CN115611516B - 一种彩色金砂釉及其瓷砖 - Google Patents
一种彩色金砂釉及其瓷砖 Download PDFInfo
- Publication number
- CN115611516B CN115611516B CN202211576976.4A CN202211576976A CN115611516B CN 115611516 B CN115611516 B CN 115611516B CN 202211576976 A CN202211576976 A CN 202211576976A CN 115611516 B CN115611516 B CN 115611516B
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- gold sand
- colored
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于陶瓷领域，公开了一种彩色金砂釉及其瓷砖。彩色金砂釉由金砂基础釉(长石30～52份、石英5～15份、高岭土3～12份、萤石8～20份、硅灰石10～20份、铁红4～15份、云母氧化铁0.5～6份)和适量无机着色剂组成，所述无机着色剂选自包裹红、包裹黄、包裹橙或钒兰中的一种。发明人在现有金砂基础釉的基础上，通过使用特定的色料，克服了传统金砂釉中铁红对其他色料发色的影响，打破了现有金砂釉效果仅有黑色或偏黑色金砂效果的不足，开发出了彩色金砂釉及彩色金砂釉砖。
Description
技术领域
本发明属于陶瓷领域，具体涉及一种彩色金砂釉及其瓷砖。
背景技术
金砂釉与锌、钛结晶釉不一样，它的结晶不是由针状晶体组成的放射状晶簇或者晶群，而是由许多相互孤立的像小金箔一样闪闪放光的单个薄片状晶体；这些晶体不是浮在釉面之上，而是埋藏在釉的表面之下，悬浮在透明的玻璃基体之中，由于这些晶体对入射光的反射作用，所以看上去像金星一样光辉闪耀，酷似天然砂金石一样闪闪发光。其独特的装饰效果受到人们的喜爱及欢迎。
发明人在CN107759090A公开了一种仿黑金砂大理石效果的釉料及其应用，仿黑金砂大理石效果的釉料由砂晶保护釉、云母氧化铁、陶瓷印膏组成。砂晶保护釉的原料质量组成为：钠长石为40～60份，石英为5～15份，高岭土为5～12份，萤石为3～8份，硅灰石为10～30份，三氧化二铁为5～25份。通过调整釉料配方改善工艺，可以烧制出不同效果的仿大理石效果的釉料，其产品的釉面黑色纯正，金光闪闪的金砂藏在釉中，金砂感丰满，光彩夺目。
周知的，金砂釉的装饰效果严重依赖于氧化铁，而氧化铁在釉的颜色较深，肉眼观察下为黑色或黑偏棕色，具有良好的遮盖能力，导致其他色料无法成功发色。因此，现有的金砂釉也以黑色或近黑色的深色为主。由于金砂釉的独特发色原理，导致一般认为无法得到彩色的金砂釉，限制了金砂釉的应用范围。打破现有金砂釉黑色为主的局限，开发出不同颜色的金砂效果釉料，对于扩展金砂釉的品种，扩大其应用领域具有非常重要的意义。
发明内容
本发明的目的在于克服现有技术的至少一个不足，提供一种彩色金砂釉及其瓷砖。
基于其良好的装饰效果，发明人尝试在该釉料的基础上，打破常规，开发一种彩色金砂釉。
本发明所采取的技术方案是：
本发明的第一个方面，提供：
一种彩色金砂釉，由金砂基础釉和适量无机着色剂组成，其中，所述金砂基础釉的质量原料组成为：长石：30～52份、石英：5～15份、高岭土：3～12份、萤石：8～20份、硅灰石：10～20份、铁红：4～15份、云母氧化铁：0.5～6份；所述无机着色剂选自包裹红、包裹黄、包裹橙或钒兰中的一种。
在一些彩色金砂釉的实例中，所述金砂基础釉的质量原料组成为：长石：35～50份、石英：6～12份、高岭土：5～10份、萤石：10～20份、硅灰石：10～15份、铁红：6～14份、云母氧化铁：1～5份。
