CN116726981A - 封装有纳米金属原子的sba分子筛及其制备方法以及在制备环己酮和环己醇中的应用 - Google Patents
封装有纳米金属原子的sba分子筛及其制备方法以及在制备环己酮和环己醇中的应用 Download PDFInfo
- Publication number
- CN116726981A CN116726981A CN202210210290.7A CN202210210290A CN116726981A CN 116726981 A CN116726981 A CN 116726981A CN 202210210290 A CN202210210290 A CN 202210210290A CN 116726981 A CN116726981 A CN 116726981A
- Authority
- CN
- China
- Prior art keywords
- molecular sieve
- sba
- solution
- metal
- atom
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种封装有纳米金属原子的SBA分子筛及其制备方法以及在制备环己酮和环己醇中的应用。封装有纳米金属原子的SBA分子筛,其中,金属原子以单质形式存在于SBA分子筛内。纳米金属原子封装在SBA分子筛的制备方法包括以下步骤:1)将SBA分子筛原粉与钝化剂混合进行第一反应,然后与碱性溶液混合进行第二反应,过滤、洗涤,并与金属络合物溶液进行混合,得到溶液A;2)将有机模板剂、水、酸和硅源混合成胶,得到溶液B;3)将所述溶液A与所述溶液B混合并进行水热晶化,过滤、洗涤、干燥和焙烧。本发明的催化剂具有更优的催化剂性能。采用该方法制备的分子筛中,纳米粒子均在分子筛孔道中,进而能够提高催化剂的催化性能。
Description
技术领域
本发明涉及一种纳米金属原子封装在SBA分子筛的制备方法,得到的封装有纳米金属原子的SBA分子筛,以及在制备环己酮和环己醇中的应用。
背景技术
自Mobil公司1992年第一次成功合成规整的MCM-41以来,介孔材料在吸附剂、催化剂和催化剂载体方面表面出了很多潜在的应用价值。在1998年,赵东元第一次成功合成了比M41S分子筛具有更大比表面积、规则的孔径分布、更厚的孔壁以及更好的热稳定性的新型介孔材料SBA-15和SBA-16,这种材料在催化剂方面显示出了更大的应用价值。与常规的M41S系列分子筛相比,三维孔道能够使反应物更加容易的进入到分子筛内部进行反应,而不至于引起分子筛孔道的堵塞。然而纯硅的SBA分子筛本身不带有任何酸性、碱性和氧化还原中心,其表面仅存在一种官能团-硅羟基(Si-OH),很大程度上限制了其在某些领域的应用。近年来,将杂原子引入到介孔分子筛中以提高其的酸性和稳定性引起了越来越多的关注。几乎所有的过渡金属和主族元素都可以通过水热合成法和浸渍法引入分子筛中,作为催化活性中心来提高分子筛的催化活性。在这些杂原子中,钒原子和钛原子作为一种变价金属在氧化还原反应中表现出了优异的催化性能,尤其是对环己烷的选择性氧化制备环己酮和环己醇的催化反应中具有很好的催化性能,钒催化剂的活性和钒原子的含量及结合状态有直接的关系。
金属纳米粒子催化剂可用于生产精细化学品、改进燃料、制氢、利用太阳能和消除污染物等。然而,在某些高温反应中,金属粒子往往会发生颗粒聚集,或因为金属浸出而失活。为解决金属纳米粒子稳定性的问题,人们付出了很大的努力,包括加强金属-负载物之间相互作用、添加促进剂和调整金属粒子的直径或形貌等。金属纳米粒子在分子筛中的包覆主要可分为两种策略:后合成法和原位约束法。后合成策略是指在完成沸石结构构建后引入金属纳米粒子。相比之下,原位约束法需要沸石和金属前驱体的共结晶,并通过原位还原得到金属纳米粒子。
