CN115559042A - Preparation method of four-side stretch denim fabric not prone to wrinkling - Google Patents
Preparation method of four-side stretch denim fabric not prone to wrinkling Download PDFInfo
- Publication number
- CN115559042A CN115559042A CN202211206942.6A CN202211206942A CN115559042A CN 115559042 A CN115559042 A CN 115559042A CN 202211206942 A CN202211206942 A CN 202211206942A CN 115559042 A CN115559042 A CN 115559042A
- Authority
- CN
- China
- Prior art keywords
- yarn
- yarns
- sizing
- wrinkle
- dyeing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A preparation method of a four-side stretch jean fabric difficult to wrinkle comprises the steps of firstly, winding prepared comprehensive covering yarns on a warp beam in parallel according to the specified length and width through a warping machine, arranging the warp beam in batches, then carrying out water washing treatment on the comprehensive covering yarns on the warp beam, drying after the water washing treatment is finished, and carrying out yarn slicing, winding beam sizing, weaving, preshrinking, impurity removal, dyeing and sizing after the drying is finished. The prepared four-side elastic jean fabric which is not easy to wrinkle adopts the same warp and weft, is not easy to wrinkle and has good comfort level; meanwhile, the warp-wise and weft-wise composite core yarn structure breaks through the limitation of elasticity, so that the finished product made of the four-side stretch fabric is stiff and smooth and has strong free dynamic sense.
Description
Technical Field
The invention relates to the technical field of fabric processing, in particular to a preparation method of a four-side stretch jean fabric which is not easy to wrinkle.
Background
With the continuous improvement of living standard, the requirements of people on the type and comfort level of clothes are also continuously improved. The jean fabric has extensive application in the fields of advanced fashionable dress and common tools due to rough style, simple and natural style, practicality and wear resistance, but the traditional jean fabric is thick in texture, airtight, hard in hand feeling and insufficient in elasticity, so that the wearing freedom and dynamic sense are insufficient, squatting or crossing is affected, clothes folds after the jean fabric is worn for a period of time, and particularly knee parts, elbow parts and the like of the clothes are prevented from deforming and bulging due to long wearing time.
Lycra is a registered trademark of dupont for spandex, and is thus spandex fiber. Spandex fiber has such a high elasticity because its polymer chain is composed of a matrix of low-melting, amorphous soft segments and embedded therein high-melting, crystalline hard segments. The flexible chain segments are crosslinked to form a network structure, and can freely stretch and retract due to small interaction force among the chains to form the elongation performance; the bonding force of the rigid chain segment is higher, and the chain can not extend without limit, so that high resilience is caused; therefore, the application of the Lycra to the four-side elastic jean fabric has important significance.
Disclosure of Invention
The invention aims to provide a method for preparing a four-side elastic jean fabric which is not easy to wrinkle so as to solve the problems in the background technology.
The technical problem solved by the invention is realized by adopting the following technical scheme:
a preparation method of a four-side stretch jean fabric which is not easy to wrinkle comprises the following specific steps:
1) Warping machine
Winding the prepared comprehensive covered yarn on a warp beam in parallel according to the specified length and width by a warping machine;
the warp and the weft are both formed wrap yarns and elastic wrap yarns, and are blended into a comprehensive wrap yarn; the core yarn of the sizing covering yarn is lycra filament, the covering layer is cellulose fiber, the core yarn of the elastic covering yarn is formed by bonding high-elastic polyester and spandex, and the covering layer is long staple cotton fiber;
2) Sizing
The warp beam is finished in batches, then the comprehensive covered yarns on the warp beam are washed by water, and then are dried after the washing treatment is finished, and the yarns are sliced and wound on a loom beam for sizing after the drying is finished;
3) Weaving
Merging warps of the slashes obtained in the step 2), then drafting and reeding, and weaving a creel subjected to the reeding to a loom to form gray cloth by the same warps and the same wefts;
4) Preshrinking
Placing the gray cloth woven in the step 3) on a preshrinking machine for preshrinking treatment;
5) Removing impurities
Placing the gray cloth woven in the step 4) in a blending liquid for treatment so as to remove impurities covered on the gray cloth;
6) Dyeing process
Placing the gray cloth subjected to impurity removal in the step 5) in a dyeing solution for dyeing, and washing with water after dyeing until no floating color appears to obtain dyed cloth;
7) Shaping
Dehydrating the dyed cloth obtained in the step 5), and then adopting steam for shaping;
8) Drying by baking
Drying the fabric shaped in the step 7);
9) Cloth inspection
And (4) detecting the dried fabric in the step 8), packaging after the dried fabric is qualified, and storing in a warehouse.
