CN117431689A - 一种多功能面料及其制备方法和服装 - Google Patents
一种多功能面料及其制备方法和服装 Download PDFInfo
- Publication number
- CN117431689A CN117431689A CN202210818417.3A CN202210818417A CN117431689A CN 117431689 A CN117431689 A CN 117431689A CN 202210818417 A CN202210818417 A CN 202210818417A CN 117431689 A CN117431689 A CN 117431689A
- Authority
- CN
- China
- Prior art keywords
- fabric
- coffee carbon
- yarn
- multifunctional fabric
- yarns
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种多功能面料及其制备方法和服装。以重量份计,所述多功能面料的原料包括咖啡碳纱线25~95份和弹性纱线5~20份,所述咖啡碳纱线包括30~300根咖啡碳纤维单丝。所述多功能面料的制备方法包括:将咖啡碳纱线与弹性纱线进行编织,得到所述多功能面料。本发明中,所述多功能面料采用特定的咖啡碳纱线和弹性纱线复配,使得所述面料具有柔软、高弹、保暖、抑菌消臭、防紫外线、抗衰老等多种功能,不需要设置多种功能层或额外加入抗菌剂等,具有广泛的应用价值和前景。
Description
技术领域
本发明属于纤维面料技术领域,具体涉及一种多功能面料及其制备方法和服装。
背景技术
随着社会的不断进步,纺织技术和纺织设备不断发展,市场上的面料层出不穷,材质结构各不相同,广泛应用于织布、制绳、制线、针织和刺绣等生活领域。纱线作为各种面料的基础,纱线的性能很大程度决定面料的功能。随着生活质量的逐渐提高,人们对舒适性和功能多样化的服装面料的需求也越来越高。
现有技术中,多采用通过设置多种功能层来实现面料功能多样化。例如CN216733271U公开了一种双面柔软蓄热保暖针织面料,包括基布层、保温层、里层、抗菌层、防静电层和面层。所述双面柔软蓄热保暖针织面料,面层和里层均由麻纱面料层和丝绸面料层组成,且麻纱面料层粘接在丝绸面料层的上表面,保证了该面料的双面柔软度,进一步的通过保温层的设置,也提高了该面料蓄热保温效果,再有通过抗菌层的设置,使得该面料还具备抗菌抑菌的效果,使得该面料不仅保温效果好,而且还不易滋生细菌。但是,所述面料的成本高、工艺复杂。
CN105881998A公开了一种带有贴面柔软层的保暖型防水面料,它包括面料本体,面料本体的上表面设置有防辐射层,防辐射层内埋设有多根纵横交错的防辐射条,所述防辐射层的上表面设置有加强层,加强层的上表面设置有上防水层,所述面料本体的下表面设置有抗菌层,抗菌层由镀银纤维纺织而成,所述抗菌层的下表面设置有防火层,防火层的下表面设置有下防水层;所述防辐射条包括中心的弹性纤维、绕设于弹性纤维表面的防辐射金属丝组以及包覆于外层的保护层。所述带有贴面柔软层的保暖型防水面料具有立体感,还同时具备抗菌、防辐射、防火、防水等功能。但是所述面料的柔软舒适度差,且成本高,工艺复杂。
CN207310738U公开了一种抗菌、耐磨、防静电家纺面料,包括耐磨层、抗菌层、防静电层及柔软保暖层,通过多种功能层的设置,使得所述面料具有耐磨性、吸湿性、抗菌杀菌、防霉防臭、高强吸湿、透气排汗等功能。但是,所述面料的成本高、工艺复杂。