原位约束法是金属纳米粒子或前驱体可以通过一步水热合成法引入到分子筛晶体内部。该方法首先将合成的金属纳米粒子或可溶性金属前驱体与分子筛的合成凝胶混合,然后进行高温晶化。合成的产物经进一步煅烧去除有机物,在还原剂下还原生成金属纳米粒子。该方法简单有效,但是由于金属颗粒要比分子筛孔道大,因此在还原的过程中,被还原的金属会撑大分子筛的孔道结构,造成分子筛本身结构发生破坏从而导致催化剂催化效果降低。后合成法由于具有不限制分子筛骨架种类的优点,而被广泛应用。通过分子筛载体在金属胶体或可溶性金属前驱体中浸渍,可以使金属纳米粒子进入分子筛内部的孔道中。但此方法实际上金属纳米粒子大部分都在分子筛表面而很少一部分才能进入分子筛的孔道中,从而发挥不出金属纳米粒子的催化作用。
发明内容
针对现有技术存在的上述问题,本发明提供一种新的纳米金属原子封装在SBA分子筛的制备方法,采用该方法制备的分子筛中,纳米粒子均在分子筛孔道中,进而能够提高催化剂的催化性能。具体地,本方法先使用钝化剂将SBA分子筛外表面的硅羟基进行钝化处理,这些经过钝化处理的外表面在碱性物质的作用下不会发生脱硅反应,从而起到保护SBA分子筛外表面的作用,而后碱性物质进行分子筛孔道内部发生脱硅反应,在形成了新的介孔和大孔孔道,然后将金属粒子嵌入到分子筛的孔道中,根据分子筛孔道的大小随时调控金属纳米粒子的大小,最后利用二次晶化将被碱性物质刻蚀的外孔道进行封装,从而利用了分子筛孔道中的限域作用而不发生团聚。
本发明第一方面提供了一种封装有纳米金属原子的SBA分子筛,其中,金属原子以单质形式存在于SBA分子筛内。
在本发明中,例如但不限于,可以通过XPS测定,钒原子的XPS为512eV,钛原子的XPS为454eV,可以证明金属原子仅以单质形式存在于SBA分子筛内,而不存在氧化物形式。而且仅存在于SBA分子筛内部,而不存在于SBA分子筛的表面。如果存在氧化物形式或存在于SBA分子筛表面,则钒原子的XPS为524.5eV,钛原子的XPS为458.5eV。
根据本发明所述的分子筛的一些实施方式,优选地,所述金属原子为钒原子和/或钛原子。
根据本发明所述的分子筛的一些实施方式,优选地,当金属原子为钒原子时,钒原子的XPS为512eV。
根据本发明所述的分子筛的一些实施方式,优选地,当金属原子为钛原子时,钛原子的XPS为454eV。
根据本发明所述的分子筛的一些实施方式,优选地,所述封装有纳米金属原子的SBA分子筛的比表面积为940~1100m2/g。本发明的封装有纳米金属原子的SBA分子筛具有更大的比表面积,进而能够提高转化率和选择性。
根据本发明所述的分子筛的一些实施方式,优选地,所述封装有纳米金属原子的SBA分子筛中的金属纳米粒子大小可控制在5~50nm。
本发明第二方面提供了一种纳米金属原子(M)封装在SBA分子筛的制备方法,包括以下步骤:
1)将SBA分子筛原粉与钝化剂混合进行第一反应,然后与碱性溶液混合进行第二反应,过滤、洗涤,并与金属络合物溶液进行混合,得到溶液A;
2)将有机模板剂、水、酸和硅源混合成胶,得到溶液B;
3)将所述溶液A与所述溶液B混合并进行水热晶化,过滤、洗涤、干燥和焙烧。
根据本发明所述的制备方法的一些实施方式,优选地,所述钝化剂包括通式RaRbRcSiRd所示的有机硅烷,其中,Ra、Rb、Rc和Rd相同或不同,各自独立地选自氢、卤素、C1-C20的烷基、C1-C20的烷氧基、C3-C20的环烷基、C6-C20的芳基和C1-C20的卤代烷基中的任意一种,且Ra、Rb、Rc和Rd不同时为氢和/或卤素;优选地,Rd为卤素,Ra、Rb和Rc不同时为氢和/或卤素;所述钝化剂进一步优选选自二苯基二氯硅烷、三甲基氯硅烷和二甲基二氯硅烷中的至少一种。
根据本发明所述的制备方法的一些实施方式,优选地,所述钝化剂与分子筛原粉的重量比为4:5~1:10,优选为3:5~1:10,进一步优选为3:7~1:9。
