CN1167457A - 皮肤接触部件 - Google Patents

皮肤接触部件 Download PDF

Info

Publication number
CN1167457A
CN1167457A CN95196527.1A CN95196527A CN1167457A CN 1167457 A CN1167457 A CN 1167457A CN 95196527 A CN95196527 A CN 95196527A CN 1167457 A CN1167457 A CN 1167457A
Authority
CN
China
Prior art keywords
shave
engaging member
skin engaging
agent
polystyrene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN95196527.1A
Other languages
English (en)
Other versions
CN1104312C (zh
Inventor
M·M·茨恩
尹玉岭
F·E·巴迪恩
T·T·恩都
B·A·罗杰斯
L·K·里姆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Gillette Co LLC
Original Assignee
Gillette Co LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US08/497,194 external-priority patent/US6298558B1/en
Application filed by Gillette Co LLC filed Critical Gillette Co LLC
Publication of CN1167457A publication Critical patent/CN1167457A/zh
Application granted granted Critical
Publication of CN1104312C publication Critical patent/CN1104312C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及用于剃须刀盒式组件和湿刮式修面系统的改进了的皮肤接触部件(64)。根据本发明的一个方面，提供了一种双组分、控制释放的修面部件，它是由(a)热塑性树脂制成的其上有一些开孔的护套层(72)和(b)内部装有修面助剂的芯区(70)组成。该部件可保持表面外观、控制释放修面助剂、使修面助剂的降解减少到最小并可防止修面助剂被截留在带中。此外，将低熔点的添加剂添加到修面助剂中是可行的，因而润滑带组合物中的修面助剂与修面助剂载体例如聚苯乙烯的相容性就变得不太关键。

Description

皮肤接触部件
本发明涉及用于剃须刀盒式组件和湿刮式修面系统的改进了的皮肤接触部件。本发明主要在于提供了接触皮肤的帽和/或防护面层，它们具有当剃须刀拖过皮肤时能释放修面助剂的结构。适宜的修面助剂包括润滑剂、胡须软化剂、剃须刀清洁剂、药剂、美容剂或其组合物。本发明还涉及生产本发明皮肤接触部件的新方法。
在湿刮式修面系统中，一些因素，例如剃须刀横过皮肤的摩擦阻力、切断毛发所需的力以及对原有皮肤损伤处的刺激都会引起一定程度的修面不适感。伴随着湿式修面系统的不适感和其他的问题可以通过将修面助剂涂覆在皮肤上而减轻。可以在修面之前、修面过程中或修面之后涂覆修面助剂。采用预涂或后涂修面助剂会伴随发生一些问题。预涂的修面助剂会蒸发或由于剃须刀的往复行程而使其从涂覆的部位带走。后涂的修面助剂在修面过程中并不存在于皮肤上，这样，它们就涂得太迟而不能防止不希望有的影响。预涂和后涂修面助剂都会使修面过程增加另外的步骤。
已有一些建议提出，将修面助剂例如润滑剂、胡须软化剂、剃须刀清洁剂、药剂、美容剂或其组合物装入剃须刀中，例如将修面助剂存放在剃须刀的凹槽内、将修面助剂直接包括在一个或多个剃须刀的模塑聚合物元件中、采用粘结的方式将修面助剂组合物固定在剃须刀上、以及采用机械将修面助剂组合物与剃须刀连接。如美国专利4,170,821(Booth)和5,113,585(Rogers)中所述，将水溶性的修面助剂例如聚氧化乙烯与非水溶性材料例如聚苯乙烯混合，以形成不溶性聚合物/可溶性修面助剂的组合物。在靠近单刀片或多刀片修面系统的修面刃口或一些刃口处，将该组合物装在剃须刀和修面盒式结构上。当与水接触时，水溶性的修面助剂会从组合物中浸出而涂在皮肤上。在前几次修面时上述组合物往往会释放出大量的修面助剂，而在随后修面时修面助剂显著地减少。此外，具有较大量修面剂材料(至多80％(重量))和较少量水不溶性基材(低至20％(重量))的挤出组合物强度较低，在组装和使用时易于机械损坏。随着增加不溶性基材的用量可使机械强度得到提高。然而，这样的提高会降低修面助剂材料的释放能力。