因此,开发一种不需要设置多种功能层就能实现集抗菌、保暖、柔软舒适、高弹等多种功能于一体,且成本低,制备方法简单的面料,是本领域亟待解决的问题。
发明内容
针对现有技术存在的不足,本发明的目的在于提供一种多功能面料及其制备方法和服装。所述多功能面料通过特定的咖啡碳纱线和弹性纱线复配,使得所述面料具有柔软、高弹、保暖、抑菌消臭、防紫外线、抗衰老等多种功能,不需要设置多种功能层或额外加入抗菌剂等,具有广泛的应用价值和前景。
为达此目的,本发明采用以下技术方案:
第一方面,本发明提供一种多功能面料,以质量百分含量计,所述多功能面料的原料包括咖啡碳纱线25~95份和弹性纱线5~20份,所述咖啡碳纱线包括30~300根咖啡碳纤维单丝。
本发明中,所述咖啡碳纤维能够发射远红外线,有利于面料的保暖;咖啡碳的多孔吸附效果有利于面料的抑菌防臭,并且还能够防紫外线、抗衰老;通过特定含量以及咖啡碳纤维单丝数目的咖啡碳纱线和弹性纱线复配,使得所述面料能够集柔软舒适、高弹、保暖、抑菌消臭、防紫外线、抗衰老等多种功能于一体,简化了工艺且降低了成本,并且性能稳定。
本发明中,所述“多功能”指所述面料具有柔软、高弹、保暖、抑菌消臭、速干、防紫外线、抗衰老等多种功能。
优选地,以重量份计,所述多功能面料的原料包括咖啡碳纱线25~95份,例如可以为26份、28份、30份、32份、34份、36份、38份、40份、42份、44份、46份、48份、50份、52份、54份、56份、58份、60份、62份、64份、66份、68份、70份、72份、74份、76份、78份、80份、82份、84份、86份、88份、90份、92份、94份等。
优选地,以重量份计,所述多功能面料的原料包括弹性纱线5~20份,例如可以为6份、8份、10份、12份、14份、16份、18份等。
优选地,所述咖啡碳纱线包括30~300根咖啡碳纤维单丝,例如可以为36根、38根、40根、44根、48根、52根、56根、58根、62根、68根、72根、76根、80根、85根、90根、94根、98根、100根、110根、120根、130根、140根、144根、148根、150根、154根、158根、160根、180根、200根、220根、240根、260根、280根、288根、292根、296根等。
优选地,所述多功能面料的原料中咖啡碳纱线与弹性纱线的质量比为(5.7~19):1,例如可以为5.8:1、5.9:1、6:1、6.2:1、6.4:1、6.6:1、6.8:1、7:1、7.2:1、7.4:1、7.8:1、8.2:1、8.4:1、8.8:1、9:1、9.2:1、9.4:1、9.6:1、10:1、10.4:1、10.8:1、11:1、11.2:1、11.6:1、11.8:1、12:1、12.5:1、13:1、13.5:1、14:1、15:1、16:1、17:1、18:1等。
本发明中,所述咖啡碳纱线与弹性纱线在特定的质量比范围内,所述面料的综合性能更优。
优选地,所述咖啡碳纱线为含有咖啡碳颗粒的涤纶纱线。
优选地,所述咖啡碳颗粒包括纳米咖啡碳颗粒。
优选地,所述咖啡碳纱线中咖啡碳颗粒的含量为1~10%,例如可以为1%、1.2%、1.4%、1.6%、1.8%、2%、2.2%、2.4%、2.6%、2.8%、3%、3.2%、3.4%、3.6%、3.8%、4%、4.2%、4.4%、4.6%、4.8%、5%、5.4%、5.8%、6.2%、6.6%、7%、7.4%、7.8%、8.2%、8.6%、9%、9.4%、9.8%等,优选为1~5%,进一步优选为1~3%。
