CN115305014B - 一种皮革制品用亮洁剂及其制备方法 - Google Patents
一种皮革制品用亮洁剂及其制备方法 Download PDFInfo
- Publication number
- CN115305014B CN115305014B CN202210594160.8A CN202210594160A CN115305014B CN 115305014 B CN115305014 B CN 115305014B CN 202210594160 A CN202210594160 A CN 202210594160A CN 115305014 B CN115305014 B CN 115305014B
- Authority
- CN
- China
- Prior art keywords
- brightening agent
- parts
- leather
- preparation
- leather products
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种皮革制品用亮洁剂及其制备方法，制备原料包括硅油5‑10份，聚醚改性聚硅氧烷5‑15份，表面活性剂3‑10份，油脂1‑8份，助剂1‑3份，溶剂20‑30份、酸性调节剂0.5‑2份，制备得到的亮洁剂可以提供较强清洁力度的同时，还具有优异的抗菌性能。
Description
技术领域
本发明涉及C11D1/825，尤其涉及一种皮革制品用亮洁剂及其制备方法
背景技术
皮革制品在我们的日常生活中应用广泛，皮革长期使用会出现粗糙，无光等，并且汗渍，灰尘等污垢沾到皮革上，如果长期不清洁容易造成发霉，需要定期进行后期维护和清洗，目前市面上所具有的亮洁剂大多数对于皮革会造成不可逆的损害，影响皮革制品的光泽度和寿命。
专利文献CN103045411A公开了一种皮革清洁剂，其原料包括：乙酸薄荷酯、鲸蜡硬脂醇、甘油等，所制得的皮革清洁剂具有防止皮革出现老化、龟裂等问题的效果。但是存在使用后光泽度不好的问题；专利文件CN105695132A公开了一种皮革清洁剂，制备原料包括非离子表面活性剂、皮革加脂剂、上光剂等，可以对皮革制品表面的污垢、污渍进行清洁，保持皮革表面的光泽度，但是存在清洁力度不够强、皮革产品易老化的问题。
发明内容
为了解决上述问题，本发明提供一种可以提供较强清洁力度的同时，还具有优异的抗菌性能以及耐摩擦牢度的皮革制品用亮洁剂及其制备方法。
本发明提供的具体技术方案如下：制备原料包括5-10重量份的硅油、5-15重量份的聚醚改性聚硅氧烷、3-10重量份的表面活性剂、1-8重量份的油脂、0.5-2重量份的酸性调节剂。
在一种实施方式中，所述制备原料还包括助剂1-3份，溶剂20-30份。
作为一种优选的实施方式，所述表面活性剂选自磺基甜菜碱、羧酸基甜菜碱、聚乙烯醇、聚氧乙烯醚、脂肪醇醚、月桂醇磷酸酯中的一种或任意几种的组合。
优选地，本申请使用的表面活性剂为异构醇聚氧乙烯醚1308，重量份5份，购自广州市炳耀化工有限公司。
作为一种优选的实施方式，所述助剂包括防霉剂、防老剂、消泡剂中的一种或几种。
作为一种优选的实施方式，所述防霉剂为a,β-不饱和羰基化合物和/或酚类物质。
优选地，所述a,β-不饱和羰基化合物为4-苯基-3-丁烯-2-酮，重量份为0.8份，所述酚类物质为苯酚，重量份为0.5份。
作为一种优选的实施方式，所述溶剂选自(a)去离子水和(b)乙醇、异丙醇、丙三醇中的一种或几种的组合。
