CN201400747Y - Terry fabric - Google Patents
Terry fabric Download PDFInfo
- Publication number
- CN201400747Y CN201400747Y CN200920036558XU CN200920036558U CN201400747Y CN 201400747 Y CN201400747 Y CN 201400747Y CN 200920036558X U CN200920036558X U CN 200920036558XU CN 200920036558 U CN200920036558 U CN 200920036558U CN 201400747 Y CN201400747 Y CN 201400747Y
- Authority
- CN
- China
- Prior art keywords
- fabric
- yarns
- tram
- weave
- warp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a terry fabric, belonging to textile technical field. The terry fabric is woven from warp yarns and weft yarns. The fabric is woven in a combined satin weave and 1/1plain weave structuring mode by taking 75D/72F-150D/144 polyester filament yarn (FDY) as wrap yarns and 200D/72F-300D/144 easy-to-shrink polyester filament yarn (FDY) as weft yarns, with the warp-direction density of the fabric be 40-60 yarns per centimeter and the weft-direction density be 40-60 yarns per centimeter. The two types of fibers with different shrinkage in the warp easy-to-shrink fibers change, and the fiber with big shrinkage shrinks about 50% while the rest part of fiber does not shrink and forms terries. The terry fabric is simple and reasonable in structure and easy to weave and canbe woven by existing looms; the terry fabric is soft in handle and has good breathability and comfortableness and stronger water absorption, therefore, the terry fabric can be used as fabric for high-quality garment and home textile products, and the surface of the fabric is soft and presents unique stereoscopic effect due to the terries.
Description
Technical field
The utility model relates to a kind of loop fabric, and particularly a kind of structure of different shrinkage fiber loop fabric belongs to textile technology field.
Background technology
Development along with society, growth in the living standard, people are to clothes, the comfortableness of family's textile fabric, functional requirement is more and more higher, terylene is the very good textile fabric of a kind of physical property, its fabric conformality is good, well-pressed crease-resistant, dimensionally stable, but also exist the feel plate hard, problem that water imbibition is not enough or the like, these drawbacks limit the application of polyester fiber raw materials, the knop cloth of simultaneously traditional terry cloth loom weaving can not satisfy aesthetic level and personalization that people improve constantly owing to be subjected to the machinery restriction to make cloth style more common, the demand of differentiation.
The utility model content
The purpose of this utility model is exactly the deficiency that exists at above-mentioned prior art, and a kind of different shrinkage fiber loop fabric is provided, and this fabric conformality is good, well-pressed crease-resistant, dimensionally stable, soft, good water absorption satisfies aesthetic level and demand personalized, differentiation that people improve constantly.
The purpose of this utility model is to realize like this, a kind of loop fabric, be interwoven by organizine 1 and tram 2, it is characterized in that: described organizine 1 is 75D/72F~150D/144FDY polyester filament, tram 2 is 200D/72F~300D/144FDY terylene hetero-shrinkage continuous yarn, interweaves in the united organization mode of satin weave+1/1 plain weave and makes.
The warp-wise density that described organizine 1 and tram 2 interweave is every centimetre of 40-60 root, and latitudinal density is every centimetre of 40-60 root.The Origin And Destination of the looped pile that tram forms is crossed over organizine 5-9 root, and the diameter of tram is equal to or greater than through filament diameter.
The utility model is rational in infrastructure simple, weaves easily.This fabric is owing to adopt polyester filament and hetero-shrinkage continuous yarn to interweave, and the fiber of two kinds of shrinkage difference changes in the tram different shrinkage fiber, and a part of fiber shrinkage that shrinkage is big reaches about 50%, does not form looped pile thereby another part fiber then has shrinkage.By raw material select for use, fabric construction design makes this loop fabric feel soft more with the back finishing technique, has air permeability and good, comfortableness, water imbibition is stronger.This fabric has been broken through the single limitation of traditional weaving towel cloth pattern, is not carrying out under the prerequisite of weaving loom modification, and fabric is after printing and dyeing processing, and cloth cover presents unique looped pile stereoeffect and soft cloth style, becomes a kind of high-grade clothing and tame textile fabric.
Description of drawings
Fig. 1 is that structural representation is organized on plane of the present utility model;
Fig. 2 is an institutional framework schematic diagram of the present utility model;
Among the figure: 1 organizine, 2 trams.
