CN117396594A - 表面活性剂组合物 - Google Patents
表面活性剂组合物 Download PDFInfo
- Publication number
- CN117396594A CN117396594A CN202280038713.XA CN202280038713A CN117396594A CN 117396594 A CN117396594 A CN 117396594A CN 202280038713 A CN202280038713 A CN 202280038713A CN 117396594 A CN117396594 A CN 117396594A
- Authority
- CN
- China
- Prior art keywords
- composition
- range
- average value
- groups
- nonionic surfactant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了包含非离子表面活性剂和0.1重量%至30重量%的低摩尔烷氧基化物的组合物。一些低摩尔烷氧基化物具有式R‑O‑(AO)pH其中R为直链或支链C8‑C16烷基或烷醇酰胺基团,AO为氧化丙烯(PO)、氧化乙烯(EO)、或其以无规或嵌段构型的组合,p具有在0.5至7范围内的平均值,PO基团的平均数量在0.5至4的范围内,并且EO基团的平均数量在0至3的范围内。相较于仅包含非离子表面活性剂的溶液,包含所述非离子表面活性剂和较小比例的低摩尔烷氧基化物的稀水溶液能更有效地润湿疏水性表面、抑制起泡并更好地脱脂。所述低摩尔烷氧基化物有助于在需要低泡表面活性剂,诸如自动餐具清洁剂和洗衣剂的应用中提高润湿性能。所述低摩尔烷氧基化物扩大了广泛范围的商业化非离子表面活性剂的效用,特别是那些通常难以润湿疏水性表面的表面活性剂。
Description
技术领域
本发明涉及非离子表面活性剂组合物,其具有改善的疏水性表面润湿性、易于配制性、低泡应用适用性以及增强的脱脂。
背景技术
非离子表面活性剂用于清洁剂、个人清洁剂、油田化学品、农用制剂、工业脱脂、油漆和涂料、洗衣剂以及其他多种应用中。大多数非离子表面活性剂具有极性和非极性链段的组合,使它们能够作为表面活性剂有效地发挥作用。许多常见的非离子表面活性剂作为油性污垢的润湿剂和脱脂剂的效果不如预期,并且一些表面活性剂难以润湿疏水性表面,例如高摩尔醇乙氧基化物。
所谓“扩展的”非离子表面活性剂是已知的,其中的疏水性部分(通常为烷基基团)直接与一个或多个氧化丙烯(PO)单元连接,然后进行四个或更多个氧化乙烯(EO)单元的封端。参见,例如,美国专利号9,303,240或美国公开号2019/0099720。该表面活性剂建议作为壬基酚聚氧乙烯醚的环保替代品。
在一些情况下,乙氧基化醇表面活性剂与较小比例的游离脂肪醇的组合可以改善非离子表面活性剂润湿疏水性表面的能力。例如,P.Phaodee等人(J.Surfact.Deterg.22(2019)1175)表明,包含直链(非烷氧基化)C6-C9醇作为添加剂与C10-C16醇7EO乙氧基化物一起可将固体椰子油的接触角从约48度降低至33至44度(参见表2)。尽管文章中显示其润湿性明显改善,但游离脂肪醇的存在可能会产生不良后果。这些缺点可能包括以下中的一项或多项:(1)水溶性降低,从而使制剂的整体增溶负荷达到极限,并可能导致待润湿的表面上油滴的分离或不良沉积;(2)制剂的表面张力(IFT)或浊点的可测量的扰动;(3)表面活性剂的胶束聚集的破坏;以及(4)接触角根据游离脂肪醇的链长而显著变化。
