聚磷酸等无机酸，能在基材表面形成一层保护膜，隔绝了空气；同时受热后易放出氨气、氮气、水蒸气和氮氧化物等不燃性气体，这些气体阻断了氧的供应，达到阻燃目的。
无机阻燃剂把具有本质阻燃性的无机元素以单质或化合物的形式添加到基材中，以物理分散状态与高聚物充分混合，在气相或凝聚相通过化学或物理变化起到阻燃作用，在合成材料中除有阻燃效果外，还有抑制发烟和氯化氢生成的作用，而且赋予材料无毒性、无腐蚀性。
在本方案中，阻燃剂的组分形成无卤复配阻燃剂，使多种阻燃元素协同作用，从而较好地平衡阻燃剂用量、性能与成本的关系，更加环保与安全。
在一些实施例中，所述P系阻燃剂包括次磷酸铝、次磷酸钙、二乙基次磷酸铝(ADP)、甲基乙基次磷酸铝和苯基次磷酸铝中的一种或多种，优选为二乙基次磷酸铝(ADP)。
在一些实施例中，所述N系阻燃剂包括氰尿酸三聚氰胺盐(MCA)、双氰胺、三聚氰胺中的一种或多种，优选为氰尿酸三聚氰胺盐(MCA)。
在一些实施例中，所述无机阻燃剂包括氢氧化镁、氢氧化铝、碳酸钙中的一种或多种，优选为氢氧化铝。
在一些实施例中，所述阻燃剂包括10份P系阻燃剂和0份N系阻燃剂。
在一些实施例中，所述阻燃剂包括0份P系阻燃剂和10份N系阻燃剂。
在一些实施例中，所述阻燃剂包括5份P系阻燃剂和5份N系阻燃剂。
在一些实施例中，所述阻燃剂包括0份P系阻燃剂、0份N系阻燃剂和20份无机阻燃剂。
进一步地，所述XLPO护套料的配料还包括润滑剂0.2-1份、抗氧剂0.5-2和光稳定剂0.2-1份；所述润滑剂为硬脂酸、硬脂酸钙、硬脂酸镁、聚乙烯蜡、石蜡、硅酮中一种或多种的组合；所述抗氧剂包括抗氧剂1035、抗氧剂168、抗氧剂TH-412S、抗氧剂1098、抗氧剂1010中的至少一种；所述光稳定剂包括氧化锌，二氧化钛，二苯甲酮，水杨酸，苯并三唑中的一种或几种。润滑剂使得密炼过程中塑化状态下的混合进料具有更好的相容性和流平性，确保护套料的整体外观均一、表面光滑，抗氧剂能够防止弹性体热氧化降解，抗水解剂能够提高聚合物分子量，提高力学强度；消光剂能够改变表面粗糙度，降低表面光泽，光稳定剂能够提高护套料的耐热、耐光性能，有效地阻止或延迟护套料的光老化的过程，从而达到延长护套料使用寿命的目的。
在一些实施例中，所述润滑剂包括硬脂酸、硬脂酸钙、硬脂酸镁、聚乙烯蜡、石蜡、硅酮中一种或多种组合，优选为硅酮，XLPO护套料的配料包括润滑剂，优选为0.5份。
在一些实施例中，所述抗氧剂包括受阻酚类抗氧剂、受阻胺类抗氧剂、磷酸酯类抗氧剂中的一种或几种，优选为抗氧剂1010，XLPO护套料的配料包括抗氧剂，优选为0.5份。
在一些实施例中，所述光稳定剂包括氧化锌，二氧化钛，二苯甲酮，水杨酸，苯并三唑中的一种或几种，XLPO护套料的配料包括光稳定剂，优选为0.3份。
进一步地，所述磷酸酯改性POSS阻燃剂由缩水甘油醚氧丙基笼状聚倍半硅氧烷、2-胺乙基-2,3-二羟丙基-羟基磷酸酯与催化剂添加于有机溶液中反应得到。在本方案中，通过将2-胺乙基-2,3-二羟丙基-羟基磷酸酯分子与缩水甘油醚氧丙基笼状聚倍半硅氧烷反应，使磷酸酯接入到POSS分子上，从而使POSS不仅具有了优异的成炭性，而且具有很高效率的阻燃性，也解决了磷酸酯因为分子量的原因容易析出的问题。
进一步地，相容剂为PE接枝马来酸酐、POE接枝马来酸酐、PP接枝马来酸酐、EMA接枝马来酸酐中的一种或多种。合适的相容剂含量对TPS护套料的力学性能、分子结构及热性能等有积极作用。
