CN115449241A - 一种抗病毒的干粉艺术涂料及其制备方法与应用 - Google Patents
一种抗病毒的干粉艺术涂料及其制备方法与应用 Download PDFInfo
- Publication number
- CN115449241A CN115449241A CN202211105213.1A CN202211105213A CN115449241A CN 115449241 A CN115449241 A CN 115449241A CN 202211105213 A CN202211105213 A CN 202211105213A CN 115449241 A CN115449241 A CN 115449241A
- Authority
- CN
- China
- Prior art keywords
- powder
- chinese herbal
- antiviral
- herbal medicine
- dry powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种抗病毒的干粉艺术涂料及其制备方法与应用。该抗病毒的干粉艺术涂料包括1‑5％中草药粉；该中草药粉包括金银花、连翘、野菊花、板蓝根、蒲公英、艾叶、广藿香、石菖蒲、丁香、桂枝、川芎、佩兰、龙脑。该抗病毒的干粉艺术涂料包括增稠剂0.1‑0.5％、纤维素0.1‑0.3％、分散剂0.1‑0.3％、润湿剂0.1‑0.3％、消泡剂0.05‑0.2％、钛白粉0.5‑5％、中草药粉1‑5％、重钙粉10‑20％、石膏粉20‑35％、石英砂43.5‑57.65％、胶粘剂0.5‑3％、缓凝剂0.05‑0.3％。该抗病毒的干粉艺术涂料不含有害物质、不燃、环保性能更高、涂膜质感好、更具有艺术性、方便快捷且具有成本效益。
Description
技术领域
本文涉及涂料技术，尤指一种抗病毒的干粉艺术涂料及其制备方法与应用。
背景技术
当前，室内墙面普遍采用抹涂1－2道粉刷石膏、2－3道内墙腻子，一道底漆、两道内墙乳胶漆的涂层体系。这样的涂层体系施工道数多、对每一道的涂层平整度及粗糙度要求严格，同时对施工人员的施工技术要求特别高，所以平米造价相对高。同时近两年来，一些国内外大涂料公司推出了抗病毒涂料并受到人们的青睐。当下的抗病毒涂料多数是通过添加含有银离子、铜离子的添加剂来实现涂料的抗病毒性能，这种办法使得涂料中重金属容易超标，同时添加铜离子后漆膜颜色发黄，另外涂膜表观形式单一，满足不了人们对涂料装饰效果个性化需求。
发明内容
以下是对本文详细描述的主题的概述。本概述并非是为了限制权利要求的保护范围。
本申请提供了一种抗病毒的干粉艺术涂料及其制备方法与应用。本申请提供的抗病毒的干粉艺术涂料不含有害物质、不燃、环保性能更高、涂膜质感好、更具有艺术性、方便快捷且具有成本效益。
本申请的实施方式中，提供了一种抗病毒的干粉艺术涂料，所述抗病毒的干粉艺术涂料包括1-5％中草药粉；并且所述中草药粉包括：金银花、连翘、野菊花、板蓝根、蒲公英、艾叶、广藿香、石菖蒲、丁香、桂枝、川芎、佩兰、龙脑。
本申请的一些实施方式中，所述中草药粉可以包括：金银花13-17％、连翘13-17％、野菊花4-8％、板蓝根4-8％、蒲公英4-8％、艾叶8-12％、广藿香 4-8％、石菖蒲13-17％、丁香3-7％、桂枝3-7％、川芎3-7％、佩兰3-7％、龙脑0.1-3％。
本申请的一些实施方式中，所述中草药粉可以包括：金银花15％、连翘 15％、野菊花6％、板蓝根6％、蒲公英6％、艾叶10％、广藿香6％、石菖蒲 15％、丁香5％、桂枝5％、川芎5％、佩兰5％、龙脑1％。