本发明中,所述咖啡碳含量过低,面料保暖、抗菌、速干、防紫外线等效果差;含量太高,面料容易起静电、耐磨性差。
优选地,所述咖啡碳纱线的细度为50~150D,例如可以为55D、60D、65D、70D、75D、80D、85D、90D、95D、100D、105D、110D、115D、120D、125D、130D、135D、140D、145D等,进一步优选为70~100D。
本发明中,所述咖啡碳纱线的细度在特定范围内,面料的柔软舒适度最好,亲肤效果好;细度过高或过低都会影响面料克重和密度,导致舒适度下降。
优选地,所述咖啡碳纱线包括100~300根咖啡碳纤维单丝。
本发明中,所述咖啡碳纱线中,咖啡碳纤维单丝数目在特定范围内,面料的柔软舒适度最好,亲肤效果好;咖啡碳纤维单丝数目过高,使得面料柔软过度,影响使用效果;咖啡碳纤维单丝数目过低,导致面料柔软性下降。
优选地,所述弹性纱线包括聚氨酯纤维和/或聚醚酯纤维。
优选地,所述弹性纱线的细度为10~50D,例如可以为12D、15D、20D、22D、24D、26D、28D、30D、32D、34D、36D、38D、40D、42D、44D、46D、48D等。
优选地,以重量份计,所述多功能面料的原料还包括第三纱线5~70份,例如可以为6份、8份、10份、14份、18份、22份、26份、30份、32份、34份、36份、38份、40份、42份、44份、46份、48份、50份、52份、54份、56份、58份、60份、62份、64份、66份、68份等。
优选地,所述第三纱线包括涤纶纱线、涤纶粘胶混纺纱线或粘胶纱线中的任意一种或至少两种的组合。
优选地,所述第三纱线的细度为50~150D,例如可以为55D、60D、65D、70D、75D、80D、85D、90D、95D、100D、105D、110D、115D、120D、125D、130D、135D、140D、145D等,例如可以为进一步优选为70~100D。
优选地,所述第三纱线包括30~300根纤维单丝,例如可以为36根、38根、40根、44根、48根、52根、56根、58根、62根、68根、72根、76根、80根、85根、90根、94根、98根、100根、110根、120根、130根、140根、144根、148根、150根、154根、158根、160根、180根、200根、220根、240根、260根、280根、288根、292根、296根等,优选为30~100根纤维单丝。
本发明中,所述第三纱线中,纤维单丝数目在特定范围内,面料的柔软舒适度最好,亲肤效果好且耐磨性好;纤维单丝数目过高或过低都会导致柔软性下降;并且所述第三纱线与咖啡碳纱线配合,进一步提高面料的柔软舒适度和耐磨性。
优选地,所述多功能面料的编织结构为纬平针结构。
优选地,所述多功能面料的表层和/或里层各自独立地设置有毛绒结构。
优选地,所述多功能面料表层和/或里层的毛绒长度各自独立地为0.1~10mm,例如可以为0.2mm、0.4mm、0.6mm、0.8mm、1mm、1.2mm、1.4mm、1.6mm、1.8mm、2mm、2.2mm、2.4mm、2.6mm、2.8mm、3mm、3.5mm、4mm、4.5mm、5mm、5.5mm、6mm、6.5mm、7mm、7.5mm、8mm、8.5mm、9mm、9.5mm等。
优选地,所述多功能面料表层的毛绒长度为0.1~1mm。
优选地,所述多功能面料里层的毛绒长度为0.5~3mm。
本发明中,所述多功能面料表层和里层的毛绒长度在优选的范围内,既能保证面料的保暖效果,又能不影响外观效果,且适用于制作贴身衣物,不影响舒适度;所述表层面料毛绒长度太长,外观效果差;里层毛绒长度太长,舒适度差,不适合制作贴身衣物。