根据本发明所述的制备方法的一些实施方式,优选地,所述SBA分子筛为SBA-15分子筛和/或SBA-16分子筛。
根据本发明所述的制备方法的一些实施方式,优选地,在所述碱性溶液中,碱的含量为1~5重量%。
根据本发明所述的制备方法的一些实施方式,优选地,所述碱性溶液为氢氧化钠溶液。
根据本发明所述的制备方法的一些实施方式,优选地,所述碱性溶液与分子筛原粉的重量比为1:20~1:10,优选为3:50~2:25。
根据本发明所述的制备方法的一些实施方式,优选地,所述金属络合物溶液包括金属原子源以及能与所述金属原子源络合的溶液,其中,所述金属为钒和/或钛,所述金属原子源为含钒源的草酸溶液和/或钛源。
根据本发明所述的制备方法的一些实施方式,优选地,所述钒源选自偏钒酸铵、正钒酸钠和焦钒酸钠中的至少一种。
根据本发明所述的制备方法的一些实施方式,优选地,草酸与钒源的摩尔比大于2。例如2.5:1、3:1、3.5:1、4:1、4.5:1、5:1、10:1、20:1、50:1等。
根据本发明所述的制备方法的一些实施方式,优选地,所述钛源选自钛酸四丁酯、四氯化钛和硫酸钛中的至少一种。
根据本发明所述的制备方法的一些实施方式,优选地,所述能与所述金属原子源络合的溶液选自柠檬酸、酒石酸和三乙醇中的至少一种。
根据本发明所述的制备方法的一些实施方式,优选地,在金属络合物溶液中,金属原子源的含量不大于8重量%。
根据本发明所述的制备方法的一些实施方式,优选地,所述金属络合物溶液与分子筛原粉的重量比为0.5~1:5。
根据本发明所述的制备方法的一些实施方式,优选地,所述第一反应的条件包括:温度为50~80℃,优选为60~70℃;时间为2~6h,优选为3~5h。
根据本发明所述的制备方法的一些实施方式,优选地,所述第二反应的条件包括:温度为20~40℃,时间为1~2h。
根据本发明所述的制备方法的一些实施方式,优选地,所述有机模板剂R双亲性非离子三嵌段表面活性剂,优选为F127(EO106PO70EO106)、F108(EO132PO50EO132)、六亚甲基四胺(HMTA)、P123(EO20PO70EO20)和P104(EO27PO61EO27)中的至少一种。更优选地,当所制备分子筛为SBA-15时,有机模板剂R选自P123和/或P104;当所制备分子筛为SBA-16时,有机模板剂R选自F127、F108和HMTA中的至少一种。
根据本发明所述的制备方法的一些实施方式,优选地,所述硅源选自白炭黑、正硅酸乙酯、硅酸钠和硅溶胶的至少一种。优选为正硅酸乙酯。
根据本发明所述的制备方法的一些实施方式,优选地,所述酸选自盐酸、硫酸和硝酸中的至少一种,优选为盐酸。
根据本发明所述的制备方法的一些实施方式,优选地,所述溶液B满足以摩尔计,SiO2:a H2O:b R:c H+,其中,R为有机模板剂,a的值为80~200,优选为100~160;b的值为0.005~0.030,优选为0.010~0.025;c的值为0.10~0.25,优选为0.15~0.20。在本发明中,硅源以SiO2计,钒源以V计,钛源以Ti计,酸以H+计,溶剂以H2O计,有机模板剂以R计。
根据本发明所述的制备方法的一些实施方式,优选地,所述水热晶化的条件包括:温度为80~130℃,优选为90~120℃;时间为24~90h,优选为40~70h。
根据本发明所述的制备方法的一些实施方式,优选地,所述干燥的条件包括:温度为100~140℃,优选为110~130℃;时间为4~6h。通过干燥,除去分子筛表面的水分和有机模板剂。
根据本发明所述的制备方法的一些实施方式,优选地,所述焙烧的条件包括:温度为400~700℃,优选为500~600℃;焙烧时间为5~8h。通过焙烧,除去分子筛孔道内有机模板剂和水分,增加分子筛骨架强度等。
