CN117306248A - 一种浓缩柔顺剂组合物 - Google Patents
一种浓缩柔顺剂组合物 Download PDFInfo
- Publication number
- CN117306248A CN117306248A CN202311343152.7A CN202311343152A CN117306248A CN 117306248 A CN117306248 A CN 117306248A CN 202311343152 A CN202311343152 A CN 202311343152A CN 117306248 A CN117306248 A CN 117306248A
- Authority
- CN
- China
- Prior art keywords
- softener
- bis
- concentrated
- cationic
- cationic softener
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种浓缩柔顺剂组合物，由以下重量百分比的组分制成：阳离子柔顺剂15‑25％；稳定剂0.2‑0.5％；降粘剂0.1‑1％；酸度调节剂0.1‑0.5％；助剂0.01‑5％以及余量的软水。本发明涉及一种浓缩柔顺剂组合物，通过将不同类型的阳离子柔顺剂与稳定剂复配，使得产品不仅具有优良的柔顺效果，而且具有极佳的高温(45℃)、常温、低温(‑5℃)稳定性能。经过这种浓缩柔顺剂组合物处理的织物在经过高温烘干(＞125℃)后仍然具有良好的顺滑及蓬松效果且不发生明显黄变。
Description
技术领域
本发明涉及柔顺剂领域，具体涉及一种浓缩柔顺剂组合物。
背景技术
随着生活水平的不断提高，人们对洗涤后织物的品质提出了更高要求，因此，柔顺、抗静电等功能受到了广泛关注。市售柔顺剂的浓度不高，按QB/T4535的指标要求，普通柔顺剂的固含量≥3.5％即可。低浓度柔顺剂单次洗涤添加量高(≥80ml)，这造成柔顺剂的瓶体很大，使用起来很不方便。节能减排是每个企业社会责任感的表现，洗涤剂的浓缩化不仅能很好地完成节能减排的目标，而且能减少包材的使用，更可提高企业利润，带来企业的良性发展。柔顺剂所用阳离子表面活性剂在水中溶解度较差，该类表面活性剂在水溶液中呈分散状态，在阳离子表面活性剂浓度较高的情况下，柔顺剂容易出现低温凝胶且不可恢复、高温分层等现象。为了解决这一问题，市面上产品大都采用耐高-低温性能好的酰胺基季铵盐，该解决方案虽说解决了稳定性问题，但在柔顺效果上却差强人意。
发明内容
为了克服现有技术的缺点与不足，本发明提供一种浓缩柔顺剂组合物，可满足以下要求：(1)该浓缩柔顺剂组合物具有较高的浓度以及极佳的高温(45℃)、常温、低温(-5℃)稳定性能；(2)织物经该浓缩柔顺剂组合物处理烘干后具有优良的手感；(3)织物经该浓缩柔顺剂组合物处理后高温烘干不发生明显黄变。
本发明的目的通过下述技术方案实现：
第一方面，本发明提供一种浓缩柔顺剂组合物，由以下重量百分比的组分制备得到：
阳离子柔顺剂15-25％；
稳定剂0.2-0.5％；
降粘剂0.1-1％；
酸度调节剂0.1-0.5％；
助剂0.01-5％；
余量的软水。
所述的阳离子柔顺剂包括酰胺基阳离子柔顺剂、酯基阳离子柔顺剂和烷基阳离子柔顺剂。
所述阳离子柔顺剂中酰胺基阳离子柔顺剂的重量占比为40-60％。
所述阳离子柔顺剂中酯基阳离子柔顺剂的重量占比为30-45％。
所述阳离子柔顺剂中烷基阳离子柔顺剂的重量占比为10-20％。
所述的酰胺基阳离子柔顺剂为甲基双(牛脂酰胺基乙基)-2-羟乙基甲基硫酸铵、甲基双(油基酰胺基乙基)-2-羟乙基甲基硫酸铵和甲基双(氢化牛脂酰胺基乙基)-2-羟乙基甲基硫酸铵中的一种，优选甲基双(牛脂酰胺基乙基)-2-羟乙基甲基硫酸铵。
