CN116328017A - 高抗菌垂直吸收藻酸盐敷料及其制备方法 - Google Patents
高抗菌垂直吸收藻酸盐敷料及其制备方法 Download PDFInfo
- Publication number
- CN116328017A CN116328017A CN202310396513.8A CN202310396513A CN116328017A CN 116328017 A CN116328017 A CN 116328017A CN 202310396513 A CN202310396513 A CN 202310396513A CN 116328017 A CN116328017 A CN 116328017A
- Authority
- CN
- China
- Prior art keywords
- stirring
- mixing
- colloid
- antibacterial
- mixed solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及医用敷料技术领域，具体涉及一种高抗菌垂直吸收藻酸盐敷料及其制备方法，包括如下步骤：将海藻酸钠加入去离子水中混合搅拌，再加入酸处理溶液混合搅拌，得到混合溶液；混合溶液中依次倒入乙醇和氯化钠进行混合搅拌，得到氧化混合溶液；将氧化混合溶液过滤并与凝胶搅拌混合，得到海藻酸钠胶体；取出硝酸银和硝酸锌进行搅拌混合，得到第一混合物；将抗菌物和黄凡士林进行搅拌混合，得到第二混合物；将第一混合物和第二混合物混合搅拌得到高抗菌胶体；海藻酸钠胶体和高抗菌胶体混合搅拌，得到混合胶体；静置使混合胶体凝固，进行拉伸，水洗，绕卷，干燥，随后经针刺机制成敷料，以此使敷料具有较高的抗菌效果。
Description
技术领域
本发明涉及医用敷料技术领域，尤其涉及一种高抗菌垂直吸收藻酸盐敷料及其制备方法。
背景技术
目前在对患者皮肤伤口进行治疗时，为了避免伤口恶化，加快伤口恢复，通常在伤口处使用藻酸盐敷料，医用敷料可以暂时性的起到一部分皮肤遮挡职能的作用，为伤口的愈合提供有利的条件，但传统的医用敷料并没有抗菌效果，导致患者伤口容易与空气中的细菌或者误触细菌导致伤口恢复缓慢，甚至加重病情。
在现有技术中，在制作藻酸盐敷料时，均匀撒上抗菌粉并进行搅拌，随后经针刺机制成抗菌敷料。
但在前述的现有技术中，仅依靠抗菌粉制作的敷料抗菌效果不佳，且不利于人体皮肤快速吸收，使用效果较差，影响患者伤口愈合恢复。
发明内容
本发明的目的在于提供一种高抗菌垂直吸收藻酸盐敷料及其制备方法，解决现有技术中仅依靠抗菌粉制作的敷料抗菌效果不佳，且不利于人体皮肤快速吸收，使用效果较差，影响患者伤口愈合恢复的问题。
为实现上述目的，本发明提供了一种高抗菌垂直吸收藻酸盐敷料，按重量份计，其制备原料包括：
10-20份海藻酸钠、2-6份凝胶、10-20份酸处理溶液、1-3份硝酸银、1-3份硝酸锌、1-3份抗菌物和1-3份黄凡士林。
其中，所述凝胶为透明质酸钠凝胶、交联葡聚糖凝胶和琼脂糖凝胶的一种。
其中，所述酸处理溶液为过碘酸钠溶液或碳酸钠溶液的一种。
其中，所述抗菌物为金霉素、莫匹罗星和红霉素的一种。
本发明还提供一种高抗菌垂直吸收藻酸盐敷料的制备方法，包括如下步骤：
将所述海藻酸钠加入去离子水中混合搅拌，再加入所述酸处理溶液混合搅拌，得到混合溶液；
所述混合溶液中依次倒入乙醇和氯化钠进行混合搅拌，得到氧化混合溶液；
将所述氧化混合溶液过滤并与所述凝胶搅拌混合，得到海藻酸钠胶体；
取出所述硝酸银和所述硝酸锌进行搅拌混合，得到第一混合物；
将所述抗菌物和所述黄凡士林进行搅拌混合，得到第二混合物；
将所述第一混合物和所述第二混合物混合搅拌得到高抗菌胶体；
