CN117413324A - 固体电解质材料及使用了它的电池 - Google Patents
固体电解质材料及使用了它的电池 Download PDFInfo
- Publication number
- CN117413324A CN117413324A CN202280036615.2A CN202280036615A CN117413324A CN 117413324 A CN117413324 A CN 117413324A CN 202280036615 A CN202280036615 A CN 202280036615A CN 117413324 A CN117413324 A CN 117413324A
- Authority
- CN
- China
- Prior art keywords
- solid electrolyte
- electrolyte material
- battery
- positive electrode
- examples
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本公开的固体电解质材料(100)包含锂及多个阴离子元素。多个阴离子元素包含锑和选自除锑以外的氮族元素、硫族元素及卤族元素中的至少1种元素。本公开的电池(1000)具备:正极(201)、负极(203)及配置于正极(201)及负极(203)之间的电解质层(202),选自正极(201)、负极(203)及电解质层(202)中的至少1者含有本公开的固体电解质材料(100)。
Description
技术领域
本公开涉及固体电解质材料及使用了它的电池。
背景技术
在非专利文献1中,作为包含阳离子的锑的固相电解质,公开了Li3SbS4。
现有技术文献
非专利文献
非专利文献1:T.Kimura等.Solid StateIonics 333(2019)45-49
发明内容
发明所要解决的课题
本公开的目的在于提供具有锂离子导电性的新型固体电解质材料。
用于解决课题的手段
本公开提供一种固体电解质材料,其包含锂及多个阴离子元素,
上述多个阴离子元素包含锑和选自除锑以外的氮族元素、硫族元素及卤族元素中的至少1种元素。
发明效果
本公开能够提供具有锂离子导电性的新型固体电解质材料。
附图说明
图1表示第2实施方式的电池1000的截面图。
图2表示为了评价固体电解质材料的离子电导率所使用的加压成型冲模300的示意图。
图3是表示实施例4的固体电解质材料的通过阻抗测定得到的科尔-科尔(Cole-Cole)标绘的图表。
图4是表示实施例2的电池的初期充放电特性的图表。
具体实施方式
以下,在参照附图的同时对本公开的实施方式进行说明。
(第1实施方式)
本实施方式的固体电解质材料包含锂及多个阴离子元素。多个阴离子元素包含锑和选自除锑以外的氮族元素、硫族元素及卤族元素中的至少1种元素。
固体电解质材料是适合于锂离子电导率提高的固体电解质材料。固体电解质材料例如具有高的锂离子电导率。因此,固体电解质材料可被用于获得充放电特性优异的电池。该电池的例子为全固体二次电池。
这里,高的锂离子电导率的一个例子例如在室温附近为6.3×10-5S/cm以上。固体电解质材料例如可以具有6.3×10-5S/cm以上的离子电导率。室温例如为25℃。
锑具有比硫族元素(即第16族元素)、卤族元素(即第17族元素)及氮更低的电负性。通过使用锑作为阴离子,从而阴离子与锂的相互作用变弱,固体电解质材料的离子导电性提高。
需要说明的是,所谓阴离子是指与单质金属相比更带负电的状态。作为阴离子的锑的一个例子,可列举出带-3价电的Sb3-。这样一来,本实施方式的固体电解质材料包含带负电的锑。
用于判定元素是否为阴离子的方法之一可列举出XPS测定(X射线光电子分光测定)。在通过XPS测定得到的键合能比单质金属小的情况下,测定对象的元素带负电,可以将测定对象的元素判定为阴离子。