该行业将受益于具有增强的通用性的非离子表面活性剂组合物,尤其是稀水表面活性剂溶液润湿非极性表面的能力的改善。改善的组合物将作为润湿剂起到更有效的作用,同时避免过度发泡。基于可商购非离子表面活性剂(诸如脂肪醇乙氧基化物或低泡醇烷氧基化物)的组合物将是优选的。令人满意的是,这些产品可以经配制,同时避免包含游离脂肪醇的不良副作用。理想情况下,产品将具有物理性能优势,诸如在没有不利地影响低泡性能、浊点、胶束聚集或溶解度的情况下,接触角和临界胶束浓度能持续且大幅度降低。
发明内容
在一方面,本发明涉及一种包含非离子表面活性剂和低摩尔烷氧基化物的组合物。该组合物包含70重量%至99.9重量%的非离子表面活性剂,以及0.1重量%至30重量%的低摩尔烷氧基化物。该低摩尔烷氧基化物具有式:
R-O-(AO)pH
在该式中,R为直链或支链C8-C16烷基基团,AO为氧化丙烯(PO)、氧化乙烯(EO)、或其以无规或嵌段构型的组合,p具有在0.5至7范围内的平均值,PO基团的平均数量在0.5至4的范围内,并且EO基团的平均值在0至3的范围内。
在一个具体方面,本发明涉及组合物,其包含92重量%至98重量%的作为非离子表面活性剂的C8-C16脂肪醇乙氧基化物,以及2重量%至8重量%的具有以下式的低摩尔烷氧基化物:
R-O-(PO)m(EO)nH
其中R为直链或支链C8-C16烷基基团,PO为氧化丙烯,EO为氧化乙烯,m具有在0.5至4范围内的平均值,并且n具有在0至1范围内的平均值。
在另一方面,本发明涉及一种包含非离子表面活性剂和低摩尔烷氧基化物的组合物。该组合物包含70重量%至99.9重量%的非离子表面活性剂,以及0.1重量%至30重量%的低摩尔烷氧基化物。该低摩尔烷氧基化物具有式:
R-O-(AO)pH
在该式中,R为直链或支链C8-C16烷基基团或烷醇酰胺基团,AO为氧化丙烯(PO)、氧化乙烯(EO)、或其以无规或嵌段构型的组合,p具有在0.5至7范围内的平均值,PO基团的平均数量在0.5至4的范围内,并且EO基团的平均值在0至3的范围内。
在再一方面,本发明涉及一种组合物,其包含:
(a)92重量%至98重量%的C8-C16脂肪醇乙氧基化物表面活性剂;和
(b)2重量%至8重量%的具有以下式的低摩尔烷氧基化物:
R-O-(PO)m(EO)nH
其中R为直链或支链C8-C16烷基或烷醇酰胺基团,PO为氧化丙烯,EO为氧化乙烯,m具有在0.5至4范围内的平均值,并且n具有在0至1范围内的平均值。
在另一方面,本发明涉及一种方法,该方法包括将非离子表面活性剂与0.1重量%至30重量%的具有以下式的低摩尔烷氧基化物组合来形成混合物:
R-O-(AO)pH
其中R为直链或支链C8-C16烷基或烷醇酰胺基团,AO为氧化丙烯(PO)、氧化乙烯(EO)、或其以无规或嵌段构型的组合,p具有在0.5至7范围内的平均值,PO基团的平均数量在0.5至4的范围内,并且EO基团的平均数量在0至3的范围内;
其中以能够有效改善以下中的至少一项的量包含低摩尔烷氧基化物:(a)混合物润湿疏水性表面的能力;(b)混合物的脱脂能力;(c)混合物抵抗过度发泡的能力;以及(d)易于使非离子表面活性剂增溶以得到稳定制剂。
在一个具体方面,本发明涉及组合物,其包含92重量%至98重量%的作为非离子表面活性剂的C8-C16脂肪醇乙氧基化物,以及2重量%至8重量%的具有以下式的低摩尔烷氧基化物:
R-O-(PO)m(EO)nH
其中R为直链或支链C8-C16烷基基团,PO为氧化丙烯,EO为氧化乙烯,m具有在0.5至4范围内的平均值,并且n具有在0至1范围内的平均值。
在其他方面,本发明涉及一种方法。该方法包括将非离子表面活性剂与0.1重量%至30重量%的具有以下式的低摩尔烷氧基化物组合来形成混合物
R-O-(AO)pH
其中R为直链或支链C8-C16烷基基团,AO为氧化丙烯(PO)、氧化乙烯(EO)、或其以无规或嵌段构型的组合,p具有在0.5至7范围内的平均值,PO基团的平均数量在0.5至4的范围内,并且EO基团的平均值在0至3的范围内。在该方法中,以能够有效改善以下中的至少一项的量包含低摩尔烷氧基化物:(a)混合物润湿疏水性表面的能力;(b)混合物的脱脂能力;(c)混合物抵抗过度发泡的能力;以及(d)易于使非离子表面活性剂增溶以得到稳定制剂。
