CN117255671A - 具有生物聚合物的水凝胶 - Google Patents
具有生物聚合物的水凝胶 Download PDFInfo
- Publication number
- CN117255671A CN117255671A CN202280030714.XA CN202280030714A CN117255671A CN 117255671 A CN117255671 A CN 117255671A CN 202280030714 A CN202280030714 A CN 202280030714A CN 117255671 A CN117255671 A CN 117255671A
- Authority
- CN
- China
- Prior art keywords
- hydrogel
- weight
- xanthan
- carrageenan
- use according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请涉及一种化妆品水凝胶,其包含:a)至少两种选自脱氢黄原胶、黄原胶和卡拉胶的聚合物,以及b)水,并且涉及黄原胶和/或卡拉胶用于稳定具有脱氢黄原胶的水凝胶的粘度的用途。
Description
技术领域
一般来说,化妆品不仅让人看起来漂亮且有吸引力,其功效还极大地增强人们的自尊和幸福感。因此,各种各样的化妆品被用于人体皮肤的日常清洁和护理。
本发明涉及一种含水透明凝胶(水凝胶),它除了水之外还包含至少两种胶凝剂。优选的是,根据本发明的凝胶含有至少一种化妆品有效物质。
背景技术
水凝胶及其用于向人体皮肤或粘膜施用化妆品成分的用途是已知的。在技术意义上,术语"凝胶"是指由至少两种组分组成的相对尺寸稳定、易变形的分散体系,通常由以下组成:一种(通常是固体)由长链分子组组成的胶体分解物质(如明胶、硅酸、多糖)作为骨架形成剂,以及一种液体分散剂(例如水)。胶体分散物质通常称为增稠剂、胶凝剂或胶冻剂。它在分散剂中形成空间网络,其中通过静电相互作用,各个作为胶体存在的颗粒可以或多或少地彼此牢固联结。
丙烯酸聚合物主要用作增稠剂。这些聚合物中存在的游离羧基被碱(如氢氧化钠溶液或胺)转化为盐的形式,从而因强交联而导致粘度增加。此外,纤维素衍生物或其他多糖(如瓜尔豆粉或黄原胶)也可用作胶凝剂。根据增稠剂的种类和用量,凝胶的稠度可以从液态调整为耐切割状态。
网络周围的分散剂以与增稠剂的静电亲和力为特征,即主要为极性(特别是亲水性)的增稠剂优选地胶凝极性分散剂(特别是水),而主要为非极性的增稠剂优选地胶凝非极性分散剂。
强静电相互作用,例如导致增稠剂和分散剂之间的氢键以及分散剂分子彼此之间的氢键的静电相互作用,也导致分散剂的强烈交联。水凝胶可以几乎100%由水(此外还有例如约0.2-1.0%的胶凝剂)组成,进而具有相当坚固的稠度。
在化妆品盖伦制剂中,凝胶通常具有半固体、通常可流动的稠度。
本领域技术人员尤其由DE2005056497 A1知晓水凝胶。
在现有技术中,已知丙烯酸酯基聚合物通常用于凝胶形成。丙烯酸酯基聚合物是由丙烯酸和/或甲基丙烯酸均聚或共聚而成的聚合物。例子尤其有聚丙烯酸钠或丙烯酸酯共聚物。作为丙烯酸酯基聚合物的替代品,也可以使用由乙烯基吡咯烷酮均聚或共聚而成的聚合物来形成凝胶。
此外,醇类水凝胶尤其用丙烯酰二甲基牛磺酸铵/VP共聚物增稠,并稳定化以防粘度损失。
然而不利的是,由于上述聚合物的生物降解性尚未完全明确,其使用受到越来越多的批评。因此,需要不使用这些聚合物的水凝胶。