固体电解质材料也可以含有不可避免地被混入的元素。该元素的例子为氢。这样的元素会存在于固体电解质材料的原料粉或者用于制造或保管固体电解质材料的气氛中。固体电解质材料中不可避免地被混入的元素例如为1摩尔%以下。
在本公开中,所谓氮族元素是指氮、磷、砷及锑。所谓硫族元素是指氧、硫、硒及碲。所谓卤族元素是指氟、氯、溴及碘。
固体电解质材料也可以由锂、锑及氮族元素制成。
所谓“由锂、锑及氮族元素制成”是指除了不可避免的杂质以外未有意地添加其他的元素。例如,锂、锑及氮族元素的物质的量的合计相对于构成固体电解质材料的全部元素的物质的量的合计的摩尔比(即,摩尔分率)为95%以上。这也适用于氮族元素被置换成硫族元素或卤族元素的情况。
固体电解质材料也可以为由以下的组成式(1)表示的材料。
Li3SbxPn1-x(1)
这里,满足0<x<1。Pn为选自N、P及As中的至少1个。由组成式(1)表示的固体电解质材料具有高的离子电导率。
为了提高固体电解质材料的离子电导率,在组成式(1)中,也可以满足0.01≤x≤0.9,也可以满足0.2≤x≤0.8。
固体电解质材料也可以由锂、锑及硫族元素制成。
固体电解质材料也可以为由以下的组成式(2)表示的材料。
Li2+ySbyCh1-y(2)
这里,满足0<y<1。Ch为选自O、S、Se及Te中的至少1个。由组成式(2)表示的固体电解质材料具有高的离子电导率。
为了提高固体电解质材料的离子电导率,在组成式(2)中,Ch也可以包含Te。在组成式(2)中,Ch也可以为Te。
为了提高固体电解质材料的离子电导率,在组成式(2)中,也可以满足0.01≤y≤0.9,也可以满足0.2≤y≤0.8。
固体电解质材料也可以由锂、锑及卤族元素制成。
固体电解质材料也可以为由以下的组成式(3)表示的材料。
Li1+2zSbzHal1-z(3)
这里,满足0<z<1。Hal为选自F、Cl、Br及I中的至少1个。由组成式(3)表示的固体电解质材料具有高的离子电导率。
为了提高固体电解质材料的离子电导率,在组成式(3)中,Hal也可以包含I。在组成式(3)中,Hal也可以为I。
为了提高固体电解质材料的离子电导率,在组成式(3)中,也可以满足0.01≤z≤0.9,也可以满足0.2≤z≤0.8。
固体电解质材料可以为结晶质,或者也可以为非晶质。
固体电解质材料的形状没有限定。该形状的例子为针状、球状或椭圆球状。固体电解质材料也可以为粒子。固体电解质材料也可以具有颗粒或板的形状。
在固体电解质材料的形状为粒子状(例如球状)的情况下,固体电解质材料也可以具有0.1μm以上且100μm以下的中值粒径,也可以具有0.5μm以上且10μm以下的中值粒径。由此,固体电解质材料及其他的材料可良好地分散。粒子的中值粒径是指以体积为基准的粒度分布中的累积堆积等于50%的情况下的粒径。以体积为基准的粒度分布例如通过激光衍射式测定装置或图像解析装置来测定。
<固体电解质材料的制造方法>
固体电解质材料例如通过下述的方法来制造。
例如将锑化物的原料粉进行混合,以具有目标组成。
作为一个例子,在目标组成为Li2.2Sb0.2Te0.8的情况下,将Li3Sb原料粉及Li2Te原料粉以大概为0.2:0.8=Li3Sb:Li2Te的摩尔比进行混合。为了抵消在合成工艺中会产生的组成变化,也可以以预先调整过的摩尔比将原料粉进行混合。
如果增加Li3Sb,则上述的组成式(1)~(3)中的x、y及z的值变大。
作为原料,也可以使用Li金属或Sb金属。
使原料粉的混合物在行星型球磨机那样的混合装置内机械化学地彼此进行反应,得到反应物。即,使用机械化学研磨的方法,使原料粉彼此进行反应。反应物也可以在真空中或不活泼气氛中进行烧成。或者,也可以将原料粉的混合物在真空中或不活泼气氛中进行烧成,得到反应物。作为不活泼气氛,可列举出氦气氛、氩气氛、氮气氛等。
通过上述这些方法,得到第1实施方式的固体电解质材料。
(第2实施方式)
以下,对第2实施方式进行说明。在第1实施方式中说明的事项会被适当省略。
