CN116496661A - 一种喷墨打印用的墨水及其制备方法 - Google Patents
一种喷墨打印用的墨水及其制备方法 Download PDFInfo
- Publication number
- CN116496661A CN116496661A CN202310601040.0A CN202310601040A CN116496661A CN 116496661 A CN116496661 A CN 116496661A CN 202310601040 A CN202310601040 A CN 202310601040A CN 116496661 A CN116496661 A CN 116496661A
- Authority
- CN
- China
- Prior art keywords
- ink
- agent
- inorganic
- printing according
- jet printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种喷墨打印用的墨水及其制备方法，包括以下重量百分比的组分：15‑30％无机熔剂、0.5‑1.5％分散剂、8‑12％无机颜料、0.5‑1％润滑流平剂、20‑50％有机溶剂，5‑10％助剂；通过使用氧化钠、三氧化二硼和氧化锂中的一种或两种以上代替氧化铅来调节墨水的熔点，减少墨水对人体的伤害，使墨水更符合环保的要求的同时，也使墨水对玻璃形成较好的结合力，二氧化钛、氧化锌和氧化锆中的一种或两种以上能够提高墨水的耐酸碱性和提升机械强度，使玻璃上的图案具有耐酸碱性和热稳定性,可保持长久的颜色鲜艳的效果。
Description
技术领域
本发明涉及喷墨打印油墨技术领域，具体涉及一种喷墨打印用的墨水及其制备方法。
背景技术
高温烧结墨水数码打印是指数码打印机在计算机软件的支持下，将预先设计好的图案墨水.打印到介质表面，然后再进行烘干和高温烧结的过程。与传统的丝印、辊涂相比，数码喷墨打印制作的装饰品图案饱满，使用性能更好。
传统烧结墨水主要由釉料、无机颜料、有机溶剂及助剂混合均匀后研磨制成，一般是通过丝网印刷将油墨印刷在基板上，经过烘干和高温烧结，油墨中的其它成分基本挥发分解完成，釉料和无机颜料熔融并覆盖在玻璃或陶瓷等难附着材料的表面，形成带有颜色的油墨薄膜层。传统的油墨通过添加大量的氧化铅来调节熔点适用于不同的应用，但是氧化铅属于有毒物质，会造成人体铅中毒，对人体生命安全造成威胁。而且传统丝网印刷工艺本身就是一个高污染的印刷方式，绿色环保数码喷墨打印方式代替传统高污染的印刷方式是印刷行业发展的必然趋势，因而，本发明提供一种喷墨打印用的墨水及其制备方法。
发明内容
针对现有技术的缺陷，本发明的目的是提供一种喷墨打印用的墨水及其制备方法，以解决上述背景技术中提出的问题。
本发明解决技术问题采用如下技术方案：
本发明提供了一种喷墨打印用的墨水，包括以下重量百分比的组分：15-30％无机熔剂、0.5-1.5％分散剂、8-12％无机颜料、0.5-1％润滑流平剂、20-50％有机溶剂，5-10％助剂。
优选地，所述无机熔剂为二氧化硅、二氧化钛、氧化锌、氧化锆、氧化钠、三氧化二硼和氧化锂中的一种或多种。
优选地，所述分散剂为水性分散剂，所述分散剂为聚酰胺。
优选地，所述无机颜料为铁丹、钛白色素、普鲁士蓝、钛镍黄色素和群青中的一种或多种。
优选地，所述润湿流平剂为水性流平剂，所述润湿流平剂为氟硅聚合物。
优选地，所述有机溶剂为醇类、醚类、酮类、酯类、苯类中的一种或多种。
醇类有机溶剂包括但不限于甲醇、乙醇、正丙醇、异丙醇、丁醇等。
醚类有机溶剂包括但不限于甲醚、乙醚、甲基叔丁基醚等。
酮类有机溶剂包括但不限于丙酮、甲基乙基酮、二丙基酮、甲基异丁基酮、甲基异丙基酮、环戊酮等。
酯类有机溶剂包括但不限于乙酸甲酯、乙酸乙酯、乙酸正丙酯、乙酸正丁酯、乙酸异丁酯等。
苯类溶剂包括但不限于甲苯、二甲苯、均三甲苯等
优选地，所述助剂包括硬挺整理剂和抗静电剂，且硬挺整理剂和抗静电剂的质量比为1:0.4-0.8。