金银花、连翘、野菊花、板蓝根、蒲公英、丁香、桂枝、佩兰、广藿香、石菖蒲、川芎采用与中国药典2020版中一致的中药材名称(参见： https://zhiku.bopuyun.com/pc/book/4？zch＝QJNK8a,seobds)
龙脑可以选自右旋龙脑、左旋龙脑或合成龙脑中的任一种。
本申请的一些实施方式中，提供了一种抗病毒的干粉艺术涂料，按重量百分比计，所述抗病毒的干粉艺术涂料可以包括以下组分：
增稠剂0.1-0.8％、纤维素0.1-0.6％、分散剂0.1-0.6％、润湿剂0.1-0.6％、消泡剂0.05-0.5％、钛白粉0.5-8％、中草药粉1-5％、重钙粉10-30％、石膏粉 20-45％、石英砂43.5-67.65％、胶粘剂0.5-6％、缓凝剂0.05-0.6％。
本申请的实施方式中，提供了一种抗病毒的干粉艺术涂料按重量百分比计，所述抗病毒的干粉艺术涂料可以包括以下组分：
增稠剂0.1-0.5％、纤维素0.1-0.3％、分散剂0.1-0.3％、润湿剂0.1-0.3％、消泡剂0.05-0.2％、钛白粉0.5-5％、中草药粉1-5％、重钙粉10-20％、石膏粉 20-35％、石英砂43.5-57.65％、胶粘剂0.5-3％、缓凝剂0.05-0.3％。
本申请的一些实施方式中，所述增稠剂可以为钙基膨润土。所述钙基膨润土可以为高提纯改性的钙基膨润土。膨润土厂家(例如宣化燕北矿业有限公司)将原矿的钙基膨润土通过浮选工序将里面的铁、镁等杂质除掉成为高提纯钙基膨润土，一来提高产品白度，二来为后续改性做准备。高提纯钙基膨润与纯碱按9：1的重量配比在混合机中经均匀混合搅拌成为高提纯改性的钙基膨润土。
本申请的一些实施方式中，所述纤维素可以为丙基甲纤维素。所述丙基甲纤维素可以为粉状羟丙基甲基纤维素，并且粘度为3-20万厘泊。
纤维素粘度测试方法如下：在容器中加入98份纯净水，在低速搅拌下 (300-500转/分钟)细流方式加入粉状羟丙基甲基纤维素，搅拌30分钟成均匀透明溶液，然后用布氏粘度计测定、选用64#转子测试纤维素水溶液的布氏粘度。
本申请的一些实施方式中，所述分散剂可以为多聚磷酸钾。所述多聚磷酸钾可以为粉状多聚磷酸钾，粒度为400目以上。
本申请的一些实施方式中，所述润湿剂可以为聚氧乙烯醚材料。所述聚氧乙烯醚材料可以为粉状聚氧乙烯醚材料，其不含APEO物质及其他GB18582 中规定的限量物质。
本申请的一些实施方式中，所述消泡剂可以为有机硅氧烷。所述有机硅氧烷可以为粉状有机硅氧烷，粒度为300目以上。
本申请的一些实施方式中，所述钛白粉可以为金红石型，粒度为325目以上。
本申请的一些实施方式中，所述重钙粉的粒径可以为250－325目。
本申请的一些实施方式中，所述石膏粉可以为工业产生的石膏废渣或天然的石膏经粉碎到250-400目的原料。
本申请的一些实施方式中，所述石英砂可以为白色的20-200目的天然矿石粉碎的原料。
本申请的一些实施方式中，所述胶粘剂可以为单独的VAE乳胶粉、单独的PVA胶粉，或两者。
本申请的一些实施方式中，所述缓凝剂可以为蛋白类粉体材料，粒径为800-1000目。
本申请的一些实施方式中，所述中草药粉可以为粉碎的混合物。
本申请的一些实施方式中，所述高提纯改性的钙基膨润土可以具有 0.4-0.6cm3/g的有效孔容。
本申请的一些实施方式中，所述抗病毒的干粉艺术涂料还可以包括水性涂料专用有机颜料和无机颜料，其中所述有机颜料为酞菁蓝、酞菁绿、大红、中黄、碳黑等，所述无机颜料为氧化铁红、氧化铁黄、氧化铁黑。
本申请的实施方式中，提供了上述抗病毒的干粉艺术涂料的制备方法，所述制备方法可以包括以下步骤：
