CN115957367A - 一种高生物相容性涂覆液及疏水抗菌纱布敷料 - Google Patents
一种高生物相容性涂覆液及疏水抗菌纱布敷料 Download PDFInfo
- Publication number
- CN115957367A CN115957367A CN202211552855.6A CN202211552855A CN115957367A CN 115957367 A CN115957367 A CN 115957367A CN 202211552855 A CN202211552855 A CN 202211552855A CN 115957367 A CN115957367 A CN 115957367A
- Authority
- CN
- China
- Prior art keywords
- coating liquid
- gauze
- water
- coating
- silicone oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种高生物相容性涂覆液及疏水抗菌纱布敷料，所述涂覆液包括海藻酸盐、硅油乳液和水，且其质量比为(0.1～10)：(0.1～20):100，所述涂覆液能与离子液体发生凝胶反应，所述离子液体中包括钙离子、镁离子、锌离子中的至少一种。本方案通过特定的成分及配比制备的将涂覆液及与该涂覆液配合使用的纱布，使涂覆液也可以与纱布进行涂覆或浸润复合，以特制涂层赋予产品强疏水性(拒水性)特性，避免致病细菌和真菌由于亲水性而附着在受伤组织表面，减少伤口的发芽率，在治疗过程中可以持续使用，且不会产生过敏反应，为自然伤口愈合过程创造最佳条件。
Description
技术领域
本发明涉及医用敷料技术领域，具体为一种高生物相容性涂覆液及疏水抗菌纱布敷料。
背景技术
日常用品、医疗卫生用品或器械，在自然环境中容易受潮，滋生微生物，易导致各种感染。通过在材料表面赋予疏水性，可减少材料的潮变、发霉。
另外，在一些材料上赋予疏水性，可达到特殊的应用效果。德国倍思恩医疗公司(BSN Medical GmbH)发明了一种医用敷料：用脂肪酸酯例如DACC(二烷基氨基甲酰氯)或AKD(烷基烯酮二聚体)处理纱布材料，以使纱布具备强疏水性，当该纱布与创面中的病原微生物接触时，该微生物通过疏水相互作用附着于纱布上，以此可以降低创面中病原微生物的密度，促进伤口的愈合。
通常为获得疏水的材料表面，需要以活性有机硅单体、或氟化物对材料表面进行化学改性，例如三甲基氯硅烷、六甲基硅氮烷、三甲基乙氧基硅烷、甲基三乙氧基硅烷，二甲基二氯硅烷等，这些物质通常为易燃、易爆或有一定毒性，化学处理过程易导致安全、环保问题，另外部分的残留物也会影响材料本身的安全性。
发明内容
(一)解决的技术问题
针对现有技术的不足，本发明提供了一种高生物相容性涂覆液及疏水抗菌纱布敷料，解决了上述背景技术中提出的问题。
(二)技术方案
为实现以上目的，本发明通过以下技术方案予以实现：一种高生物相容性涂覆液及疏水抗菌纱布敷料，所述涂覆液包括海藻酸盐、硅油乳液和水，且其质量比为0.1～10：0.1～20:100，所述涂覆液能与离子液体发生凝胶反应，所述离子液体中包括钙离子、镁离子、锌离子中的至少一种。
优选的，所述涂覆液包括海藻酸盐、碳酸钙粉末、硅油乳液、葡萄糖酸内酯和水，且其质量比为0.1～10：0.1～10：0.1～20：0.1～10：100。