商品润滑带，特别是如美国专利4,170,821(Booth)和5,113,585(Rogers)中所述的聚氧化乙烯润滑剂含量高的润滑带往往在使用后性能变坏。在修面过程中，浸出率发生变化，通常大约有50％的聚氧化乙烯截留在润滑带中。Polyox载体(即非水溶性基材)的选择局限于具有低熔点或软化点且至少能部分与polyetheneoxide混溶的载体。此外，由于该润滑带是在约为180℃的高温下制成的，因此，一些添加剂例如香味剂和增塑剂均难以添加到润滑带中。
1989年10月10日颁发给Etheredge，III的美国专利4,872,263公开了一种由采用特定酸性皂浸渍过的多孔基质组成的润滑部件。采用水不溶性的有孔片材覆盖在浸渍过的基质上，尽力防止润滑剂冲蚀太快并对皮肤提供平和的“按摩”效果。这类润滑部件尚未获得商业上的成功。由于需要另外装配覆盖在基质上的片材结构，因而这类润滑部件的生产费用昂贵。当用粘结剂将其固定在剃须刀盒上时，它们往往还会溶胀和脱层。此外，这种柔软的多孔基质不适用于以经济的机械手段将润滑带固定在剃须刀盒上。
我们已证实，制作双组分、控制释放的修面部件是可行的，该部件由有一些孔的外表面层和含有修面助剂的内层组成。使用这种部件的潜在优点是1)可以保持均匀的表面外观，2)1-4次修面后达到接近零级释放修面助剂，3)使材料的降解减少到最低限度，4)使截留在该部件中的修面助剂材料减少到最低限度，5)提供一种易于生产的修面助剂部件和/或6)提供一种容易与剃须刀盒式系统集成的修面助剂部件。本发明的上述和其他的目的从下文中可以明显看出。
根据本发明的一个方面，提供了一种双组分、控制释放的修面部件，它是由(a)热塑性树脂制成的其上有一些孔的护套层和(b)内部装有修面助剂的芯区组成。该部件可以是带、剃须刀防护罩、剃须刀帽、剃须刀座或剃须刀套的形状，它可通过(1)共挤出或双色(即双组分)模塑，或(2)分别地挤出或模塑表面层和修面助剂然后再组装的方法制成。该部件可以保持表面外观、控制释放修面助剂、使修面助剂的降解减少到最低限度并可防止修面助剂被截留在带中。此外，将低熔点的添加剂添加到修面助剂中是可行的，因而润滑带组合物中的修面助剂与修面助剂carrie例如聚苯乙烯的相容性就变得不太关键。
图1是本发明的剃须刀组合件的透视图；
图2是沿图1中2-2线截取的剖面图；
图3是本发明的另一种剃须刀组合件的剖面图；
图4是本发明的皮肤接触部件的放大透视图；
图5是沿图4中3-3线截取的剖面图；
图6是可在图2中见到的皮肤接触部件42的剖面图；
图7是适用于生产图3的皮肤接触部件的挤出模具的剖面示意图；
图8-11是本发明另外的一些皮肤接触部件的放大透视图；
图12是通过常规的润滑带与本发明的润滑带比较而绘制的修面助剂释放率对理论修面次数的图。
参看这些附图，图1和图2中所示的修面组合件10包括由耐冲击性聚苯乙烯模塑的底或座部件12，它包括用以连接剃须刀柄的整体偶合槽结构14和限定横向延伸的前部接触皮肤的面层18的保护结构16。在座12的上表面上放置具有锐利刀刃22的钢制前置刀片20、具有锐利刀刃26的钢制后置刀片24以及使刀片20与24保持相互隔开的铝垫片件28。帽件30由耐冲击性聚苯乙烯模塑而成，它具有限定向前突出的端壁36之间横向延伸的后部接触皮肤的面层34以及具有放置在刀片刃口26后面的前刃口38的帽体部分32。整体的铆钉部分40从横向延伸的帽体部分32向下延伸并穿过刀片20和24、垫片28和座12的孔，将帽30、刀片20、24和垫片28固定在座12上。粘结固定在接触皮肤的面层34上的是皮肤接触部件42。
示于图3中的修面组合件50是美国专利4,586,255(Jacobson)中所示的类型，该专利引入本文作为参考，并包括具有前部54和后部56的实体52。弹性地固定在实体52上的是保护件58、前置刀片元件60和后置刀片元件62。将呈细长的插入件64形状的修面助剂组合物借助摩擦力锁定在后面部分56的开孔66中。