在一些彩色金砂釉的实例中，所述金砂基础釉的化学质量组成为：SiO2： 29.45～69.5份、Al2O3： 5.4～13份、K2O：1～3份、Na2O： 1～2.5份、CaO： 5.2～13.8份、 MgO： 0～1份、Fe2O3：4～15份、F：2.56～6.4份。
在一些彩色金砂釉的实例中，所述包裹型无机色料可以耐受不低于1120℃的高温。
在一些彩色金砂釉的实例中，所述无机着色剂的用量不低于金砂基础釉将原料质量的8%。
在一些彩色金砂釉的实例中，所述包裹红、包裹黄或包裹橙的包裹层为硅酸锆、氧化硅、氧化铝、氧化锆。
在一些彩色金砂釉的实例中，所述包裹红为硅酸锆包裹硫硒化镉、包裹黄为硅酸锆包裹硫硒化镉、包裹橙为硅酸锆包裹硫硒化镉。
本发明的第二个方面，提供：
一种彩色金砂釉砖，包括坯体，所述坯体上设有底釉层，所述底釉层上设有本发明第一个方面所述彩色金砂釉形成的面釉层。
在一些彩色金砂釉砖的实例中，其制备方法包括如下步骤：
按金砂基础釉的组成称取原料，混匀、加入助剂和无机着色剂，制备得到彩色金砂釉浆；
在砖坯上先施一层底釉，之后施加彩色金砂釉浆，干燥；
烧成、后续经过抛光/不抛得到彩色金砂釉砖。
在一些彩色金砂釉砖的实例中，烧成的温度为1150～1230℃。
在一些彩色金砂釉砖的实例中，烧成的时间为40～70min。
本发明的有益效果是：
发明人意外发现，在众多的无机着色剂中，极少数几种无机着色剂，如包裹红、包裹黄、包裹橙或钒兰可以与金砂基础釉复合，得到彩色金砂釉，克服了铁红对其他色料发色的影响，打破了现有金砂釉效果仅有黑色或偏黑色金砂效果的不足，开发出了彩色金砂釉及彩色金砂釉砖。
附图说明
图1～4分别是实施例1～4样品的照片。
图5～8分别是对比例1～4样品的照片。
具体实施方式
本发明的第一个方面，提供：
一种彩色金砂釉，由金砂基础釉和适量无机着色剂组成，其中，所述金砂基础釉的质量原料组成为：长石：30～52份、石英：5～15份、高岭土：3～12份、萤石：8～20份、硅灰石：10～20份、铁红：4～15份、云母氧化铁：0.5～6份；所述无机着色剂选自包裹红、包裹黄、包裹橙或钒兰中的一种。
在一些彩色金砂釉的实例中，所述金砂基础釉的质量原料组成为：长石：35～50份、石英：6～12份、高岭土：5～10份、萤石：10～20份、硅灰石：10～15份、铁红：6～14份、云母氧化铁：1～5份。
在一些彩色金砂釉的实例中，所述金砂基础釉的化学质量组成为：SiO2： 29.45～69.5份、Al2O3： 5.4～13份、K2O：1～3份、Na2O： 1～2.5份、CaO： 5.2～13.8份、 MgO： 0～1份、Fe2O3：4～15份、F：2.56～6.4份。
在一些彩色金砂釉的实例中，所述包裹型无机色料可以耐受不低于1120℃的高温。
在一些彩色金砂釉的实例中，所述无机着色剂的用量不低于金砂基础釉将原料质量的8%。
在一些彩色金砂釉的实例中，所述包裹红、包裹黄或包裹橙的包裹层为硅酸锆、氧化硅、氧化铝、氧化锆。通过将色料包裹，可以提高着色剂的高温稳定性。发明人将包裹色料与本发明的金砂基础釉复配，出人意料地发现可以有效发色，克服了金砂基础釉固有的黑色或近黑色效果。
硫硒化镉 (Cd(SxSe1-x))是一系列商品化的色料，在陶瓷行业被广泛应用。随x值不同，其呈色从大红转变为橙，继而转变为黄。通过将硫硒化镉包裹，可以提高其高温稳定性。在一些彩色金砂釉的实例中，所述包裹红为硅酸锆包裹硫硒化镉、包裹黄为硅酸锆包裹硫硒化镉、包裹橙为硅酸锆包裹硫硒化镉。
本发明的第二个方面，提供：
一种彩色金砂釉砖，包括坯体，所述坯体上设有底釉层，所述底釉层上设有本发明第一个方面所述彩色金砂釉形成的面釉层。