在一些实施例中，相容剂在此不作具体限定，优选为PP接枝马来酸酐，TPS护套料的配料包括相容剂5份。
为解决上述问题，本发明还提出一种XLPO护套料的制备方法，包括以下步骤：
S1：催化反应得到磷酸酯改性POSS阻燃剂；
在本方案中，得到的磷酸酯改性POSS阻燃剂可以保证热塑性聚氨酯弹性体原有的良好加工性能和弹性，同时提升了电缆护套料的抗开裂性能。
S2：EVA、PE、POE、相容剂、磷酸酯改性POSS阻燃剂、阻燃剂、润滑剂混合均匀，进行密炼挤出造粒，得到颗粒料；将所述颗粒料通过干燥得到所述XLPO护套料。
在一些实施例中，混炼在密炼机中进行。
在一些实施例中，还加入抗氧剂和光稳定剂。
S3：将所述颗粒料通过干燥得到所述XLPO护套料。
在一些实施例中，挤出造粒通过双螺杆挤出机实现。
在一些实施例中，双螺杆挤出机的长径比为(35-40)：1。
在一些实施例中，将所述不均匀颗粒通过挤出造粒得到XLPO预制料的温度为110℃-150℃。
在一些实施例中，将所述颗粒料进行干燥处理的温度为80℃-90℃。
进一步地，催化反应得到磷酸酯改性POSS阻燃剂，包括以下步骤：
将缩水甘油醚氧丙基笼状聚倍半硅氧烷溶于有机溶剂溶液中，在催化剂的作用下，加入2-胺乙基-2,3-二羟丙基-羟基磷酸酯，进行催化反应后清洁干燥，得到磷酸酯改性POSS阻燃剂。
在一些实施例中，将所述缩水甘油醚氧丙基笼状聚倍半硅氧烷和2-胺乙基-2,3-二羟丙基-羟基磷酸酯进行催化反应的摩尔比为1：8。
进一步地，所述催化剂包括有机酸和/或无机酸的一种或几种；和/或，所述有机溶剂包括醇类、芳香烃类、脂肪烃类、脂环烃类、醚类、酮类及二醇衍生物中的至少一种。
在一些实施例中，所述催化剂在此不作具体限定，优选为乙酸。
在一些实施例中，所述有机溶剂在此不作具体限定，优选为四氢呋喃。
为解决上述问题，本发明还提出一种护套，应用于充电电缆，包括上述的护套料。
以下通过具体实施例及数据解释本发明的内容。
实施例1：
将1mol缩水甘油醚氧丙基笼状聚倍半硅氧烷溶于100ml四氢呋喃溶液中，向溶液中加入0.2mol乙酸催化剂，搅拌的条件下加入8mol2-胺乙基-2,3-二羟丙基-羟基磷酸酯。搅拌反应2-4h，停止反应，减压旋蒸，加水洗涤，干燥，得到磷酸酯改性POSS阻燃剂；
将50份EVA、5份PE、10份POE、5份相容剂、5份磷酸酯改性POSS阻燃剂、50份阻燃剂(0份ADP、0份MCA、50份氢氧化铝)、0.5份润滑剂、0.5份抗氧剂、0.3份光稳定剂混合均匀，通过130℃双螺杆挤出造粒，经过85℃干燥后得到一种高阻燃高性能XLPO护套料。
实施例2：
制备方式与实施例1相同，不同的是：
将50份EVA、5份PE、10份POE、5份相容剂、10份磷酸酯改性POSS阻燃剂、50份阻燃剂(0份ADP、0份MCA、50份氢氧化铝)、0.5份润滑剂、0.5份抗氧剂、0.3份光稳定剂混合均匀，通过130℃双螺杆挤出造粒，经过85℃干燥后得到一种高阻燃高性能XLPO护套料。
实施例3：
制备方式与实施例1相同，不同的是：
将50份EVA、5份PE、10份POE、5份相容剂、15份磷酸酯改性POSS阻燃剂、50份阻燃剂(0份ADP、0份MCA、50份氢氧化铝)、0.5份润滑剂、0.5份抗氧剂、0.3份光稳定剂混合均匀，通过130℃双螺杆挤出造粒，经过85℃干燥后得到一种高阻燃高性能XLPO护套料。
实施例4：
制备方式与实施例1相同，不同的是：