然而,在提供透明水凝胶时会出现预料不到的问题。例如,水凝胶的粘度通常会在储存过程中不断增加,因此水凝胶的特性随着储存时间的变化而改变。
如果是醇类水凝胶,就更成问题了。
发明内容
本发明的任务是克服上述缺点。
令人惊奇的是,现在发现通过本发明可以消除或减轻现有技术的缺点。
本发明的主题是一种化妆品水凝胶,其具有
a)至少两种选自脱氢黄原胶、黄原胶和卡拉胶的聚合物,以及
b)水。
本发明的另一个主题是一种化妆品水凝胶,其具有
a)至少两种选自脱氢黄原胶、黄原胶和卡拉胶的聚合物,
b)水,和
c)5至25重量%的乙醇,基于水凝胶的总重量。
本发明的另一个主题是一种化妆品水凝胶,其具有
a)脱氢黄原胶,和
b)黄原胶和/或卡拉胶;和
c)水。
本发明的另一个主题是具有至少两种选自脱氢黄原胶、黄原胶和卡拉胶的聚合物的化妆品水凝胶用于稳定水凝胶的粘度的用途。
本发明的另一个主题是具有至少两种选自脱氢黄原胶、黄原胶和卡拉胶的聚合物的化妆品水凝胶用于稳定水凝胶的粘度的用途,所述水凝胶具有5至25重量%的乙醇,基于水凝胶的总重量。
本发明的另一个主题是黄原胶和/或卡拉胶用于稳定包含脱氢黄原胶和水的水凝胶的粘度的用途。
如果下文给出的重量百分比(重量%)没有提及具体的组合物或特定的混合物,则该数据始终指的是水凝胶的总重量。如果下文公开了组分/物质/物质组的比例,则这些比例是指所述组分/物质/物质组的重量比。
如果下文给出了水凝胶各组分的重量百分比范围,则本申请的公开内容也包括这些重量百分比范围内以0.1重量%为步长的所有单个值。
"根据本发明"、"根据本发明有利"、"在本发明的意义上有利"等表述在本公开的范围内总是指根据本发明的水凝胶和根据本发明的用途。
除非另有说明,所有试验均在标准条件下进行。术语"标准条件"是指20℃、1013hPa和50%的相对湿度。
当使用"皮肤"一词时,优选是指人的皮肤。
乳化剂指《国际化妆品成分词典和手册》(2010年第十三版)(ISBN 1-882621-47-6)中"乳化剂"一词下所列的所有物质。表面活性剂指《国际化妆品成分词典和手册》(2010年第十三版)(ISBN 1-882621-47-6)中"表面活性剂"一词下所列的所有物质。
如果本公开中给出粘度值,则所有数值均涉及在25℃下通过proRheo公司的Rheomat R 123在150ml宽颈瓶(VWR编号:807-001)中进行的测量。proRheo GmbH公司的Rheomat R 123是一种旋转粘度计,即测量体在待测物质中旋转。测量的是使测量体以指定转速在样品中旋转所需的力。由这个力矩、测量体的转速和所用测量系统的几何尺寸计算粘度。使用1号测量体(商品编号200 0191)作为测量体,其适用于最高达10,000[m·Pas]的粘度范围,转速范围62.5min-1。
根据本发明有利的是,化妆品水凝胶包含脱氢黄原胶。在本发明的意义上有利的是,脱氢黄原胶的份额为0.1重量%至5重量%,优选地为0.3重量%至3.5重量%,特别优选地为0.6重量%至2重量%,基于水凝胶的总重量。
此外,根据本发明,包含黄原胶和/或卡拉胶。有利的是,黄原胶和/或卡拉胶的总份额为0.1至3重量%,优选地为0.15重量%至1.5重量%,特别优选地为0.2至0.7重量%,基于水凝胶的总重量。
如果含有黄原胶,黄原胶的份额有利地为0.1至3重量%,优选地为0.15重量%至1.5重量%,特别优选地为0.2至0.7重量%,基于水凝胶的总重量。
如果含有卡拉胶,卡拉胶的份额有利地为0.1至3重量%,优选0.15重量%至1.5重量%,特别优选0.2至0.7重量%,基于水凝胶的总重量。