所述的酯基阳离子柔顺剂为双(牛脂基羧乙基)-羟乙基甲基硫酸甲酯铵、双(氢化牛脂基羧乙基)-羟乙基甲基硫酸甲酯铵、双(油基羧乙基)-羟乙基甲基硫酸甲酯铵、双(棕榈基羧乙基)-羟乙基甲基硫酸甲酯铵、双(氢化棕榈基羧乙基)-羟乙基甲基硫酸甲酯铵中的一种，优选双(棕榈基羧乙基)羟乙基甲基硫酸甲酯铵。
所述的烷基阳离子柔顺剂为双氢化牛脂基二甲基氯化铵、双氢化棕榈基二甲基氯化铵、双十八烷基二甲基氯化铵中的一种，优选双十八烷基二甲基氯化铵。
所述的稳定剂为脂肪醇聚氧乙烯醚、脂肪胺聚氧乙烯醚、烷基糖苷中的一种。稳定剂的作用在于可显著降低高浓度阳离子柔顺剂容易产生的稳定性问题(低温凝胶、高温分层)。
进一步的，所述脂肪醇聚氧乙烯醚的脂肪醇为C16-C18醇，聚氧乙烯醚的聚合度≥20；脂肪胺聚氧乙烯醚的脂肪胺为C16-18胺，聚氧乙烯醚的聚合度≥25；烷基糖苷的脂肪醇为C12-16醇，多糖聚合度在1.1-3之间。
所述的降粘剂为氯化钙、氯化镁、氯化钠、硫酸钠中的至少一种，优选氯化钙和氯化镁。
所述的酸度调节剂为盐酸、硫酸、硝酸中的至少一种，优选盐酸和硫酸。
所述的助剂为助溶剂、防腐剂、色素、荧光增白剂、香精、改性硅氧烷柔顺剂、消泡剂中的一种或多种。
与现有的技术方案相比，本发明的浓缩柔顺剂组合物具有以下优点：
1、本发明解决了高浓缩柔顺剂的稳定性问题。本发明的浓缩柔顺剂组合物采用三种阳离子柔顺剂与稳定剂复配，产品高温不分层、低温不凝胶、高-低温粘度变化小。
2、三种阳离子柔顺剂复配能提供更好的柔顺效果。该柔顺剂组合物采用三种阳离子柔顺剂复配，相较于单一组分的酰胺基阳离子组分柔顺剂或酯基阳离子组分柔顺剂具有更优的柔顺效果，其柔顺性能趋近于单一组分的烷基阳离子组分柔顺剂。
3、经本发明的浓缩柔顺剂组合物处理的织物高温烘干后黄变小。酰胺基阳离子柔顺剂、酯基阳离子柔顺剂柔顺性能一般但耐黄变性能好，烷基阳离子柔顺剂柔顺性能好但耐黄变性能差。因此本发明的浓缩柔顺剂组合物很好地平衡了柔顺与抗黄变性能，柔顺性能佳、耐黄变性能好。
4、本发明的浓缩柔顺剂组合物尤其适用于酒店布草洗涤。酒店布草洗涤由专用的洗涤设备完成，所用洗涤化料的添加也是通过分配器进行。由于分配器程序设置的特殊性，需要在短时间内添加足够的洗涤剂，因此水洗工厂所采用的洗涤剂均为浓缩或超浓缩产品且粘度随着温度的变化越小越好(粘度严重影响分配器的进样量)。随着水洗厂的高度集中化，洗涤效率高且省水、省电的隧道式洗衣机正被大规模所采用。贯通式烘干机为隧道式洗衣机的配套烘干设备，它使用特殊的加热器和独特的3D立体风道结构，热风和布草能够充分接触，使得机器具备优异的烘干能力。贯通式烘干机烘干温度(＞125℃)远高于单体式烘干机(＜90℃),在如此高温的烘干条件下，布草极易因快速失水出现发硬现象。本发明的浓缩柔顺剂组合物很好的解决了这一行业难题。
具体实施方式
下面将对实施例中的技术方案进行清楚、完整地描述。显然，以下将描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
应当理解，当在本说明书和所附权利要求书中使用时，术语“包括”和“包含”指示所描述特征、整体、步骤、操作、元素和/或组件的存在，但并不排除一个或多个其它特征、整体、步骤、操作、元素、组件和/或其集合的存在或添加。
还应当理解，在此本发明实施例说明书中所使用的术语仅仅是出于描述特定实施例的目的而并不意在限制本发明实施例。如在本发明实施例说明书和所附权利要求书中所使用的那样，除非上下文清楚地指明其它情况，否则单数形式的“一”、“一个”及“该”意在包括复数形式。
本发明涉及的原料均可从市场上直接购买。对于未特别注明的工艺参数，可参照常规技术进行。