优选地，所述硬挺整理剂为聚氰胺树脂、脲醛树脂、聚丙烯酸脂、聚醋酸乙烯酯及其共聚物、聚乙烯醇类、聚酯类中的一种或多种；所述抗静电剂为乙氧基化脂肪族烷基胺、乙氧基化烷基酸胺、甘油-硬脂酸酯中的一种或多种。
优选地，所述无机熔剂粉制备方法，包括以下步骤：
步骤一、将所述无机熔剂中的氧化物混合后，升温至115-1300℃并保温60-120min使玻璃充分熔融，再将上述的熔融物倒入水中，水淬得到无机熔剂渣；
步骤二、将步骤一中得到的无机熔剂渣置于球磨机中，以无水乙醇为球磨介质，以500-600r/min的转速球磨8-10h，取出干燥后得到无机熔剂粉。
本发明还提供了一种喷墨打印用的墨水的制备方法，包括以下步骤：
将分散剂、无机颜料、润滑流平剂、有机溶剂、助剂与无机熔剂粉混合，在分散机中搅拌以1500-3000r/min搅拌20-40min后，在砂磨机上以500-800r/min研磨12-36h，过滤。
与现有技术相比，本发明具有如下的有益效果：
通过使用氧化钠、三氧化二硼和氧化锂中的一种或两种以上代替氧化铅来调节墨水的熔点，减少墨水对人体的伤害，使墨水更符合环保的要求的同时，也使墨水对玻璃形成较好的结合力。
通过使用二氧化钛、氧化锌和氧化锆中的一种或两种以上能够提高墨水的耐酸碱性和提升机械强度，使玻璃上的图案具有耐酸碱性和热稳定性,可保持长久的颜色鲜艳的效果。
具体实施方式
下面结合具体实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1.
本实施例的本发明提供了一种喷墨打印用的墨水，包括以下重量百分比的组分：15％无机熔剂、0.5％分散剂、8％无机颜料、0.5％润滑流平剂、20％有机溶剂，5-10％助剂。
本实施例的无机熔剂为二氧化硅、二氧化钛、氧化锌。
本实施例的分散剂为水性分散剂，分散剂为聚酰胺。
本实施例的无机颜料为铁丹、钛白色素、普鲁士蓝。
本实施例的润湿流平剂为水性流平剂，润湿流平剂为氟硅聚合物。
本实施例的有机溶剂为醇类、醚类。
本实施例的助剂包括硬挺整理剂和抗静电剂，且硬挺整理剂和抗静电剂的质量比为1:0.4。
本实施例的硬挺整理剂为聚氰胺树脂、脲醛树脂、聚丙烯酸脂；抗静电剂为乙氧基化脂肪族烷基胺。
本实施例的无机熔剂粉制备方法，包括以下步骤：
步骤一、将无机熔剂中的氧化物混合后，升温至115℃并保温60min使玻璃充分熔融，再将上述的熔融物倒入水中，水淬得到无机熔剂渣；
步骤二、将步骤一中得到的无机熔剂渣置于球磨机中，以无水乙醇为球磨介质，以500r/min的转速球磨8h，取出干燥后得到无机熔剂粉。
本实施例的一种喷墨打印用的墨水的制备方法，包括以下步骤：
将分散剂、无机颜料、润滑流平剂、有机溶剂、助剂与无机熔剂粉混合，在分散机中搅拌以1500r/min搅拌20min后，在砂磨机上以500r/min研磨12h，过滤。
实施例2.
本实施例的本发明提供了一种喷墨打印用的墨水，包括以下重量百分比的组分：30％无机熔剂、1.5％分散剂、12％无机颜料、1％润滑流平剂、50％有机溶剂，10％助剂。
本实施例的无机熔剂为氧化钠、三氧化二硼和氧化锂。
本实施例的分散剂为水性分散剂，分散剂为聚酰胺。
本实施例的无机颜料为钛镍黄色素和群青。
本实施例的润湿流平剂为水性流平剂，润湿流平剂为氟硅聚合物。
本实施例的有机溶剂为酮类、酯类。
本实施例的助剂包括硬挺整理剂和抗静电剂，且硬挺整理剂和抗静电剂的质量比为1:0.8。
本实施例的硬挺整理剂为聚醋酸乙烯酯及其共聚物、聚乙烯醇类、聚酯类；抗静电剂为乙氧基化烷基酸胺、甘油-硬脂酸酯。
本实施例的无机熔剂粉制备方法，包括以下步骤：
步骤一、将无机熔剂中的氧化物混合后，升温至1300℃并保温120min使玻璃充分熔融，再将上述的熔融物倒入水中，水淬得到无机熔剂渣；
步骤二、将步骤一中得到的无机熔剂渣置于球磨机中，以无水乙醇为球磨介质，以600r/min的转速球磨10h，取出干燥后得到无机熔剂粉。
本实施例的一种喷墨打印用的墨水的制备方法，包括以下步骤：
将分散剂、无机颜料、润滑流平剂、有机溶剂、助剂与无机熔剂粉混合，在分散机中搅拌以3000r/min搅拌40min后，在砂磨机上以800r/min研磨36h，过滤。
实施例3.