根据本发明所述的制备方法的一些具体实施方式,优选地,纳米金属原子(M)封装在SBA分子筛的制备方法包括但不限于以下步骤:
(1)将SBA分子筛粉与钝化剂在一定温度下搅拌一段时间,然后将碱性溶液加入所得产物中,在常温下反应一段时间后,将产物过滤、洗涤,随后将洗涤后的产物与金属络合物溶液进行混合即为A;
(2)将有机模板剂、水、酸和硅源混合成胶,所得到反应混合物的摩尔比为SiO2:aH2O:b R:c H+,其中,R为有机模板剂,a的值为80~200,b的值为0.005~0.030,c的值为0.10~0.25,此时混合后的溶液即为B;
(3)将B加入A中并在一定晶化温度下水热晶化一段时间,将产物进行过滤、洗涤、干燥和焙烧,得到M@SBA分子筛。
本发明第三方面提供了根据上述的制备方法制得的封装有纳米金属原子的SBA分子筛,金属原子以单质形式存在于SBA分子筛内,该分子筛记为M@SBA。
M@SBA是指封装有纳米金属原子M的SBA分子筛。
在本发明中,例如但不限于,可以通过XPS测定,钒原子的XPS为512eV,钛原子的XPS为454eV,可以证明金属原子仅以单质形式存在于SBA分子筛内,而不存在氧化物形式。而且仅存在于SBA分子筛内部,而不存在于SBA分子筛的表面。如果存在氧化物形式或存在于SBA分子筛表面,则钒原子的XPS为524.5eV,钛原子的XPS为458.5eV。
根据本发明所述的分子筛的一些实施方式,优选地,所述M@SBA的比表面积为910~990m2/g。本发明的M@SBA具有更大的比表面积,进而能够提高转化率和选择性。
根据本发明所述的分子筛的一些实施方式,优选地,所述M@SBA中的金属纳米粒子大小可控制在5~25nm。
根据本发明所述的分子筛的一些实施方式,优选地,当金属原子为钒原子时,钒原子的XPS为512eV。
根据本发明所述的分子筛的一些实施方式,优选地,当金属原子为钛原时,钛原子的XPS为454eV。
本发明第四方面提供了根据上述的制备方法或上述的封装有纳米金属原子的SBA分子筛在环己烷选择性氧化制备环己酮和环己醇中的应用。
本发明的有益效果:
本发明首先利用钝化剂将分子筛外部的硅羟基进行保护,碱性物质会进入分子筛孔道从内部进行刻蚀而不会对分子筛外表面进行刻蚀破坏,内部分子筛两套独立的孔道结构由于碱性物质的刻蚀从而相互连接形成新的大孔和介孔结构,根据碱性物质的浓度和量来调节分子筛内部孔道结构的大小,随后将金属纳米粒子引入到分子筛孔道中,由于分子筛孔道结构的限域效应,金属纳米粒子不会超过分子筛孔道的大小而破坏分子筛内部结构,最后利用二次晶化将内部被刻蚀的孔道重新封装,彻底将金属纳米粒子封装在分子筛孔道中。与常规的后处理法相比,后处理法只能将大部分的金属纳米粒子负载在分子筛的外表面,同时由于金属纳米粒子暴露在外部,经过高温等处理,金属纳米粒子会继续团聚甚至流失,从而造成催化效果的下降。与常规的一步法水热合成相比,一步法方法简单,但必须经过还原将纳米颗粒还原成金属单质态,但还原后金属纳米颗粒的比分子筛本身孔道要大得多,因此势必会造成一部分分子筛孔道内部结构被撑大破坏,从而造成催化剂催化性能的下降。本发明的方法能够有效解决上述问题,提高催化剂的催化性能。
附图说明
图1为本发明实施例1得到的V@SBA-16分子筛HRTEM图;
图2为本发明实施例3得到的V@SBA-16分子筛小角XRD图;
图3为本发明实施例3得到的V@SBA-16分子筛HRTEM图;
图4为本发明实施例3得到的V@SBA-16分子筛XPS图;
图5为本发明实施例4得到的V@SBA-16分子筛HRTEM图;
图6为本发明实施例5得到的Ti@SBA-15分子筛XPS图。
具体实施方式
为使本发明更加容易理解,下面将结合实施例来详细说明本发明,这些实施例仅起说明性作用,并不局限于本发明的应用范围。