The specific embodiment
Further the utility model is described below in conjunction with accompanying drawing.
A kind of loop fabric, be interwoven by organizine 1 and tram 2, organizine 1 is 75D/72F~150D/144FDY polyester filament, and tram 2 is 200D/72F~300D/144FDY terylene hetero-shrinkage continuous yarn, and the fabric that is woven into is the united organization mode pilotaxitic texture with satin weave+1/1 plain weave.The warp-wise density that organizine 1 and tram 2 interweave is every centimetre of 40-60 root, and latitudinal density is every centimetre of 40-60 root.The Origin And Destination of the looped pile that tram forms is crossed over organizine 5-9 root, but the tram overstriking.Concrete implementation step and requirement are:
(1) Fabric Design
1, organizine 1 is the 200D/96FFDY polyester filament
2, tram 2 is a 105D/36F+105D/36F terylene hetero-shrinkage continuous yarn
3, be organized as 1/9 satin weave+1/1 plain weave united organization
4, total warp: 6336, porter: metric system 14# reed, every reed are worn two, 126.3 centimetres of reed widths, 58 of following machine filling densities
(2) technological design
1, do not have the twisting filament characteristic at organizine for the FDY type, should make long filament in preparatory process, guarantee certain elasticity and moisture regain, weave confidential asking, prevent because of the elasticity and the too small cracked ends phenomenon that causes that gets damp again to satisfy.
2, be the different contraction terylene long filament of 105D/36F+105D/36F at tram, should guarantee that its network degree is even, the off-grid phenomenon can not be arranged.
3, this kind broadwise shrinkage is bigger, needs weaving on 230 centimetres of wealthy width of cloth water jet loomss, will prevent short latitude phenomenon to take place in weaving process, must adjust knitting technology, guarantees fabric quality and style.
(3) master operation technology
1, warping process
Adopt field, Japanese Tianjin coltfoal high-speed warping machine, this warping machines principal character is: equipment can guarantee that in running thread-tension is even.Several 1056 of row's tube, 180 meters/minute of speed of beamings, monofilament tension force 16 grams, warper drum pressure is 3KG.
2, slurry wire process
Adopt field, a Japanese Tianjin coltfoal slurry silk machine, this slurry silk machine principal character is: organizine does not contact the dipping slurries mutually, to the slurries of no twisting filament by the reinstate fruit better, twines because of single fiber glues with alleviation and to cause that to weave opening unclear, influences normal wefting insertion.Concrete technology is:
Row's tube number | 1056 | Percentage elongation | -0.9% | |
The slurry silk speed of a motor vehicle | 120m/min | Coiling tension | 20kg | |
Move back Jie's tension force | | Drying room | 1 temperature | 120℃ |
Pressure roller pressure | 1.0 | Drying room | 2 temperature | 130℃ |
The submergence roller pressure | 3.0 | Drying cylinder | 1 temperature | 105℃ |
The slurry place of production | Suzhou | |
105℃ | |
Slurry concentration | 11° | Drying cylinder 3 temperature | 105℃ |
3, looming operation
It is 1~12 suitable wearing in proper order that the ground tissue is gaited, and always through 6336, porter is the 14# reed, and every reed is worn 2,226.3 centimetres of reed widths.
4, weaving process
Adopt homemade multi-arm 230 type water jet loomss, last machine is counter to be knitted, and concrete weaving process is:
5, dyeing and finishing process
The dyeing and finishing technology flow process is: open-width desizing → preshrunk processing → dyeing → back typing.
Claims (3)
1, a kind of loop fabric, be interwoven by organizine (1) and tram (2), it is characterized in that: described organizine (1) is 75D/72F~150D/144FDY polyester filament, tram (2) is 200D/72F~300D/144FDY terylene hetero-shrinkage continuous yarn, interweaves in the united organization mode of satin weave+1/1 plain weave and makes.
2, a kind of loop fabric according to claim 1 is characterized in that: the warp-wise density that described organizine (1) and tram (2) interweave is every centimetre of 40-60 root, and latitudinal density is every centimetre of 40-60 root.
3, a kind of loop fabric according to claim 1 is characterized in that: the Origin And Destination of the looped pile that described tram forms is crossed over organizine 5-9 root, and the diameter of tram is equal to or greater than through filament diameter.