我们发现,相较于仅包含非离子表面活性剂的溶液,包含非离子表面活性剂和较小比例(例如5重量%)的低摩尔烷氧基化物的稀水溶液能更有效地润湿疏水性表面、抑制起泡并更好地脱脂。低摩尔烷氧基化物是一种低泡至无泡表面活性剂,有助于在需要低泡表面活性剂,诸如自动餐具清洁剂和洗衣剂的应用中提高润湿性能。低摩尔烷氧基化物扩大了广泛范围的商业化非离子表面活性剂的效用,特别是那些通常难以润湿疏水性表面的表面活性剂。
附图说明
图1为泡沫曲线图,表明了相比于其他添加剂,将0.1重量%的DA-1PO-1EO与低泡表面活性剂(DA-12EO-17PO)组合的优势。
图2显示了来自0.094% DA-12EO-17PO与0.006% EXXAL 10(左图)或与0.006%DA-1PO-1EO(右图)的两种不同溶液的照片。左图为Exxal 10的油滴沉积在浸入溶液中的脱湿的PVC塑料盖玻片(Fisher Sci.牢固盖玻片12-547)的表面上。右图显示了0.0094% DA-12EO-17PO与0.006%DA-1PO-1EO的溶液的照片。该溶液完全润湿塑料盖玻片,表现为片状且无相分离。
具体实施方式
组合物
在一些方面,本发明涉及包含非离子表面活性剂和低摩尔烷氧基化物的组合物。
1.非离子表面活性剂
该组合物包含70重量%至99.9重量%的非离子表面活性剂。在一些方面,该组合物包含85重量%至99重量%、或90重量%至98重量%的非离子表面活性剂。重量百分比基于组合物的量,该组合物包括非离子表面活性剂、低摩尔烷氧基化物和其他任意组分。
合适的非离子表面活性剂是众所周知的。在一些方面,非离子表面活性剂选自由以下项组成的组:烷氧基化醇、脂肪醇乙氧基化物、乙氧基化烷醇酰胺、乙氧基化烷基酚、乙氧基化苯乙烯基酚、脂肪胺乙氧基化物、EO/PO嵌段共聚物、乙氧基化蓖麻油、甲酯乙氧基化物、烷基聚葡糖苷、聚山梨醇酯,以及脂肪酸乙氧基化物。也可以使用这类非离子表面活性剂的改性物。因此,可以根据众所周知的方法将非离子表面活性剂的一个或多个末端羟基基团转化或封端为卤化物、醚、酯或其他合适的官能团。
在优选的方面,非离子表面活性剂为烷氧基化醇。烷氧基化醇优选具有C8-C16烷基链以及一个或多个氧化乙烯(EO)基团、氧化丙烯(PO)基团、或它们的组合。氧烷基烯单元可以以嵌段、多嵌段或无规构型排列。
在一些方面,烷氧基化醇具有式:
R1-O-(AO)qH
在该式中,R1为直链或支链C8-C16烷基基团,AO为氧化乙烯、氧化丙烯、或其组合,并且q具有在3至50范围内的平均值。在一些优选的方面,AO为氧化乙烯,并且q具有在5至20范围内的平均值。在其他优选的方面,AO为氧化乙烯,R1为直链或支链C9-C13烷基基团,并且q具有在5至20范围内的平均值。适合使用的非离子表面活性剂为包括由在非离子表面活性剂制造中使用的催化剂选择和/或反应物比例所产生的宽泛范围或狭窄范围的产品分布,正如本领域技术人员所熟知的。
合适的非离子表面活性剂可从Stepan公司和其他供应商商购。合适的Stepan非离子表面活性剂包括例如在 和/>标记下销售的产品,特别是在/>和/>标记下销售的乙氧基化醇和其他产品。实例包括/>N1-5、/>N91-6、N91-8、/>N25-7、/>DA-9、/>TD-9、/>TD-12、/>TD-18、/>NF-180、/>DG、/>UD-8等。
2.低摩尔烷氧基化物
本发明的组合物包括低摩尔烷氧基化物。该低摩尔烷氧基化物与非离子表面活性剂的组成不同,并且与非离子表面活性剂的量相比时,以添加剂的比例存在。
该低摩尔烷氧基化物具有式:
R-O-(AO)pH