图4-6和图8-11-般地描绘了本发明的几种不同方案。本文中所用的术语“芯”指的是在剖面上可观察到的皮肤接触部件的内部。该芯通常是沿着轴贯穿皮肤接触部件。该轴不必是中心轴。图中的芯均以编号70表示。本发明的实施方案至少有一个芯元件。本文中所用的术语“护套”指的是芯材料70上的外覆盖层。图中的这些护套均以编号72表示。
本发明的双组分、控制释放的修面部件由围绕内芯的外护套组成，其中所述芯含有修面助剂例如水溶性聚合物和添加剂。接触皮肤的面层74可以是具有内在开孔的不溶性层，或柔软层例如在使用过程中会成为多孔的商品带(聚氧化乙烯/聚苯乙烯)。
再参看附图，特别是图3，图中示出了细长的皮肤接触部件64。部件64具有接触皮肤的面层74和细长的插入元件76。如图3所示，该插入件76设计成借助摩擦力固定在开孔中。此外，皮肤接触部件还包括被护套材料环绕的含有修面助剂的芯材料70。该护套材料包括至少一个孔以便将添加剂释放到皮肤上。优选该护套包括均匀地沿着接触皮肤的面层74分布的约3-30个孔，最优选10-15个孔。孔的直径随所选择的特定修面助剂而变化：然而，我们已观察到最佳的结果是孔直径约为0.020至约0.040英寸。优选孔直径约为0.035英寸。应该指出的是，这些孔不必是圆形的，且任何形状的孔均可满足需要。参看例如图7-11。沿着接触皮肤的面层上的微孔面积是重要的。优选微孔面积约为0.0005至约0.0250平方英寸。当芯中采用高含量的聚氧化乙烯润滑剂时，优选的微孔面积约为0.0125平方英寸。许多修面助剂在与水接触时往往会溶胀。通过将这些溶胀性的修面助剂结合在不溶性基材内，可改善其溶胀度以避免产生美学上令人不愉快的结果。最优选的孔型式示于图4-5。
修面助剂材料选自聚氧化乙烯、聚乙烯pyrrolideone、聚丙烯酰胺、羟丙基纤维素、聚乙烯咪唑啉、聚乙二醇、聚乙烯醇、聚甲基丙烯酸羟乙酯、硅酮共聚物、蔗糖硬脂酸酯、维生素E、皂类、表面活性剂类、泛酰醇、芦荟、增塑剂例如聚乙二醇；胡须软化剂；辅助润滑剂例如硅油、Teflon聚四氟乙烯粉末(DuPont生产)、和蜡；香精油例如薄荷醇、樟脑、丁子香酚、桉油醇、黄樟脑和水杨酸甲酯；增粘剂例如HerculesRegalrez 1094和1126；不挥发的凉爽剂、润肤剂与环糊精的包合配合物；香味剂；止痒剂/抗刺激剂材料；抗微生物的/角蛋白溶解剂材料例如间苯二酚；抗炎症剂例如Candilla蜡和甘草亭酸；止血剂例如硫酸锌；表面活性剂例如pluronic和iconol材料；相容剂例如苯乙烯-b-EO共聚物；及其组合物。这些修面助剂可以从面层释放以改善修面效果。这些组分分布在整个芯中，此外，外护套也可以含少量的这些修面助剂。
所述修面助剂优选的是水溶性的或水混溶性的材料；然而，只要非水溶性的添加剂能随着水溶性芯组分带出，也可以掺入。
优选的修面助剂包括润滑性的水溶性聚合物。这类水溶性聚合物优选包括芯材料重量的至少50％，更优选至少60％。更优选的水溶性聚合物是通常称为POLYOX(可从Union Carbide Corporation买到)或ALKOX(可从Meisei Chemical Works，Kyoto，Japan买到)的聚氧化乙烯。这些聚氧化乙烯的分子量优选约为100,000-6百万，最优选约为300,000-5百万。最优选的聚氧化乙烯包括约40-80％的平均分子量约为5百万的聚氧化乙烯(例如POLYOX COAGULANT)和约60-20％的平均分子量约为300,000的聚氧化乙烯(例如POLYOX WSR-N-750)的掺合物。该聚氧化乙烯掺合物也可以有利地含至多约10％(重量)的低分子量(即，MW＜10,000)的聚乙二醇例如PEG-100。
修面助剂也可以有利地包括不挥发的凉爽剂或润肤剂与环糊精的包合配合物，其用量优选至多为芯材料重量的约25％，最优选为10-20％。
不挥发的凉爽剂指的是对皮肤有生理上的凉爽作用且其挥发性显著低于薄荷醇的试剂。优选的不挥发的凉爽剂是，当进行热重分析时(例如采用DuPont生产的951热重分析仪，每分钟升温20℃)，在160℃的温度下能保留其起始重量的至少50％，更优选在160℃的温度下能保留其起始重量的至少80％，最优选在175℃的温度下能保留其起始重量的至少50％的那种凉爽剂。
可利用的适宜凉爽剂包括不挥发的薄荷醇类似物例如乳酸酯、乙氧基乙酸酯、酮甘油缩醛、3-1-氧基丙烷-1，2-二醇、碳酸乙基1-基酯、(1S，3S，4R)-p--8-烯-3-醇、基吡咯烷酮羧酸酯、N-取代的-p-烷-3-羧酰胺类(如美国专利4,136,163中所述，该专利引入本文作为参考)包括例如N-乙基-p-烷-3-羧酰胺、具有下式的无环羧酰胺