在一些彩色金砂釉砖的实例中，其制备方法包括如下步骤：
按金砂基础釉的组成称取原料，混匀、加入助剂和无机着色剂，制备得到彩色金砂釉浆；
在砖坯上先施一层底釉，之后施加彩色金砂釉浆，干燥；
烧成、后续经过抛光/不抛得到彩色金砂釉砖。
在一些彩色金砂釉砖的实例中，烧成的温度为1150～1230℃。这样可以更好地保证烧成效果。
在一些彩色金砂釉砖的实例中，烧成的时间为40～70min。这样可以更好地保证烧成效果。
下面结合实例，进一步说明本发明的技术方案。
以下实例中，如无特别说明，百分比均为质量百分比，份数均为质量份。
以下实例中使用的包裹红为硅酸锆包裹硫硒化镉。包裹黄为硅酸锆包裹硫硒化镉。
实施例1
①金砂基础釉原料配比：长石：45份、石英：10份、萤石：15份、硅灰石：15份、高岭土：10份、铁红：10份、云母氧化铁：2份
②工艺参数：按配比准确称取原料，加入30-45%的水，羧甲基纤维素钠0.1%、三聚磷酸钠0.2%，细化得到彩色金砂釉浆基础，再加入总釉浆15%的包裹红色料搅拌均匀后直接布施在面釉砖坯上、烧成。
③工艺流程：坯体→面釉→淋彩色金砂效果釉浆→1180℃烧成60 min→抛光。
实施例2
①金砂基础釉原料配比：长石：35份、石英：6份、萤石：15份、硅灰石：15份、高岭土：5份、铁红：6份、云母氧化铁：3份；
②工艺参数：按配比准确称取原料，加入30-45%的水，羧甲基纤维素钠0.1%、三聚磷酸钠0.2%，细化得到彩色金砂；釉浆基础，再加入总釉浆15%的包裹黄色料搅拌均匀后直接布施在面釉砖坯上、烧成
③工艺流程：坯体→面釉→淋彩色金砂效果釉浆→1190℃烧成50 min→抛光。
实施例3
①金砂基础釉原料配比：长石：50份、石英：12份、萤石：20份、硅灰石：15份、高岭土：10份、铁红：12份、云母氧化铁：4份；
②工艺参数：按配比准确称取原料，加入30-45%的水，羧甲基纤维素钠0.1%、三聚磷酸钠0.2%，细化得到彩色金砂釉浆基础，再加入总釉浆15%的钒锆兰色料搅拌均匀后直接布施在面釉砖坯上、烧成
③工艺流程：坯体→面釉→淋彩色金砂效果釉浆→1200℃烧成40 min→抛光。
实施例4
①金砂基础釉原料配比：长石：45份、石英：12份、萤石：10份、硅灰石：10份、高岭土：8份、铁红：14份、云母氧化铁：5份；
②工艺参数：按配比准确称取原料，加入30-45%的水，羧甲基纤维素钠0.1%、三聚磷酸钠0.2%，细化得到彩色金砂釉浆基础，再加入总釉浆10%的钒锆兰搅拌均匀后直接布施在面釉砖坯上、烧成
③工艺流程：坯体→面釉→淋彩色金砂效果釉浆→1210℃烧成70 min→抛光。
对比例1:
①金砂基础釉原料配比：长石：45份、石英：10份、萤石：15份、硅灰石：15份、高岭土：10份、铁红：10份、云母氧化铁：2份；
②工艺参数：按配比准确称取原料，加入30-45%的水，羧甲基纤维素钠0.1%、三聚磷酸钠0.2%，细化得到彩色金砂釉浆基础，再加入总釉浆15%的锆铁红搅拌均匀后直接布施在面釉砖坯上、烧成
③工艺流程：坯体→面釉→淋彩色金砂效果釉浆→1180℃烧成60 min→抛光。
对比例2:
①金砂基础釉原料配比：长石：35份、石英：6份、萤石：15份、硅灰石：15份、高岭土：5份、铁红：6份、云母氧化铁：3份；
②工艺参数：按配比准确称取原料，加入30-45%的水，羧甲基纤维素钠0.1%、三聚磷酸钠0.2%，细化得到彩色金砂釉浆基础，再加入总釉浆15%的氧化铜搅拌均匀后直接布施在面釉砖坯上、烧成
③工艺流程：坯体→面釉→淋彩色金砂效果釉浆→1190℃烧成50 min→抛光。
对比例3:
①金砂基础釉原料配比：长石：50份、石英：12份、萤石：20份、硅灰石：15份、高岭土：10份、铁红：12份、云母氧化铁：4份；