(1)将中草药按比例粉碎获得中草药粉备用；
(2)将增稠剂、纤维素、分散剂、润湿剂、消泡剂、钛白粉、中草药粉、重钙粉、石膏粉、石英砂、胶粘剂、缓凝剂贮存在各自贮料仓中；
(3)将所述石膏粉、所述重钙粉、所述钛白粉输送到干粉混合机中；
(4)将所述增稠剂、所述纤维素、所述分散剂、所述润湿剂、所述消泡剂、所述中草药粉、所述胶粘剂、所述缓凝剂输送到干粉混合机中继续搅拌；
(5)将石英砂输送到干粉混合机中；
(6)然后继续搅拌3-5分钟停机，检测合格后包装。
本申请的一些实施方式中，步骤(3)可以通过螺旋输送机进行输送。
本申请的一些实施方式中，步骤(3)的干粉混合机可以处于搅拌状态。
本申请的一些实施方式中，所述中草药粉可以通过以下步骤获得：
(a)将金银花15％、连翘15％、野菊花6％、板蓝根6％、蒲公英6％、艾叶10％、广藿香6％、石菖蒲15％、丁香5％、桂枝5％、川芎5％、佩兰5％、龙脑1％的干燥中草药中长的组分切割为2-5厘米药段；
(b)将步骤(a)的中草药输送到微粉机中粉碎，获得中草药粉；
(c)将所述中草药粉输送到旋风分离装置中，将中草药粉中的粉尘通过除尘装置回收利用，将中草药粉输送到中草药粉包装工艺进行包装备用。
本申请的一些实施方式中，步骤(a)的切割可以在切割机中进行。
本申请的一些实施方式中，步骤(b)的输送可以通过皮带输送机或螺旋输送机进行。
本申请的一些实施方式中，将步骤(b)的粉碎可以进行约15-20分钟，获得100-400目的中草药粉。
本申请的实施方式中，提供了上述抗病毒的干粉艺术涂料可以在建筑装修中的应用。
与相关技术相比，本申请包括不含VOC组份，不含GB18582--2020标准中规定的有害物质，不燃。较之液体涂料产品环保性能更高，涂膜质感好，可以施涂成浮雕、仿砖、仿树皮、拉毛等不同风格涂层，更具有艺术性，提高了墙面装饰档次。可以省去腻子、面漆，降低人工和材料综合成本。通过添加颜料可以调成不同颜色。涂料中添加石膏粉，可以自主调节室内湿度，同现有腻子相比减少涂层开裂现象，并且石膏具有辅助抗病毒功能。本发明结合中国传统防瘟疫药方文献，选取多种中草药加入到涂料中，形成有效抗病毒防疫涂层以实现抗病毒防疫效果，而且中草药粉无毒无害、安全环保。
本申请的其它特征和优点将在随后的说明书中阐述，并且，部分地从说明书中变得显而易见，或者通过实施本申请而了解。本申请的其他优点可通过在说明书以及附图中所描述的方案来实现和获得。
附图说明
附图用来提供对本申请技术方案的理解，并且构成说明书的一部分，与本申请的实施例一起用于解释本申请的技术方案，并不构成对本申请技术方案的限制。
图1为中草药粉制备工艺；21为中草药切割机，22为微粉机，23为旋风分离装置，24为除尘装置。
图1中所用的装置购自山东经欣粉体设备有限公司，或者根据中草药粉的日用量选择适宜生产能力的设备。
图2为抗病毒的中草药干粉艺术涂料的制备工艺图；1为石膏粉贮料仓， 2为重钙粉贮料仓，3为石英砂贮料仓，4为钛白粉贮料仓，5为中药粉贮料仓，6为胶粘剂贮料仓，7为增稠剂贮料仓，8为纤维素贮料仓，9为分散剂贮料仓，10为润湿剂贮料仓，11为消泡剂贮料仓，12为缓凝剂贮料仓，13 为计量秤，14为计量秤，15为干粉混合机。
图2中1-12料仓为非标产品，采取外购(苏州一工机械有限公司)。各设备规格、型号如下表所示：以日产50吨抗病毒的中草药干粉艺术涂料为例。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将结合本发明实施例对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动的前提下所获得的所有其他实施例，都属于本发明保护的范围。