其中R为直链或支链C8-C16烷基基团,AO为氧化丙烯(PO)、氧化乙烯(EO)、或其以无规或嵌段构型的组合,p具有在0.5至7范围内的平均值,PO基团的平均数量在0.5至4的范围内,并且EO基团的平均数量在0至3的范围内。
在一些方面,优选地,R为支链。在一些方面,低摩尔烷氧基化物具有每个分子0.6至2、或0.8至1.2、或约为1个PO单元的平均值和每个分子0至1、或0至0.5、或0至0.1个EO单元的平均值。在一些方面,R为直链或支链C9-C14烷基基团,或直链或支链C10-C13烷基基团。
组合物包含基于组合物的量的0.1重量%至30重量%的低摩尔烷氧基化物。在一些方面,组合物包含0.5重量%至15重量%或1重量%至8重量%的低摩尔烷氧基化物。
在一些方面,该低摩尔烷氧基化物具有式:
R-O-(PO)m(EO)nH
其中R为直链或支链C8-C16烷基基团,PO为氧化丙烯,EO为氧化乙烯,m具有在0.5至4范围内的平均值,并且n具有在0至1范围内的平均值。在其他方面,m具有在0.6至2、0.8至1.2、或约1范围内的平均值,并且n具有在0至0.5范围内、或0至0.1范围内的平均值。
在一些方面,该低摩尔烷氧基化物具有式:
R-O-(EO)n(PO)mH
其中R为直链或支链C8-C16烷基基团,EO为氧化乙烯,PO为氧化丙烯,n具有在0至1范围内的平均值,并且m具有在0.5至4范围内的平均值。在其他方面,n具有在0至0.5范围内、或0至0.1范围内的平均值,并且m具有在0.6至2、0.8至1.2、或约1范围内的平均值。在一些方面,低摩尔烷氧基化物仅具有氧化丙烯(并且没有氧化乙烯)单元。因此,在一些方面,该低摩尔烷氧基化物具有式:
R-O-(PO)mH
其中R为直链或支链C8-C16烷基基团,PO为氧化丙烯,并且m具有在0.5至4、0.6至2、0.8至1.5、或0.9至1.2范围内的平均值。在其他方面,m优选为约1。在优选的方面,R为支链C10-C13烷基基团。
在优选的方面,低摩尔烷氧基化物具有每个分子约1个PO单元的平均值和每个分子0至1、0至0.5、或0至0.1个EO单元的平均值。
3.透明各向同性流体
在一些方面,本发明的组合物与足够的水组合,以赋予物理稳定性并形成透明、各向同性混合物。因此,在一些方面,本发明的组合物包含基于本发明的组合物的量的0.1重量%至20重量%、或1重量%至15重量%的水。
方法
本发明的方法包括将非离子表面活性剂与0.1重量%至30重量%、0.5重量%至15重量%、或1重量%至8重量%的低摩尔烷氧基化物组合来形成混合物。该低摩尔烷氧基化物具有式:
R-O-(AO)pH
其中R为直链或支链C8-C16烷基基团,AO为氧化丙烯(PO)、氧化乙烯(EO)、或其以无规或嵌段构型的组合,p具有在0.5至7范围内的平均值,PO基团的平均数量在0.5至4的范围内,并且EO基团的平均数量在0至3的范围内。以能够有效改善以下中的至少一项的量包含低摩尔烷氧基化物:(a)混合物润湿疏水性表面的能力;(b)混合物的脱脂能力;(c)混合物抵抗过度发泡的能力;以及(d)易于使非离子表面活性剂增溶以得到稳定制剂。
在其他本发明的方法中,低摩尔烷氧基化物具有上文先前所述的组合物中的任一者,并且具有前述段落的性能属性(a)-(d)中的至少一者。
水溶液
在一些方面,本发明包括一种水溶液,其包含水和0.005重量%至50.0重量%、0.05重量%至5.0重量%、或0.1重量%至5.0重量%的如上所述的组合物。
其他组分
在一些方面,本发明的组合物包括除非离子表面活性剂和低摩尔烷氧基化物之外的其他组分。这些组分的性质和比例将取决于具体的最终用途应用。组合物可以包括其他表面活性剂、溶剂、pH调节剂、消泡剂、聚合物、酶、助洗剂、分散剂、染料、香料、油、活性成分等、以及其组合。
应用