②工艺参数：按配比准确称取原料，加入30-45%的水，羧甲基纤维素钠0.1%、三聚磷酸钠0.2%，细化得到彩色金砂釉浆基础，再加入总釉浆15%的钴兰色料搅拌均匀后直接布施在面釉砖坯上、烧成
③工艺流程：坯体→面釉→淋彩色金砂效果釉浆→1200℃烧成40 min→抛光。
对比例4:
①金砂基础釉原料配比：长石：45份、石英：12份、萤石：10份、硅灰石：10份、高岭土：8份、铁红：14份、云母氧化铁：5份；
②工艺参数：按配比准确称取原料，加入30-45%的水，羧甲基纤维素钠0.1%、三聚磷酸钠0.2%，细化得到彩色金砂釉浆基础，再加入总釉浆10%的氧化钴搅拌均匀后直接布施在面釉砖坯上、烧成
③工艺流程：坯体→面釉→淋彩色金砂效果釉浆→1210℃烧成70 min→抛光。
图1～4分别是实施例1～4样品的照片。图5～8分别是对比例1～4样品的照片。
实施例1和对比例1的区别仅在于使用的无机红色着色剂不同。从图1可看出：釉面呈鲜红色，细小金箔颗粒闪闪发光，釉面平整；从图5可看出：釉面整体为哑光、朱红，无金砂效果。
实施例2和对比例2的区别仅在于使用的无机黄色着色剂不同。从图2可看出：包裹黄与金砂基础釉反应，釉面呈绿色，贴近自然，颗粒在绿色釉层楼格外闪耀；从图6可看出：氧化铜添加无法改变金砂基础釉的原色，但是依然保持了黑金砂效果。
实施例3和对比例3的区别仅在于使用的无机蓝色着色剂不同。从图3可看出：釉面呈蓝色，仿佛深海碧蓝中的金碧，耀眼夺目；从图7可看出：釉面为哑光黑色，无金砂效果。
实施例4和对比例4的区别仅在于使用的无机蓝色着色剂不同。从图4可看出：釉面呈浅蓝色，天空中繁星点点；从图8可看出：釉面为亮黑色，无金砂效果。
上述实验数据说明不同颜料与金砂基础釉存在复杂的作用关系，特别是实施例2，使用包裹黄却得到了绿金砂效果。
以上是对本发明所作的进一步详细说明，不可视为对本发明的具体实施的局限。对于本发明所属技术领域的普通技术人员来说，在不脱离本发明构思的简单推演或替换，都在本发明的保护范围之内。
Claims (7)
1.一种彩色金砂釉，其特征在于，由金砂基础釉和适量无机着色剂组成，其中，所述金砂基础釉的质量原料组成为：长石：30～52份、石英：5～15份、高岭土：3～12份、萤石：8～20份、硅灰石：10～20份、铁红：4～15份、云母氧化铁：0.5～6份；所述无机着色剂选自包裹红、包裹黄、包裹橙或钒兰中的一种，所述包裹红为硅酸锆包裹硫硒化镉、包裹黄为硅酸锆包裹硫硒化镉、包裹橙为硅酸锆包裹硫硒化镉，所述无机着色剂的用量不低于金砂基础釉将原料质量的8%。
2.根据权利要求1所述的彩色金砂釉，其特征在于，所述金砂基础釉的质量原料组成为：长石：35～50份、石英：6～12份、高岭土：5～10份、萤石：10～20份、硅灰石：10～15份、铁红：6～14份、云母氧化铁：1～5份。
3.根据权利要求1或2所述的彩色金砂釉，其特征在于，所述金砂基础釉的化学质量组成为：SiO2： 29.45～69.5份、Al2O3： 5.4～13份、K2O：1～3份、Na2O： 1～2.5份、CaO： 5.2～13.8份、 MgO： 0～1份、Fe2O3：4～15份、F：2.56～6.4份。
4.一种彩色金砂釉砖，包括坯体，所述坯体上设有底釉层，其特征在于，所述底釉层上设有权利要求1～3任一项所述彩色金砂釉形成的面釉层。
5.根据权利要求4所述的彩色金砂釉砖，其特征在于，其制备方法包括如下步骤：
按金砂基础釉的组成称取原料，混匀、加入助剂和无机着色剂，制备得到彩色金砂釉浆；
在砖坯上先施一层底釉，之后施加彩色金砂釉浆，干燥；
烧成、后续经过抛光/不抛得到彩色金砂釉砖。
6.根据权利要求5所述的彩色金砂釉砖，其特征在于，烧成的温度为1150～1230℃。
7.根据权利要求5或6所述的彩色金砂釉砖，其特征在于，烧成的时间为40～70min。