其中，在一些实施例中，酰胺基阳离子柔顺剂为赢创特种化学所生产的的VARISOFT 222LM、VARI SOFT 222AP，斯特潘化学生产的ACCOSOFT 501中的一种，优选VARISOFT222LM。
在一些实施例中，酯基阳离子柔顺剂为赢创特种化学生产的的RewopolWE28、Rewopol WE45，斯泰潘化学生产的Stepantex SP90、Stepantex VT90、Stepantex VK90，索尔维精细化工生产的TEP-88中的一种，优选Stepantex VK90。
在一些实施例中，烷基阳离子柔顺剂为天津先光生产的SUNQAT SM-75,诺力昂生产的ARQUAD 2HT-75，索尔维精细化工生产的DHT21 E75中的一种，优选SUNQAT SM-75。
对比例1-6
对比例1-6分别提供一种柔顺剂。用于制备对比例1-6的柔顺剂的成分和配比如下表1所示。
表1对比例1-6柔顺剂的成分、配比
实施例1-4
实施例1-4分别提供一种浓缩柔顺剂组合物。用于制备实施例1-4的浓缩柔顺剂组合物的成分和配比如下表2所示。
表2实施例1-4浓缩柔顺剂组合物的成分、配比
试验例1--高-低温稳定性及粘度变化测试
其中的低温稳定性测试方法：将样品置于-5℃的冰箱内放置4周，测试粘度(-5℃)并恢复室温观察产品外观。
其中的常温稳定性测试方法：将样品置于常温环境放置3个月，测试粘度(室温粘度)并观察产品外观。
其中的高温稳定性测试方法：将样品置于45℃的烘箱内放置4周，测试粘度(45℃)并恢复室温观察产品外观。
按上述方法测试对比例1-6，实施例1-4的低温、室温、高温稳定性，测试结果如表3所示。
表3对比例1-6、实施例1-4低温、室温、高温外观及粘度测试数据
根据表3的测试结果可知：对比例中除对比例1、对比例4高-低温稳定外，其余对比例均出现了高温分层或低温凝胶现象。单独采用酯基阳离子柔顺剂或烷基阳离子柔顺剂的柔顺剂稳定性不佳，复配酰胺基阳离子柔顺剂可明显改善产品的稳定性，通过对比例4-6、实施例1-4可知，酰胺基阳离子柔顺剂的添加量不足阳离子柔顺剂的40％时，稳定性依然不能通过。通过对比例6、实施例1的对比可知，稳定剂对于整个体系的高-低温稳定性至关重要。采用本发明实施例提供的方案，具有很好的低温(-5℃)、室温、高温(45℃)稳定性能，在高-低温下放置30天无明显凝胶或分层现象出现。
采用SEKO隔膜泵对实施例1进行流量标定，标定结果如表4所示。
表4不同温度下SEKO隔膜泵10s抽样量
| 温度 | 抽样量(ml) |
| 0℃ | 269 |
| 5℃ | 274 |
| 10℃ | 280 |
| 15℃ | 291 |
| 20℃ | 298 |
| 25℃ | 304 |
| 30℃ | 308 |
| 35℃ | 311 |
根据表4的测试结果可知：随着粘度的波动，SEKO隔膜泵的抽样量也有波动，粘度越高(温度越低)，抽样量越少。实施例1在0℃至35℃的极值为42ml，可满足绝大多数地区洗衣厂的要求。
试验例2--柔顺效果测试
柔顺效果测试方法：将测试样品按照有效物浓度0.02％溶解到水盆中，分别将处理好的织物(客房用浴巾或毛巾，经过表面活性剂、氢氧化钠高温洗涤，用中和酸中和至中性)浸泡在水盆中，浸泡5min后拧干、自然晾干、手工搓散毛巾纤维。通过10位(5男5女)受过训练的测评人员评估毛巾的柔软舒适度，按照1～5分评分，手感越好，分值越高。
按上述方法测试对比例1-6，实施例1-4的柔顺效果，测试结果如表5所示。
表5对比例1-6，实施例1-4的柔顺度得分
| 柔顺度得分 | |
| 对比例1 | 2.5 |
| 对比例2 | 2.7 |
| 对比例3 | 4.6 |
| 对比例4 | 3.9 |