本发明的组合物和含有这些组合物的水溶液用于多种最终用途应用。在一些情况下,本发明的组合物和水溶液可以改善到达界面的速度。最终用途应用包括例如,硬表面清洁剂、杀菌清洁剂、抗菌活性增强或递送、无纺布加工助剂、无纺布擦拭清洁剂和消毒剂、油墨、防污助剂、金属加工液、脱脂制剂、润滑剂、自动餐具洗涤剂、漂洗助剂、洗衣剂和预处理剂、消泡剂、防沫剂、除胶剂以及玻璃、塑料和纸张回收。此外,本发明有助于免漂洗的应用,例如无纺布擦拭清洁剂和消毒剂、地板护理和地板清洁剂、日常淋浴清洁剂、汽车和车队清洗、建筑物、甲板、庭院和窗户的外部清洁剂。本发明的组合物和水溶液也可用于配制农用助剂(如活化剂和桶混助剂)、包括一种或多种农药的农用组合物、用于油田应用的回流助剂、矿物和颜料脱水、预涂层金属防锈剂、多种油漆、油墨或涂料、以及霜剂、乳液或其他个人护理或肠胃外制剂。本发明的组合物可以通过将各组分直接组合成共混物或单独加入组分以实现上述应用,其中单个组分是其他组合物的一部分。
以下实例仅说明本发明主题。在权利要求的范围内的许多类似变型对于本领域技术人员来说将是显而易见的。
低摩尔烷氧基化物与
N91-8共混对接触角的影响
制备N91-8(C9-C11醇8EO乙氧基化物,0.1重量%)的水溶液。表1中列出的添加剂为0.005重量%(即,基于所用表面活性剂的量的5重量%)。将5-μL液滴沉积后的大约10至30秒内,在准平衡下,使用Krüss DSA100液滴形状分析仪器测量稀水溶液在聚乙烯薄膜(/>M,Bemis的产品)上的接触角。10滴液滴测量的平均值如表1所示。临界胶束浓度(CMC)还通过在Krüss K100张力仪上使用Wilhelmy平板法,用超纯水对0.1重量%的表面活性剂溶液进行梯度稀释来确定,并且值如表中所示。
如表1所示,与观察单独N91-8的值相比,将具有1至5个PO单元和0或1个EO单元(实例1至8)的5重量%的异癸醇的低摩尔烷氧基化物添加到/>N91-8中减小接触角和临界胶束浓度(CMC)。与仅含有PO的类似物相比,含有1摩尔PO和1摩尔EO的低摩尔烷氧基化物在减小接触角方面的效果稍差。结果还表明了多个PO单元在减小接触角方面不如单个PO单元有效(将实例1与实例2至4进行比较,或将实例5与实例6至8进行比较)。
当低摩尔烷氧基化物为9(异壬醇)和2个PO单元的加合物时,相比于对照组,还观察到接触角减小。有趣的是,当烷氧基化物为2个EO单元和/>9的加合物时,观察到接触角或CMC的减小很小或没有减小(对比实例10)。将/>N91-8与5重量%的乙二醇单己醚共混(对比实例11),未能改善聚乙烯膜的润湿性。
对低摩尔烷氧基化物的接触角的影响:支链醇乙氧基化物
将一系列支链醇乙氧基化物的接触角与3重量%或6重量%的低摩尔烷氧基化物(DA-1PO或DA-1PO-1EO)的共混物的接触角进行比较。结果如表2所示。
与直链醇乙氧基化物相比,支链醇乙氧基化物往往能更好地润湿疏水性表面;因此,表2中显示的接触角的减小相对不易察觉。然而,针对含有低摩尔烷氧基化物与较高乙氧基化产品(例如TD-12和/>TD-18)的组合的稀水溶液测量的接触角表现出大幅度减小,即使添加剂为3重量%。一般来说,DA-1PO在减小接触角方面比DA-1PO-1EO更有效。
添加剂和漂洗助剂表面活性剂共混物的接触角的前进/后退
使用Wilhelmy方法和Krüss K100张力仪测量接触角的前进/后退。接触角是将聚丙烯薄膜(Goodfellow Cambridge Ltd.)缓慢浸入溶液中并将其从该溶液抽回的三次拟合实验的平均值。结果如表3所示。
如表3所示,后退的接触角产生放大的差异(与前进接触角测量相比),并表明了低摩尔烷氧基化物相较于支链C10醇(对比实例5),其润湿能力得到改善。这些实例说明了包括5重量%的低摩尔烷氧基化物,尤其是具有单个PO单元的低摩尔烷氧基化物(实例4),对于增强漂洗助剂表面活性剂的润湿能力的价值。观察到的后退接触角的减小与需要片材性能的应用尤其相关,例如在漂洗助剂中。此外,实施例6至8表明了增加烷氧基化物中EO含量对润湿性的增强,特别是DA普遍具有负面影响。此外,实施例11至16显示了EO对润湿性增强,特别是对2PH影响的相反趋势。这些实施例共同表明,由低摩尔烷氧基化物实现的润湿性增强取决于PO和EO两者以及疏水物的量。
