CN1158877A - 颗粒活性炭表面涂层方法 - Google Patents
颗粒活性炭表面涂层方法 Download PDFInfo
- Publication number
- CN1158877A CN1158877A CN 96122352 CN96122352A CN1158877A CN 1158877 A CN1158877 A CN 1158877A CN 96122352 CN96122352 CN 96122352 CN 96122352 A CN96122352 A CN 96122352A CN 1158877 A CN1158877 A CN 1158877A
- Authority
- CN
- China
- Prior art keywords
- active
- carbong
- surface coating
- coating method
- rain surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及化工产品颗粒活性炭表面涂层方法,其通过高分子合成树脂水性乳液加涂层着色剂、稳定增稠剂混合的乳液浸渍颗粒活性炭,再在120℃下烘干,即可在颗粒活性炭表面形成涂层;生产工艺简单,易操作,产品不但改变其外观,扩大了使用范围,减少炭耗,而且对其固有性能影响少,可大力推广应用。
Description
本发明涉及林产化工产品颗粒活性炭的表面涂层方法。
颗粒活性炭用途十分广泛,然其外表黑且易掉粉末,既不雅观,又增加炭耗,如不进行涂层处理将极大地影响它的使用范围中国专利90100218公开的《活性炭表面涂层的方法》也只适于粉末活性炭的表面涂层处理,颗粒活性的表层至今尚未有一种很好的处理方法及产品。
本发明的目的是提供一种颗粒活性炭表面涂层的方法及产品。
一种颗粒活性炭表面涂层的方法是:取50-65份水加热到60-80℃,加入2-8份稳定增稠剂和10-15份高分子合成树脂水性乳液,搅拌使之混合均匀;再加入100份颗粒活性炭浸渍,经5-8小时,把浸渍过的颗粒活性炭置于120℃左右下烘干即可。
上述稳定增稠剂可以是琼脂、明胶、海藻酸钠、果胶、阿拉伯胶或羟甲基纤维素。
上述高分子合成树脂水性乳液,可以是45%的聚醋酸乙烯树脂乳液。
上述颗粒活性表面涂层的方法,还可以直接在水加热到50-60℃时加入碘化亚铜或二氧化钛作为着色剂,使表面涂层着色,产生色炭。
采用上述涂层方法,方法简单,易操作,生产方便,可以很容易地在颗粒活性炭表面形成涂层,即产生包裹层成为包裹活性炭,而且可以加入色剂,生产出色碳,其对颗粒活性炭的固有性能影响小,不但可很好地改变颗粒活性炭的外观,而且不掉粉,减少损耗。
实施例1
a、量取700ml的水在烧杯内加热至70℃,逐渐加入70克羧甲基纤维素和120克45%聚醋酸乙烯树脂乳液,搅拌均匀制成水乳液备用。
b、称取1000克颗粒活性炭,浸渍于a所制备的水乳液中。
c、把经b浸渍7小时后的颗粒活性炭至于120℃的烘箱中烘干即可。
实施例2
a、量取700ml的水在烧杯内加热,当加热到60℃左右时加入190克碘化亚铜不断搅拌,加热升温至70℃,再加入70克羧甲基纤维素和120克的45%聚醋酸乙烯树脂乳液,搅拌均匀制成水乳液备用。
其它如实施例1,即可制作出色碳。
Claims (4)
1、一种颗粒活性炭表面涂层方法:其特征是先把50-65份水加热到60-80℃,加入2-8份稳定增稠剂和10-15份高分子合成树脂水性乳液,搅拌均匀后,再加入100份颗粒活性炭,浸渍5-8小时,然后把经浸渍5-8小时的颗粒活性炭置于120℃下烘干即可。
2、根据权利要求1所述的一种颗粒活性炭表面涂层方法,其特征是所采用的稳定增稠剂可以是琼脂、明胶、海藻酸钠、果胶、阿拉伯胶或羧甲基纤维素,优化选择为羧甲基纤维素。
3、根据权利要求1所述的一种颗粒活性炭表面涂层方法,其特征是高分子合成树脂采用45%聚醋酸乙烯树脂乳液。
4、根据权利要求1、2、3所述的一种颗粒活性炭表面涂层方法,其特征是当水加热至60-80℃时,可加入碘化亚铜或二氧化钛作着色剂。