优选地，本申请中使用的溶剂为(a)去离子水和(b)异丙醇，总重量份为23份，重量份之比为离子水:异丙醇＝2:3。
作为一种优选的实施方式，所述油脂选自棕榈蜡，蜂蜡，羊毛毡酯，石蜡中的一种或几种。
优选地，本申请中使用的油脂为石蜡，购自南通润丰石油化工有限公司，重量份为4份。
作为一种优选地实施方式，所述硅油为甲基硅油，购自山东鑫润锦化工有限公司，重量份为8份。
作为一种优选的实施方式，所述酸性调节剂为柠檬酸和/或富马酸。
优选地，本申请中使用的酸性调节剂为柠檬酸，购自安徽巨达生物科技有限公司，重量份为0.7份。
本发明还提出了一种皮革制品用亮洁剂的制备方法，所述制备原料经过混合、加热、保温、降温、出料得到亮洁剂。
作为一种优选的实施方式，所述加热温度为80-90℃，保温时间为0.5-1h。
申请人在之前申请的一篇一种皮具用高效消毒剂及其制备方法专利申请中，虽然用主剂、润湿剂、消毒助剂制备得到了一种皮具用的消毒剂，但是这种消毒剂存在各个组分之间相容性不好，使用材料不环保的问题，故本申请对之前的实验进行了一系列的改进，得到了一种清洁能力强，各组分相容性好、环保、并且可以有效除菌的亮洁剂。
本发明的有益效果如下：
1、本发明通过将异构醇聚氧乙烯醚和聚醚改性聚硅氧烷进行复配，得到的最终产品在清洗剂用量较少的前提下具有较强的清洁能力，同时具有优异的抗静电和润湿功能，二者存在协同作用，改善了其他各个组分分子间作用力，降低了分子内摩擦力，使得亮洁剂各个组分相容性变好。
2、本发明中通过往亮洁剂中加入甲基硅油，相当于是亮洁剂中的一种稳定剂，改善了传统皮革清洗剂中使用后皮革制品光泽度不好的问题，清洗后的皮革制品柔软性更好，还具有抗皱、耐洗等特性。
3、本发明加入的防霉剂a,β-不饱和羰基化合物，杀菌能力强，能够杀灭和抑制制革常见的微生物；毒性低，与亮洁剂中其他产品的相容性好。
4、本发明通过往亮洁剂中加入柠檬酸，使产品中的PH维持在5-7之间，防止溶液碱性过强对真皮造成一定的腐蚀；对于皮革(尤其是牛皮真皮)的保护性强。
具体实施方式
实施例1：一种皮革制品用亮洁剂及其制备方法
(一)由以下重量份原料制备而成
所述甲基硅油甲基硅油购自山东鑫润锦化工有限公司。所述聚醚改性聚硅氧烷购自上海荟研新材料有限公司，粘度为80-150cp，牌号为HY-67。所述a,β-不饱和羰基化合物为4-苯基-3-丁烯-2-酮。所述石蜡购自南通润丰石油化工有限公司。所述柠檬酸购自安徽巨达生物科技有限公司。
(二)一种皮革制品用亮洁剂的制备方法，包括以下步骤：
将甲基硅油、聚醚改性聚硅氧烷、异构醇聚氧乙烯醚、石蜡、a,β-不饱和羰基化合物、苯酚、去离子水、异丙醇、柠檬酸搅拌混合均匀，加热到80-90℃，保温0.5-1h，降温出料得到亮洁剂。
实施例2：一种皮革制品用亮洁剂及其制备方法
(一)由以下重量份原料制备而成
所述甲基硅油甲基硅油购自山东鑫润锦化工有限公司。所述聚醚改性聚硅氧烷购自上海荟研新材料有限公司，粘度为80-150cp，牌号为HY-67。所述a,β-不饱和羰基化合物为4-苯基-3-丁烯-2-酮。所述石蜡购自南通润丰石油化工有限公司。所述柠檬酸购自安徽巨达生物科技有限公司
(二)一种皮革制品用亮洁剂的制备方法，包括以下步骤：
将甲基硅油、聚醚改性聚硅氧烷、异构醇聚氧乙烯醚、石蜡、a,β-不饱和羰基化合物、苯酚、去离子水、异丙醇、柠檬酸搅拌混合均匀，加热到80-90℃，保温0.5-1h，降温出料得到亮洁剂。
实施例3：一种皮革制品用亮洁剂及其制备方法