脱脂实验
制备含有0.2重量%的非离子表面活性剂(参见表4)和0.01重量%的DA-1PO-1EO添加剂的表面活性剂溶液。
将起酥油(介于0.1000g与0.1100g之间)薄甚至分层地涂在预先称重好的不锈钢试样(接近0.1mg)的一面的2/3至3/4处。当涂了所需量的起酥油时,确定涂覆试样的质量(最小记录到0.1mg)。
将表面活性剂溶液添加到五个烧杯中,每个烧杯配备磁力搅拌子,并使用数字搅拌器在室温以1400rpm的速度搅拌溶液。将涂覆试样浸入溶液中,其中被涂覆的一侧朝向液体流动方向。浸泡30min后,去除试样,用去离子水轻轻漂洗,并在通风橱中干燥。干燥后,重新称重试样以确定去除的油污量。每个样品重复十次,并取结果的平均值。结果如表4所示。
如表4所示,当表面活性剂与5重量%的低摩尔烷氧基化物(具有1个PO单元和1个EO单元的10加合物)组合时,含有各种醇乙氧基化物表面活性剂的稀水溶液的脱脂能力可以得到改善。轻微的(实例E和F)或显著的(实例A至D和G)油污去除性能的变化取决于使用哪种非离子表面活性剂。
消泡实验
通过在25℃喷射25s,来测试低泡表面活性剂DA-12EO-17PO的起泡性。将50-mL溶液的0.1重量%的总活性物质(0.094重量%DA-12EO-17PO+0.006重量%的添加剂)在KrüssDFA100仪器内以0.5L/m使用空气进行喷射。记录并分析主动喷射期间获得的瞬时泡沫生成曲线。泡沫剖面随时间的变化如图1所示。最大泡沫高度(mm)在表5中进行比较。
如表5和图1所示,作为添加剂的低摩尔乙氧基化物(TD-3,对比实例7)在喷射条件下产生大量的泡沫积累,并且当喷射停止时,泡沫不会立即坍塌。相反,当低摩尔烷氧基化物(DA-1PO-1EO,实例2)中包含PO时,最大泡沫高度最小,并且泡沫在去除活性喷射后立即坍塌。此外,图2中的左图显示,使用EXXAL 10脂肪醇(无PO且无EO)作为添加剂会导致表面和界面上产生不良的油性沉积,而右图显示使用DA-1PO-1EO不会观察到此类沉积,这表明没有片状残留。
前述实例仅用作说明;以下权利要求限定本发明的范围。
Claims (48)
1.一种组合物,其包含:
(a)70重量%至99.9重量%的非离子表面活性剂;和
(b)0.1重量%至30重量%的具有以下式的低摩尔烷氧基化物:
R-O-(AO)pH
其中R为直链或支链C8-C16烷基基团,AO为氧化丙烯(PO)、氧化乙烯(EO)、或其以无规或嵌段构型的组合,p具有在0.5至7范围内的平均值,PO基团的平均数量在0.5至4的范围内,并且EO基团的平均数量在0至3的范围内。
2.根据权利要求1所述的组合物,其包含85重量%至99重量%的非离子表面活性剂。
3.根据权利要求1所述的组合物,其包含90重量%至98重量%的非离子表面活性剂。
4.根据权利要求1所述的组合物,其中所述非离子表面活性剂选自由以下项组成的组:烷氧基化醇、脂肪醇乙氧基化物、乙氧基化烷醇酰胺、乙氧基化烷基酚、乙氧基化苯乙烯基酚、脂肪胺乙氧基化物、EO/PO嵌段共聚物、乙氧基化蓖麻油、甲酯乙氧基化物、烷基聚葡糖苷、聚山梨醇酯、脂肪酸乙氧基化物,以及其改性物,其中一个或多个末端羟基基团被封端为醚、酯或卤化物。
5.根据权利要求1所述的组合物,其中所述的非离子表面活性剂为烷氧基化醇。
6.根据权利要求5所述的组合物,其中所述烷氧基化醇具有式:
R1-O-(AO)qH
其中R1为直链或支链C8-C16烷基基团,AO为氧化乙烯、氧化丙烯、或其以无规或嵌段构型的组合,并且q具有在3至50范围内的平均值。
7.根据权利要求6所述的组合物,其中所述烷氧基化醇中的AO为氧化乙烯,并且q具有在5至20范围内的平均值。