第2实施方式的电池具备正极、电解质层及负极。电解质层被配置于正极及负极之间。选自正极、电解质层及负极中的至少1者含有第1实施方式的固体电解质材料。
第2实施方式的电池由于含有第1实施方式的固体电解质材料,因此具有优异的充放电特性。
图1表示第2实施方式的电池1000的截面图。
电池1000具备正极201、电解质层202及负极203。电解质层202被设置于正极201及负极203之间。
正极201含有正极活性物质204及固体电解质100。
负极203含有负极活性物质205及固体电解质100。
固体电解质100包含第1实施方式的固体电解质材料。固体电解质100也可以为包含第1实施方式的固体电解质材料作为主要成分的粒子。包含第1实施方式的固体电解质材料作为主要成分的粒子是指以摩尔比计被最多包含的成分为第1实施方式的固体电解质材料的粒子。固体电解质100也可以为由第1实施方式的固体电解质材料制成的粒子。
正极201含有能够嵌入及脱嵌锂离子那样的金属离子的材料。该材料例如为正极活性物质204。
正极活性物质的例子为含锂过渡金属氧化物、过渡金属氟化物、聚阴离子材料、氟化聚阴离子材料、过渡金属硫化物、过渡金属氟氧化物、过渡金属硫氧化物或过渡金属氮氧化物。含锂过渡金属氧化物的例子为Li(Ni,Co,Mn)O2、Li(Ni,Co,Al)O2或LiCoO2。
在本公开中,“(A,B,C)”是指“选自A、B及C中的至少1个”。
正极活性物质204的形状并不限于特定的形状。正极活性物质204也可以为粒子。正极活性物质204也可以具有0.1μm以上且100μm以下的中值粒径。在正极活性物质204具有0.1μm以上的中值粒径的情况下,在正极201中,正极活性物质204及固体电解质100可良好地分散。由此,电池1000的充放电特性提高。在正极活性物质204具有100μm以下的中值粒径的情况下,正极活性物质204内的锂扩散速度提高。由此,电池1000能够以高输出功率工作。
正极活性物质204也可以具有比固体电解质100更大的中值粒径。由此,正极活性物质204及固体电解质100可良好地分散。
为了提高电池1000的能量密度及输出功率,在正极201中,正极活性物质204的体积相对于正极活性物质204的体积及固体电解质100的体积的合计之比也可以为0.30以上且0.95以下。
为了提高电池1000的能量密度及输出功率,正极201也可以具有10μm以上且500μm以下的厚度。
电解质层202含有电解质材料。该电解质材料例如为固体电解质材料。电解质层202也可以为固体电解质层。电解质层202也可以含有第1实施方式的固体电解质材料。
电解质层202也可以包含50质量%以上的第1实施方式的固体电解质材料。电解质层202也可以包含70质量%以上的第1实施方式的固体电解质材料。电解质层202也可以包含90质量%以上的第1实施方式的固体电解质材料。电解质层202也可以仅由第1实施方式的固体电解质材料制成。
以下,第1实施方式的固体电解质材料被称为第1固体电解质材料。与第1固体电解质材料不同的固体电解质材料被称为第2固体电解质材料。
电解质层202不仅含有第1固体电解质材料,还可以含有第2固体电解质材料。在电解质层202中,第1固体电解质材料及第2固体电解质材料也可以均匀地分散。由第1固体电解质材料形成的层及由第2固体电解质材料形成的层也可以沿着电池1000的层叠方向被层叠。
电解质层202也可以仅由第2固体电解质材料制成。
电解质层202也可以具有1μm以上且1000μm以下的厚度。在电解质层202具有1μm以上的厚度的情况下,正极201及负极203变得不易短路。在电解质层202具有1000μm以下的厚度的情况下,电池1000能够以高输出功率工作。
负极203含有能够嵌入及脱嵌锂离子那样的金属离子的材料。该材料例如为负极活性物质205。
负极活性物质205的例子为金属材料、碳材料、氧化物、氮化物、锡化合物或硅化合物。金属材料也可以为单质的金属,或者也可以为合金。金属材料的例子为锂金属或锂合金。碳材料的例子为天然石墨、焦炭、石墨化途中碳、碳纤维、球状碳、人造石墨或非晶质碳。从容量密度的观点出发,负极活性物质205的优选例子为硅(即Si)、锡(即Sn)、硅化合物或锡化合物。