Figure A9519652700091
式中R和R”，当其分开时，各自为氢、C1-C5烷基或C1-C8羟烷基且提供的碳原子总数不大于8个，但是，当R是氢时R”也可以是至多6个碳原子的烷基羧烷基；R和R”，当其合在一起时，代表至多6个碳原子的亚烷基，从而形成一个氮杂环，该亚烷基链可任选被氧间断；R1是氢或C1-C5烷基；而R2和R3各自为C1-C5烷基(美国专利4,153,679中对这种无环羧酰胺作了介绍，该专利引入本文作为参考)包括例如N，2，3-三甲基-2-异丙基丁酰胺，以及缩酮凉爽剂(如WO 93/23005中所述，该专利引入本文作为参考)包括例如1-酮-/d-异薄荷酮甘油缩酮。
可用于环糊精包合配合物中的适宜的润肤剂包括薄荷醇、樟脑、丁子香酚、桉油醇、黄樟脑和水杨酸甲酯以及上述的薄荷醇类似物。任何适宜的环糊精均可用来形成包合配合物，包括α-环糊精、β-环糊精、γ-环糊精和改性的环糊精例如羟丙基-β-环糊精、甲基-β-环糊精以及乙酰基-β-环糊精。优选的环糊精是β-环糊精和γ-环糊精。
当修面助剂包括环糊精包合配合物时，芯材料也可以有利地包括至多约10％、优选约2-7％(重量)的置换剂，在与水接触时，该置换剂能将润肤剂从包合配合物中置换出来，从而在使用时增进润肤剂从芯材料中的释放。该置换剂是一种能与环糊精形成较之与润肤剂形成的配合物更稳定的配合物的材料，因此，当修面助剂与水接触时它能将润肤剂从该配合物中置换出来。适宜的置换剂包括表面活性剂、苯甲酸以及某些胺类(例如尿素)。
关于上述凉爽剂、环糊精包合配合物和置换剂的进一步细节可参阅以下共同未决的美国专利申请，这些专利申请所公开的内容均引入本文作为参考：1995年6月30日提交的Docket No.7995，题为”具有润肤剂和环糊精的包合配合物的修面助剂组合物”(Shaving Aid Composite WithAn Inclusion Complex Of A Skin-Soothing Agent And A Cyclodextrin)；和1995年6月30日提交的Docket No.7995，题为”具有不挥发性凉爽剂的修面助剂组合物”(Shaving Aid Composite With A Non-VolatileCooling Agent)。
该芯材料包括约0％至约50％(重量)、优选0％至约20％的水不溶性基材和约50％至约100％(重量)、优选约80％至约100％的修面助剂材料。适宜的水不溶性基材包括例如耐纶、乙烯-乙酸乙烯酯(EVA)、聚乙烯、聚丙烯、聚氨酯、聚苯乙烯、聚苯乙烯-丁二烯、聚缩醛、多酚/聚苯乙烯掺合物(例如NOREL牌的聚合物)及其组合物。
护套材料必须具有足够的机械强度和刚性，以便为整个皮肤接触部件在开始制成时和大量水不溶性材料已从皮肤接触部件浸出之后，提供相当的机械强度。优选该护套区包含至少35％、最优选至少40％(重量)的水不溶性聚合物，特别是热塑性树脂。适用于本发明的护套材料包括聚苯乙烯、耐冲击性聚苯乙烯(聚苯乙烯-丁二烯)、聚丙烯、填充聚丙烯、聚乙烯、耐纶以及例如70％耐纶/30％聚氧化乙烯、60％聚苯乙烯/40％聚氧化乙烯的掺合物。优选的护套材料是耐冲击性聚苯乙烯、聚苯乙烯、乙烯-乙酸乙烯酯(EVA)及其组合物。除了水不溶性聚合物之外，护套区也可以包含一些水溶性聚合物，例如聚氧化乙烯，但是，为了保持护套区的结构完整性，其含量通常不大于约65％(重量)，优选小于60％(重量)。护套材料可任选包含添加剂例如润滑剂或增塑剂、填料例如CaCO3和着色剂例如TiO2。
在本发明的一个实施方案中，当护套材料和芯材料由完全不同的着色材料(例如白色的护套和蓝色的芯)组成时，可以产生指示磨损量的效果。通过使用，芯材料从皮肤接触部件中浸出出来。随着充分使用，芯内的着色区会浸出。通过沿着接触皮肤的面层检查释放孔，为用户提供一种指示，即修面组合件和/或接触皮肤的面层已达到其有效寿命。在一个优选的实施方案中，该芯材料由白色的聚氧化乙烯/聚苯乙烯的混合物组成，而护套由已用靛蓝，FD&C#2染料着色的耐纶和/或苯乙烯组成。
根据本发明，可以采用粘合剂例如Loctite Super Bonder 499、采用机械的锁紧机构、采用热焊接或其组合方法将皮肤接触部件固定。