8.根据权利要求1所述的组合物,其包含1重量%至8重量%的低摩尔烷氧基化物。
9.根据权利要求1所述的组合物,其中所述低摩尔烷氧基化物具有式:
R-O-(PO)m(EO)nH
其中R为直链或支链C8-C16烷基基团,PO为氧化丙烯,EO为氧化乙烯,m具有在0.5至4范围内的平均值,并且n具有在0至1范围内的平均值。
10.根据权利要求9所述的组合物,其中m具有在0.8至1.5范围内的平均值,并且n具有在0至0.5范围内的平均值。
11.根据权利要求9所述的组合物,其中R为支链C10-C13烷基基团。
12.一种透明、各向同性组合物,其包含根据权利要求1所述的组合物,以及基于各向同性组合物的量的0.1重量%至20重量%水。
13.一种水溶液,其包含水和0.005重量%至50.0重量%的根据权利要求1所述的组合物。
14.根据权利要求13所述的水溶液,其包含0.5重量%至5.0重量%的根据权利要求1所述的组合物。
15.一种硬表面清洁剂、地板护理产品或清洁剂、自动餐具清洁剂、漂洗助剂、洗衣剂、洗衣预处理剂、杀菌清洁剂、抗菌擦拭剂、消泡剂、防沫剂、金属加工液、润滑剂、防污助剂、外墙或窗户清洗剂、日常淋浴清洗剂、去粘剂、汽车和车队清洗剂、或脱脂制剂,其包含根据权利要求1所述的组合物。
16.一种农用助剂或含农药组合物,其包含根据权利要求1所述的组合物。
17.一种用于油田应用的回流助剂,其包含根据权利要求1所述的组合物。
18.一种油漆、涂料或油墨制剂,其包含根据权利要求1所述的组合物。
19.一种乳膏剂、洗剂、肠胃外制剂或其他个人护理制剂,其包含根据权利要求1所述的组合物。
20.一种玻璃、塑料或纸张回收制剂,其包含根据权利要求1所述的组合物。
21.一种组合物,其包含:
(a)92重量%至98重量%的C8-C16脂肪醇乙氧基化物表面活性剂;和
(b)2重量%至8重量%的具有以下式的低摩尔烷氧基化物:
R-O-(PO)m(EO)nH
其中R为直链或支链C8-C16烷基基团,PO为氧化丙烯,EO为氧化乙烯,m具有在0.5至4范围内的平均值,并且n具有在0至1范围内的平均值。
22.根据权利要求21所述的组合物,其中m具有在0.8至1.2范围内的平均值,并且n具有在0至0.5范围内的平均值。
23.根据权利要求21所述的组合物,其中R为支链,m为约1,并且n具有在0至0.1范围内的平均值。
24.一种方法,其包括将非离子表面活性剂与0.1重量%至30重量%的具有以下式的低摩尔烷氧基化物组合来形成混合物:
R-O-(AO)pH
其中R为直链或支链C8-C16烷基基团,AO为氧化丙烯(PO)、氧化乙烯(EO)、或其以无规或嵌段构型的组合,p具有在0.5至7范围内的平均值,PO基团的平均数量在0.5至4的范围内,并且EO基团的平均数量在0至3的范围内;
其中以能够有效改善以下中的至少一项的量包含所述低摩尔烷氧基化物:(a)所述混合物润湿疏水性表面的能力;(b)所述混合物的脱脂能力;(c)所述混合物抵抗过度发泡的能力;以及(d)易于使所述非离子表面活性剂增溶以得到稳定制剂。
25.一种组合物,其包含:
(a)70重量%至99.9重量%的非离子表面活性剂;和
(b)0.1重量%至30重量%的具有以下式的低摩尔烷氧基化物:
R-O-(AO)pH
其中R为直链或支链C8-C16烷基或烷醇酰胺基团,AO为氧化丙烯(PO)、氧化乙烯(EO)、或其以无规或嵌段构型的组合,p具有在0.5至7范围内的平均值,PO基团的平均数量在0.5至4的范围内,并且EO基团的平均数量在0至3的范围内。
26.根据权利要求25所述的组合物,其包含85重量%至99重量%的非离子表面活性剂。
27.根据权利要求25所述的组合物,其包含90重量%至98重量%的非离子表面活性剂。