负极活性物质205的形状并不限于特定的形状。负极活性物质205也可以为粒子。负极活性物质205也可以具有0.1μm以上且100μm以下的中值粒径。在负极活性物质205具有0.1μm以上的中值粒径的情况下,在负极203中,负极活性物质205及固体电解质100可良好地分散。由此,电池1000的充放电特性提高。在负极活性物质205具有100μm以下的中值粒径的情况下,负极活性物质205内的锂扩散速度提高。由此,电池1000能够以高输出功率工作。
负极活性物质205也可以具有比固体电解质100更大的中值粒径。由此,负极活性物质205及固体电解质100可良好地分散。
为了提高电池1000的能量密度及输出功率,在负极203中,负极活性物质205的体积相对于负极活性物质205的体积及固体电解质100的体积的合计之比也可以为0.30以上且0.95以下。
为了提高电池1000的能量密度及输出功率,负极203也可以具有10μm以上且500μm以下的厚度。
出于提高离子导电性、化学稳定性及电化学稳定性的目的,选自正极201、电解质层202及负极203中的至少1者还可以含有第2固体电解质材料。
第2固体电解质材料也可以为卤化物固体电解质。
卤化物固体电解质的例子为Li2MgX’4、Li2FeX’4、Li(Al,Ga,In)X’4或Li3(Al,Ga,In)X’6。这里,X’为选自F、Cl、Br及I中的至少1个。
卤化物固体电解质的其他例子为由LipMeqYrZ6表示的化合物。这里,满足p+m’q+3r=6及r>0。Me为选自Li及Y以外的金属元素和半金属元素中的至少1个元素。m’的值表示Me的价数。“半金属元素”为B、Si、Ge、As、Sb及Te。“金属元素”为周期表的第1族~第12族中所含的全部元素(其中,氢除外)及周期表的第13族~第16族中所含的全部元素(但是,B、Si、Ge、As、Sb、Te、C、N、P、O、S及Se除外)。Z为选自F、Cl、Br及I中的至少1个。从卤化物固体电解质的离子电导率的观点出发,Me也可以为选自Mg、Ca、Sr、Ba、Zn、Sc、Al、Ga、Bi、Zr、Hf、Ti、Sn、Ta及Nb中的至少1个。
第2固体电解质材料也可以为硫化物固体电解质。
硫化物固体电解质的例子为Li2S-P2S5、Li2S-SiS2、Li2S-B2S3、Li2S-GeS2、Li3.25Ge0.25P0.75S4或Li10GeP2S12。
第2固体电解质材料也可以为氧化物固体电解质。
氧化物固体电解质的例子为:
(i)LiTi2(PO4)3或其元素取代物那样的NASICON型固体电解质、
(ii)(LaLi)TiO3那样的钙钛矿型固体电解质、
(iii)Li14ZnGe4O16、Li4SiO4、LiGeO4或其元素取代物那样的LISICON型固体电解质、
(iv)Li7La3Zr2O12或其元素取代物那样的石榴石型固体电解质、或
(v)Li3PO4或其N取代物。
第2固体电解质材料也可以为有机聚合物固体电解质。
有机聚合物固体电解质的例子为高分子化合物及锂盐的化合物。高分子化合物也可以具有环氧乙烷结构。具有环氧乙烷结构的高分子化合物能够含有大量锂盐,因此能够进一步提高离子电导率。
锂盐的例子为LiPF6、LiBF4、LiSbF6、LiAsF6、LiSO3CF3、LiN(SO2CF3)2、LiN(SO2C2F5)2、LiN(SO2CF3)(SO2C4F9)或LiC(SO2CF3)3。也可以单独使用选自它们中的1种锂盐。或者,也可以使用选自它们中的2种以上的锂盐的混合物。
出于使锂离子的授受变得容易、提高电池的输出功率特性的目的,选自正极201、电解质层202及负极203中的至少1者也可以含有非水电解质液、凝胶电解质或离子液体。
非水电解液包含非水溶剂及溶于该非水溶剂中的锂盐。