将50份EVA、5份PE、10份POE、5份相容剂、20份磷酸酯改性POSS阻燃剂、50份阻燃剂(0份ADP、0份MCA、50份氢氧化铝)、0.5份润滑剂、0.5份抗氧剂、0.3份光稳定剂混合均匀，通过130℃双螺杆挤出造粒，经过85℃干燥后得到一种高阻燃高性能XLPO护套料。
实施例5：
制备方式与实施例1相同，不同的是：
将50份EVA、5份PE、10份POE、5份相容剂、25份磷酸酯改性POSS阻燃剂、50份阻燃剂(0份ADP、0份MCA、50份氢氧化铝)、0.5份润滑剂、0.5份抗氧剂、0.3份光稳定剂混合均匀，通过130℃双螺杆挤出造粒，经过85℃干燥后得到一种高阻燃高性能XLPO护套料。
实施例6：
制备方式与实施例1相同，不同的是：
将50份EVA、5份PE、10份POE、5份相容剂、30份磷酸酯改性POSS阻燃剂、50份阻燃剂(0份ADP、0份MCA、50份氢氧化铝)、0.5份润滑剂、0.5份抗氧剂、0.3份光稳定剂混合均匀，通过130℃双螺杆挤出造粒，经过85℃干燥后得到一种高阻燃高性能XLPO护套料。
实施例7：
制备方式与实施例1相同，不同的是：
将50份EVA、5份PE、10份POE、5份相容剂、20份磷酸酯改性POSS阻燃剂、60份阻燃剂(5份ADP、5份MCA、50份氢氧化铝)、0.5份润滑剂、0.5份抗氧剂、0.3份光稳定剂混合均匀，通过130℃双螺杆挤出造粒，经过85℃干燥后得到一种高阻燃高性能XLPO护套料。
对比例1：
将50份EVA、5份PE、10份POE、5份相容剂、80份阻燃剂(30份ADP、0份MCA、50份氢氧化铝)、0.5份润滑剂、0.5份抗氧剂、0.3份光稳定剂混合均匀，通过130℃双螺杆挤出造粒，经过85℃干燥后得到一种高阻燃高性能XLPO护套料。
对比例2：
将50份EVA、5份PE、10份POE、5份相容剂、80份阻燃剂(0份ADP、30份MCA、50份氢氧化铝)、0.5份润滑剂、0.5份抗氧剂、0.3份光稳定剂混合均匀，通过130℃双螺杆挤出造粒，经过85℃干燥后得到一种高阻燃高性能XLPO护套料。
对比例3：
将50份EVA、5份PE、10份POE、5份相容剂、30份2-胺乙基-2,3-二羟丙基-羟基磷酸酯，50份阻燃剂(0份ADP、0份MCA、50份氢氧化铝)、0.5份润滑剂、0.5份抗氧剂、0.3份光稳定剂混合均匀，通过130℃双螺杆挤出造粒，经过85℃干燥后得到一种高阻燃高性能XLPO护套料。
对比例4：
将50份EVA、5份PE、10份POE、5份相容剂、30份缩水甘油醚氧丙基笼状聚倍半硅氧烷，50份阻燃剂(0份ADP、0份MCA、50份氢氧化铝)、0.5份润滑剂、0.5份抗氧剂、0.3份光稳定剂混合均匀，通过130℃双螺杆挤出造粒，经过85℃干燥后得到一种高阻燃高性能XLPO护套料。
将实施例1-7及对比例1-4的组分及重要制备变量汇总成表1。
表1.本发明实施例1-7和对比例1-4的组分表
按照GB/T 1040.2、UL94和GB/T 2406.2的规定测试，对上述实施例1-7和对比例1-4中的XLPO护套料进行拉伸强度、断裂伸长率、阻燃等级、氧指数与析出性的测试，将测试结果记录为下表2：
表2.本发明实施例1-7和对比例1-4的性能