28.根据权利要求25所述的组合物,其中所述非离子表面活性剂选自由以下项组成的组:烷氧基化醇、脂肪醇乙氧基化物、乙氧基化烷醇酰胺、乙氧基化烷基酚、乙氧基化苯乙烯基酚、脂肪胺乙氧基化物、EO/PO嵌段共聚物、乙氧基化蓖麻油、甲酯乙氧基化物、烷基聚葡糖苷、聚山梨醇酯、脂肪酸乙氧基化物,以及其改性物,其中一个或多个末端羟基基团被封端为醚、酯或卤化物。
29.根据权利要求25所述的组合物,其中所述的非离子表面活性剂为烷氧基化醇。
30.根据权利要求29所述的组合物,其中所述烷氧基化醇具有式:
R1-O-(AO)qH
其中R1为直链或支链C8-C16烷基或烷醇酰胺基团,AO为氧化乙烯、氧化丙烯、或其以无规或嵌段构型的组合,并且q具有在3至50范围内的平均值。
31.根据权利要求30所述的组合物,其中所述烷氧基化醇中的AO为氧化乙烯,并且q具有在5至20范围内的平均值。
32.根据权利要求25所述的组合物,其包含1重量%至8重量%的低摩尔烷氧基化物。
33.根据权利要求25所述的组合物,其中所述低摩尔烷氧基化物具有式:
R-O-(PO)m(EO)nH
其中R为直链或支链C8-C16烷基或烷醇酰胺基团,PO为氧化丙烯,EO为氧化乙烯,m具有在0.5至4范围内的平均值,并且n具有在0至1范围内的平均值。
34.根据权利要求33所述的组合物,其中m具有在0.8至1.5范围内的平均值,并且n具有在0至0.5范围内的平均值。
35.根据权利要求33所述的组合物,其中R为支链C10-C13烷基或烷醇酰胺基团。
36.一种透明、各向同性组合物,其包含根据权利要求25所述的组合物,以及基于各向同性组合物的量的0.1重量%至20重量%水。
37.一种水溶液,其包含水和0.005重量%至50.0重量%的根据权利要求25所述的组合物。
38.根据权利要求37所述的水溶液,其包含0.5重量%至5.0重量%的根据权利要求1至25所述的组合物。
39.一种硬表面清洁剂、地板护理产品或清洁剂、自动餐具清洁剂、漂洗助剂、洗衣剂、洗衣预处理剂、杀菌清洁剂、抗菌擦拭剂、消泡剂、防沫剂、金属加工液、润滑剂、防污助剂、外墙或窗户清洗剂、日常淋浴清洗剂、去粘剂、汽车和车队清洗剂、或脱脂制剂,其包含根据权利要求25所述的组合物。
40.一种农用助剂或含农药组合物,其包含根据权利要求25所述的组合物。
41.一种用于油田应用的回流助剂,其包含根据权利要求25所述的组合物。
42.一种油漆、涂料或油墨制剂,其包含根据权利要求25所述的组合物。
43.一种乳膏剂、洗剂、肠胃外制剂或其他个人护理制剂,其包含根据权利要求25所述的组合物。
44.一种玻璃、塑料或纸张回收制剂,其包含根据权利要求25所述的组合物。
45.一种组合物,其包含:
(a)92重量%至98重量%的C8-C16脂肪醇乙氧基化物表面活性剂;和
(b)2重量%至8重量%的具有以下式的低摩尔烷氧基化物:
R-O-(PO)m(EO)nH
其中R为直链或支链C8-C16烷基或烷醇酰胺基团,PO为氧化丙烯,EO为氧化乙烯,m具有在0.5至4范围内的平均值,并且n具有在0至1范围内的平均值。
46.根据权利要求45所述的组合物,其中m具有在0.8至1.2范围内的平均值,并且n具有在0至0.5范围内的平均值。
47.根据权利要求45所述的组合物,其中R为支链,m为约1,并且n具有在0至0.1范围内的平均值。
48.一种方法,其包括将非离子表面活性剂与0.1重量%至30重量%的具有以下式的低摩尔烷氧基化物组合来形成混合物:
R-O-(AO)pH
其中R为直链或支链C8-C16烷基或烷醇酰胺基团,AO为氧化丙烯(PO)、氧化乙烯(EO)、或其以无规或嵌段构型的组合,p具有在0.5至7范围内的平均值,PO基团的平均数量在0.5至4的范围内,并且EO基团的平均数量在0至3的范围内;
其中以能够有效改善以下中的至少一项的量包含所述低摩尔烷氧基化物:(a)所述混合物润湿疏水性表面的能力;(b)所述混合物的脱脂能力;(c)所述混合物抵抗过度发泡的能力;以及(d)易于使所述非离子表面活性剂增溶以得到稳定制剂。