本实施例的本发明提供了一种喷墨打印用的墨水，包括以下重量百分比的组分：23％无机熔剂、1％分散剂、10％无机颜料、0.8％润滑流平剂、35％有机溶剂，8％助剂。
本实施例的无机熔剂为二氧化硅、氧化锆、三氧化二硼和氧化锂。
本实施例的分散剂为水性分散剂，分散剂为聚酰胺。
本实施例的无机颜料为铁丹、钛白色素、钛镍黄色素。
本实施例的润湿流平剂为水性流平剂，润湿流平剂为氟硅聚合物。
本实施例的有机溶剂为醚类、酮类、酯类的一种或多种。
本实施例的助剂包括硬挺整理剂和抗静电剂，且硬挺整理剂和抗静电剂的质量比为1:0.6。
本实施例的硬挺整理剂为聚氰胺树脂、聚丙烯酸脂、聚乙烯醇类、聚酯类；抗静电剂为乙氧基化脂肪族烷基胺、甘油-硬脂酸酯。
本实施例的无机熔剂粉制备方法，包括以下步骤：
步骤一、将无机熔剂中的氧化物混合后，升温至1225℃并保温90min使玻璃充分熔融，再将上述的熔融物倒入水中，水淬得到无机熔剂渣；
步骤二、将步骤一中得到的无机熔剂渣置于球磨机中，以无水乙醇为球磨介质，以550r/min的转速球磨9h，取出干燥后得到无机熔剂粉。
本实施例的一种喷墨打印用的墨水的制备方法，包括以下步骤：
将分散剂、无机颜料、润滑流平剂、有机溶剂、助剂与无机熔剂粉混合，在分散机中搅拌以2250r/min搅拌30min后，在砂磨机上以650r/min研磨24h，过滤。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (10)
1.一种喷墨打印用的墨水，其特征在于，包括以下重量百分比的组分：15-30％无机熔剂、0.5-1.5％分散剂、8-12％无机颜料、0.5-1％润滑流平剂、20-50％有机溶剂，5-10％助剂。
2.根据权利要求1所述一种喷墨打印用的墨水，其特征在于，所述无机熔剂为二氧化硅、二氧化钛、氧化锌、氧化锆、氧化钠、三氧化二硼和氧化锂中的一种或多种。
3.根据权利要求1所述一种喷墨打印用的墨水，其特征在于，所述分散剂为水性分散剂，所述分散剂为聚酰胺。
4.根据权利要求1所述一种喷墨打印用的墨水，其特征在于，所述无机颜料为铁丹、钛白色素、普鲁士蓝、钛镍黄色素和群青中的一种或多种。
5.根据权利要求1所述一种喷墨打印用的墨水，其特征在于，所述润湿流平剂为水性流平剂，所述润湿流平剂为氟硅聚合物。
6.根据权利要求1所述一种喷墨打印用的墨水，其特征在于，所述有机溶剂为醇类、醚类、酮类、酯类、苯类中的一种或多种。
7.根据权利要求1所述一种喷墨打印用的墨水，其特征在于，所述助剂包括硬挺整理剂和抗静电剂，且硬挺整理剂和抗静电剂的质量比为1:0.4-0.8。
8.根据权利要求7所述一种喷墨打印用的墨水，其特征在于，所述硬挺整理剂为聚氰胺树脂、脲醛树脂、聚丙烯酸脂、聚醋酸乙烯酯及其共聚物、聚乙烯醇类、聚酯类中的一种或多种；所述抗静电剂为乙氧基化脂肪族烷基胺、乙氧基化烷基酸胺、甘油-硬脂酸酯中的一种或多种。
9.根据权利要求1所述一种喷墨打印用的墨水，其特征在于，所述无机熔剂粉制备方法，包括以下步骤：
步骤一、将所述无机熔剂中的氧化物混合后，升温至115-1300℃并保温60-120min使玻璃充分熔融，再将上述的熔融物倒入水中，水淬得到无机熔剂渣；
步骤二、将步骤一中得到的无机熔剂渣置于球磨机中，以无水乙醇为球磨介质，以500-600r/min的转速球磨8-10h，取出干燥后得到无机熔剂粉。
10.根据权利要求1-9任意一项所述的喷墨打印用的墨水的制备方法，其特征在于，包括以下步骤：
将分散剂、无机颜料、润滑流平剂、有机溶剂、助剂与无机熔剂粉混合，在分散机中搅拌以1500-3000r/min搅拌20-40min后，在砂磨机上以500-800r/min研磨12-36h，过滤。