本申请选用的所述增稠剂为高提纯改性的钙基膨润土，使得干粉涂料加水使用时中各组份均匀分布、不分层。膨润土厂家(例如宣化燕北矿业有限公司)将原矿的钙基膨润土通过浮选工序将里面的铁、镁等杂质除掉成为高提纯钙基膨润土，一来提高产品白度，二来为后续改性做准备。高提纯钙基膨润与纯碱按9：1的重量配比在混合机中经均匀混合搅拌成为高提纯改性的钙基膨润土。高提纯改性的钙基膨润土具有较大的有效孔容、因此有较强的吸附能力，无毒。同时因含有钙离子，可以增加涂层强度。
本申请可以添加一定量的粉状羟丙基甲基纤维素(赫克力士公司GL450)。所述粉状羟丙基甲基纤维素的粘度为3-20万厘泊。
纤维素粘度测试方法如下：在容器中加入98份纯净水，在低速搅拌下 (300-500转/分钟)细流方式加入粉状羟丙基甲基纤维素，搅拌30分钟成均匀透明溶液，然后用布氏粘度计测定，配套转子中有61#-64#四个规格转子，选择64#转子测试纤维素水溶液的布氏粘度。
本申请可以添加一定量粉状多聚磷酸钾(德国明凌化学KC)，粒度为400 目以上。
本申请可以选用粉状聚氧乙烯醚材料(德国巴斯夫公司R66)，其不含 APEO物质及其他GB18582中规定的限量物质，例如不含甲醛，不含铅，不含镉、铬、汞可溶性重金属等物质)。
本申请可以添加一定量粉状有机硅氧烷(陶氏公司SP100)，粒度为300 目以上。
本申请可以添加一定量重钙粉(广福建材公司CC250)。
本申请可以添加一定比例的中草药粉。该中草药粉是多种中草药按一定比例混在一起并经过粉碎适当目数的混合物。本发明的中草药通过涂层孔隙通道持续散放芳香气味，刺激人体呼吸道黏膜产生了分泌型免疫球蛋白，对病毒和细菌有较强的灭杀作用，因而具有较强的预防传染病的作用。
本申请可以添加一定量的金红石型钛白粉(攀钢钒钛集团公司产品)，粒度为325目以上。
本申请可以添加一定量的不同目数级配的石英砂(广福建材公司)。
本申请选用石膏粉(河北安益石膏建材有限公司的天然石膏或附近电厂、磷酸厂等工业副产品石膏废渣)作为主要粉体填料。添加石膏的干粉涂料强度高、耐水性好。同时石膏粉具有辅助抗病毒防疫作用。石膏粉可以选择为工业产生的石膏废渣或天然的石膏经粉碎到适宜目数的产品。
本申请可以添加一定量的胶粘剂(德国瓦克公司的VAE乳胶粉或山西三维公司的PVA胶粉)。胶粘剂可以选用粉状的胶粉，胶粉可以为VAE乳胶粉或PVA胶粉或者两者。
本申请可以添加一定量的蛋白类石膏缓凝剂(德国瓦克公司DH25)。
本申请可以选择性添加一定量的水性涂料专用有机颜料、无机颜料(德国拜耳或上海一品公司的颜料)，其中所述有机颜料为酞菁蓝、酞菁绿、大红、中黄、碳黑，所述无机颜料为氧化铁红、氧化铁黄、氧化铁黑。
下面结合具体实施方式对本发明做进一步的详细描述：
实施例1：
中草药粉的组分：
金银花15％(采用花的部分，从山东临沂或河南封丘中药材批发市场采购)、连翘15％(采用果实部分，从河北省邯郸市涉县中药材批发市场采购)、野菊花6％(采用花的部分，从浙江省桐乡市中药材市场采购)、板蓝根6％ (采用根部，从安徽省阜阳市太和县中药材批发市场采购)、蒲公英6％(采用全株，从黑龙江鸡西市中药材批发市场采购)、艾叶10％(采用全株，从湖北省蕲春县中药材批发市场采购)、广藿香6％(采用茎叶部分，从广东省湛江市中药材批发市场采购)、石菖蒲15％(采用根茎部分，从浙江省金华市浦江县中药材批发市场采购)、丁香5％(采用花蕾部分，从吉林省白山市长白县中药材批发市场采购)、桂枝5％(采用枝条部分，从广西省玉林市中药材批发市场采购)、川芎5％(采用根茎部分，从四川省都江堰市中药材批发市场采购)、佩兰5％(采用全株，从江苏省宿迁市泗阳县中药材批发市场采购)、龙脑1％(从江西雪松天然药用油有限公司采购)。
