CN113564936A - 一种带芳香味的环保涂料及其墙布涂层的制备方法 - Google Patents
一种带芳香味的环保涂料及其墙布涂层的制备方法 Download PDFInfo
- Publication number
- CN113564936A CN113564936A CN202110816521.4A CN202110816521A CN113564936A CN 113564936 A CN113564936 A CN 113564936A CN 202110816521 A CN202110816521 A CN 202110816521A CN 113564936 A CN113564936 A CN 113564936A
- Authority
- CN
- China
- Prior art keywords
- layer
- coating
- parts
- environment
- wall cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种芳香味的环保涂料，包括以下重量分数的组分：纯丙烯酸酯软乳液：30‑40份；纯丙烯酸酯硬乳液：4‑6份；水：65‑75份；微胶囊香精：0.5‑1.5份；增稠剂：0.1‑0.2份，一种如上所述的芳香味的环保涂料被用在墙布上，给墙布提供怡人的香气。本发明还提供了一种带有芳香味的环保涂层墙布的制备方法，包括基层面料、防水层、底层，中间层和面层，所述基层面料即为基础布料，防水层被赋予到基层上，底层则是上述提供的一种芳香味的环保涂料，中间层为钛白浆层，面层为一层保护层，包括以下步骤：S1：基层布料进行防水处理，在一定温度下的烘箱中烘干定型；S2：上述的芳香味的环保涂料涂覆在S1步骤得到的布上烘干；S3：随后进行中间层和面层涂覆得到墙布。
Description
技术领域
本发明涉及墙布涂层技术领域，具体涉及一种带芳香味的环保涂料及其墙布涂层的制备方法。
背景技术
墙布，即一种可以糊裱于室内墙面的纤维类材料，可以起到装饰墙面、保护墙体等作用。而且墙布材料由于具有强力高、施工时不易破裂，可以进行大幅宽生产、使用无接缝和视觉舒适、触感柔和、少许隔音、高度透气、亲和性佳等优点，因此近年来越来越受到中国消费者的青睐。统计数据显示，2018年我国的墙纸销量相较于2017年减少了24.2%，而与墙纸材料形成鲜明的对比，2018年墙布的销量已经达到了7.28亿平方米，相较于前一年增加了高达72.9%。墙布表面为纺织材料，可以通过改性使墙布表面具备简单的吸湿、透气、抗菌功能，然而随着人们生活水平和生活质量的提高，这些已经已经不能够满足人们高生活品质所需，亟待改进。
香气不仅能使人产生美好遐想，对人体有镇静、消除身心疲劳、感到轻松、清香能诱发人令人爽朗，让人积极向上，添加胶囊化香精的产品，大幅度提高了香精在织物等基底上的沉积量、沉积时间和持续释香的效果。为满足人们高生活品质所需问题，现发明一种带芳香味的环保涂料及其墙布涂层的制备方法，从而实现人们对美好生活的遐想。
发明内容
本发明的目的在于提供一种带芳香味的环保涂料及其墙布涂层的制备方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种带有芳香味的环保涂料，包括以下重量分数的组分：
纯丙烯酸酯软乳液：30-40份
纯丙烯酸酯硬乳液：4-6份
水：65-75份
微胶囊香精：0.5-1.5份
增稠剂：0.1-0.2份
所述纯丙烯酸酯软乳液为丙烯酸丙酯，丙烯酸丁酯等单体共聚而成，该乳液具有良好的成膜性，柔软性，可以制得柔软的涂层；
所述纯丙烯酸酯硬乳液为丙烯酸甲酯，丙烯酸乙酯等单体共聚而成，该乳液成膜后具有良好硬挺感，可以增加涂层硬挺度；
所述微胶囊香精呈水溶性体系，微胶囊粒径为1-30μm，香精可控性释放，用高分子化合物聚脲/聚氨酯等包裹其中，保护香精不受氧化，热量，酸性，碱性，湿度或蒸发作用等影响，配方和操作安全。
进一步地，一种带芳香味的环保涂层墙布，包括基层面料、防水层、底层，中间层和面层；
所述基层面料材质为涤纶、锦纶、腈纶中的一种或多种，底层则是上述提供的一种芳香味的环保涂料，中间层为钛白浆层，面层为一层保护层。
进一步地，所述底层+中间层+面层克重为80-100g/m2。
一种带有芳香味的环保涂层墙布，制备包括以下步骤：
S1：制备防水层：将基层面料涂覆防水剂后烘干定型；
S2：制备底层：上述的一种带有芳香味的环保涂料刮涂在防水过的基层面料上进行烘干；
S3：制备中间层和面层：对上述S2步骤得到的墙布进行中间层和面层涂覆后得到墙布。
进一步地，一种带有芳香味的环保涂层墙布制备方法，
S1.1：防水剂烘干温度为170℃，烘干时间为1.5min；
S2.1：底层烘干温度为烘干温度为150℃，烘干时间为1.5min；