所述海藻酸钠胶体和所述高抗菌胶体混合搅拌，得到混合胶体；
静置使所述混合胶体凝固，进行拉伸，水洗，绕卷，干燥，随后经针刺机制成敷料，得到高抗菌垂直吸收藻酸盐敷料。
其中，在将所述海藻酸钠加入去离子水中混合搅拌，再加入所述酸处理溶液混合搅拌，得到混合溶液的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min。
其中，在所述混合溶液中依次倒入乙醇和氯化钠进行混合搅拌，得到氧化混合溶液的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min。
其中，在将所述氧化混合溶液过滤并与所述凝胶搅拌混合，得到海藻酸钠胶体的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min。
其中，在取出所述硝酸银和所述硝酸锌进行搅拌混合，得到第一混合物的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min。
其中，在将所述抗菌物和所述黄凡士林进行搅拌混合，得到第二混合物的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min；
在将所述第一混合物和所述第二混合物混合搅拌得到高抗菌胶体的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min；
在所述海藻酸钠胶体和所述高抗菌胶体混合搅拌，得到混合胶体的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min；
在静置使所述混合胶体凝固，进行拉伸，水洗，绕卷，干燥，随后经针刺机制成敷料，得到高抗菌垂直吸收藻酸盐敷料的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min。
本发明的一种高抗菌垂直吸收藻酸盐敷料及其制备方法，通过将所述海藻酸钠加入去离子水中混合搅拌，再加入所述酸处理溶液混合搅拌，得到混合溶液；所述混合溶液中依次倒入乙醇和氯化钠进行混合搅拌，得到氧化混合溶液；将所述氧化混合溶液过滤并与所述凝胶搅拌混合，得到海藻酸钠胶体；取出所述硝酸银和所述硝酸锌进行搅拌混合，得到第一混合物；将所述抗菌物和所述黄凡士林进行搅拌混合，得到第二混合物；将所述第一混合物和所述第二混合物混合搅拌得到高抗菌胶体；所述海藻酸钠胶体和所述高抗菌胶体混合搅拌，得到混合胶体；静置使所述混合胶体凝固，进行拉伸，水洗，绕卷，干燥，随后经针刺机制成敷料，得到高抗菌垂直吸收藻酸盐敷料，以此制作出的敷料具有较强的抗菌效果，且能够利于人体皮肤快速垂直吸收，利于患者伤口愈合恢复。
附图说明
为了更清楚地说明本申请实施例或现有技术中的技术方案，下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍。
图1是本发明的第一实施例的整体的步骤流程图。
图2是本发明的第二实施例的整体的步骤流程图。
图3是本发明的第三实施例的整体的步骤流程图。
具体实施方式
下面详细描述本发明的实施例，所述实施例的示例在附图中示出，下面通过参考附图描述的实施例是示例性的，旨在用于解释本发明，而不能理解为对本发明的限制。
第一实施例：
请参阅图1，其中图1是本发明的第一实施例的步骤流程图，本发明提供一种高抗菌垂直吸收藻酸盐敷料的制备方法，包括如下步骤：
S1：将10份所述海藻酸钠加入去离子水中，按照200r/min的搅拌速率混合搅拌10min，再加入10份所述过碘酸钠溶液混合搅拌，得到混合溶液；
