CN103589218A - 一种低柔性弹性腻子的研制 - Google Patents
一种低柔性弹性腻子的研制 Download PDFInfo
- Publication number
- CN103589218A CN103589218A CN201310553570.9A CN201310553570A CN103589218A CN 103589218 A CN103589218 A CN 103589218A CN 201310553570 A CN201310553570 A CN 201310553570A CN 103589218 A CN103589218 A CN 103589218A
- Authority
- CN
- China
- Prior art keywords
- putty
- bouncing putty
- interior wall
- good
- wall coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种低柔性弹性腻子的研制按重量百分比计算为:水:5-7%;1.5%纤维素醚溶液:16-20%;分散剂:0.4-0.7%;消泡剂:0.3-0.5%;润湿剂:0.8-1%;木质纤维素:0.2-0.4%;滑石粉:8-12%;石英砂:35-40%;白水泥:8-12%;重钙:2-4%;硬脂酸锌:0.5-1.5%;弹性乳液:20-25%;该弹性腻子不仅具有防水抗裂性能,更具优异的打磨性能,极佳的低柔弹性,提高墙面打磨平整效果,施工性好,显著提高与之配套涂料的装饰性能。
Description
技术领域 本发明涉及一种腻子,特别涉及一种防止建筑物外墙开裂的易打磨弹性腻子,属于化工涂料技术领域。
背景技术 在建筑涂料的施工过程中,腻子质量的好坏对涂膜质量起着决定性的作用,涂膜表面出现的开裂、脱落等问题与底层腻子有直接的联系。而现在市场上的弹性腻子虽然有很好的抗开裂性,有很好的防水性,能够满足墙面抗裂要求,也有很好的施工性,但是打磨性很差,腻子刮涂上墙干燥后没有办法打磨,墙面平整度无法保证,致使与腻子配套涂料装饰性很差。因此研究具有防水抗裂、低柔抗渗性和容易打磨能的弹性腻子意义重大。
发明内容 本发明的目的是提供一种弹性腻子,该弹性腻子不仅具有防水抗裂性能,更具优异的打磨性能,极佳的低柔弹性,提高墙面打磨平整效果,施工性好,显著提高与之配套涂料的装饰性能。
一种低柔性弹性腻子的研制按重量百分比计算为:
水:5-7%;1.5%纤维素醚溶液:16-20%;分散剂:0.4-0.7%;消泡剂:0.3-0.5%;润湿剂:0.8-1%;木质纤维素:0.2-0.4%;滑石粉:8-12%;石英砂:35-40%;白水泥:8-12%;重钙:2-4%;硬脂酸锌:0.5-1.5%;弹性乳液:20-25%;
本发明使用的弹性乳液为无增塑剂的阴离子型苯乙烯/丙烯酸酯共聚物,固体含量为54-56%,最低成膜温度在-10℃。可以改善水泥的柔软性,并具有优良的耐水,耐碱及低柔弹性。
本发明使用的纤维素醚溶液为1.5%的羟丙基甲基纤维素溶液,分子量为55000。具有优异的保水性,良好的温度稳定性,改善腻子施工性,提高粘结强度。
本发明使用的木质纤维素长度为300-400μm,密度为0.8~1.3g/cm3。具有优异的和易性,抗流坠性能,提高材料表面强度和与基层的粘结强度,并能起到了很好的抗裂作用。
本发明使用的分散剂为低分子量聚丙烯酸铵盐分散剂,有很好的耐水性,可以显著提高填料分散浆的浓度及其稳定性,通过这种分散剂,可以在填料颗粒表面包围一层电荷,使颗粒之间相互排斥,从而达到稳定浆料的效果。
本发明使用的滑石粉为325目,石英砂为200目,重钙为400目,白水泥的标号为425#,硬脂酸锌为一等品。
具体实施方式 下面是本发明的一个实施例。
一种低柔性弹性腻子的研制组份其含量如下:
6份的水、16份的1.5%纤维素醚溶液、0.5份的分散剂、0.4份的消泡剂、1份的润湿剂、0.5份的木质纤维素、10份的滑石粉、36份的石英砂、8份的白水泥、2份的重钙、0.6份的硬脂酸锌、19份的弹性乳液、PH值调解。
制备一种低柔性弹性腻子的研制的步骤如下:
(1)将配方中的水、1.5%纤维素醚溶液、分散剂、消泡剂、润湿剂、母料、及石英砂、白水泥等各种粉料混合物在分散机中高速分散,转速为1500~2000r/min,分散时间为40~60min。
(2)将乳液在低速搅拌状态下缓慢加入浆料中,在搅拌机中搅拌混合均匀,转速为200~400r/min,分散时间为30min。
(3)通过加入分散剂、增稠剂等助剂来调节各项实测值均符合要求的涂料状态。
(4)经均匀混合后的产物过筛,即得成品。
依据本发明制作的低柔性弹性腻子其各项指标均达到JG/T157-2009关于外墙腻子所规定的要求,而且具有优异的抗开裂性,附着力好,抗渗性能显著,能显著改善墙体的防水。有很好的打磨性能,极佳的低温柔弹性,干燥后易打磨,能很好提高墙面平整度,防止墙面开裂,覆盖建筑物上的小裂缝,可保证建筑物外墙表面能长久地保持清洁华丽的表面,施工性好,深受广大施工者喜爱。
Claims (5)
1.本发明的一种低柔性弹性腻子的研制按重量百分比计算为:
水:5-7%;1.5%纤维素醚溶液:16-20%;分散剂:0.4-0.7%;消泡剂:0.3-0.5%;润湿剂:0.8-1%;木质纤维素:0.2-0.4%;滑石粉:8-12%;石英砂:35-40%;白水泥:8-12%;重钙:2-4%;硬脂酸锌:0.5-1.5%;弹性乳液:20-25%。
2.根据权利要求1所述的一种易打磨弹性腻子的内墙涂料,其特征是所说的纤维素醚溶液为1.5%的羟丙基甲基纤维素溶液,分子量为55000。具有优异的保水性,良好的温度稳定性,改善腻子施工性,提高粘结强度。
3.根据权利要求1所述的一种易打磨弹性腻子的内墙涂料,其特征是所说的木质纤维素长度为300-400μm,密度为0.8~1.3g/cm3。具有优异的和易性,抗流坠性能,提高材料表面强度和与基层的粘结强度,并能起到了很好的抗裂作用。
4.根据权利要求1所述的一种易打磨弹性腻子的内墙涂料,其特征是所说的分散剂为低分子量聚丙烯酸铵盐分散剂,有很好的耐水性,可以显著提高填料分散浆的浓度及其稳定性。
5.根据权利要求1所述的一种易打磨弹性腻子的内墙涂料,其特征是所说的滑石粉为325目,石英砂为200目,重钙为400目,白水泥的标号为425#,硬脂酸锌为一等品。