优选的，所述硅油乳液包括活性有机硅氧烷。
优选的，所述涂覆液中加入0.01％～2％质量比的银离子。
优选的，所述涂覆液中加入0.05～5％质量比的壳寡糖或水溶性壳聚糖。
优选的，所述涂覆液中加入0.5～5％质量比的水性硅溶胶，并用使用酸调节至pH值6-8。
一种疏水抗菌纱布敷料，其特征在于，包括以下步骤。
S1、使权利要求1-6所述的涂覆液，覆盖于纱布表面；
S2、将S1中得到纱布浸泡于二价金属离子溶液0-24小时；
S3、将S2得到纱布置于50-200℃干燥设备中干燥。
优选的，所述纱布为吸水性无纺布或吸水性网格布。
优选的，所述二价金属离子溶液包括硫酸盐、盐酸盐、乳酸盐、醋酸盐、柠檬酸盐、苹果酸盐、酒石酸盐中的至少一种。
优选的，所述S3之前，可先进行真空冷冻干燥。
(三)有益效果
本发明提供了一种高生物相容性涂覆液及疏水抗菌纱布敷料。具备以下
有益效果：
1、本方案通过特定的成分及配比制备的将涂覆液及与该涂覆液配合使用的纱布，使涂覆液也可以与纱布进行涂覆或浸润复合，并以特制涂层赋予产品强疏水性(拒水性)特性，避免致病细菌和真菌由于亲水性而附着在受伤组织表面，减少伤口的发芽率，在治疗过程中可以持续使用，且不会产生过敏反应，为自然伤口愈合过程创造最佳条件。
附图说明
图1为本发明细菌粘附数量的示意图；
图2为本发明疏水性接触角示意图。
具体实施方式
本发明实施例提供一种高生物相容性涂覆液及疏水抗菌纱布敷料，如图1所示，涂覆液包括海藻酸盐、硅油乳液和水，且其质量比为(0.1～10)：(0.1～20):100，涂覆液能与离子液体发生凝胶反应，离子液体中包括钙离子、镁离子、锌离子中的至少一种。
涂覆液包括海藻酸盐、碳酸钙粉末、硅油乳液、葡萄糖酸内酯和水，且其质量比为(0.1～10)：(0.1～10)：(0.1～20)：(0.1～10)：100。
硅油乳液包括活性有机硅氧烷。
涂覆液中加入(0.01％～2％)质量比的银离子。
涂覆液中加入(0.05～5％)质量比的壳寡糖或水溶性壳聚糖。
涂覆液中加入(0.5～5％)质量比的水性硅溶胶，并用使用酸调节至pH值6-8。
一种疏水抗菌纱布敷料，其特征在于，包括以下步骤。
S1、将涂覆液涂覆于纱布表面，或将纱布浸泡于涂覆液内，使涂覆液覆盖于纱布表面；
S2、将S1中得到纱布浸泡于二价金属离子溶液0-24小时；
S3、将S2得到纱布置于50-200℃干燥设备中干燥，在S3之前，可先进行真空冷冻干燥。
纱布为吸水性无纺布或吸水性网格布。
二价金属离子溶液包括硫酸盐、盐酸盐、乳酸盐、醋酸盐、柠檬酸盐、苹果酸盐、酒石酸盐中的至少一种。
将1.5g海藻酸氨溶于80ml水中，充分溶解后，加入甲基乙氧基硅油3g，甲基羟基硅油乳液6g、甲基含氢硅油5g，搅拌均匀，得到具有一定粘度的水性涂覆液，将该涂覆液涂于物品表面，例如纸张表面，然后将纸张浸没于5％的氯化钙水溶液中1-5S，拿出纸张，沥干水滴，置于150℃烘箱中，干燥20min，拿出纸张，已涂覆过的纸张表面即具有了疏水效果，如图2所示。
在另一实施例中，将1.0g海藻酸钠溶于80ml水中，充分溶解后，加入甲基羟基硅油乳液5g、甲基含氢硅油3g，搅拌均匀，加入硝酸银0.1g，得到具有一定粘度的含银离子水性涂覆液，将1mm厚的无纺布浸透该涂覆液，取出，浸没于含有2％乳酸钙和1％乳酸锌的混合水溶液中5min，取出无纺布，沥干水滴，先置于100℃干燥60min，后置于160℃烘箱中，干燥30min，即得到了含银离子的疏水抗菌无纺布。