非水溶剂的例子为环状碳酸酯溶剂、链状碳酸酯溶剂、环状醚溶剂、链状醚溶剂、环状酯溶剂、链状酯溶剂或氟溶剂。环状碳酸酯溶剂的例子为碳酸乙烯酯、碳酸丙烯酯或碳酸丁烯酯。链状碳酸酯溶剂的例子为碳酸二甲酯、碳酸乙甲酯或碳酸二乙酯。环状醚溶剂的例子为四氢呋喃、1,4-二噁烷或1,3-二氧杂环戊烷。链状醚溶剂的例子为1,2-二甲氧基乙烷或1,2-二乙氧基乙烷。环状酯溶剂的例子为γ-丁内酯。链状酯溶剂的例子为乙酸甲酯。氟溶剂的例子为氟代碳酸乙烯酯、氟代丙酸甲酯、氟苯、氟代碳酸乙甲酯或氟代二亚甲基碳酸酯。也可以单独使用选自它们中的1种非水溶剂。或者,也可以使用选自它们中的2种以上的非水溶剂的混合物。
锂盐的例子为LiPF6、LiBF4、LiSbF6、LiAsF6、LiSO3CF3、LiN(SO2CF3)2、LiN(SO2C2F5)2、LiN(SO2CF3)(SO2C4F9)或LiC(SO2CF3)3。也可以单独使用选自它们中的1种锂盐。或者,也可以使用选自它们中的2种以上的锂盐的混合物。锂盐的浓度例如为0.5mol/升以上且2mol/升以下。
作为凝胶电解质,可使用浸渗有非水电解液的聚合物材料。聚合物材料的例子为聚环氧乙烷、聚丙烯腈、聚偏氟乙烯、聚甲基丙烯酸甲酯或具有环氧乙烷键的聚合物。
离子液体中所含的阳离子的例子为:
(i)四烷基铵或四烷基鏻那样的脂肪族链状季盐类、
(ii)吡咯烷鎓类、吗啉鎓类、咪唑啉鎓类、四氢嘧啶鎓类、哌嗪鎓类或哌啶鎓类那样的脂肪族环状铵、或
(iii)吡啶鎓类或咪唑鎓类那样的含氮杂环芳香族阳离子。
离子液体中所含的阴离子的例子为PF6 -、BF4 -、SbF6 -、AsF6 -、SO3CF3 -、N(SO2CF3)2 -、N(SO2C2F5)2 -、N(SO2CF3)(SO2C4F9)-或C(SO2CF3)3-。
离子液体也可以含有锂盐。
出于提高粒子彼此的密合性的目的,选自正极201、电解质层202及负极203中的至少1者也可以含有粘结剂。
粘结剂的例子为聚偏氟乙烯、聚四氟乙烯、聚乙烯、聚丙烯、芳族聚酰胺树脂、聚酰胺、聚酰亚胺、聚酰胺酰亚胺、聚丙烯腈、聚丙烯酸、聚丙烯酸甲酯、聚丙烯酸乙酯、聚丙烯酸己酯、聚甲基丙烯酸、聚甲基丙烯酸甲酯、聚甲基丙烯酸乙酯、聚甲基丙烯酸己酯、聚乙酸乙烯酯、聚乙烯基吡咯烷酮、聚醚、聚醚砜、六氟聚丙烯、丁苯橡胶或羧甲基纤维素。共聚物也可作为粘结剂来使用。这样的粘结剂的例子为选自四氟乙烯、六氟乙烯、六氟丙烯、全氟烷基乙烯基醚、偏氟乙烯、氯三氟乙烯、乙烯、丙烯、五氟丙烯、氟甲基乙烯基醚、丙烯酸及己二烯中的2种以上的材料的共聚物。也可以使用选自上述的材料中的2种以上的混合物作为粘结剂。
出于提高电子导电性的目的,选自正极201及负极203中的至少1者也可以含有导电助剂。
导电助剂的例子为:
(i)天然石墨或人造石墨那样的石墨类、
(ii)乙炔黑或科琴黑那样的炭黑类、
(iii)碳纤维或金属纤维那样的导电性纤维类、
(iv)氟化碳、
(v)铝那样的金属粉末类、
(vi)氧化锌或钛酸钾那样的导电性晶须类、
(vii)氧化钛那样的导电性金属氧化物、或
(viii)聚苯胺、聚吡咯或聚噻吩那样的导电性高分子化合物。
为了低成本化,也可以使用上述(i)或(ii)的导电助剂。
第2实施方式的电池的形状的例子为硬币型、圆筒型、方型、片材型、纽扣型、扁平型或层叠型。
实施例
以下,在参照实施例的同时对本公开更详细地进行说明。
(实施例1)
(原料的制作)
在具有-60℃以下的露点的氩气氛(以下,称为“干燥氩气氛”)中,作为原料粉,按照成为3.5:1=Li:Sb的摩尔比的方式准备Li及Sb。将这些原料粉在研钵中进行粉碎并混合。像这样操作,得到混合粉。混合粉在干燥氩气氛下在650度下烧成1小时。通过将所得到的粉末在研钵中进行粉碎,得到Li3Sb的粉末。
接着,在干燥氩气氛中,作为原料粉,按照成为2.5:1=Li:Te的摩尔比的方式准备Li及Te。将这些原料粉在研钵中进行粉碎并混合。像这样操作,得到混合粉。混合粉在干燥氩气氛下在500度下烧成1小时。通过将所得到的粉末在研钵中进行粉碎,得到Li2Te的粉末。
