CN115491130A - 一种抗菌人造石材抛光液及其制备方法 - Google Patents
一种抗菌人造石材抛光液及其制备方法 Download PDFInfo
- Publication number
- CN115491130A CN115491130A CN202211223766.7A CN202211223766A CN115491130A CN 115491130 A CN115491130 A CN 115491130A CN 202211223766 A CN202211223766 A CN 202211223766A CN 115491130 A CN115491130 A CN 115491130A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- artificial stone
- polishing solution
- agent
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗菌型人造石材抛光液及其制备方法，属于抛光剂技术领域。所述抗菌型人造石抛光液包括以下成分：增光剂、抗菌剂、润滑剂、防污剂、去离子水，所述抗菌剂为Ag离子掺杂的纳米TiO2分散液，经过硅烷偶联剂改性后，更容易填充在人造石材表面的粗糙凹槽上。本发明所述的抛光液在光照条件下能发挥TiO2的自清洁抗菌性能，同时由于Ag离子的加入可达到在无光照下的抗菌效果，因此抗菌效果持久，大肠杆菌抑菌率达到99％以上，且石材光泽度高，耐久性强，使用方便。制备方法简单，有利于市场推广。
Description
技术领域
本发明属于抛光液生产技术领域，涉及一种抗菌人造石材抛光液及其制备方法。
背景技术
人造石材是以天然大理石或方解石、白云石、硅砂、玻璃粉、建筑废料、矿渣等无机物粉料，以不饱和聚酯树脂为黏结剂，并加入适量的阻燃剂、无机颜料等，经配料混合、瓷铸、压缩、挤压等方法成型固化制成的。与天然石材相比，人造石具有色彩艳丽，光洁度高、颜色均匀一致，抗压耐磨、结构致密、坚固耐用等特点，且由于采用建筑废料或矿渣等作为原材料，节能环保，是一种绿色环保的建材产品。然而人造石在使用一段时间后或者在一定的环境下(厨房、医院等)使用时，石材表面光泽度下降，容易滋生细菌、发生霉变，不仅造成石材美观度下降，而且对于特定环境下石材的污染度增加。
目前对于人造石材的抛光方法主要由物理抛光和化学抛光两种方法。物理的方法主要是利用砂纸对石材表面进行打磨，再涂上釉面漆，使其光亮。化学的方法主要是使用一些抛光剂对表面进行处理，使其光亮度和耐久性都得以恢复。再者抛光剂的使用比较方便，容易实施，更受广大消费者的喜欢。
目前市面上也有很多抛光液，但是一般都不具有抗菌性能，且成分比较复杂，且有些抛光液的成分价格不具有市场优势。我们针对人造石材在生产工艺中的特点：最后一道工序就需要对人造石材进行抛光。因此我们将具有抗菌性能的抛光液对人造石材进行抛光，赋予人造石材抗菌的性能。
发明内容
本发明提供了一种抗菌人造石材抛光液，可用于人造石材在成型过程中的抛光，同时起到抗菌功效，满足特定的环境使用(厨房台面或医院墙面等)，同时这种抛光材料还可以用于后期维护石材表面的抛光液。
为实现上述目的，本发明具体技术方案为：一种抗菌人造石材的抛光液，以重量份为单位，包括以下原料：增光剂5-20份，润滑剂1-6份，防污剂4-10份，抗菌剂1-10份，去离子水20-150份。
优选地，所述增光剂为丙三醇、乙二醇的一种或两种混合组成。
优选地，润滑剂选自丙三醇、乙二醇、甲基硅油中的一种或多种。
优选地，所述防污剂为丙烯酸甲酯、丙烯酸丁酯、丙烯酸、甲基丙烯酸酯的一种或几种混合而成。
优选地，所述抗菌剂为加入硅烷偶联剂的Ag/TiO2粉末分散液组成。其中抗菌剂的制备方法如下：纳米二氧化钛和一定量的Ag+，并加入一定量的硅烷偶联剂KH550或KH560或KH57，一定量的去离子水，搅拌分散，然后在超声波中分散，调整溶液pH为4-5，在室温下反应1-3h，得到硅烷偶联剂改性的Ag掺杂的TiO2分散液(Ag/TiO2)，抽滤，乙醇洗涤，真空干燥。优选地纳米二氧化钛的尺寸为200nm，100nm，50nm，30nm，20nm，5nm。
