CN115368689A - 一种芳香型中药养生装饰板及其制备方法 - Google Patents
一种芳香型中药养生装饰板及其制备方法 Download PDFInfo
- Publication number
- CN115368689A CN115368689A CN202210940761.XA CN202210940761A CN115368689A CN 115368689 A CN115368689 A CN 115368689A CN 202210940761 A CN202210940761 A CN 202210940761A CN 115368689 A CN115368689 A CN 115368689A
- Authority
- CN
- China
- Prior art keywords
- traditional chinese
- substrate
- aromatic
- chinese medicine
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种芳香型中药养生装饰板，包括基板，以及浇注在所述基板表面上的面板层，所述面板层由以下重量份的材料制成：PVC粉、干姜片、芳香型中药材、滑石粉、氢氧化镁、乙氧基化烷基胺、抗氧剂DNP、氯化聚乙烯、碳酸氢钠和炭黑，该装饰板制造方便，成本低，模量高，抗蠕变，采用中药配合PVC粉制成具有养生功能的装饰板，会使装饰板散发出淡淡的、无毒的天然植物芳香，且根据不同的室内环境进行选择对人体有益的芳香型中药草，给消费者提供一个绿色、健康的居住环境，可应用于楼堂馆所、居家办公场合。
Description
技术领域
本发明具体涉及一种芳香型中药养生装饰板及其制备方法。
背景技术
近年来，复合材料的研究与应用受到了高度的关注，它具有优良的防腐、防水、防裂和抗污性能，无需二次加工，安装方便，不含有毒化学成分，低碳环保，无需上漆、打磨、易于维护，更易清洁，隔热隔音等，因而可广泛应用于楼堂馆所、居家办公的各种场合，可用作装饰材料。
然而，随着社会的发展及人类的需求变化，仅简单的采用复合材料的制备装饰板并无法满足消费者的需求，针对卧室，消费者希望具有能够促进睡眠的方式，因此衍生出各种各样的中草药制成的香包，但香包的气味散发快，需要经常更换，因此本领域技术人员针对装饰板的原材料改进，调配出应对不同生活环境的装饰用板，针对卧室助眠的、针对书房提神醒脑的……且工艺简单，所制成的装饰板自身的耐候性、芳香持久性都具有明显的优势。
发明内容
本发明要解决的技术问题是提供一种给消费者提供一个绿色、健康的居住环境的芳香型中药养生装饰板，可应用于楼堂馆所、居家办公场合，同时其制备方法简单快捷。
本发明解决上述技术问题的方案如下：
一种芳香型中药养生装饰板，包括基板，以及浇注在所述基板表面上的面板层，所述面板层由以下重量份的材料制成：PVC粉67-79％、干姜片4-6％、芳香型中药材12-18％、滑石粉1-2％、氢氧化镁0.9-1％、乙氧基化烷基胺0.1-0.3％、抗氧剂DNP0.3-0.5％、氯化聚乙烯0.1-0.2％、碳酸氢钠1.4-3％和炭黑1.2-2％。
进一步的，所述干姜片采用含水量≤5％的老姜。
进一步的，所述芳香型中药材为干制的艾草、檀香、松脂和茶香叶中的其中一种，所述茶香叶由60-70％炒制茶叶、11-15％干制柠檬叶、13-15％干制薰衣草和6-10％干制荷叶混合制成。