接着,在干燥氩气氛中,作为原料粉,按照成为2.5:1=Li:Se的摩尔比的方式准备Li及Se。将这些原料粉在研钵中进行粉碎并混合。像这样操作,得到混合粉。混合粉在干燥氩气氛下在500度下烧成1小时。通过将所得到的粉末在研钵中进行粉碎,得到Li2Se的粉末。
(固体电解质材料的制作)
在干燥氩气氛中,作为原料粉,按照成为2:8=Li3Sb:Li2Te的摩尔比的方式准备Li3Sb及Li2Te。将这些原料粉在研钵中进行粉碎并混合。像这样操作,得到混合粉。混合粉使用行星型球磨机以12小时、500rpm进行研磨处理。像这样操作,得到实施例1的固体电解质材料的粉末。实施例1的固体电解质材料具有Li2.2Sb0.2Te0.8表示的组成。
实施例1的固体电解质材料的每单位重量的Li、Sb及Te的含量通过XPS测定法来测定。基于由这些测定结果得到的Li、Sb及Te的含量,算出Li:Sb:Te摩尔比。其结果是,实施例1的固体电解质材料与原料粉的摩尔比同样具有2.2:0.2:0.8=Li:Sb:Te的摩尔比。
(离子电导率的评价)
图2是表示为了评价固体电解质材料的离子电导率所使用的加压成型冲模300的示意图。
加压成型冲模300具备冲头上部301、模框302及冲头下部303。冲头上部301及冲头下部303都由电子导电性的不锈钢来形成。模框302由绝缘性的聚碳酸酯来形成。
使用图2中所示的加压成型冲模300,通过下述的方法,测定实施例1的固体电解质材料的离子电导率。
在具有-30℃以下的露点的干燥气氛中,实施例1的固体电解质材料的粉末(即,图2中为固体电解质材料的粉末101)被填充于加压成型冲模300的内部。在加压成型冲模300的内部,对实施例1的固体电解质材料的粉末101使用冲头上部301及冲头下部303施加300MPa的压力。
在施加压力的状态下,冲头上部301及冲头下部303与搭载有频率响应分析仪的恒电位仪(Princeton Applied Research公司、VersaSTAT4)连接。冲头上部301与工作电极及电位测定用端子连接。冲头下部303与对电极及参比电极连接。固体电解质材料的阻抗在室温下通过电化学阻抗测定法来测定。
图3是表示实施例4的固体电解质材料的通过阻抗测定得到的科尔-科尔标绘的图表。
图3中,复数阻抗的相位的绝对值最小的测定点处的阻抗的实数值被视为固体电解质材料对于离子传导的电阻值。关于该实数值,参照图3中所示的箭头Rse。使用该电阻值,基于以下的数学式(4),算出离子电导率。
σ=(Rse×S/t)-1 (4)
这里,σ表示离子电导率。S表示固体电解质材料的与冲头上部301的接触面积。S与图2中模框302的中空部的截面积相等。Rse表示阻抗测定中的固体电解质材料的电阻值。t表示固体电解质材料的厚度。t在图2中表示由固体电解质材料的粉末101形成的层的厚度。
在22℃下测定的实施例1的固体电解质材料的离子电导率为6.3×10-5S/cm。
(电池的制作)
在干燥氩气氛中,按照成为1:1的体积比的方式准备实施例1的固体电解质材料及石墨。将这些材料在研钵中进行混合。像这样操作,得到混合物。
在具有9.5mm的内径的绝缘性的筒中,将硫银锗矿型硫化物固体电解质即Li6PS5Cl(80mg)、实施例1的固体电解质材料(30mg)、上述的混合物依次层叠。混合物的量为包含4mg的石墨的量。对该层叠体施加740MPa的压力,形成固体电解质层及第1电极。
接着,在固体电解质层上层叠金属Li箔。对该层叠体施加40MPa的压力,形成第2电极。
接着,在第1电极及第2电极上安装由不锈钢形成的集电体,在该集电体上安装集电引线。
最后,使用绝缘性套圈,将绝缘性的筒的内部与外气气氛阻断,将该筒的内部密闭。像这样操作,得到实施例1的电池。
(初期充放电试验)
初期充放电特性通过下述的方法来测定。
实施例1的电池被配置于25℃的恒温槽中。