(一)由以下重量份原料制备而成
所述甲基硅油甲基硅油购自山东鑫润锦化工有限公司。所述聚醚改性聚硅氧烷购自上海荟研新材料有限公司，粘度为80-150cp，牌号为HY-67。所述a,β-不饱和羰基化合物为4-苯基-3-丁烯-2-酮。所述石蜡购自南通润丰石油化工有限公司。所述柠檬酸购自安徽巨达生物科技有限公司。
(二)一种皮革制品用亮洁剂的制备方法，包括以下步骤：
将甲基硅油、聚醚改性聚硅氧烷、异构醇聚氧乙烯醚、石蜡、a,β-不饱和羰基化合物、苯酚、去离子水、异丙醇、柠檬酸搅拌混合均匀，加热到80-90℃，保温0.5-1h，降温出料得到亮洁剂。
对比例1
对比例1与实施例3基本相同，区别仅在于聚醚改性聚硅氧烷重量份为3份。
制备方法见实施例3。
对比例2
对比例1与实施例3基本相同，区别仅在于聚醚改性聚硅氧烷重量份为17份。
制备方法见实施例3。
对比例3
对比例1与实施例3基本相同，区别仅在于a,β-不饱和羰基化合物的添加量为2份。
制备方法见实施例3。
对比例4
对比例1与实施例3基本相同，区别仅在于将甲基硅油替换为氨基硅油。
制备方法见实施例3。
性能测试方法
1、抗菌性测试
将实施例提供的消毒剂进行皮革杀菌模拟实验，其中实验均为大肠杆菌，制备方法根据消毒技术规范(2002)制备，试验时，用无菌棉签沾取菌悬液在表面经过消毒处理的皮革上均匀涂抹5cm×5cm的区块12块，阳性对照区设两个区块，试验区设10个区块。待自然干燥后进行试验。用无菌棉签沾取消毒剂对试验区块进行擦拭消毒，(对照组以PBS对对照区进行擦拭)，作用至30min，用含中和剂的采样液浸湿无菌棉签涂抹采样。将棉签头以无菌方式剪入采样液中，洗脱棉签上的菌，取洗脱液作活菌计数，计算杀灭对数值。结果为3次试验平均值，并根据杀灭对数值评价杀菌性能，评为1～5级，其中1级为杀灭对数值小于1.5，2级为杀灭对数值小于2.5，小于等于1.5，3级为杀灭对数值小于3.5，大于等于2.5，4级为杀灭对数值小于4.5，大于等于3.5，5级为杀灭对数值大于等于4.5，测试结果显示，实施例1杀菌性能为4级、实施例2、3，对比例1、2、4杀菌性能为5级，对比例3杀菌性能为2级。
2、稳定性测试
将实施例1～3和对比例1～4的样品置于(1)40℃，(2)15℃，(3)-5℃依次放置72h，循环20次，取出后恢复至室温(26℃)，观察是否出现分层、变色、絮凝、沉淀现象。
每个样品设置20个平行样品，记录出现性状异常的样品个数为n，定义n＝0为稳定性优，1≤n≤3为稳定性良，n＞3为稳定性差。检测结果为：实施例1为稳定性优，实施例2、3以及对比例2为稳定性良，对比例1、3、4为稳定性差。
3、保护性
采用实施例1～3和对比例1～4的样品对皮革制品(具体为牛皮真皮材料)进行擦拭，擦拭后将皮革制品置于紫外灯下照射8h，取出后观察皮革制品是否出现断裂、变色现象，未出现异养为保护性A级，出现异养为保护性B级。测试结果为：实施例1～3为保护性A级，对比例1～4为保护性B级。
Claims (1)
1.一种皮革制品用亮洁剂，其特征在于：由以下重量份原料制备而成：
所述聚醚改性聚硅氧烷粘度为80-150cp，牌号为HY-67；
所述a,β-不饱和羰基化合物为4-苯基-3-丁烯-2-酮；
所述皮革制品用亮洁剂的制备方法，包括以下步骤：
将甲基硅油、聚醚改性聚硅氧烷、异构醇聚氧乙烯醚、石蜡、a,β-不饱和羰基化合物、苯酚、去离子水、异丙醇、柠檬酸搅拌混合均匀，加热到80-90℃，保温0.5-1h，降温出料得到亮洁剂。