优选地,所述多功能面料里层的起绒量大于多功能面料表层的起绒量。
本发明中,所述面料具有毛绒结构,进一步提高面料的柔软程度和防紫外线性能,并且面料毛绒之间可以携带更多的静止空气,空气的导热系数小,有利于面料的保暖;而通过在面料表层和里层设置不同的毛绒长度和起绒量,能够进一步提高面料的保暖和柔软舒适度。
第二方面,本发明提供一种根据第一方面所述的多功能面料的制备方法,所述制备方法包括:
将咖啡碳纱线与弹性纱线进行编织,得到所述多功能面料。
优选地,所述编织的设备包括纬编机。
优选地,所述纬编机为22~36针纬编机,例如可以为24针、26针、28针、30针、32针、34针等。
优选地,所述面料的编织原料还包括涤纶纱线、涤纶粘胶混纺纱线或粘胶纱线中的任意一种或至少两种的组合。
优选地,所述编织后还包括预定型、后加工和定型的步骤。
优选地,所述预定型的温度为180~210℃,例如可以为182℃、185℃、188℃、190℃、192℃、195℃、198℃、200℃、202℃、204℃、206℃、208℃等。
优选地,所述预定型时的布速为20~28码,例如可以为21码、22码、23码、24码、25码、26码、27码等。
本发明中,所述面料的制备方法中可根据实际需要在预定型完成后进行染色的步骤。
优选地,所述染色前还包括前处理。
优选地,所述前处理包括将预定型后的面料在前处理浆液中进行浸渍。
优选地,所述染色的温度为120~135℃,例如可以为122℃、124℃、126℃、128℃等。
优选地,所述染色完成后还包括洗涤的步骤。
优选地,所述后加工包括对编织得到的织物表层和/或里层各自独立地进行磨毛和/或拉毛处理。
优选地,所述磨毛在磨毛机中进行。
优选地,所述磨毛处理时的布速为15~40码,例如可以为16码、18码、20码、22码、24码、26码、28码、30码、34码、38码等。
优选地,所述磨毛机中砂纸的目数为180~320目,例如可以为200目、220目、240目、260目、280目、300目等。
优选地,所述拉毛在拉毛机中进行。
优选地,所述拉毛处理时,布速为10~30码,例如可以为12码、14码、16码、18码、20码、22码、24码、26码、28码等。
优选地,所述定型的温度为180~210℃,例如可以为185℃、190℃、195℃、200℃、205℃。
优选地,所述定型时的布速为15~30码,例如可以为16码、18码、20码、22码、24码、26码、28码等。
第三方面,本发明提供一种服装,所述服装包括如第一方面所述的多功能面料。
优选地,所述服装包括贴身衣物。
优选地,所述服装包括内衣、保暖上衣或保暖裤。
本发明所述的数值范围不仅包括上述列举的点值,还包括没有列举出的上述数值范围之间的任意的点值,限于篇幅及出于简明的考虑,本发明不再穷尽列举所述范围包括的具体点值。
与现有技术相比,本发明的有益效果为:
本发明提供的多功能面料,通过特定含量和咖啡碳纤维单丝数目的咖啡碳纱线和弹性纱线复配,使得所述面料能够集柔软舒适、高弹、保暖、抑菌消臭、防紫外线、抗衰老等多种功能于一体,简化了工艺且降低了成本。
附图说明
图1为本发明实施例1提供的多功能面料的结构示意图;
其中,1-面料表层的毛绒结构,2-面料里层的毛绒结构,3-面料基体。
具体实施方式
下面通过具体实施方式来进一步说明本发明的技术方案。本领域技术人员应该明了,所述实施例仅仅是帮助理解本发明,不应视为对本发明的具体限制。
实施例1