In the invention, in step 1), the process parameters of the warping machine are as follows: the process parameters of the warping machine are as follows: the speed of the warping machine is 360m/min, the angle of a tension rod is 110 degrees, the tension ring is 15g, the middle is 17g, the lower is 15g, the front is 20g, the middle is 17g, the rear is 21g, the middle is 16g, the side is 20g, and the maximum number of hung yarns on a warping creel is 1683.
In the invention, in step 2), the sizing process parameters are as follows: 125kg of modified starch, 48kg of glue, 20kg of rubber powder, 8kg of wax sheets, 1350L of volume, 12 percent of elongation and 10 percent of sizing rate.
In the invention, in step 6), the dyeing solution comprises water, a dispersion regulator and a fixing agent, and the color of the dispersion regulator is determined according to the printing and dyeing; and dyeing and keeping the temperature for 50 to 60min.
In the invention, in step 8), the process parameters of the drying machine are as follows: the drying temperature is 155-165 ℃.
Has the advantages that: the prepared four-side elastic jean fabric which is not easy to wrinkle adopts the same warp and the same weft, is not easy to wrinkle and has good comfort level; meanwhile, the warp-wise and weft-wise composite core yarn structure breaks through the limitation of elasticity, so that the finished product made of the four-side stretch fabric is stiff and smooth and has strong free dynamic sense.
Detailed Description
In order to make the technical means, the creation characteristics, the achievement purposes and the effects of the invention easy to understand, the invention is further described with the specific embodiments.
A preparation method of a four-side stretch jean fabric difficult to wrinkle comprises the following specific steps:
1) Warping machine
The prepared comprehensive covered yarn is wound on a warp beam in parallel according to the specified length and width through a warping machine, and the technological parameters of the warping machine are as follows: the speed is 360m/min, the angle of a tension rod is 110 degrees, the tension ring is 15g, the middle 17g, the lower 15g, the front 20g, the middle 17g and the rear 21g, the middle yarn tension is 16g, the edge yarn tension is 20g, the maximum number of hung yarns on a warping creel is 1683, and the yarn tension is controlled within the range of standard +/-0.5 g under the condition of ensuring no damage or damage to the yarn form;
the warp yarns and the weft yarns are blended into a comprehensive covering yarn by processing and blending the sizing covering yarn and the elastic covering yarn; the core yarn of the sizing covering yarn is lycra filament, the covering layer is cellulose fiber, the core yarn of the elastic covering yarn is formed by bonding high-elastic polyester and spandex, and the covering layer is long staple cotton fiber;
2) Sizing
The warp beam is finished in batches, then the comprehensive covered yarns on the warp beam are washed by water, and then are dried after the washing treatment is finished, and the yarns are sliced and wound on a loom beam for sizing after the drying is finished; the sizing process parameters are as follows: 125kg of modified starch, 48kg of glue, 20kg of rubber powder, 8kg of wax sheets, 1350L of volume, 12% of elongation and 10% of sizing rate;
3) Weaving
Merging warps of the slashes obtained in the step 2), then drafting and reeding, and weaving a creel subjected to the reeding to a loom to form gray cloth by the same warps and the same wefts;
the drafting reed is 1, 2 and 3, 4, and the drafting reed is required to penetrate according to the process specification and cannot penetrate more or less;
4) Preshrinking
Placing the gray cloth woven in the step 3) on a preshrinking machine for preshrinking treatment;
5) Removing impurities
Placing the gray cloth woven in the step 4) in a blending liquid for treatment so as to remove impurities covered on the gray cloth;
6) Dyeing process
Placing the gray cloth subjected to impurity removal in the step 5) in a dyeing solution for dyeing, and washing with water after dyeing until no floating color appears to obtain dyed cloth;
the dyeing liquid comprises water, a dispersion regulator and a fixing agent, and the color of the dispersion regulator is determined according to the printing and dyeing; dyeing and keeping the temperature for 50 to 60min;
7) Shaping
Dehydrating the dyed cloth obtained in the step 5), and then adopting steam for shaping;
8) Drying by baking
Drying the fabric shaped in the step 7), wherein the process parameters of a drying machine are as follows: the drying temperature is 155-165 ℃;
9) Cloth inspection
And (4) detecting the dried fabric in the step 8), packaging after the dried fabric is qualified, and storing in a warehouse.