有利的是,脱氢黄原胶与黄原胶和/或卡拉胶的总份额的重量比为10:1至1:1,优选为8:1至1.5:1,特别优选为5:1至2:1。
如果含有黄原胶和卡拉胶,有利的是黄原胶与卡拉胶的重量比为10:1至1:10,优选地为5:1至1:5,特别优选地为2:1至1:2。
水的总份额有利地为至少70重量%,优选地为至少75重量%,特别优选地为至少77重量%,基于水凝胶的总重量。水的总份额有利地低于99重量%,基于水凝胶的总重量。
此外有利的是含有乙醇。如果含有乙醇,优选的是乙醇的份额为5至25重量%,优选地为8至20重量%,特别优选地为10至16重量%,基于水凝胶的总重量。尤其令人惊奇的是,具有这种高乙醇份额的水凝胶中粘度随着时间推移的稳定化是可能的。
根据本发明的水凝胶优选地不含由乙烯基吡咯烷酮、丙烯酸和/或甲基丙烯酸均聚或共聚得到的聚合物。本发明意义上的不含是指所述物质的总份额小于0.05重量%,特别优选为0重量%,其中这些数据基于水凝胶的总重量。
此外有利的是,水凝胶不含乳化剂和表面活性剂。
此外,根据本发明有利的是,水凝胶包含通常用于此类配制物的其他成分。
因此有利的是,水凝胶含有一种或多种具有2至8个碳原子的短链多元醇。有利的是,这些具有2至8个碳原子的多元醇的份额为1至30重量%,优选地为2至23重量%,特别优选地为3至20重量%,基于水凝胶的总重量。
具有2至8个碳原子的优选多元醇选自甘油、甲基丙二醇、丙二醇、1,2-己二醇、辛甘醇、丁二醇和戊二醇组成的组。
如果水凝胶含有甘油,优选的是甘油的份额为3至16重量%,优选地为5至15重量%,优选地为7至12.5重量%,特别优选为8至12重量%,基于水凝胶的总重量。
如果水凝胶含有甲基丙二醇,优选的是甲基丙二醇的份额为1至10重量%,优选地为2至8重量%,特别优选地为3至5重量%,基于水凝胶的总重量。
如果水凝胶中含有丙二醇,优选的是丙二醇的份额为1至10重量%,优选地为2至8重量%,特别优选地为3至5重量%,基于水凝胶的总重量。
如果水凝胶含有1,2-己二醇,优选的是1,2-己二醇的份额为0.2至2重量%,优选地为0.5至1.5重量%,特别优选地为0.7至1.3重量%,基于水凝胶的总重量。
同样有利的是水凝胶含有苯氧乙醇,其中有利的是,苯氧乙醇的份额为0.2至1.5重量%,优选地为0.4至1.0重量%,特别优选地为0.5至0.9重量%,基于水凝胶的总重量。
此外,根据本发明有利的是,包含其他有效物质。它们有利地选自透明质酸钠、1-甲基乙内酰脲-2-酰亚胺、肌酸、叶酸、泛醇、泛酰内酯、维生素C、厚朴酚、泛酸钙和抗坏血酸磷酸酯钠。有利的是,该组中提到的有效物质以最高达2重量%的总份额使用,基于水凝胶的总重量。
此外,还可以包含其他化妆品辅料,如其他有效物质、染料、流变改性剂、醇、油和蜡,只要它们不对本发明的特性产生不利影响。
有利的是,本发明的凝胶的特征在于它们是透明的。这种特性通常会受到消费者的青睐。如果在标准条件下凝胶在500nm处的透射率达到85%,则被认为是透明的。
具体实施方式
比较试验和实施例
以下实施例旨在说明本发明,而不对其进行限制。除非另有说明,所有数量、份额和百分比均基于重量和总量或制剂的总重量。
下表给出了水凝胶的不同组成以及在标准条件下储存不同长度的时间后测得的粘度。粘度的测量如上述说明所示进行。实施例1至实施例4为比较实施例。实施例5至实施例8为根据本发明的实施例。
比较结果表明,在贮存至120天期间,通过添加卡拉胶或黄原胶,可以降低粘度的提升。因此,可以提供粘度更稳定的水凝胶。根据本发明的水凝胶看起来是透明的。
下面列出醇类水凝胶F1至F6的其他比较试验:
下面示出更多根据本发明的实施例:
表1
表2