进一步的，所述基板为PVC板。
一种芳香型中药养生装饰板的制备方法，包括以下具体步骤：
S1、原料预处理，包括以下具体步骤：
S11、将准备好的干姜片4-6％和芳香型中药材12-18％通过打粉机加工制成粗粉，然后再利用研磨机研磨制备得到100目的粉末，使得干姜与芳香型中药材粉末充分混合均匀，得到粉状香料，备用；
S12、将S11制得的粉状香料放入搅拌桶中，并将PVC粉67-79％、滑石粉1-2％、氢氧化镁0.9-1％、乙氧基化烷基胺0.1-0.3％、抗氧剂DNP0.3-0.5％、氯化聚乙烯0.1-0.2％、碳酸氢钠1.4-3％和炭黑1.2-2％％同时加入，经过高速搅拌，使得材料混合均匀，制得原料，备用；
S2、原料成型处理：利用双辊炼胶机将S1制得原料熔融并挤出成型得到面板层，厚度为0.6-1cm，备用；
S3、基板选取处理：采用PVC制成的基板，且基板的厚度为0.4-0.6cm，备用；
S4、面板层与基板成型处理：在模压成型模具型腔的底部放置基板，然后在其上铺放面板层，排气5mi n，合模，在170-190℃范围内预热10-20mi n后，采用10-20MPa的压力模压成型，制的成品。
该装饰板的特点在于:
第一、能够根据不同的使用环境进行调整芳香型中药材，并与干姜片进行配合使用，在散发出香味的同时也能够防虫驱虫；
第二、芳香型中药材和干姜片在整体装饰板的占有量≤30％，因此，相比较类似中央填充型板材，不仅在板材硬度上，还是在板材防腐防霉上都具有优势。
本发明的有益效果为：该装饰板制造方便，成本低，模量高，抗蠕变，采用中药配合PVC粉制成具有养生功能的装饰板，会使装饰板散发出淡淡的、无毒的天然植物芳香，且根据不同的室内环境进行选择对人体有益的芳香型中药草，给消费者提供一个绿色、健康的居住环境，可应用于楼堂馆所、居家办公场合。
说明书附图
图1位本发明一种芳香型中药养生装饰板的结构图。
具体实施方式
对本发明的具体实施方式作进一步详述，以使本发明技术方案更易于理解和掌握。
一种芳香型中药养生装饰板，包括基板1，以及浇注在所述基板1表面上的面板层2，所述面板层2由以下重量份的材料制成：PVC粉67-79％、干姜片4-6％、芳香型中药材12-18％、滑石粉1-2％、氢氧化镁0.9-1％、乙氧基化烷基胺0.1-0.3％、抗氧剂DNP0.3-0.5％、氯化聚乙烯0.1-0.2％、碳酸氢钠1.4-3％和炭黑1.2-2％。
所述干姜片采用含水量≤5％的老姜。
所述芳香型中药材为干制的艾草、檀香、松脂和茶香叶中的其中一种。
所述茶香叶由60-70％炒制茶叶、11-15％干制柠檬叶、13-15％干制薰衣草和6-10％干制荷叶混合制成。
所述基板1为PVC板。
一种芳香型中药养生装饰板的制备方法，包括以下具体步骤：
S1、原料预处理，包括以下具体步骤：
S11、将准备好的干姜片4-6％和芳香型中药材12-18％通过打粉机加工制成粗粉，然后再利用研磨机研磨制备得到100目的粉末，使得干姜与芳香型中药材粉末充分混合均匀，得到粉状香料，备用；
S12、将S11制得的粉状香料放入搅拌桶中，并将PVC粉67-79％、滑石粉1-2％、氢氧化镁0.9-1％、乙氧基化烷基胺0.1-0.3％、抗氧剂DNP0.3-0.5％、氯化聚乙烯0.1-0.2％、碳酸氢钠1.4-3％和炭黑1.2-2％％同时加入，经过高速搅拌，使得材料混合均匀，制得原料，备用；
S2、原料成型处理：利用双辊炼胶机将S1制得原料熔融并挤出成型得到面板层2，厚度为0.6-1cm，备用；