本实施例提供一种多功能面料,以重量份计,所述多功能面料的原料包括46份咖啡碳纱线(细度75D,咖啡碳纤维单丝数目为288根,咖啡碳纱线中咖啡碳含量为3%)、46份涤纶纱线(细度为75D,涤纶纤维单丝数目为36根)和8份弹性纱线(氨纶,厂家:晓星氨纶(嘉兴)有限公司,细度为20D);所述多功能面料的结构示意图如图1所示,包括面料表层的毛绒结构1(长度为0.75mm)、面料里层的毛绒结构2(长度为1.5mm)和面料基体3;所述面料表层的起绒量少于面料里层的起绒量。
本实施例提供一种所述多功能面料的制备方法,具体包括以下步骤:
(1)将咖啡碳纱线、弹性纱线和涤纶纱线采用纬编机(32针/25.4mm)编织得到具有纬平针结构的织物;所述纬编机的编织方法为:一个组织循环中,将一路包括咖啡碳纱线和弹性纱线与另一路包括弹性纱线与涤纶纱线编织而成。
(2)对步骤(1)得到的面料在200℃,布速为25码条件下预定型;将所述预定型后的面料的表层采用磨毛机(砂纸目数200目,布速35码)进行磨毛处理后,对所述面料的里层采用拉毛机(布速23码)进行拉毛处理,在195℃,布速为20码下定型,得到所述面料。
实施例2
本实施例提供一种多功能面料,以重量份计,所述多功能面料的原料包括67份咖啡碳纱线(细度75D,咖啡碳纤维单丝数目为288根,咖啡碳纱线中咖啡碳含量为2%)、23份涤纶纱线(细度为75D,涤纶纤维单丝数目为72根)和10份弹性纱线(氨纶,厂家:晓星氨纶(嘉兴)有限公司,细度为30D);所述多功能面料表层的毛绒结构长度为0.5mm、面料里层的毛绒结构长度为1mm;所述面料表层的起绒量少于面料里层的起绒量。
本实施例提供一种所述多功能面料的制备方法,其与实施例1的区别仅在于,所述制备方法步骤(1)中将咖啡碳纱线、弹性纱线和涤纶纱线采用纬编机编织得到具有纬平针结构的织物;所述纬编机的编织方法为:一个组织循环中,将三路包括咖啡碳纱线和弹性纱线与另一路包括弹性纱线与涤纶纱线编织而成,其它步骤及参数均与实施例1相同。
实施例3
本实施例提供一种多功能面料,以质量百分含量计,所述多功能面料的原料包括90份咖啡碳纱线(细度75D,咖啡碳纤维单丝数目为288根,咖啡碳纱线中咖啡碳含量为1%)和10份弹性纱线(氨纶,厂家:晓星氨纶(嘉兴)有限公司,细度为30D);所述多功能面料表层的毛绒结构长度为1mm、面料里层的毛绒结构长度为3mm;所述面料表层的起绒量少于面料里层的起绒量。
本实施例提供一种所述多功能面料的制备方法,其与实施例1的区别仅在于,所述制备方法步骤(1)中采用纬编机编织得到具有纬平针结构的织物;所述纬编机的编织方法为:将咖啡碳纱线和弹性纱线循环编织而成,其它步骤及参数均与实施例1相同。
实施例4
本实施例提供一种多功能面料,其与实施例1的区别仅在于,所述咖啡碳纱线中咖啡碳颗粒的含量为5%,其它原料、参数及制备方法均与实施例1相同。
实施例5
本实施例提供一种多功能面料,其与实施例1的区别仅在于,所述咖啡碳纱线包括72根咖啡碳纤维单丝,其它原料、参数及制备方法均与实施例1相同。
实施例6
本实施例提供一种多功能面料,其与实施例1的区别仅在于,所述咖啡碳纱线的细度为70D,其它原料、参数及制备方法均与实施例1相同。
实施例7
本实施例提供一种多功能面料,其与实施例1的区别仅在于,所述咖啡碳纱线的细度为150D,其它原料、参数及制备方法均与实施例1相同。
实施例8
本实施例提供一种多功能面料,其与实施例1的区别仅在于,所述涤纶纱线包括涤纶纤维单丝144根,其它原料、参数及制备方法均与实施例1相同。
实施例9