成分 | 配制物7 | 配制物8 | 配制物9 | 配制物10 | 配制物11 |
透明质酸钠 | 0.21 | 0.22 | 0.25 | 0.15 | |
1,2-己二醇 | 1 | 0.8 | 1 | 0.75 | 1 |
甲基丙二醇 | 3.5 | 4 | 3.7 | 4 | 3.85 |
丙二醇 | 4.6 | 3.95 | 4.6 | 4.75 | 4.6 |
甘油 | 9.5 | 10 | 7.5 | 10 | 10.75 |
苯氧乙醇 | 0.8 | 0.92 | 0.8 | 0.85 | 0.8 |
卡拉胶 | 0.2 | 0.3 | 0.28 | 0.3 | 0.4 |
脱氢黄原胶 | 1.4 | 1.65 | 1.4 | 0.8 | 1.15 |
1-甲基乙内酰脲-2-酰亚胺 | |||||
肌酸 | |||||
叶酸 | |||||
泛醇+泛酰内酯+柠檬酸 | |||||
厚朴提取物 | |||||
抗坏血酸 | |||||
泛酸钙 | 0.05 | ||||
抗坏血酸磷酸酯钠 | |||||
水 | 加至100 | 加至100 | 加至100 | 加至100 | 加至100 |
表3
成分 | 配制物1 | 配制物2 | 配制物3 | 配制物4 | 配制物5 | 配制物6 |
透明质酸钠 | 0.225 | 0.185 | 0.195 | 0.175 | 0.18 | 0.19 |
1,2-己二醇 | 1 | 1.2 | 1 | 0.9 | 1 | 1.35 |
甲基丙二醇 | 4.35 | 4 | 4.5 | 4 | 4.2 | 4 |
丙二醇 | 4.6 | 4.2 | 4.6 | 5 | 4.6 | 3.6 |
甘油 | 8 | 10 | 11 | 10 | 12.5 | 10 |
苯氧乙醇 | 0.8 | 0.82 | 0.8 | 0.75 | 0.8 | 0.9 |
黄原胶 | 0.35 | 0.3 | 0.32 | 0.3 | 0.26 | 0.3 |
脱氢黄原胶 | 1.4 | 1.2 | 1.4 | 0.95 | 1.4 | 1.5 |
1-甲基乙内酰脲-2-酰亚胺 | 0.03 | |||||
肌酸 | 0.15 | |||||
叶酸 | 0.12 | |||||
泛醇+泛酰内酯+柠檬酸 | 0.55 | |||||
厚朴提取物 | 0.07 | |||||
抗坏血酸 | 0.5 | |||||
泛酸钙 | ||||||
抗坏血酸磷酸酯钠 | 0.45 | |||||
水 | 加至100 | 加至100 | 加至100 | 加至100 | 加至100 | 加至100 |
表4
表5
成分 | 配制物1 | 配制物2 | 配制物3 | 配制物4 | 配制物5 | 配制物6 |
透明质酸钠 | 0.225 | 0.185 | 0.195 | 0.175 | 0.18 | 0.19 |
1,2-己二醇 | 1 | 1.2 | 1 | 0.9 | 1 | 1.35 |
甲基丙二醇 | 4.35 | 4 | 4.5 | 4 | 4.2 | 4 |
丙二醇 | 4.6 | 4.2 | 4.6 | 5 | 4.6 | 3.6 |
甘油 | 8 | 10 | 11 | 10 | 12.5 | 10 |
苯氧乙醇 | 0.8 | 0.82 | 0.8 | 0.75 | 0.8 | 0.9 |
黄原胶 | 0.15 | 0.15 | 0.17 | 0.15 | 0.13 | 0.3 |
卡拉胶 | 0.2 | 0.15 | 0.15 | 0.15 | 0.1 | 0.1 |
脱氢黄原胶 | 1.4 | 1.2 | 1.4 | 0.95 | 1.4 | 1.5 |