该部件可以是由双色(双组分)模塑或共挤出而制得的带，或通过分别地挤出或模塑表层和修面助剂然后再组装。然后，可将该部件粘结或咬合在剃须刀盒上。该部件也可以是通过双色模塑而制成的剃须刀帽、座或套。例如，1)有孔的表面可通过模塑或双色模塑制成，和2)有导槽的表面可以通过模塑制成。挤出和共挤出方法是优选的，因为它们所需的资金和熟练工较少。当共挤出该带时，必须在接触皮肤的面层打孔。采用以下任一种方法将这些孔打在护套上：钻孔、激光、水力喷射、雕刻或刺孔。必须在不同的挤出机筒体温度下加工修面助剂和表层以使材料的降解减小到最低限度。为了易于将包括液体和粉末的功能性添加剂掺入修面助剂中，应考虑将双螺杆挤出机当成是用于挤出和共挤出方法的单螺杆挤出机的代替物。最佳的护套材料具有坚硬到适中硬度的表面。
优选的皮肤接触部件采用共挤出法生产，从而至少在接触皮肤的面层74上有一个护套。护套和芯的聚合物材料的性质和相对比例是这样，使得皮肤接触部件在开始制成时和大量水溶性材料已浸出之后仍具有足够的强度，水溶性材料的量在刀片和一些刀片的总预期寿命中足以提供有效的修面辅助例如润滑作用。护套材料的作用不仅可以提供附加的刚性而且还可计量供给修面助剂。在例如美国专利5,063,667；5,095,619；和5,113,585中所述的常规皮肤接触部件中，大量的修面助剂材料被截留在不溶性基质中。随着增加修面助剂的浓度，可使其增加扩散并达到更有效的传递。此外，如果将不溶性基质添加到芯材料中也可以提供一定的附加机械强度。
图7是沿着适用于生产本发明的皮肤接触部件的挤出机长度的剖面示意图。通过挤出螺杆、热熔或其他的手段将芯材料送进挤入模具51。在芯进口52中，紧束芯的孔53与护套材料相遇，在模具材料流道的横断面上可观察到该芯在那里被护套材料包封。然后，被包封的芯前进到模具出口55处，连续的皮肤接触部件可在该处固化和/或收缩以便提供适宜的尺寸。关于共挤出技术的一般讨论参见Levi，Plastics ExtrusionTechnology Handbook，Industrial Press Inc.，第168-188页(1981)，该文献引入本文作为参考。在连续的皮肤接触部件产生后，将该线材送去进一步加工，通常在该处收缩到合适的尺寸并切割成适合于安放在剃须刀盒体中的长度。可以采用刀刃切割、激光或水力喷射实现切割。本发明的接触皮肤的面层通常是矩形的，其宽度约为0.05英寸至约0.1英寸，长度约为1.2英寸。
双组分部件可以使修面助剂在较低的温度下加工以减少材料的降解。例如，聚氧化乙烯可在低于常规的带，即不溶性基质润滑带中的聚氧化乙烯所需的温度下加工。修面助剂可以由水溶性聚合物例如聚氧化乙烯、聚乙二醇和聚乙烯醇等制成。可以容易地将添加剂例如香料、增湿剂、维生素E以及增塑剂等添加到修面助剂中。只要添加剂可以通过面层的开孔带出，它们也可以是水不溶性材料。虽然挤出法是优选的，但是也可以将修面助剂模塑或挤出。
修面助剂的浸出率取决于面层的厚度、开孔的数量和形状以及表面结构(多孔的或非多孔的)。该面层也可制成可拆卸的以便在使用时能将修面助剂添加到该部件中。
申请人认为等效的实施方案是本发明的一部分。例如，可能被采用的非矩形(例如椭圆形)接触皮肤的面层区和可能被采用的非平面的面层型式。本发明也关注这些或其他的等效实施方案。本发明以及有关制作和使用的方法从以下实施例将是显而易见的。
                 实施例1-8
将例如表1中所列的修面助剂大约在表中所示的温度下共挤出到具有图7中所示横截面的装置中。在小于2％的收缩后，典型的完工宽度为1/8英寸。这些装置不需要另外组装。共挤出生产线包括两个3/4”的HBI System 90挤出机(Haake生产)和一个共挤出模具。共挤出后的部件面层由所示的挤出机筒体温度下的混合物制成，而修面助剂由所示材料制成。用直径为0.030英寸的钻头将孔钻成图4中图形的型式。用刀刃切割器切割成1.25英寸长、每条带上有13个孔的成品带。
典型的加工条件
温度(℃)：
区段             1   2    3    4    5
挤出机1(内部)  130  180  180  180  180
挤出机2(外部)  150  180  180  180  180
转子转速：
挤出机1        42rpm
挤出机2        48rpm
线速度：       约为15-20英尺/分钟
表11.  外层  50％  耐冲击性聚苯乙烯(Mobil 4324)
      40％  聚氧化乙烯掺合物：
            3份POLYOX WSR Coagulant(MW 5,000,000)(续表1)
          2份POLYOX WSR N-750(MW 300,000)
          (两者均由Union Carbide Corp.Danbury，CT生产)