S3、基板1选取处理：采用PVC制成的基板，且基板的厚度为0.4-0.6cm，备用；
S4、面板层2与基板1成型处理：在模压成型模具型腔的底部放置基板1，然后在其上铺放面板层2，排气5mi n，合模，在170-190℃范围内预热10-20mi n后，采用10-20MPa的压力模压成型，制的成品。
实施例1
一种芳香型中药养生装饰板，包括基板1，以及浇注在所述基板1表面上的面板层2，所述面板层2由以下重量份的材料制成：PVC粉67-79％、干姜片4-6％、艾草12-18％、滑石粉1-2％、氢氧化镁0.9-1％、乙氧基化烷基胺0.1-0.3％、抗氧剂DNP0.3-0.5％、氯化聚乙烯0.1-0.2％、碳酸氢钠1.4-3％和炭黑1.2-2％。
在本实施例中，所述干姜片采用含水量≤5％的老姜。
在本实施例中，所述基板1为PVC板。
一种芳香型中药养生装饰板的制备方法，包括以下具体步骤：
S1、原料预处理，包括以下具体步骤：
S11、将准备好的干姜片4-6％和艾草12-18％通过打粉机加工制成粗粉，然后再利用研磨机研磨制备得到100目的粉末，使得干姜与芳香型中药材粉末充分混合均匀，得到粉状香料，备用；
S12、将S11制得的粉状香料放入搅拌桶中，并将PVC粉67-79％、滑石粉1-2％、氢氧化镁0.9-1％、乙氧基化烷基胺0.1-0.3％、抗氧剂DNP0.3-0.5％、氯化聚乙烯0.1-0.2％、碳酸氢钠1.4-3％和炭黑1.2-2％％同时加入，经过高速搅拌，使得材料混合均匀，制得原料，备用；
S2、原料成型处理：利用双辊炼胶机将S1制得原料熔融并挤出成型得到面板层2，厚度为0.6-1cm，备用；
S3、基板1选取处理：采用PVC制成的基板，且基板的厚度为0.4-0.6cm，备用；
S4、面板层2与基板1成型处理：在模压成型模具型腔的底部放置基板1，然后在其上铺放面板层2，排气5mi n，合模，在170-190℃范围内预热10-20mi n后，采用10-20MPa的压力模压成型，制的具有驱虫效果的装饰板。
实施例2
一种芳香型中药养生装饰板，包括基板1，以及浇注在所述基板1表面上的面板层2，所述面板层2由以下重量份的材料制成：PVC粉67-79％、干姜片4-6％、檀香12-18％、滑石粉1-2％、氢氧化镁0.9-1％、乙氧基化烷基胺0.1-0.3％、抗氧剂DNP0.3-0.5％、氯化聚乙烯0.1-0.2％、碳酸氢钠1.4-3％和炭黑1.2-2％。
在本实施例中，所述干姜片采用含水量≤5％的老姜。
在本实施例中，所述基板1为PVC板。
一种芳香型中药养生装饰板的制备方法，包括以下具体步骤：
S1、原料预处理，包括以下具体步骤：
S11、将准备好的干姜片4-6％和檀香12-18％通过打粉机加工制成粗粉，然后再利用研磨机研磨制备得到100目的粉末，使得干姜与芳香型中药材粉末充分混合均匀，得到粉状香料，备用；
S12、将S11制得的粉状香料放入搅拌桶中，并将PVC粉67-79％、滑石粉1-2％、氢氧化镁0.9-1％、乙氧基化烷基胺0.1-0.3％、抗氧剂DNP0.3-0.5％、氯化聚乙烯0.1-0.2％、碳酸氢钠1.4-3％和炭黑1.2-2％％同时加入，经过高速搅拌，使得材料混合均匀，制得原料，备用；
S2、原料成型处理：利用双辊炼胶机将S1制得原料熔融并挤出成型得到面板层2，厚度为0.6-1cm，备用；