本实施例提供一种多功能面料,其与实施例1的区别仅在于,所述咖啡碳纱线与弹性纱线的总量不变,质量比为5.5:1,其它原料、参数及制备方法均与实施例1相同。
实施例10
本实施例提供一种多功能面料,其与实施例1的区别仅在于,所述咖啡碳纱线与弹性纱线的总量不变,质量比为19:1,其它原料、参数及制备方法均与实施例1相同。
实施例11
本实施例提供一种多功能面料,其与实施例1的区别仅在于,将所述涤纶纱线替换为等量的棉纤维纱线,其它原料、参数及制备方法均与实施例1相同。
实施例12
本实施例提供一种多功能面料,其与实施例1的区别仅在于,所述制备方法中,没有进行步骤(2)中的磨毛和拉毛处理,其它原料、参数及制备方法均与实施例1相同。
实施例13
本实施例提供一种多功能面料,其与实施例1的区别仅在于,所述制备方法中,步骤(2)没有对织物表层进行磨毛处理,其它原料、参数及制备方法均与实施例1相同。
对比例1
本对比例提供一种多功能面料,其与实施例1的区别仅在于,所述咖啡碳纱线的份数为25份,所述多功能面料原料总量不变,弹性纱线与涤纶纱线的配比不变,其它参数及制备方法均与实施例1相同。
对比例2
本对比例提供一种多功能面料,其与实施例1的区别仅在于,所述面料的原料总量不变,没有弹性纱线,咖啡碳纱线与涤纶纱线的配比不变,其它原料参数及制备方法均与实施例1相同。
性能测试
(1)柔软舒适度:面料触感舒适、体贴、温暖,则标记为“优”;面料触感粗糙、僵硬,则标记为“差”;
(2)保暖性:根据JIS L 1096A法ASTM型保温性实验,测出保温率(%)、克罗值(clo);
(3)抗菌性:根据《JIS L 1902纺织产品的抗菌性试验》提供的方法进行测定,得出面料洗前和洗涤40次后金黄色葡萄球菌、肺炎杆菌的抗菌活性值;
(4)耐磨性:以试样破损的总摩擦次数表示,测定标准主要依据GB/T 21196.2-2007《纺织品马丁代尔法织物耐磨性的测定》;
(5)弹性:将面料平放在手中,选取经、纬、斜不同方向分别用两手的大拇指和食指捏住,两手之间的距离为10cm,然后双手轻轻向相反方向拉伸面料,如两手之间的距离大于等于15cm,且松开后,5s内回复到10cm,则为优,不能恢复到10cm,则为差。
(6)抗静电性:用手揉搓面料10s,用手贴近面料,如果面料没有吸附,且快速摩擦,没有“噼啪”的静电声,则标记为“合格”;如果面料吸附或有“噼啪”的静电声,则标记为“差”。
(7)防紫外线:使用分光光度计,测量波长在280~400nm的紫外线的透过率,计算出紫外线遮蔽率:紫外线遮蔽率(%)=100-紫外线的平均透过率(%)。评价分为A、B、C三个等级。其中,遮蔽率≥90%为A级、80%≤遮蔽率<90%为B级、遮蔽率<80%为C级。
具体测试结果如表1所示:
表1
由上表可知,本发明提供的多功能面料,通过采用特定的咖啡碳纤维和弹性纤维复配,使得所述面料具有柔软、高弹、保暖、抑菌消臭、防紫外线、抗衰老等多种功能,不需要设置多种功能层或额外加入抗菌剂等。由实施例1~3可知,所述多功能面料柔软舒适、保温率为42.14~42.3%,克罗值为0.32~0.33col,保暖性好;洗涤40次后抗菌率为98.2~99.9%,摩擦6370~7200次不破损,且弹性好,不易起静电,防紫外线等级达到A级。
由实施例1与实施例4比较可知,所述咖啡碳纱线中咖啡碳用量太多时,所述面料的耐磨性及抗静电性下降;由实施例1与实施例5~7比较可知,所述咖啡碳纱线的细度或咖啡碳纤维单丝数目不在特定的范围内,所述面料的柔软舒适度下降,或耐磨性、保暖性或防紫外线性能变差;由实施例1与实施例8比较可知,所述涤纶纱线中涤纶纤维单丝数目太多时,所述面料的综合性能下降;由实施例1与实施例9~11可知,所述面料的原料并非特定的组合或咖啡碳纱线与弹性纱线并非特定配比时,所述面料的综合性能差;由实施例1与实施例12和13比较可知,所述面料的表层和/或里层没有毛绒结构时,所述面料的柔软舒适度和保暖性差且防紫外线性能变差。