S2：所述混合溶液中依次倒入乙醇和氯化钠，按照200r/min的搅拌速率混合搅拌10min，得到氧化混合溶液；
S3：将所述氧化混合溶液过滤并与2份所述透明质酸钠凝胶按照200r/min的搅拌速率混合搅拌10min，得到海藻酸钠胶体；
S4：取出1份所述硝酸银和1份所述硝酸锌，按照200r/min的搅拌速率混合搅拌10min，得到第一混合物；
S5：将1份所述金霉素和1份所述黄凡士林按照200r/min的搅拌速率混合搅拌10min，得到第二混合物；
S6：将所述第一混合物和所述第二混合物按照200r/min的搅拌速率混合搅拌10min，得到高抗菌胶体；
S7：所述海藻酸钠胶体和所述高抗菌胶体按照200r/min的搅拌速率混合搅拌10min，得到混合胶体；
S8：静置使所述混合胶体凝固，进行拉伸，水洗，绕卷，干燥，随后经针刺机制成敷料，得到高抗菌垂直吸收藻酸盐敷料。
其中，将10份所述海藻酸钠加入去离子水中，按照200r/min的搅拌速率混合搅拌10min，再加入10份所述过碘酸钠溶液混合搅拌，得到混合溶液，所述混合溶液中依次倒入乙醇和氯化钠，按照200r/min的搅拌速率混合搅拌10min，得到氧化混合溶液，将所述氧化混合溶液过滤并与2份所述透明质酸钠凝胶按照200r/min的搅拌速率混合搅拌10min，得到海藻酸钠胶体，取出1份所述硝酸银和1份所述硝酸锌，按照200r/min的搅拌速率混合搅拌10min，得到第一混合物，将1份所述金霉素和1份所述黄凡士林按照200r/min的搅拌速率混合搅拌10min，得到第二混合物，将所述第一混合物和所述第二混合物按照200r/min的搅拌速率混合搅拌10min，得到高抗菌胶体，所述海藻酸钠胶体和所述高抗菌胶体按照200r/min的搅拌速率混合搅拌10min，得到混合胶体，静置使所述混合胶体凝固，进行拉伸，水洗，绕卷，干燥，随后经针刺机制成敷料，得到高抗菌垂直吸收藻酸盐敷料。
所述海藻酸钠为所述高抗菌垂直吸收藻酸盐敷的主要制作原料，所述透明质酸钠凝胶与粉末状的所述海藻酸钠混合后成为胶体，便于敷在患者伤口，便于进行垂直吸收，提高使用效果，依靠多种所述金霉素和所述黄凡士林结合，在配合所述硝酸银和所述硝酸锌，使得藻酸盐敷料具有较强的抗菌性。
第二实施例：
请参阅图2，其中图2是本发明的第二实施例的步骤流程图，本发明提供一种高抗菌垂直吸收藻酸盐敷料的制备方法，包括如下步骤：
S1：将20份所述海藻酸钠加入去离子水中，按照600r/min的搅拌速率混合搅拌30min，再加入20份所述过碘酸钠溶液混合搅拌，得到混合溶液；
S2：所述混合溶液中依次倒入乙醇和氯化钠，按照600r/min的搅拌速率混合搅拌30min，得到氧化混合溶液；
S3：将所述氧化混合溶液过滤并与6份所述交联葡聚糖凝胶按照600r/min的搅拌速率混合搅拌30min，得到海藻酸钠胶体；
S4：取出3份所述硝酸银和3份所述硝酸锌，按照600r/min的搅拌速率混合搅拌30min，得到第一混合物；
S5：将3份所述莫匹罗星和3份所述黄凡士林按照600r/min的搅拌速率混合搅拌30min，得到第二混合物；
S6：将所述第一混合物和所述第二混合物按照600r/min的搅拌速率混合搅拌30min，得到高抗菌胶体；
S7：所述海藻酸钠胶体和所述高抗菌胶体按照600r/min的搅拌速率混合搅拌30min，得到混合胶体；
S8：静置使所述混合胶体凝固，进行拉伸，水洗，绕卷，干燥，随后经针刺机制成敷料，得到高抗菌垂直吸收藻酸盐敷料。