S3、基板1选取处理：采用PVC制成的基板，且基板的厚度为0.4-0.6cm，备用；
S4、面板层2与基板1成型处理：在模压成型模具型腔的底部放置基板1，然后在其上铺放面板层2，排气5mi n，合模，在170-190℃范围内预热10-20mi n后，采用10-20MPa的压力模压成型，制的能够净化空气和调节情绪的装饰板。
实施例3
一种芳香型中药养生装饰板，包括基板1，以及浇注在所述基板1表面上的面板层2，所述面板层2由以下重量份的材料制成：PVC粉67-79％、干姜片4-6％、松脂12-18％、滑石粉1-2％、氢氧化镁0.9-1％、乙氧基化烷基胺0.1-0.3％、抗氧剂DNP0.3-0.5％、氯化聚乙烯0.1-0.2％、碳酸氢钠1.4-3％和炭黑1.2-2％。
在本实施例中，所述干姜片采用含水量≤5％的老姜。
在本实施例中，所述基板1为PVC板。
一种芳香型中药养生装饰板的制备方法，包括以下具体步骤：
S1、原料预处理，包括以下具体步骤：
S11、将准备好的干姜片4-6％和松脂12-18％通过打粉机加工制成粗粉，然后再利用研磨机研磨制备得到100目的粉末，使得干姜与芳香型中药材粉末充分混合均匀，得到粉状香料，备用；
S12、将S11制得的粉状香料放入搅拌桶中，并将PVC粉67-79％、滑石粉1-2％、氢氧化镁0.9-1％、乙氧基化烷基胺0.1-0.3％、抗氧剂DNP0.3-0.5％、氯化聚乙烯0.1-0.2％、碳酸氢钠1.4-3％和炭黑1.2-2％％同时加入，经过高速搅拌，使得材料混合均匀，制得原料，备用；
S2、原料成型处理：利用双辊炼胶机将S1制得原料熔融并挤出成型得到面板层2，厚度为0.6-1cm，备用；
S3、基板1选取处理：采用PVC制成的基板，且基板的厚度为0.4-0.6cm，备用；
S4、面板层2与基板1成型处理：在模压成型模具型腔的底部放置基板1，然后在其上铺放面板层2，排气5min，合模，在170-190℃范围内预热10-20min后，采用10-20MPa的压力模压成型，制的助眠安神的装饰板。
实施例4
一种芳香型中药养生装饰板，包括基板1，以及浇注在所述基板1表面上的面板层2，所述面板层2由以下重量份的材料制成：PVC粉67-79％、干姜片4-6％、茶香叶12-18％、滑石粉1-2％、氢氧化镁0.9-1％、乙氧基化烷基胺0.1-0.3％、抗氧剂DNP0.3-0.5％、氯化聚乙烯0.1-0.2％、碳酸氢钠1.4-3％和炭黑1.2-2％。
在本实施例中，所述干姜片采用含水量≤5％的老姜。
在本实施例中，所述茶香叶由60-70％炒制茶叶、11-15％干制柠檬叶、13-15％干制薰衣草和6-10％干制荷叶混合制成。
在本实施例中，所述基板1为PVC板。
一种芳香型中药养生装饰板的制备方法，包括以下具体步骤：
S1、原料预处理，包括以下具体步骤：
S11、将准备好的干姜片4-6％和茶香叶12-18％通过打粉机加工制成粗粉，然后再利用研磨机研磨制备得到100目的粉末，使得干姜与芳香型中药材粉末充分混合均匀，得到粉状香料，备用；
S12、将S11制得的粉状香料放入搅拌桶中，并将PVC粉67-79％、滑石粉1-2％、氢氧化镁0.9-1％、乙氧基化烷基胺0.1-0.3％、抗氧剂DNP0.3-0.5％、氯化聚乙烯0.1-0.2％、碳酸氢钠1.4-3％和炭黑1.2-2％％同时加入，经过高速搅拌，使得材料混合均匀，制得原料，备用；
S2、原料成型处理：利用双辊炼胶机将S1制得原料熔融并挤出成型得到面板层2，厚度为0.6-1cm，备用；