本发明的测试方法以及测试中所用设备如下:
(1)XRD采用Philips公司X-Pert系列X-射线衍射仪来测定分子筛的结构。
(2)HRTEM采用Rigku公司Jem-3010型高分辨透射电子显微镜来测定分子筛的规整度。
(3)XPS采用Thermo公司ESCALAB 250spectrometer型X-射线光电子能谱仪进行测定金属粒子成键情况。
(4)BET采用采用Micromeritics公司ASAP2020型全自动比表面分析仪进行测定。
本发明硅源以SiO2计,钒源以V计,钛源以Ti计,酸以H+计,溶剂以H2O计,有机模板剂以R计。
以下实施例中
(1)模板剂F127购自Sigma-Aldrich公司;
(2)模板剂F108购自Sigma-Aldrich公司;
(3)模板剂HMTA购自Sigma-Aldrich公司;
(4)模板剂P123购自Sigma-Aldrich公司。
【实施例1】
取5.0g的SBA-16分子筛原粉与2.1g三甲基氯硅烷在50℃的条件下搅拌2h,而后将产物与0.4g的1重量%的氢氧化钠溶液混合均匀,并在常温下搅拌1h,随后将产物过滤、洗涤,即为溶液D,将2g偏钒酸铵和2.5g草酸,充分搅拌均匀至蓝色澄清溶液,随后加入4.8g酒石酸,即为溶液C,从C中取出1.0g溶液加入D中并混合均匀,得到溶液A。
将1.6g的F127和34.5g去离子水依次加入反应器中,搅拌均匀,再加入24.1mL的0.1mol/L盐酸溶液,继续搅拌,缓慢逐滴加入5g正硅酸乙酯(TEOS),得到的反应混合物的摩尔配比为SiO2:80H2O:0.005R:0.1H+,即为溶液B,将B和A进行混合后转移至晶化釜中,升温至90℃,恒温晶化40h。晶化完全后,待温度降至室温,将反应后的混合物经过分离、洗涤并在100℃条件下进行干燥,最后在400℃下焙烧8h后即可得V@SBA-16分子筛。样品的高倍透射电镜图见图1,样品经BET分析所得产物的比表面积见表1。
【实施例2】
与实施例1不同之处在于,钝化剂改为二甲基二氯硅烷,用量改为0.56g,钝化温度改为60℃,钝化时间改为3h,氢氧化钠溶液重量分数改为2重量%,用量为0.3g,钒源络合物溶液C的量改为0.5g,将模版剂改为F108,用量为4.4g,水的量改为54g,硅源改为白炭黑(二氧化硅含量为90重量%),用量为2g,酸改为硫酸,用量改为44.8mL,晶化温度改为100℃,晶化时间改为50h,干燥温度改为110℃,焙烧温度改为500℃,焙烧时间改为6h,其余组分和合成条件不变,得到的反应混合物的摩尔配比为SiO2:100H2O:0.01R:0.15H+,样品经BET分析所得产物的比表面积见表1。
【实施例3】
与实施例1不同之处在于,钝化剂改为二苯基二氯硅烷,用量改为1.25g,钝化温度改为70℃,钝化时间改为4h,氢氧化钠溶液重量分数改为3重量%,用量为0.35g,反应时间改为2h,将模版剂改为HMTA,用量为0.15g,水的量改为82.5g,硅源改为硅溶胶(SW-25,二氧化硅含量为25重量%),用量为10g,酸源改为硝酸,用量为83mL,晶化温度改为110℃,晶化时间改为60h,干燥温度改为120℃,焙烧温度改为550℃,焙烧时间改为7h,其余组分和合成条件不变,得到的反应混合物的摩尔配比为SiO2:110H2O:0.025R:0.2H+,样品经BET分析所得产物的比表面积见表1,样品的小角粉末XRD衍射见图2,高倍透射电镜图见图3,钒原子在分子筛的状态分析XPS见图4。
【实施例4】
与实施例3不同之处在于,氢氧化钠溶液重量分数改为4重量%,其余组分和合成条件不变。样品的高倍透射电镜图见图5,样品经BET分析所得产物的比表面积见表1。
【实施例5】
取5.0g的SBA-15分子筛原粉与2.1g三甲基氯硅烷在50℃的条件下搅拌2h,而后将产物与0.4g的1重量%的氢氧化钠溶液混合均匀,并在常温下搅拌1h,随后将产物过滤、洗涤,即为溶液D,将2g钛酸四丁酯加入其中并混合均匀,即为溶液A。