Claims (7)
1. A preparation method of a four-side stretch jean fabric difficult to wrinkle is characterized by comprising the following specific steps:
1) Warping machine
The prepared comprehensive covering yarn is wound on a warp beam in parallel according to the specified length and width through a warping machine;
the warp and the weft are both formed wrap yarns and elastic wrap yarns, and are blended into a comprehensive wrap yarn; the core yarn of the sizing covered yarn is lycra filament, the covering layer is cellulose fiber, the core yarn of the elastic covered yarn is formed by bonding high-elastic polyester and spandex, and the covering layer is long staple cotton fiber;
2) Sizing
The warp beam is finished in batches, then the comprehensive covered yarns on the warp beam are washed by water, and then are dried after the washing treatment is finished, and the piece yarns and the winding beam are sized after the drying is finished;
3) Weaving
Merging warps of the slashes obtained in the step 2), then drafting and reeding, and weaving a creel subjected to the reeding to a loom to form gray cloth by the same warps and the same wefts;
4) Preshrinking
Placing the gray cloth woven in the step 3) on a preshrinking machine for preshrinking treatment;
5) Removing impurities
Placing the gray cloth woven in the step 4) in a blending liquid for treatment so as to remove impurities covered on the gray cloth;
6) Dyeing process
Placing the gray cloth subjected to impurity removal in the step 5) in a dyeing solution for dyeing, and washing with water after dyeing until no floating color appears to obtain dyed cloth;
7) Shaping
Dehydrating the dyed cloth obtained in the step 5), and then adopting steam for shaping;
8) Drying by baking
Drying the fabric shaped in the step 7);
9) Cloth inspection
And (4) detecting the dried fabric in the step 8), packaging after the dried fabric is qualified, and storing in a warehouse.
2. The preparation method of the tetrahedral elastic denim fabric difficult to wrinkle according to claim 1, wherein in the step 1), the warping machine process parameters are as follows: the process parameters of the warping machine are as follows: the speed of the warping machine is 360m/min, the angle of a tension rod is 110 degrees, the tension ring is 15g, the middle is 17g, the lower is 15g, the front is 20g, the middle is 17g, the rear is 21g, the middle is 16g, the side is 20g, and the maximum number of hung yarns on a warping creel is 1683.
3. The method for preparing the tetrahedral elastic denim fabric difficult to wrinkle according to the claim 1, wherein in the step 2), the sizing process parameters are as follows: 125kg of modified starch, 48kg of glue, 20kg of glue powder, 8kg of wax sheet, 1350L of volume, 12% of elongation and 10% of sizing rate.
4. The method for preparing the tetrahedral elastic denim fabric difficult to wrinkle according to the claim 1, characterized in that in the step 6), the dyeing liquid comprises water, dispersing agent and fixing agent.
5. The preparation method of the tetrahedral elastic denim fabric difficult to wrinkle according to claim 4, characterized in that the dyeing and heat preservation time is 50 to 60min.
6. The method for preparing the tetrahedral elastic denim fabric difficult to wrinkle according to the claim 1, characterized in that in the step 8), the dryer process parameters are as follows: the drying temperature is 155-165 ℃.
7. The four-side stretch denim fabric difficult to wrinkle is characterized in that warp yarns and weft yarns are blended into a comprehensive wrap yarn by processing and blending sizing wrap yarns and stretch wrap yarns; the core yarn of the sizing covered yarn is lycra filament, the covering layer is cellulose fiber, the core yarn of the elastic covered yarn is formed by bonding high-elastic polyester and spandex, and the covering layer is long staple cotton fiber.