1-甲基乙内酰脲-2-酰亚胺 | 0.03 | |||||
肌酸 | 0.15 | |||||
叶酸 | 0.12 | |||||
泛醇+泛酰内酯+柠檬酸 | 0.55 | |||||
厚朴提取物 | 0.07 | |||||
抗坏血酸 | 0.5 | |||||
泛酸钙 | ||||||
抗坏血酸磷酸酯钠 | 0.45 | |||||
水 | 加至100 | 加至100 | 加至100 | 加至100 | 加至100 | 加至100 |
表6
表7
Claims (17)
1.一种化妆品水凝胶,其具有:
a.至少两种选自脱氢黄原胶、黄原胶和卡拉胶的聚合物,以及
b.水。
2.具有至少两种选自脱氢黄原胶、黄原胶和卡拉胶的聚合物的化妆品水凝胶用于稳定水凝胶的粘度的用途。
3.根据权利要求1所述的水凝胶或根据权利要求2所述的用途,其特征在于,所述水凝胶具有
a.脱氢黄原胶,和
b.黄原胶和/或卡拉胶,和
c.水。
4.根据前述权利要求中任一项所述的水凝胶,其特征在于,含有5至25重量%,优选8至20重量%,特别优选10至16重量%的乙醇,基于水凝胶的总重量。
5.根据前述权利要求中任一项所述的水凝胶,其特征在于,脱氢黄原胶的份额为0.1重量%至5重量%,优选地为0.3重量%至3.5重量%,特别优选地为0.6重量%至2重量%,基于水凝胶的总重量。
6.根据前述权利要求中任一项所述的水凝胶或用途,其特征在于,黄原胶和/或卡拉胶的总份额为0.1至3重量%,优选地为0.15重量%至1.5重量%,特别优选地为0.2至0.7重量%,基于水凝胶的总重量。
7.根据前述任一项权利要求所述的水凝胶或用途,其特征在于,黄原胶的份额为0.1至3重量%,优选地为0.15重量%至1.5重量%,特别优选地为0.2至0.7重量%,基于水凝胶的总重量。
8.根据前述任一项权利要求所述的水凝胶或用途,其特征在于,卡拉胶的份额为0.1至3重量%,优选地为0.15重量%至1.5重量%,特别优选地为0.2至0.7重量%,基于水凝胶的总重量。
9.根据前述任一项权利要求所述的水凝胶或用途,其特征在于,脱氢黄原胶与黄原胶和/或卡拉胶的总份额的重量比为10:1至1:1,优选为8:1至1.5:1,特别优选为5:1至2:1。
10.根据前述权利要求中任一项所述的水凝胶或用途,其特征在于,水的总份额为至少70重量%,优选地为至少75重量%,特别优选地为至少77重量%,基于水凝胶的总重量。
11.根据前述权利要求中任一项所述的水凝胶或用途,其特征在于,水的总份额低于99重量%,基于水凝胶的总重量。
12.根据前述权利要求中任一项所述的水凝胶或用途,其特征在于,水凝胶不含由乙烯基吡咯烷酮、丙烯酸和/或甲基丙烯酸均聚或共聚得到的聚合物。
13.根据前述权利要求中任一项所述的水凝胶或用途,其特征在于,水凝胶含有一种或多种具有2至8个碳原子的短链多元醇。
14.根据权利要求13所述的水凝胶或用途,其特征在于,多元醇的份额为1至30重量%,优选地为2至23重量%,特别优选地为3至20重量%,基于水凝胶的总重量。
15.根据权利要求13或14所述的水凝胶或用途,其特征在于,具有2至8个碳原子的多元醇选自甘油、甲基丙二醇、丙二醇、1,2-己二醇、辛甘醇、丁二醇和戊二醇组成的组。
16.根据前述权利要求中任一项所述的水凝胶或用途,其特征在于,水凝胶含有1,2-己二醇,其中优选的是1,2-己二醇的份额为0.2至2重量%,优选地为0.5至1.5重量%,特别优选地为0.7至1.3重量%,基于水凝胶的总重量。
17.黄原胶和/或卡拉胶用于稳定具有脱氢黄原胶和水的水凝胶的粘度的用途。