将4.2g的P104和38.9g去离子水依次加入反应器中,搅拌均匀,再加入60mL的0.1mol/L盐酸溶液,继续搅拌,缓慢逐滴加入5g正硅酸乙酯(TEOS),得到的反应混合物的摩尔配比为SiO2:90H2O:0.03R:0.25H+,即为溶液B,将B和A进行混合后转移至晶化釜中,升温至130℃,恒温晶化90h。晶化完全后,待温度降至室温,将反应后的混合物经过分离、洗涤并在130℃条件下进行干燥,最后在400℃下焙烧8h后即可得Ti@SBA-15分子筛。样品经BET分析所得产物的比表面积见表1,将所得的样品用于环己烷选择性氧化制备环己酮和环己醇实验,结果见表1。钛原子在分子筛的状态分析XPS见图6。
【实施例6】
与实施例5不同之处在于,钝化剂改为二苯基二氯硅烷,用量改为0.56g,钝化温度改为70℃,钝化时间改为5h,氢氧化钠溶液质量分数改为3重量%,用量为0.3g,反应时间改为2h,钛酸四丁酯的量改为3g,将模版剂改为P123,用量为1.8g,水的量改为70.2g,将硅源改为白炭黑(二氧化硅含量为90重量%),用量为2g,酸源改为硝酸,用量为45mL,晶化温度改为120℃,晶化时间改为70h,干燥温度改为120℃,焙烧温度改为600℃,焙烧时间改为5h,其余组分和合成条件不变,得到的反应混合物的摩尔配比为SiO2:130H2O:0.01R:0.15H+,样品经BET分析所得产物的比表面积见表1。
【对比例1】
将2g偏钒酸铵和2.5g草酸,充分搅拌均匀至蓝色澄清溶液,随后加入4.8g酒石酸,即为溶液C;
将1.6g的F127和34.5g去离子水依次加入反应器中,搅拌均匀,再加入24.1mL的0.1mol/L盐酸溶液,从C中取出1.0g溶液加入其中并混合均匀,继续搅拌,缓慢逐滴加入5g正硅酸乙酯(TEOS),得到的反应混合物的摩尔配比为SiO2:80H2O:0.005R:0.1H+,将混合后的溶液转移至晶化釜中,升温至90℃,恒温晶化40h。晶化完全后,待温度降至室温,将反应后的混合物经过分离、洗涤并在100℃条件下进行干燥,最后在400℃下焙烧8h后即可得V-SBA-16分子筛原粉,将V-SBA-16分子筛置于石英管底部并通入氢气,以3°/min的升温速率升至400℃并保持2h,最后得到的即为V@SBA-16分子筛,样品经BET分析所得产物的比表面积见表1。
【对比例2】
将2g偏钒酸铵和2.5g草酸,充分搅拌均匀至蓝色澄清溶液,随后加入4.8g酒石酸,即为溶液C;
将1.6g的F127和34.5g去离子水依次加入反应器中,搅拌均匀,再加入24.1mL的0.1mol/L盐酸溶液,搅拌均匀,缓慢逐滴加入5g正硅酸乙酯(TEOS),得到的反应混合物的摩尔配比为SiO2:80H2O:0.005R:0.1H+,将混合后的溶液转移至晶化釜中,升温至90℃,恒温晶化40h。晶化完全后,待温度降至室温,将反应后的混合物经过分离、洗涤并在100℃条件下进行干燥,最后在400℃下焙烧8h后即可得SBA-16分子筛原粉,将SBA-16分子筛和1.0g C溶液进行混合均匀,随后将反应后的混合物经过分离、洗涤并在100℃条件下进行干燥,最后在400℃下焙烧8h,最后得到的即为V/SBA-16分子筛,样品经BET分析所得产物的比表面积见表1。
【对比例3】
取5.0g的SBA-16分子筛原粉与0.4g的1重量%的氢氧化钠溶液混合均匀,并在常温下搅拌1h,随后将产物过滤、洗涤,即为溶液D,将2g偏钒酸铵和2.5g草酸,充分搅拌均匀至蓝色澄清溶液,随后加入4.8g酒石酸,即为溶液C,从C中取出1.0g溶液加入D中并混合均匀,得到溶液A。