S3、基板1选取处理：采用PVC制成的基板，且基板的厚度为0.4-0.6cm，备用；
S4、面板层2与基板1成型处理：在模压成型模具型腔的底部放置基板1，然后在其上铺放面板层2，排气5mi n，合模，在170-190℃范围内预热10-20mi n后，采用10-20MPa的压力模压成型，制的提神醒脑的装饰板。
实验例
为考察本发明制得装饰板的性能及效果，通过以下相关实验表征数据体现：
将四组组实施例生产所得的装饰板通过提取样品进行送检，同时购买市面上通用的中药埋填式装饰板进行对比实验。
检验方法如下表1所示：
表1
检验结果如表2所示：
表2
综上所示，根据表2的数据展示，本发明生产的装饰板均由于常规的中药填充型装饰板。
本发明的有益效果为：该装饰板制造方便，成本低，模量高，抗蠕变，采用中药配合PVC粉制成具有养生功能的装饰板，会使装饰板散发出淡淡的、无毒的天然植物芳香，且根据不同的室内环境进行选择对人体有益的芳香型中药草，给消费者提供一个绿色、健康的居住环境，可应用于楼堂馆所、居家办公场合。
当然，以上只是本发明的典型实例，除此之外，本发明还可以有其它多种具体实施方式，凡采用等同替换或等效变换形成的技术方案，均落在本发明要求保护的范围之内。
Claims (6)
1.一种芳香型中药养生装饰板，包括基板，以及浇注在所述基板表面上的面板层，其特征在于，所述面板层由以下重量份的材料制成：PVC粉67-79％、干姜片4-6％、芳香型中药材12-18％、滑石粉1-2％、氢氧化镁0.9-1％、乙氧基化烷基胺0.1-0.3％、抗氧剂DNP0.3-0.5％、氯化聚乙烯0.1-0.2％、碳酸氢钠1.4-3％和炭黑1.2-2％。
2.如权利要求1所述的一种芳香型中药养生装饰板，其特征在于：所述干姜片采用含水量≤5％的老姜。
3.如权利要求1所述的一种芳香型中药养生装饰板，其特征在于：所述芳香型中药材为干制的艾草、檀香、松脂和茶香叶中的其中一种。
4.如权利要求3所述的一种芳香型中药养生装饰板，其特征在于：所述茶香叶由60-70％炒制茶叶、11-15％干制柠檬叶、13-15％干制薰衣草和6-10％干制荷叶混合制成。
5.如权利要求1所述的一种芳香型中药养生装饰板，其特征在于：所述基板为PVC板。
6.一种如权利要求1-5所述的芳香型中药养生装饰板的制备方法，其特征在于，包括以下具体步骤：
S1、原料预处理，包括以下具体步骤：
S11、将准备好的干姜片4-6％和芳香型中药材12-18％通过打粉机加工制成粗粉，然后再利用研磨机研磨制备得到100目的粉末，使得干姜与芳香型中药材粉末充分混合均匀，得到粉状香料，备用；
S12、将S11制得的粉状香料放入搅拌桶中，并将PVC粉67-79％、滑石粉1-2％、氢氧化镁0.9-1％、乙氧基化烷基胺0.1-0.3％、抗氧剂DNP0.3-0.5％、氯化聚乙烯0.1-0.2％、碳酸氢钠1.4-3％和炭黑1.2-2％％同时加入，经过高速搅拌，使得材料混合均匀，制得原料，备用；
S2、原料成型处理：利用双辊炼胶机将S1制得原料熔融并挤出成型得到面板层，厚度为0.6-1cm，备用；
S3、基板选取处理：采用PVC制成的基板，且基板的厚度为0.4-0.6cm，备用；
S4、面板层与基板成型处理：在模压成型模具型腔的底部放置基板，然后在其上铺放面板层，排气5min，合模，在170-190℃范围内预热10-20min后，采用10-20MPa的压力模压成型，制的成品。