根据上方测试结果可以看出，实施例1-6中随着磷酸酯改性POSS阻燃剂份数的增加，阻燃性能逐渐提高，证明磷酸酯改性POSS阻燃剂有很好的阻燃性，阻燃效率较高，且耐析出。从实施例6和对比例4可以看出磷酸酯改性POSS阻燃剂具有更好的阻燃性；从实施例6和对比例3可以看出磷酸酯改性POSS阻燃剂具有很好的抗析出性；从实施例7可以看出磷酸酯改性POSS阻燃剂与常规阻燃剂复配使用也可以产生比较好的效果；从实施例6和对比实例1可以看出磷酸酯改性POSS阻燃剂具有更好的相容性，阻燃XLPO护套料具有更优异的物理性能；从实施例6和对比实施例2可以看出磷酸酯改性POSS阻燃剂具有更好的阻燃性。
验证了本发明通过加入磷酸酯改性POSS阻燃剂提高了XLPO护套料的阻燃性，使其具有优异的物理机械性能，具有极高的工业价值，可以被广泛应用和推广。
以上仅为本发明的优选实施例，并非因此限制本发明的专利范围，对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包括在本发明的专利保护范围。
Claims (10)
1.一种XLPO护套料，其特征在于，所述XLPO护套料的配料以重量份计，包括：
EVA35-55份，
PE5-10份，
POE10-15份，
磷酸酯改性POSS阻燃剂5-30份，
相容剂3-8份，
阻燃剂20-100份。
2.如权利要求1所述的XLPO护套料，其特征在于，所述PE包括低密度PE、中密度PE、高密度PE、线性低密度PE和茂金属PE中的一种或多种，所述POE为四碳POE或八碳POE中的一种或多种。
3.如权利要求1所述的XLPO护套料，其特征在于，所述阻燃剂包括P系阻燃剂0-10、N系阻燃剂0-20份和无机阻燃剂20-60份。
4.如权利要求1所述的XLPO护套料，其特征在于，所述XLPO护套料的配料还包括润滑剂0.2-1份、抗氧剂0.5-2和光稳定剂0.2-1份；所述润滑剂为硬脂酸、硬脂酸钙、硬脂酸镁、聚乙烯蜡、石蜡、硅酮中一种或多种的组合；所述抗氧剂包括抗氧剂1035、抗氧剂168、抗氧剂TH-412S、抗氧剂1098、抗氧剂1010中的至少一种；所述光稳定剂包括氧化锌，二氧化钛，二苯甲酮，水杨酸，苯并三唑中的一种或几种。
5.如权利要求1所述的XLPO护套料，其特征在于，所述磷酸酯改性POSS阻燃剂由缩水甘油醚氧丙基笼状聚倍半硅氧烷、2-胺乙基-2,3-二羟丙基-羟基磷酸酯与催化剂添加于有机溶液中反应得到。
6.如权利要求1所述的XLPO护套料，其特征在于，所述相容剂为PE接枝马来酸酐、POE接枝马来酸酐、PP接枝马来酸酐、EMA接枝马来酸酐中的一种或多种。
7.一种XLPO护套料的制备方法，其特征在于，包括以下步骤：
催化反应得到磷酸酯改性POSS阻燃剂；
将EVA、PE、POE、相容剂、磷酸酯改性POSS阻燃剂、阻燃剂、润滑剂混合均匀，进行密炼挤出造粒，得到颗粒料；将所述颗粒料通过干燥得到所述XLPO护套料。
8.如权利要求7所述的XLPO护套料的制备方法，其特征在于，催化反应得到磷酸酯改性POSS阻燃剂，包括以下步骤：
将缩水甘油醚氧丙基笼状聚倍半硅氧烷溶于有机溶剂溶液中，在催化剂的作用下，加入2-胺乙基-2,3-二羟丙基-羟基磷酸酯，进行催化反应后清洁干燥，得到磷酸酯改性POSS阻燃剂。
9.如权利要求8所述的XLPO护套料的制备方法，其特征在于，所述催化剂包括有机酸和/或无机酸的一种或几种；
和/或，所述有机溶剂包括醇类、芳香烃类、脂肪烃类、脂环烃类、醚类、酮类及二醇衍生物中的至少一种。
10.一种护套，其特征在于，应用于充电电缆，包括如权利要求1-6中任意一项所述的护套料。