S3.1：中间层和面层涂覆后要进行烘干，其中烘干温度为150℃，烘干时间为1.5min。
与现有技术相比，本发明的有益效果是：
（1）微胶囊香精的香味可持续、可控性释放；
（2）香味的应用使墙布织物增加了价值，提高了产品档次和附加；
（3）满足了人们高品质生活所需，实现人们对美好生活遐想；
（4）提高了墙布的受青睐度，充分体现出墙布的价值和意义。
附图说明
图1为本发明的结构示意图。
图中：1、基层面料；2、防水层；3、底层；4、中间层；5、面层。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
请参阅图1，本发明提供的一种带芳香味的环保涂料及其墙布涂层的制备方法，包括依次为基层面料1、防水层2、底层3、中间层4和面层5；
实施例1
本实施例采用的技术方案是：制备流程如下：
S1：将基层面料涂覆防水剂后烘干定型；
S2：制备具有清新海洋香味环保涂料，将得到的涂料刮涂到S1的面料上后进行烘干；其中涂料包括以下重量分数的组分：
纯丙烯酸酯软乳液：30-40份
纯丙烯酸酯硬乳液：4-6份
水：65-75份
清新海洋微胶囊香精：1份
增稠剂：0.1-0.2份
S3：对上述S2步骤得到的墙布进行中间层和面层涂覆后得到墙布。
实施例2
本实施例与实施例1不同的之处在于底层涂料中的组分含量变化，采用的技术方案是：它的加工流程如下：
S1：将基层面料涂覆防水剂后烘干定型；
S2：制备具有清新海洋香味环保涂料，将得到的涂料刮涂到S1的面料上后进行烘干；其中涂料包括以下重量分数的组分：
纯丙烯酸酯软乳液：60-80份
纯丙烯酸酯硬乳液：8-12份
水： 130-150份
清新海洋微胶囊香精：1份
增稠剂：0.1-0.2份
S3：对上述S2步骤得到的墙布进行中间层和面层涂覆后得到墙布。
实施例3
本实施例与实施例1不同的之处在于底层涂料组分变化，采用的技术方案是：它的加工流程如下：
S1：将基层面料涂覆防水剂后烘干定型；
S2：制备具有清新海洋香味环保涂料，将得到的涂料刮涂到S1的面料上后进行烘干；其中涂料包括以下重量分数的组分：
纯丙烯酸酯软乳液：30-40份
纯丙烯酸酯硬乳液：4-6份
水：65-75份
玫瑰微胶囊香精：1份
增稠剂：0.1-0.2份
S3：对上述S2步骤得到的墙布进行中间层和面层涂覆后得到墙布。
实施例4
本实施例与实施例1不同的之处在于底层涂料组分变化，采用的技术方案是：它的加工流程如下：
S1：将基层面料涂覆防水剂后烘干定型；
S2：制备具有清新海洋香味环保涂料，将得到的涂料刮涂到S1的面料上后进行烘干；其中涂料包括以下重量分数的组分：
纯丙烯酸酯软乳液：30-40份
纯丙烯酸酯硬乳液：4-6份
水：65-75份
艾草微胶囊香精：1份
增稠剂：0.1-0.2份
S3：对上述S2步骤得到的墙布进行中间层和面层涂覆后得到墙布。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。不应将权利要求中的任何附图标记视为限制所涉及的权利要求。
Claims (5)
1.一种带有芳香味的环保涂料，其特征在于：包括以下重量分数的组分：
纯丙烯酸酯软乳液：30-40份；
纯丙烯酸酯硬乳液：4-6份；
水：65-75份；
微胶囊香精：0.5-1.5份；
增稠剂：0.1-0.2份；
所述纯丙烯酸酯软乳液为丙烯酸丙酯，丙烯酸丁酯等单体共聚而成，该乳液具有良好的成膜性，柔软性，可以制得柔软的涂层；
所述纯丙烯酸酯硬乳液为丙烯酸甲酯，丙烯酸乙酯等单体共聚而成，该乳液成膜后具有良好硬挺感，可以增加涂层硬挺度；
所述微胶囊香精呈水溶性体系，微胶囊粒径为1-30μm，香精可控性释放，用高分子化合物聚脲/聚氨酯等包裹其中。
2.一种带芳香味的环保涂层墙布，其特征在于：包括基层面料、防水层、底层，中间层和面层。
所述基层面料材质为涤纶、锦纶、腈纶中的一种或多种，底层则是上述提供的一种芳香味的环保涂料，中间层为钛白浆层，面层为一层保护层。
3.根据权利要求2所述的一种带有芳香味的环保涂层墙布，其特征在于：
所述底层+中间层+面层克重为80-100g/m2。
4.根据权利要求2所述的一种带有芳香味的环保涂层墙布，其特征在于：制备包括以下步骤：
S1：制备防水层：将基层面料涂覆防水剂后烘干定型；
S2：制备底层：上述的一种带有芳香味的环保涂料刮涂在防水过的基层面料上进行烘干；
S3：制备中间层和面层：对上述S2步骤得到的墙布进行中间层和面层涂覆后得到墙布。
5.根据权利要求4所述的一种带有芳香味的环保涂层墙布制备方法，其特征在于：
S1.1：防水剂烘干温度为170℃，烘干时间为1.5min；
S2.1：底层烘干温度为烘干温度为150℃，烘干时间为1.5min；
S3.1：中间层和面层涂覆后要进行烘干，其中烘干温度为150℃，烘干时间为1.5min。