    10％  聚乙二醇MW＝4500(Dow 4500)
内层88％  聚氧化乙烯掺合物：
          3份POLYOX WSR Coagulant(MW 5,000,000)
          2份POLYOX WSR N-750(MW 300,000)
          (两者均由Union Carbide Corp.Danbury，CT生产)
    10％  聚乙二醇MW＝4500(Dow 4500)
     2％  绿色着色剂2.  外层40％  耐冲击性聚苯乙烯(Mobil 4324)
    50％  聚氧化乙烯掺合物：
          3份POLYOX WSR Coagulant(MW 5,000,000)
          2份POLYOX WSR N-750(MW 300,000)
          (两者均由Union Carbide Corp.Danbury，CT生产)
    10％  聚乙二醇MW＝4500(Dow 4500)
内层88％  聚氧化乙烯掺合物：
          3份POLYOX WSR Coagulant(MW 5,000,000)
          2份POLYOX WSR N-750(MW 300,000)
          (两者均由Union Carbide Corp.Danbury，CT生产)
    10％  聚乙二醇MW＝4500(Dow 4500)
     2％  绿色着色剂3.  外层37％  耐冲击性聚苯乙烯(Mobil 4324)
    53％  聚氧化乙烯掺合物：
          3份POLYOX WSR Coagulant(MW 5,000,000)
          2份POLYOX WSR N-750(MW 300,000)
          (两者均由Union Carbide Corp.Danbury，CT生产)
    10％  聚乙二醇MW＝4500(Dow 4500)
内层90％  聚氧化乙烯掺合物：(续表1)
          3份POLYOX WSR Coagulant(MW 5,000,000)
          2份POLYOX WSR N-750(MW 300,000)
          (两者均由Union Carbide Corp.Danbury，CT生产)
    10％  聚乙二醇MW＝4500(Dow 4500)4.  外层35％  耐冲击性聚苯乙烯(Mobil 4324)
    50％  聚氧化乙烯掺合物：
          3份POLYOX WSR Coagulant(MW 5,000,000)
          2份POLYOX WSR N-750(MW 300,000)
          (两者均由Union Carbide Corp.Danbury，CT生产)
     8％  聚乙二醇MW＝4500(Dow 4500)
     7％  Salsorb 88，交联的聚丙烯酸钠(Allied)
内层88％  聚氧化乙烯掺合物：
          3份POLYOX WSR Coagulant(MW 5,000,000)
          2份POLYOX WSR N-750(MW 300,000)
          (两者均由Union Carbide Corp.Danbury，CT生产)
    10％  聚乙二醇MW＝4500(Dow 4500)
     2％  绿色着色剂5.  外层33％  耐冲击性聚苯乙烯(Mobil 4324)
    56％  聚氧化乙烯掺合物：
          3份POLYOX WSR Coagulant(MW 5,000,000)
          2份POLYOX WSR N-750(MW 300,000)
          (两者均由Union Carbide Corp.Danbury，CT生产)
     7％  聚乙二醇MW＝4500(Dow 4500)
     4％  Salsorb 88，交联的聚丙烯酸钠(Allied)
内层90％  聚氧化乙烯掺合物：
          3份POLYOX WSR Coagulant(MW 5,000,000)
          2份POLYOX WSR N-750(MW 300,000)(续表1)
          (两者均由Union Carbide Corp.Danbury，CT生产)