由实施例1与对比例1比较可知,所述咖啡碳纱线的含量太少时,所述面料的保温效果差且抗菌性差、防紫外线性能变差;由实施例1与对比例2比较可知,所述面料中没有弹性纱线时,面料综合性能差。
综上所述,本发明提供的多功能面料,通过选用特定的咖啡碳纱线与弹性纱线复配,并且所述多功能面料采用特定的结构,使得所述面料能够集柔软、高弹、保暖、抑菌消臭、防紫外线、抗衰老等多功能于一体,尤其适合制作贴身穿着的服装,比如内衣、保暖衣、保暖裤等,具有广泛的应用价值和应用前景。
申请人声明,以上所述仅为本发明的具体实施方式,但本发明的保护范围并不局限于此,所属技术领域的技术人员应该明了,任何属于本技术领域的技术人员在本发明揭露的技术范围内,可轻易想到的变化或替换,均落在本发明的保护范围和公开范围之内。
Claims (10)
1.一种多功能面料,其特征在于,以重量份计,所述多功能面料的原料包括咖啡碳纱线25~95份和弹性纱线5~20份;
所述咖啡碳纱线包括30~300根咖啡碳纤维单丝。
2.根据权利要求1所述的多功能面料,其特征在于,所述多功能面料的原料中咖啡碳纱线与弹性纱线的质量比为(5.7~19):1;
优选地,所述咖啡碳纱线为含有咖啡碳颗粒的涤纶纱线;
优选地,所述咖啡碳颗粒包括纳米咖啡碳颗粒;
优选地,所述咖啡碳纱线中咖啡碳颗粒的含量为1~10%,优选为1~5%,进一步优选为1~3%。
3.根据权利要求1或2所述的多功能面料,其特征在于,所述咖啡碳纱线的细度为50~150D,进一步优选为70~100D;
优选地,所述咖啡碳纱线包括100~300根咖啡碳纤维单丝。
4.根据权利要求1~3任一项所述的多功能面料,其特征在于,所述弹性纱线包括聚氨酯纤维和/或聚醚酯纤维;
优选地,所述弹性纱线的细度为10~50D。
5.根据权利要求1~4任一项所述的多功能面料,其特征在于,以重量份计,所述多功能面料的原料还包括第三纱线5~70份;
优选地,所述第三纱线包括涤纶纱线、涤纶粘胶混纺纱线或粘胶纱线中的任意一种或至少两种的组合;
优选地,所述第三纱线的细度为50~150D,进一步优选为70~100D;
优选地,所述第三纱线包括30~300根纤维单丝,优选为30~100根纤维单丝。
6.根据权利要求1~5任一项所述的多功能面料,其特征在于,所述多功能面料的编织结构为纬平针结构;
优选地,所述多功能面料的表层和/或里层各自独立地设置有毛绒结构;
优选地,所述多功能面料表层和/或里层的毛绒长度各自独立地为0.1~10mm;
优选地,所述多功能面料里层的起绒量大于多功能面料表层的起绒量。
7.一种根据权利要求1~6任一项所述的多功能面料的制备方法,其特征在于,所述制备方法包括:
将咖啡碳纱线与弹性纱线进行编织,得到所述多功能面料。
8.根据权利要求7所述的制备方法,其特征在于,所述编织的设备包括纬编机;
优选地,所述纬编机为22~36针纬编机;
优选地,所述面料的编织原料还包括涤纶纱线、涤纶粘胶混纺纱线或粘胶纱线中的任意一种或至少两种的组合。
9.根据权利要求7或8所述的制备方法,其特征在于,所述编织后还包括预定型、后加工和定型的步骤;
优选地,所述后加工包括对编织得到的织物表层和/或里层各自独立地进行磨毛和/或拉毛处理。
10.一种服装,其特征在于,所述服装包括如权利要求1~6任一项所述的多功能面料。