将1.6g的F127和34.5g去离子水依次加入反应器中,搅拌均匀,再加入24.1mL的0.1mol/L盐酸溶液,继续搅拌,缓慢逐滴加入5g正硅酸乙酯(TEOS),得到的反应混合物的摩尔配比为SiO2:80H2O:0.005R:0.1H+,即为溶液B,将B和A进行混合后转移至晶化釜中,升温至90℃,恒温晶化40h。晶化完全后,待温度降至室温,将反应后的混合物经过分离、洗涤并在100℃条件下进行干燥,最后在400℃下焙烧8h后即可得V/SBA-16分子筛。样品经BET分析所得产物的比表面积见表1。
【测试例】
分别将实施例1-6和对比例1-3得到的样品用于环己烷选择性氧化制备环己酮和环己醇实验,结果见表1。
环己烷选择性氧化制备环己酮和环己醇实验是在固定床微型反应器中(H200mm×φ10mm)进行的。具体反应过程为:将5.4mL环己烷、1.5g催化剂和1.5mL H2O2(环己烷:H2O2=1:1)依次加入固定床微型反应器中,在70℃条件下反应7h。待反应完成后,经过冷却收集所得到的液体产物。用气相色谱仪对所得到的产物进行分析。
表1.环己烷选择性氧化制备环己酮和环己醇结果
由对比例1-2和实施例1,表1可知,对比例1中采用原位约束法的方式来制备V@SBA-16,此方法的过程相当简单便利,只需最后采用H2还原的方式将金属从骨架中拉出即可,但此方法一是会强制将骨架中的金属原子拉出骨架从而破坏分子筛的骨架结构,二是从骨架析出的金属原子会比孔道大,从而对孔道的结构也有一定的破坏作用,因此分子筛的整体结构会有较大的改变,因此利用此方法所得到的催化剂催化性能较低;而对比例2采用后合成策略法,此方法和普通的负载法基本一致,金属原子最终是以氧化物的形式负载在分子筛的表面,会造成反应过程中金属原子的整体性流失,在催化反应中很容易失活;对比例3中由于未使用钝化剂,所添加的碱将直接刻蚀掉分子筛表面的骨架结构,分子筛结构遭到一定的破坏,随后再添加金属源,金属原子也无法被封装在分子筛的孔道内部,从而催化剂的反应性能较差。
由图2可知,根据本发明所提供的方法得到的V@SBA-16分子筛在小角XRD中仍然具有SBA-16分子筛高规整度的特征峰,说明金属原子的修饰没有破坏分子筛本身的结构;由图3和图4可知,根据本发明所提供的方法得到的V@SBA-16分子筛中的钒原子是以单质(图4中512eV的钒单质V2p3轨道)形式存在的,且在电镜图中明显的可以看出金属单质的大小在5nm左右。
由图1、图3和图5可知,通过改变碱量的多少,可以随时调控金属纳米单质的大小,金属单质从5~50nm范围内变化。
由表1可知,随着金属纳米颗粒的增大,催化活性越来越好,但当金属纳米粒子过大时,虽然不会造成分子筛本身结构的破坏,但由于碱的刻蚀,会造成分子筛内部孔道相互连通度加大,使得分子筛本身择形催化的效果也变弱,因此在选择性上会有一定程度的下降。
以上所述的仅是本发明的优选实例。应当指出对于本领域的普通技术人员来说,在本发明所提供的技术启示下,作为本领域的公知常识,还可以做出其它等同变型和改进,也应视为本发明的保护范围。
Claims (13)
1.一种封装有纳米金属原子的SBA分子筛,其中,金属原子以单质形式存在于SBA分子筛内。
2.根据权利要求1所述的SBA分子筛,其特征在于,所述金属原子为钒原子和/或钛原子,
更优选地,当金属原子为钒原子时,钒原子的XPS为512eV;
更优选地,当金属原子为钛原子时,钛原子的XPS为454eV。
3.根据权利要求1或2所述的SBA分子筛,其特征在于,所述封装有纳米金属原子的SBA分子筛的比表面积为940~1100m2/g;
优选地,所述封装有纳米金属原子的SBA分子筛中的金属纳米粒子大小可控制在5~50nm。
4.一种纳米金属原子封装在SBA分子筛的制备方法,包括以下步骤:
1)将SBA分子筛原粉与钝化剂混合进行第一反应,然后与碱性溶液混合进行第二反应,过滤、洗涤,并与金属络合物溶液进行混合,得到溶液A;