    10％  聚乙二醇MW＝4500(Dow 4500)6.  外层40％  耐冲击性聚苯乙烯(Mobil 4324)
    50％  聚氧化乙烯掺合物：
          3份POLYOX WSR Coagulant(MW 5,000,000)
          2份POLYOX WSR N-750(MW 300,000)
          (两者均由Union Carbide Corp.Danbury，CT生产)
    10％  聚乙二醇MW＝4500(Dow 4500)
内层73％  聚氧化乙烯掺合物：
          3份POLYOX WSR Coagulant(MW 5,000,000)
          2份POLYOX WSR N-750(MW 300,000)
          (两者均由Union Carbide Corp.Danbury，CT生产)
    10％  聚乙二醇MW＝4500(Dow 4500)
    15％  酮甘油缩醛(Frescolat MGA)
     2％  绿色着色剂7.  外层40％  耐冲击性聚苯乙烯(Mobil 4324)
    50％  聚氧化乙烯掺合物：
          3份POLYOX WSR Coagulant(MW 5,000,000)
          2份POLYOX WSR N-750(MW 300,000)
          (两者均由Union Carbide Corp.Danbury，CT生产)
    10％  聚乙二醇MW＝4500(Dow 4500)
内层78％  聚氧化乙烯掺合物：
          3份POLYOX WSR Coagulant(MW 5,000,000)
          2份POLYOX WSR N-750(MW 300,000)
          (两者均由Union Carbide Corp.Danbury，CT生产)
    10％  聚乙二醇MW＝4500(Dow 4500)
    10％  N-乙基-p-烷-3-羧酰胺(WS-3)
     2％  绿色着色剂(续表1)8.  外层40％    耐冲击性聚苯乙烯(Mobil 4324)
    50％    聚氧化乙烯掺合物：
            3份POLYOX WSR Coagulant(MW 5,000,000)
            2份POLYOX WSR N-750(MW 300,000)
            (两者均由Union Carbide Corp.Danbury，CT生产)
    10％    聚乙二醇MW＝4500(Dow 4500)
内层73％    聚氧化乙烯掺合物：
            3份POLYOX WSR Coagulant(MW 5,000,000)
            2份POLYOX WSR N-750(MW 300,000)
            (两者均由Union Carbide Corp.Danbury，CT生产)
    10％    聚乙二醇MW＝4500(Dow 4500)
    15％    γ-环糊精/薄荷醇包合配合物
     2％    绿色着色剂
实施例9和10对照：
根据美国专利5,113,585(Rogers)中所述的一般方法制备外形尺寸类似于图4-5的常规润滑带。该带的配方如下：9.    33.5％  耐冲击性聚苯乙烯(Mobil 4324)
    55％  聚氧化乙烯掺合物：
          3份POLYOX WSR Coagulant(MW 5,000,000)
          2份POLYOX WSR N-750(MW 300,000)
          (两者均由Union Carbide Corp.Danbury，CT生产)
    10％  聚乙二醇MW＝4500(Dow 4500)
   1.5％  可混溶的添加剂和着色剂本发明：
根据实施例1-5中所述的一般方法制备本发明的润滑带。该带的配方如下：10.外层33.5％  耐冲击性聚苯乙烯(Mobil 4324)
     55％  聚氧化乙烯掺合物：
           3份POLYOX WSR Coagulant(MW 5,000,000)
           2份POLYOX WSR N-750(MW 300,000)
           (两者均由Union Carbide Corp.Danbury，CT生产)
     10％  聚乙二醇MW＝4500(Dow 4500)