以74.5μA/cm2的电流密度,将实施例1的电池充电至达到0V的电压为止。该电流密度相当于0.05C倍率。
接着,以74.5μA/cm2的电流密度,将实施例1的电池放电至达到0.5V的电压为止。
充放电试验的结果是,实施例1的电池具有229mAh/g的初期放电容量。
(实施例2~9)
(固体电解质材料的制作)
在实施例2~6中,作为原料粉,按照成为y:(1-y)=Li3Sb:Li2Te摩尔比的方式准备Li3Sb及Li2Te。y的值被示于表1中。
在实施例6中,在研磨处理后,在干燥氩气氛下在400度下实施0.5小时烧成。
在实施例7中,作为原料粉,按照成为0.67:0.33=Li3Sb:Li2Se摩尔比的方式准备Li3Sb及Li2Se。
在实施例8中,作为原料粉,按照成为0.67:0.33=Li3Sb:Li2S摩尔比的方式准备Li3Sb及Li2S。
在实施例9中,作为原料粉,按照成为0.5:0.5=Li3Sb:LiI摩尔比的方式准备Li3Sb及LiI。
除了上述的事项以外,与实施例1同样地操作,得到实施例2~9的固体电解质材料。y或z的值被示于表1中。
(离子电导率的评价)
实施例2~9的固体电解质材料的离子电导率与实施例1同样地进行测定。测定结果被示于表1中。
(充放电试验)
使用实施例2~9的固体电解质材料,与实施例1同样地操作,得到实施例2~5的电池。实施例2~9的电池与实施例1的电池同样良好地被充电及放电。
图4是表示实施例2的电池的初期放电特性的图表。
(比较例1~4)
(固体电解质材料的制作)
作为比较例1的固体电解质材料,准备Li2Te。
作为比较例2的固体电解质材料,准备Li2Se。
作为比较例3的固体电解质材料,准备Li2S。
作为比较例4的固体电解质材料,准备LiI。
(离子电导率的评价)
比较例1的固体电解质材料的离子电导率与实施例1同样地进行测定。测定结果被示于表1中。
[表1]
(考察)
在表1中,“y或z”的项目表示组成式(2)中的y的值或组成式(3)中的z的值。如由表1表明的那样,实施例1~9的固体电解质材料在室温附近具有6.3×10-5S/cm以上的高的离子电导率。因此,含有锂和阴离子的锑的固体电解质材料具有高的离子电导率。
就实施例1~9的全部而言,都在室温下电池被充电及放电。
即使是在使用了N、P、As、Bi等除锑以外的氮族元素的情况下也可达成实施例水平的离子电导率。这些元素的化学性质及电性质与锑很相似,可以将锑的一部分置换成这些元素。
如以上那样,本公开的固体电解质材料是可提高锂离子电导率的材料,并且为了提供能够良好地进行充电及放电的电池是适宜的。
产业上的可利用性
本公开的固体电解质材料例如在电池(例如全固体锂离子二次电池)中被利用。
符号的说明
100 固体电解质
101 固体电解质材料的粉末
201 正极
202 电解质层
203 负极
204 正极活性物质
205 负极活性物质
300 加压成型冲模
301 冲头上部
302 模框
303 冲头下部
1000 电池
Claims (6)
1.一种固体电解质材料,其包含锂及多个阴离子元素,
所述多个阴离子元素包含锑和选自除锑以外的氮族元素、硫族元素及卤族元素中的至少1种元素。
2.根据权利要求1所述的固体电解质材料,其由以下的组成式(2)来表示,
Li2+ySbyCh1-y (2)
这里,满足0<y<1,
Ch为选自O、S、Se及Te中的至少1个。
3.根据权利要求2所述的固体电解质材料,其中,在所述组成式(2)中,Ch包含Te。
4.根据权利要求1所述的固体电解质材料,其由以下的组成式(3)来表示,
Li1+2zSbzHal1-z (3)
这里,满足0<z<1,
Hal为选自F、Cl、Br及I中的至少1个。
5.根据权利要求4所述的固体电解质材料,其中,在所述组成式(3)中,Hal包含I。
6.一种电池,其具备:
正极;
负极;及
配置于所述正极及所述负极之间的电解质层,
选自所述正极、所述负极及所述电解质层中的至少1者含有权利要求1~5中任一项所述的固体电解质材料。