其中，将20份所述海藻酸钠加入去离子水中，按照600r/min的搅拌速率混合搅拌30min，再加入20份所述过碘酸钠溶液混合搅拌，得到混合溶液，所述混合溶液中依次倒入乙醇和氯化钠，按照600r/min的搅拌速率混合搅拌30min，得到氧化混合溶液，将所述氧化混合溶液过滤并与6份所述交联葡聚糖凝胶按照600r/min的搅拌速率混合搅拌30min，得到海藻酸钠胶体，取出3份所述硝酸银和3份所述硝酸锌，按照600r/min的搅拌速率混合搅拌10min，得到第一混合物，将3份所述莫匹罗星和3份所述黄凡士林按照600r/min的搅拌速率混合搅拌30min，得到第二混合物，将所述第一混合物和所述第二混合物按照600r/min的搅拌速率混合搅拌30min，得到高抗菌胶体，所述海藻酸钠胶体和所述高抗菌胶体按照600r/min的搅拌速率混合搅拌30min，得到混合胶体，静置使所述混合胶体凝固，进行拉伸，水洗，绕卷，干燥，随后经针刺机制成敷料，得到高抗菌垂直吸收藻酸盐敷料。
所述海藻酸钠为所述高抗菌垂直吸收藻酸盐敷的主要制作原料，所述交联葡聚糖凝胶与粉末状的所述海藻酸钠混合后成为胶体，便于敷在患者伤口，便于进行垂直吸收，提高使用效果，依靠多种所述莫匹罗星和所述黄凡士林结合，在配合所述硝酸银和所述硝酸锌，使得藻酸盐敷料具有较强的抗菌性。
第三实施例：
请参阅图3，其中图3是本发明的第三实施例的步骤流程图，本发明提供一种高抗菌垂直吸收藻酸盐敷料的制备方法，包括如下步骤：
S1：将15份所述海藻酸钠加入去离子水中，按照400r/min的搅拌速率混合搅拌20min，再加入15份所述碳酸钠溶液混合搅拌，得到混合溶液；
S2：所述混合溶液中依次倒入乙醇和氯化钠，按照400r/min的搅拌速率混合搅拌20min，得到氧化混合溶液；
S3：将所述氧化混合溶液过滤并与4份所述琼脂糖凝胶按照400r/min的搅拌速率混合搅拌20min，得到海藻酸钠胶体；
S4：取出2份所述硝酸银和2份所述硝酸锌，按照400r/min的搅拌速率混合搅拌20min，得到第一混合物；
S5：将2份所述红霉素和2份所述黄凡士林按照400r/min的搅拌速率混合搅拌20min，得到第二混合物；
S6：将所述第一混合物和所述第二混合物按照400r/min的搅拌速率混合搅拌20min，得到高抗菌胶体；
S7：所述海藻酸钠胶体和所述高抗菌胶体按照400r/min的搅拌速率混合搅拌20min，得到混合胶体；
S8：静置使所述混合胶体凝固，进行拉伸，水洗，绕卷，干燥，随后经针刺机制成敷料，得到高抗菌垂直吸收藻酸盐敷料。
其中，将15份所述海藻酸钠加入去离子水中，按照400r/min的搅拌速率混合搅拌20min，再加入15份所述碳酸钠溶液混合搅拌，得到混合溶液，所述混合溶液中依次倒入乙醇和氯化钠，按照400r/min的搅拌速率混合搅拌20min，得到氧化混合溶液，将所述氧化混合溶液过滤并与4份所述琼脂糖凝胶按照400r/min的搅拌速率混合搅拌20min，得到海藻酸钠胶体，取出2份所述硝酸银和2份所述硝酸锌，按照400r/min的搅拌速率混合搅拌20min，得到第一混合物，将2份所述红霉素和2份所述黄凡士林按照400r/min的搅拌速率混合搅拌20min，得到第二混合物，将所述第一混合物和所述第二混合物按照400r/min的搅拌速率混合搅拌20min，得到高抗菌胶体，所述海藻酸钠胶体和所述高抗菌胶体按照400r/min的搅拌速率混合搅拌20min，得到混合胶体，静置使所述混合胶体凝固，进行拉伸，水洗，绕卷，干燥，随后经针刺机制成敷料，得到高抗菌垂直吸收藻酸盐敷料。
所述海藻酸钠为所述高抗菌垂直吸收藻酸盐敷的主要制作原料，所述琼脂糖凝胶与粉末状的所述海藻酸钠混合后成为胶体，便于敷在患者伤口，便于进行垂直吸收，提高使用效果，依靠多种所述红霉素和所述黄凡士林结合，在配合所述硝酸银和所述硝酸锌，使得藻酸盐敷料具有较强的抗菌性。