本发明所述的抗菌人造石材抛光液，采用具有光催化效应的TiO2为主体，使石材在光照的环境下具有自清洁抗菌的性能。此外掺杂一定量的Ag离子，使抗菌剂在没有光照的环境下同时兼具抗菌性能，能够有效抑制石材在不同环境下表面细菌、霉菌的滋生。
附图说明
图1是未涂敷抛光液的人造石材的SEM图；
图2是涂敷抛光液的人造石材的SEM图；
图3是抗菌剂抗大肠杆菌的效果图，其中a为未涂敷抛光液的人造石材测试效果图，b为涂敷抛光液的人造石材测试效果图。
具体实施方式
为了更好地理解本发明，以下结合具体实施案例，进一步详细说明本发明，但是本发明不仅限于此。
实施例1
所述抗菌型人造石材抛光液，以重量份为单位，包括以下原料：液体石蜡10份，增光剂乙二醇2份，防污剂聚丙烯酸1份，抗菌剂硅烷偶联剂改性的Ag/TiO2粉末5份，去离子水90份。
所述抗菌剂的制备方法：称取10g尺寸为200nm的二氧化钛粉末，加入质量比为1.0％的Ag+(AgNO3)，和质量比为1.0％的硅烷偶联剂KH550，一定量的去离子水，搅拌分散，然后在700w超声波中分散5min，调整溶液pH为4-5，在室温下反应1-3h，得到改性的Ag掺杂的TiO2分散液，抽滤，乙醇洗涤，真空干燥，得到Ag/TiO2抗菌剂。
实施例2
所述抗菌型人造石材抛光液，以重量份为单位，包括以下原料：液体石蜡10份，增光剂丙三醇3份，防污剂聚丙烯酸1份，抗菌剂硅烷偶联剂改性的Ag/TiO2粉末5份，去离子水90份。
抗菌剂制备方法同实例1
实施例3
所述抗菌型人造石材抛光液，以重量份为单位，包括以下原料：液体石蜡10份，增光剂丙三醇3份，防污剂聚丙烯酸5份，抗菌剂硅烷偶联剂改性的Ag/TiO2粉末2份，去离子水90份。
抗菌剂制备方法同实例1
实施例4
所述抗菌型人造石材抛光液，以重量份为单位，包括以下原料：液体石蜡10份，增光剂丙三醇3份，防污剂聚丙烯酸5份，抗菌剂硅烷偶联剂改性的Ag/TiO2粉末5份，去离子水100份。
抗菌剂制备方法同实例1
应用试验
将实施例1-4的抛光液涂敷于已高温消毒的人造石材表面，进行抗菌测试，参见图1-3，结果表明，抗大肠杆菌均在99％以上，具有良好的抗菌效果。
以上所述本发明的具体实施方式，并不构成对本发明保护范围的限定。任何根据本发明的技术构思所做出的各种其他相应的改变与变形，均应包含在本发明权利要求的保护范围内。
Claims (8)
1.一种抗菌性人造石材抛光液，其特征在于，以重量份为单位，包括以下原料：增光剂5-20份，润滑剂1-6份，防污剂4-10份，抗菌剂1-10份，去离子水20-150份。
2.根据权利要求1所述的抗菌型人造石材抛光液，其特征在于，所述增光剂为丙三醇、乙二醇的一种或两种混合组成。
3.根据权利要求1所述的抗菌型人造石材抛光液，其特征在于，润滑剂选自丙三醇、乙二醇、甲基硅油中的一种或多种。
4.根据权利要求1所述的抗菌型人造石材抛光液，其特征在于，防污剂为丙烯酸甲醋、丙烯酸丁醋、丙烯酸、甲基丙烯酸醋的一种或几种混合而成。
5.根据权利要求1所述的抗菌型人造石材抛光液，其特征在于，抗菌剂为Ag掺杂的纳米二氧化钛。
6.根据权利要求5所述的抗菌型人造石材抛光液，其特征在于，Ag掺杂的纳米二氧化钛的制备步骤为：
纳米二氧化钛和一定量的Ag+，并加入一定量的硅烷偶联剂KH550或KH560或KH57，一定量的去离子水，搅拌分散，然后在超声波中分散，调整溶液pH为4-5，在室温下反应1-3h，得到硅烷偶联剂改性的Ag+掺杂的TiO2分散液，抽滤，乙醇洗涤，真空干燥。
7.根据权利要求6所述的抗菌型人造石材抛光液，其特征在于，其中，Ag+加入量为0.5～10wt％；硅烷偶联剂加入量为0.5～10wt％；TiO2的颗粒尺寸为10～500nm。
8.一种抗菌性人造石材抛光液的制备方法，其特征在于，将权利要求1-7任意一项抗菌性人造石材抛光液各原料混合而成。