CN1167042A

CN1167042A - Technology for making imitation of bronze ware

Info

Publication number: CN1167042A
Application number: CN 97105748
Authority: CN
Inventors: 薛发伟
Original assignee: Individual
Current assignee: Individual
Priority date: 1997-03-24
Filing date: 1997-03-24
Publication date: 1997-12-10
Anticipated expiration: 2017-03-24
Also published as: CN1064006C

Abstract

The process of this invention firstly makes up the semiproduct of the imitation bronze ware, then black color and green color are painted on, then the soft wet cloth is used to wipe away the green color on the protruding position of the semiproduct, and at least the loess powder layer is coated on. The advantages are simple process, life-like effect, extensive raw material and having very high value for admiring and collecting.

Description

The manufacture craft of bronzeware imitation

The present invention relates to make in a kind of industrial art field the production technology of bronze ware.

The Chinese patent communique disclosed the patent application document of a kind of porcelain base bronze ware and manufacture method thereof on January 12nd, 1994, notification number is 1080595, have in this application: be beneficial to ceramic process and prepare porcelain body, spray attached layer of copper body on porcelain body surface with the metal thermal spraying method, through rubbing down, do mouth and surface treatment to the bronze ware effect.The method of this making bronze ware not only complex process but also effect is not satisfactory, has directly influenced its ornamental value and reserve value.

The objective of the invention is to overcome above-mentioned defective, the manufacture craft of a kind of effect bronzeware imitation true to nature is provided.

The present invention realizes like this, it is implemented according to the following step: at first make the mold of bronze ware-imitating, then mold black, treating after the mold drying green, afterwards, wet cloth or other textiles with softness are wiped the green at the outstanding position of mold uniformly, then, with loess powder and the bloom brushing of ironing the bloom mediation one time.

Not only manufacture craft is simple but also effect is true to nature to adopt the present invention, the advantage widely of drawing materials in addition simultaneously, and the raw material of making mold can be yellow mud, gypsum, cement, it also can be metal, even can be timber, paper, in a word, any material that can moulding all can become the mold raw material.

Example 1:

Getting yellow mud, gypsum, silica flour and white glue with vinyl stirs, produce the bronze ware-imitating mold, this mold can be the form of embossment, then mold black, concrete grammar is: with carbon black, a little talcum powder, all make blacking with varnish and solvent or diluent accent, uniform brushing mold twice in a day, thus mold is black.Treat mold drying in the shade the back green, can brush uniformly with the coating of pure green, grass green, glue and water furnishing.After treating that afterwards mold dries in the shade, uniformly the green at the outstanding position of mold is wiped, after drying in the shade, with loess powder and the bloom brushing of ironing the bloom mediation one time with soft wet cloth or other textiles.So far, a bronzeware imitation true to nature completes.

Example 2:

Produce the foundry goods of bronze ware-imitating with metal, this foundry goods can be three-dimensional form, then foundry goods black, and concrete grammar is: carbon black, a small amount of talcum powder, varnish and solvent or diluent are transferred all made blacking, uniform brushing foundry goods twice in one day, thus foundry goods is black.Treat that foundry goods is drying afterwards green, can brush uniformly with the coating of pure green, grass green, glue and water furnishing, after treating that afterwards foundry goods dries, wet cloth or other textiles with softness are wiped the green at the outstanding position of foundry goods uniformly, after drying again, with loess powder and the bloom brushing of ironing the bloom mediation one time.So far, a bronzeware imitation true to nature completes.

Example 3:

With timber produce the mold of bronze ware-imitating, then mold black, concrete grammar is: carbon black, a small amount of talcum powder, varnish and solvent or diluent are transferred are all made blacking, brushing mold twice uniformly in a day, thereby mold is black.Treat mold oven dry back green, can brush uniformly with the coating of pure green, grass green, glue and water furnishing.After treating that afterwards mold is dried, uniformly the green at the outstanding position of mold is wiped, again after the oven dry, with loess powder and the bloom brushing of ironing the bloom mediation one time with soft wet cloth or other textiles.So far, a bronzeware imitation true to nature completes.

Claims

1, a kind of manufacture craft of bronzeware imitation is characterized in that it implements according to the following step:

(1), makes the mold of bronze ware-imitating;

(2), mold black;

(3), treating after the mold drying green;

(4), treat the mold drying after, uniformly the green at the outstanding position of mold is wiped with soft wet cloth or other textiles;

(5), treat the mold drying after, with loess powder with iron the bloom brushing one time that bloom is in harmonious proportion.

2, the manufacture craft of bronzeware imitation according to claim 1 is characterized in that blacking in the abovementioned steps (2) is based on carbon black, is added with a small amount of talcum powder and forms with sliding lacquer and solvent or diluent modulation.

3, the manufacture craft of bronzeware imitation according to claim 1 is characterized in that the green coating in the abovementioned steps (3) is to be formed with glue and water modulation by pure green and grass green pigment.