| 对比例5 | 4.3 |
| 对比例6 | 4.2 |
| 实施例1 | 4.2 |
| 实施例2 | 4.1 |
| 实施例3 | 4.3 |
| 实施例4 | 4.4 |
根据表5的测试结果可知：单纯的酰胺基阳离子柔顺剂或酯基阳离子柔顺剂的柔顺性能不佳，单独的烷基阳离子柔顺剂具有极佳的柔顺性能。从对比例4-6、实施例1-4可知，不同类型阳离子柔顺剂的复配可明显提高产品的柔顺性能，在稳定性允许及粘度可接受的范围内，酯基阳离子柔顺剂和烷基阳离子柔顺剂总和占比越高，柔顺性能越好。
试验例3--耐黄变性能测试
耐黄变性测试方法：将通过高-低温稳定性测试及柔顺效果测试筛选的实施例与对比例的样品用于笼式洗衣机上，经过洗涤、烘干后观察毛巾的黄变情况。
采用对比例1、对比例3、实施例1进行现场测试，通过现场专业人员(洗涤用品销售及售后、水洗厂资深水洗工、水洗厂老板等)对洗涤完成后的酒店布草的柔顺性能及黄变程度进行排名，结果如表6。
表6对比例1、3，实施例1的柔顺性能及耐黄变性能排名
| 柔顺性能 | 黄变程度 | |
| 对比例1 | 3 | 2 |
| 对比例3 | 1 | 3 |
| 实施例1 | 2 | 1 |
根据表6的测试结果可知：对比例3的柔顺性能最佳，但黄变最严重，不能满足水洗厂的使用需求。实施例1兼顾了柔顺性能与耐黄变性能，可满足水洗厂的使用需求。
综上所述，实施例1-4中的不同组分相互作用实现了浓缩柔顺剂高-低温稳定，柔顺性能好，耐黄变性能佳的功效。
上述实施例为本发明较佳的实施方式，但本发明的实施方式并不受上述实施例的限制，其他的任何未背离本发明的精神实质与原理下所作的改变、修饰、替代、组合、简化，均应为等效的置换方式，都包含在本发明的保护范围之内。
Claims (8)
1.一种浓缩柔顺剂组合物，其特征在于，由以下重量百分比的组分制成：
阳离子柔顺剂15-25％；
稳定剂0.2-0.5％；
降粘剂0.1-1％；
酸度调节剂0.1-0.5％；
助剂0.01-5％；
余量的软水；
所述的阳离子柔顺剂包括酰胺基阳离子柔顺剂、酯基阳离子柔顺剂和烷基阳离子柔顺剂；
所述阳离子柔顺剂中酰胺基阳离子柔顺剂的重量占比为40-60％；
所述阳离子柔顺剂中酯基阳离子柔顺剂的重量占比为30-45％；
所述阳离子柔顺剂中烷基阳离子柔顺剂的重量占比为10-20％。
2.根据权利要求1所述的浓缩柔顺剂组合物，其特征在于，所述酰胺基阳离子柔顺剂为甲基双(牛脂酰胺基乙基)-2-羟乙基甲基硫酸铵，甲基双(油基酰胺基乙基)-2-羟乙基甲基硫酸铵和甲基双(氢化牛脂酰胺基乙基)-2-羟乙基甲基硫酸铵中的一种。
3.根据权利要求1所述的浓缩柔顺剂组合物，其特征在于，所述酯基阳离子柔顺剂为双(牛脂基羧乙基)-羟乙基甲基硫酸甲酯铵、双(氢化牛脂基羧乙基)-羟乙基甲基硫酸甲酯铵、双(油基羧乙基)-羟乙基甲基硫酸甲酯铵、双(棕榈基羧乙基)-羟乙基甲基硫酸甲酯铵、双(氢化棕榈基羧乙基)-羟乙基甲基硫酸甲酯铵中的一种。
4.根据权利要求1所述的浓缩柔顺剂组合物，其特征在于，所述烷基阳离子柔顺剂为双氢化牛脂基二甲基氯化铵、双氢化棕榈基二甲基氯化铵、双十八烷基二甲基氯化铵中的一种。
5.根据权利要求1所述的浓缩柔顺剂组合物，其特征在于，所述的稳定剂为脂肪醇聚氧乙烯醚、脂肪胺聚氧乙烯醚、烷基糖苷中的一种。
6.根据权利要求1所述的浓缩柔顺剂组合物，其特征在于，所述的降粘剂为氯化钙、氯化镁、氯化钠、硫酸钠中的至少一种。
7.根据权利要求1所述的浓缩柔顺剂组合物，其特征在于，所述的酸度调节剂为盐酸、硫酸、硝酸中的至少一种。
8.根据权利要求1所述的浓缩柔顺剂组合物，其特征在于，所述的助剂为助溶剂、防腐剂、色素、荧光增白剂、香精、改性硅氧烷柔顺剂、消泡剂中的一种或多种。