以上所揭露的仅为本申请一种或多种较佳实施例而已，不能以此来限定本申请之权利范围，本领域普通技术人员可以理解实现上述实施例的全部或部分流程，并依本申请权利要求所作的等同变化，仍属于本申请所涵盖的范围。
Claims (10)
1.一种高抗菌垂直吸收藻酸盐敷料，其特征在于，按重量份计，其制备原料包括：
10-20份海藻酸钠、2-6份凝胶、10-20份酸处理溶液、1-3份硝酸银、1-3份硝酸锌、1-3份抗菌物和1-3份黄凡士林。
2.如权利要求1所述的高抗菌垂直吸收藻酸盐敷料，其特征在于，
所述凝胶为透明质酸钠凝胶、交联葡聚糖凝胶和琼脂糖凝胶的一种。
3.如权利要求2所述的高抗菌垂直吸收藻酸盐敷料，其特征在于，
所述酸处理溶液为过碘酸钠溶液或碳酸钠溶液的一种。
4.如权利要求3所述的高抗菌垂直吸收藻酸盐敷料，其特征在于，
所述抗菌物为金霉素、莫匹罗星和红霉素的一种。
5.一种高抗菌垂直吸收藻酸盐敷料的制备方法，用于制备如权利要求4所述的高抗菌垂直吸收藻酸盐敷料，其特征在于，包括如下步骤：
将所述海藻酸钠加入去离子水中混合搅拌，再加入所述酸处理溶液混合搅拌，得到混合溶液；
所述混合溶液中依次倒入乙醇和氯化钠进行混合搅拌，得到氧化混合溶液；
将所述氧化混合溶液过滤并与所述凝胶搅拌混合，得到海藻酸钠胶体；
取出所述硝酸银和所述硝酸锌进行搅拌混合，得到第一混合物；
将所述抗菌物和所述黄凡士林进行搅拌混合，得到第二混合物；
将所述第一混合物和所述第二混合物混合搅拌得到高抗菌胶体；
所述海藻酸钠胶体和所述高抗菌胶体混合搅拌，得到混合胶体；
静置使所述混合胶体凝固，进行拉伸，水洗，绕卷，干燥，随后经针刺机制成敷料，得到高抗菌垂直吸收藻酸盐敷料。
6.如权利要求5所述的高抗菌垂直吸收藻酸盐敷料，其特征在于，
在将所述海藻酸钠加入去离子水中混合搅拌，再加入所述酸处理溶液混合搅拌，得到混合溶液的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min。
7.如权利要求6所述的高抗菌垂直吸收藻酸盐敷料，其特征在于，
在所述混合溶液中依次倒入乙醇和氯化钠进行混合搅拌，得到氧化混合溶液的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min。
8.如权利要求7所述的高抗菌垂直吸收藻酸盐敷料，其特征在于，
在将所述氧化混合溶液过滤并与所述凝胶搅拌混合，得到海藻酸钠胶体的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min。
9.如权利要求8所述的高抗菌垂直吸收藻酸盐敷料，其特征在于，
在取出所述硝酸银和所述硝酸锌进行搅拌混合，得到第一混合物的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min。
10.如权利要求9所述的高抗菌垂直吸收藻酸盐敷料，其特征在于，
在将所述抗菌物和所述黄凡士林进行搅拌混合，得到第二混合物的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min；
在将所述第一混合物和所述第二混合物混合搅拌得到高抗菌胶体的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min；
在所述海藻酸钠胶体和所述高抗菌胶体混合搅拌，得到混合胶体的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min；
在静置使所述混合胶体凝固，进行拉伸，水洗，绕卷，干燥，随后经针刺机制成敷料，得到高抗菌垂直吸收藻酸盐敷料的步骤中：
搅拌速率为200～600r/min，搅拌时间为10～30min。