中草药粉制备方法(参见图1)：
(a)将上面的干燥中草药中长的组分事先在切割机中先切成2-5厘米，以便于后续制粉；
(b)切好后的中草药通过皮带输送机或螺旋输送机输送微粉机中粉碎、混匀成大约15-20分钟100-400目；
(c)粉碎后的中草药粉进入到旋风分离装置中，上面粉尘去除尘装置回收利用，下面产品去中草药粉包装工序，包装后的中草药备用。
实施例2(参见图2)：
抗病毒的中草药干粉艺术涂料制备方法：
(1)事先将配方中的组粉贮存在各自贮料仓中；
(2)生产时按配方中的计量将大宗的石膏粉、重钙粉、钛白粉等粉料通过螺旋输送机输送到涂料搅拌状态下的混合机中；
(3)将增稠剂、纤维素、分散剂、润湿剂、消泡剂、混好后的中草药粉 1-2％、胶粘剂、缓凝剂等占比小的添加剂输送到混合机中继续搅拌；
(4)将比重大的石英砂输送到混合机中；
(5)全部材料加完后继续搅拌3-5分钟停机，检测合格后包装。
实施例3：
本发明提供的抗病毒的中草药干粉艺术涂料，按重量百分比计，该抗病毒防的中草药干粉艺术涂料包括以下组分：
增稠剂0.5％、纤维素0.1％、分散剂0.1％、润湿剂0.1％、消泡剂0.05％、钛白粉0.5％、中草药粉1％、重钙粉20％、石膏粉20％、石英砂57.65％、胶粘剂0.5％、缓凝剂0.05％。
实施例4：
本发明提供的抗病毒的中草药干粉艺术涂料，按重量百分比计，该抗病毒防的中草药干粉艺术涂料包括以下组分：
增稠剂0.3％、纤维素0.2％、分散剂0.2％、润湿剂0.2％、消泡剂0.12％、钛白粉2.5％、中草药粉1.5％、重钙粉15％、石膏粉28％、石英砂49.78％、胶粘剂2.0％、缓凝剂0.2％。
实施例5：
本发明提供的抗病毒的中草药干粉艺术涂料，按重量百分比计，该抗病毒防的中草药干粉艺术涂料包括以下组分：
增稠剂0.1％、纤维素0.3％、分散剂0.3％、润湿剂0.3％、消泡剂0.2％、钛白粉5％、中草药粉2％、重钙粉10％、石膏粉35％、石英砂43.5％、胶粘剂3.0％、缓凝剂0.3％。
上述实施例3-5的产品性能指标达到JC/T517-2004粉刷石膏底层石膏指标要求，如表1所示。
表1
将上述实施例3-5的产品进行以下但不限于以下的环保指标检测，结果符合GB18582-2020标准规定的要求，如表2所示。
表2
将上述实施例3的产品依据ISO 21702：2019进行以下但不限于以下病毒的抗病毒数据指标检测，分别采用三种但不限于该三种实验病毒及宿主测试，如表3、表4、表5所示。实施例4、5中草药粉及石膏的添加量较实施例3 高，理论上抗病毒效果会更好。
表3
表4
表5
本发明公开了一种具有抗病毒防疫性能的中草药干粉艺术涂料及其制备方法。本品使用时按比例加水搅拌均匀即可使用，可采用喷涂、辊涂、抹涂等多种施工方法，制作成不同艺术风格的涂层效果。同时可以省去腻子、内墙乳胶漆工序从而降低综合成本。另外产品通过添加特定复配中草药和石膏粉而具有很好的抗病毒防疫性能。以上仅为本发明的优选实施例而已，并不用于限制本发明，对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (11)
1.一种抗病毒的干粉艺术涂料，其中，所述抗病毒的干粉艺术涂料包括1-5％中草药粉；并且
所述中草药粉包括：金银花、连翘、野菊花、板蓝根、蒲公英、艾叶、广藿香、石菖蒲、丁香、桂枝、川芎、佩兰、龙脑。