在另一实施例中，将0.5g海藻酸钾、1g海藻酸氨溶于80ml水中，充分溶解后，加入甲基乙氧基硅油5g、乙基含氢硅油5g，搅拌均匀，加入2g碳酸钙粉末，水性硅溶胶3g，分散均匀后，再加入2.5g葡萄糖酸内酯，快速搅拌后，将涂覆液浸透于三聚氰胺泡棉上，涂覆液在3min内凝胶，静置30min，放入120℃烘箱干燥60min，升温至165℃加热30min，即得到表面疏水的三聚氰胺复合材料。
在另一实施例中，将0.5g海藻酸钠、0.5g海藻酸钾溶于100ml水中，充分溶解后，加入甲基乙氧基硅油2g、甲基含氢硅油1g，搅拌均匀，加入水溶性壳聚糖0.5g，分散均匀后，将涂覆液浸透PET棉棒，取出，放入含有2％氯化镁及1％氯化锌的混合水溶液中，静置30min，取出棉棒，放入120℃烘箱干燥60min，升温至165℃加热30min，即得到疏水PET棉棒。
在另一实施例中，将0.5g海藻酸钠、0.5g海藻酸钾溶于100ml水中，充分溶解后，加入甲基羟基硅油乳液2g，甲基乙氧基硅油2g、甲基含氢硅油1g，硝酸银0.2g，搅拌60min，将涂覆液涂覆于纱布表面，或将纱布浸泡于涂覆液中，取出沥干水滴，将纱布浸泡于醋酸锌溶液2小时，取出，沥干水滴，将纱布置于80℃烘箱中干燥60min，然后在170℃干燥30min，即得到疏水含银离子抗菌纱布敷料，再进行细菌粘附实验测试，使其应用于创面敷贴时，可以降低创面中病原微生物的密度，促进伤口的愈合。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (10)
1.一种高生物相容性涂覆液，其特征在于：所述涂覆液包括海藻酸盐、硅油乳液和水，且其质量比为(0.1～10)：(0.1～20):100，所述涂覆液能与离子液体发生凝胶反应，所述离子液体中包括钙离子、镁离子、锌离子中的至少一种。
2.一种高生物相容性涂覆液，其特征在于：所述涂覆液包括海藻酸盐、碳酸钙粉末、硅油乳液、葡萄糖酸内酯和水，且其质量比为(0.1～10)：(0.1～10)：(0.1～20)：(0.1～10)：100。
3.根据权利要求1所述的一种高生物相容性涂覆液，其特征在于：所述硅油乳液包括活性有机硅氧烷。
4.根据权利要求1所述的一种高生物相容性涂覆液，其特征在于：所述涂覆液中加入(0.01％～2％)质量比的银离子。
5.根据权利要求1所述的一种高生物相容性涂覆液，其特征在于：所述涂覆液中加入(0.05～5％)质量比的壳寡糖或水溶性壳聚糖。
6.根据权利要求1所述的一种高生物相容性涂覆液，其特征在于：所述涂覆液中加入(0.5～5％)质量比的水性硅溶胶，并用使用酸调节至pH值6-8。
7.一种疏水抗菌纱布敷料，其特征在于，包括以下步骤。
S1、使权利要求1-6所述的涂覆液，覆盖于纱布表面；
S2、将S1中得到纱布浸泡于二价金属离子溶液0-24小时；
S3、将S2得到纱布置于50-200℃干燥设备中干燥。
8.根据权利要求7所述的一种疏水抗菌纱布敷料，其特征在于：所述纱布为吸水性无纺布或吸水性网格布。
9.根据权利要求7所述的一种疏水抗菌纱布敷料，其特征在于：所述二价金属离子溶液包括硫酸盐、盐酸盐、乳酸盐、醋酸盐、柠檬酸盐、苹果酸盐、酒石酸盐中的至少一种。
10.根据权利要求7所述的一种疏水抗菌纱布敷料，其特征在于：所述S3之前，可先进行真空冷冻干燥。