2)将有机模板剂、水、酸和硅源混合成胶,得到溶液B;
3)将所述溶液A与所述溶液B混合并进行水热晶化,过滤、洗涤、干燥和焙烧。
5.根据权利要求4所述的制备方法,其特征在于,所述钝化剂包括通式RaRbRcSiRd所示的有机硅烷,其中,Ra、Rb、Rc和Rd相同或不同,各自独立地选自氢、卤素、C1-C20的烷基、C1-C20的烷氧基、C3-C20的环烷基、C6-C20的芳基和C1-C20的卤代烷基中的任意一种,且Ra、Rb、Rc和Rd不同时为氢和/或卤素;优选地,Rd为卤素,Ra、Rb和Rc不同时为氢和/或卤素;所述钝化剂进一步优选选自二苯基二氯硅烷、三甲基氯硅烷和二甲基二氯硅烷中的至少一种;和/或
所述钝化剂与分子筛原粉的重量比为4:5~1:10,优选为3:5~1:10,进一步优选为3:7~1:9。
6.根据权利要求4或5所述的制备方法,其特征在于,所述SBA分子筛为SBA-15分子筛和/或SBA-16分子筛。
7.根据权利要求4-6中任一项所述的制备方法,其特征在于,在所述碱性溶液中,碱的含量为1~5重量%;优选地,所述碱性溶液为氢氧化钠溶液;和/或,
所述碱性溶液与分子筛原粉的重量比为1:20~1:10,优选为3:50~2:25。
8.根据权利要求4-7中任一项所述的制备方法,其特征在于,所述金属络合物溶液包括金属原子源以及能与所述金属原子源络合的溶液,其中,所述金属为钒和/或钛,所述金属原子源为含钒源的草酸溶液和/或钛源;
优选地,所述钒源选自偏钒酸铵、正钒酸钠和焦钒酸钠中的至少一种;
优选地,所述钛源选自钛酸四丁酯、四氯化钛和硫酸钛中的至少一种;
优选地,所述能与所述金属原子源络合的溶液选自柠檬酸、酒石酸和三乙醇中的至少一种;
更优选地,所述金属络合物溶液与分子筛原粉的重量比为0.5~1:5。
9.根据权利要求4-8中任一项所述的制备方法,其特征在于,所述第一反应的条件包括:温度为50~80℃,优选为60~70℃;时间为2~6h,优选为3~5h;和/或,
所述第二反应的条件包括:温度为20~40℃,时间为1~2h。
10.根据权利要求4-9中任一项所述的制备方法,其特征在于,所述有机模板剂为双亲性非离子三嵌段表面活性剂,优选为F127、F108、六亚甲基四胺、P123和P104中的至少一种;和/或,
所述硅源选自白炭黑、正硅酸乙酯、硅酸钠和硅溶胶的至少一种;和/或,
所述酸选自盐酸、硫酸和硝酸中的至少一种;和/或,
所述溶液B满足以摩尔计,SiO2:a H2O:b R:c H+,其中,R为有机模板剂,a的值为80~200,优选为100~160;b的值为0.005~0.030,优选为0.010~0.025;c的值为0.10~0.25,优选为0.15~0.20。
11.根据权利要求4-10中任一项所述的制备方法,其特征在于,所述水热晶化的条件包括:温度为80~130℃,优选为90~120℃;时间为24~90h,优选为40~70h;和/或,
所述干燥的条件包括:温度为100~140℃,优选为110~130℃;时间为4~6h;和/或,
所述焙烧的条件包括:温度为400~700℃,优选为500~600℃;焙烧时间为5~8h。
12.根据权利要求4-11中任一项所述的制备方法制得的封装有纳米金属原子的SBA分子筛,金属原子以单质形式存在于SBA分子筛内,该分子筛记为M@SBA;
优选地,所述M@SBA的比表面积为940~1100m2/g;
优选地,所述M@SBA中的金属纳米粒子大小可控制在5~50nm;
优选地,当金属原子为钒原子时,钒原子的XPS为512eV;
优选地,当金属原子为钛原子时,钛原子的XPS为454eV。
13.权利要求1-3和12中任意一项所述的封装有纳米金属原子的SBA分子筛或权利要求4-11中任意一项所述的制备方法在环己烷选择性氧化制备环己酮和环己醇中的应用。