2.根据权利要求1所述的抗病毒的干粉艺术涂料，其中，所述中草药粉包括：金银花13-17％、连翘13-17％、野菊花4-8％、板蓝根4-8％、蒲公英4-8％、艾叶8-12％、广藿香4-8％、石菖蒲13-17％、丁香3-7％、桂枝3-7％、川芎3-7％、佩兰3-7％、龙脑0.1-3％；
优选地，金银花15％、连翘15％、野菊花6％、板蓝根6％、蒲公英6％、艾叶10％、广藿香6％、石菖蒲15％、丁香5％、桂枝5％、川芎5％、佩兰5％、龙脑1％。
3.根据权利要求1至2中任一项所述的抗病毒的干粉艺术涂料，其中，按重量百分比计，所述抗病毒的干粉艺术涂料包括以下组分：中草药粉1-5％、增稠剂0.1-0.5％、纤维素0.1-0.3％、分散剂0.1-0.3％、润湿剂0.1-0.3％、消泡剂0.05-0.2％、钛白粉0.5-5％、重钙粉10-20％、石膏粉20-35％、石英砂43.5-57.65％、胶粘剂0.5-3％、缓凝剂0.05-0.3％。
4.根据权利要求3所述的抗病毒的干粉艺术涂料，其中，所述增稠剂为钙基膨润土；
所述纤维素为羟丙基甲基纤维素；
所述分散剂为多聚磷酸钾；
所述润湿剂为聚氧乙烯醚材料，其不含APEO物质及其他GB18582中规定的限量物质；
所述消泡剂为有机硅氧烷；
所述钛白粉为金红石型，粒度为325目以上；
所述重钙粉的粒径为250－325目；
所述石膏粉为工业产生的石膏废渣或天然的石膏经粉碎到250-400目的原料；
所述石英砂为白色的20-200目的天然矿石粉碎的原料；
所述胶粘剂为VAE乳胶粉或PVA胶粉或两者；
或者所述缓凝剂为蛋白类缓凝剂。
5.根据权利要求4所述的抗病毒的干粉艺术涂料，其中，所述钙基膨润土具有0.4-0.6cm3/g的有效孔容。
6.根据权利要求1至2中任一项所述的抗病毒的干粉艺术涂料，其中，所述中草药粉为粉碎的混合物。
7.根据权利要求1至2中任一项所述的抗病毒的干粉艺术涂料，其中，所述抗病毒的干粉艺术涂料还包括水性涂料专用有机颜料和无机颜料，其中所述有机颜料为酞菁蓝、酞菁绿、大红、中黄、碳黑，所述无机颜料为氧化铁红、氧化铁黄、氧化铁黑。
8.根据权利要求1至7中任一项所述的抗病毒的干粉艺术涂料的制备方法，所述制备方法包括以下步骤：
(1)将中草药按比例粉碎获得中草药粉备用；
(2)将增稠剂、纤维素、分散剂、润湿剂、消泡剂、钛白粉、中草药粉、重钙粉、石膏粉、石英砂、胶粘剂、缓凝剂贮存在各自贮料仓中；
(3)将所述石膏粉、所述重钙粉、所述钛白粉输送到干粉混合机中；
(4)将所述增稠剂、所述纤维素、所述分散剂、所述润湿剂、所述消泡剂、所述中草药粉、所述胶粘剂、所述缓凝剂输送到所述干粉混合机中继续搅拌；
(5)将石英砂输送到所述干粉混合机中；
(6)然后继续搅拌3-5分钟停机，检测合格后包装。
9.根据权利要求8所述的制备方法，其中，步骤(3)通过螺旋输送机进行输送；
或者步骤(3)的所述干粉混合机处于搅拌状态。
10.根据权利要求8所述的制备方法，其中，所述中草药粉通过以下步骤获得：
(a)将金银花15％、连翘15％、野菊花6％、板蓝根6％、蒲公英6％、艾叶10％、广藿香6％、石菖蒲15％、丁香5％、桂枝5％、川芎5％、佩兰5％、龙脑1％的干燥中草药中长的组分切割为2-5厘米药段；
(b)将步骤(a)的中草药输送到微粉机中粉碎，获得中草药粉；
(c)将所述中草药粉输送到旋风分离装置中，将中草药粉中的粉尘通过除尘装置回收利用，将中草药粉输送到中草药粉包装工艺，进行打包备用；任选地
步骤(a)的切割在切割机中进行；
步骤(b)的输送通过皮带输送机或螺旋输送机进行；
将步骤(b)的粉碎进行约15-20分钟，获得100-400目的中草药粉。
11.根据权利要求1至7中任一项所述的抗病毒的干粉艺术涂料在建筑装修中的应用。