    1.5％  可混溶的添加剂和着色剂
 内层85％  聚氧化乙烯掺合物：
           3份POLYOX WSR Coagulant(MW 5,000,000)
           2份POLYOX WSR N-750(MW 300,000)
           (两者均由Union Carbide Corp.Danbury，CT生产)
      5％  聚乙烯醇
      8％  聚乙二醇MW＝4500(Dow 4500)
      2％  可混溶的添加剂和着色剂
在一些模拟实验室条件下修面试验的过程中监测该部件的失重(干基)。我们认为，这些实验室条件下的试验值与在自然条件下修面的平均值相关性很好。这些结果如图12所描绘。图中示出，在实施例10中在第四次修面后，按接近零级释放曲线连续传递治疗量的润滑剂。然而，在实施例9(对照)中提供的含量很低。

Claims (16)

1.一种用于湿刮式修面系统的皮肤接触部件，该部件包括：
由热塑性树脂组成的细长的护套区；和
贯穿所述护套区轴向延伸的含有修面助剂的芯区，其中所述护套区还包括许多便于在修面过程中释放修面助剂的开孔。
2.根据权利要求1的皮肤接触部件，其中所述护套区还包括沿着护套区的至少一个外表面层延伸的细长的接触皮肤的面层。
3.根据权利要求2的皮肤接触部件，其中所述修面助剂包括选自聚氧化乙烯、聚乙烯吡咯烷酮、聚丙烯酰胺、羟丙基纤维素、聚乙烯咪唑啉、聚乙二醇、聚乙烯醇、聚甲基丙烯酸羟乙酯、硅酮共聚物、蔗糖硬脂酸酯、维生素E、皂类、表面活性剂类、泛酰醇、芦荟、香精油、增塑剂、胡须软化剂；辅助润滑剂、聚四氟乙烯粉末、蜡；薄荷醇、丁子香酚、桉油醇、黄樟脑和水杨酸甲酯；增粘剂；不挥发的凉爽剂；润肤剂与环糊精的包合配合物；香味剂；止痒剂/抗刺激剂材料；抗微生物的/角蛋白溶解剂材料；抗炎症剂；止血剂；相容剂及其组合物的材料。
4.根据权利要求3的皮肤接触部件，其中所述芯区包括0％至约50％(重量)的水不溶性基材，该基材选自耐纶、乙烯-乙酸乙烯酯、聚乙烯、聚丙烯、聚氨酯、聚苯乙烯、聚苯乙烯-丁二烯、聚缩醛、多酚/聚苯乙烯掺合物及其组合物。
5.根据权利要求4的皮肤接触部件，其中所述开孔具有约为0.0005至约0.0250平方英寸的微孔面积。
6.根据权利要求5的皮肤接触部件，该部件包括约3至约30个直径约为0.020至约0.040英寸的圆形孔。
7.根据权利要求6的皮肤接触部件，其中所述护套区包括选自聚苯乙烯、耐冲击性聚苯乙烯、聚丙烯、填充聚丙烯、聚乙烯、耐纶及其掺合物的热塑性树脂。
8.根据权利要求7的皮肤接触部件，其中所述护套区包括选自耐冲击性聚苯乙烯、聚苯乙烯、乙烯-乙酸乙烯酯及其组合物的热塑性树脂。
9.根据权利要求8的皮肤接触部件，其中所述护套区和芯区由不同颜色的材料制成，这样当芯的颜色失去时就给用户提供其上固定有皮肤接触部件的剃须刀的基本寿命的指示。
10.一种湿刮式的修面系统，该系统包括刀片部件和靠近该刀片部件修面刃口的、限定外部皮肤接触部件的结构，所述皮肤接触部件与权利要求1-9中任一项的定义相同。
11.根据权利要求10的修面系统，其中所述芯区包括至多25％(重量)的不挥发的凉爽剂。
12.根据权利要求11的修面系统，其中所述凉爽剂选自乳酸酯、乙氧基乙酸酯、酮甘油缩醛、3-1-氧基丙烷-1，2-二醇、碳酸乙基1-基酯、(1S，3S，4R)-p--8-烯-3-醇、基吡咯烷酮羧酸酯、N-乙基-p-烷-3-羧酰胺以及N，2，3-三甲基-2-异丙基丁酰胺。
13.根据权利要求10的修面系统，其中所述芯区包括至多25％(重量)的润肤剂与环糊精的包合配合物。
14.根据权利要求13的修面系统，其中所述润肤剂选自薄荷醇、樟脑、乳酸酯、乙氧基乙酸酯、酮甘油缩醛、3-1-氧基丙烷-1，2-二醇、碳酸乙基1-基酯、(1S，3S，4R)-p--8-烯-3-醇、基吡咯烷酮羧酸酯、N-乙基-p-烷-3-羧酰胺以及N，2，3-三甲基-2-异丙基丁酰胺。
15.根据权利要求13的修面系统，其中所述芯区还包括至多约为10％(重量)的置换剂，在与水接触时，该置换剂能将润肤剂从包合配合物中置换出来。
16.根据权利要求10、11或13的修面系统，其中所述护套区包括至少35％(重量)的聚苯乙烯或耐冲击性聚苯乙烯而所述芯区包括至少50％(重量)的聚氧化乙烯。
CN95196527A 1994-10-31 1995-10-24 包括提供修面助剂用的皮肤接触部件的修面盒 Expired - Fee Related CN1104312C (zh)