CN115181201B - 一种C4-C8α-单烯烃与马来酸酐的共聚方法 - Google Patents
一种C4-C8α-单烯烃与马来酸酐的共聚方法 Download PDFInfo
- Publication number
- CN115181201B CN115181201B CN202210798164.8A CN202210798164A CN115181201B CN 115181201 B CN115181201 B CN 115181201B CN 202210798164 A CN202210798164 A CN 202210798164A CN 115181201 B CN115181201 B CN 115181201B
- Authority
- CN
- China
- Prior art keywords
- maleic anhydride
- alpha
- initiator
- static mixer
- copolymerization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种C4‑C8α‑单烯烃与马来酸酐的共聚方法,包括以下步骤:(1)在惰性氛围中,将C4‑C8α‑单烯烃与含有引发剂的马来酸酐溶液在含有静止元件的混合器中停留5‑20s进行混合,得共混溶液;(2)将步骤(1)得到的共混溶液通入至少2个并联的微通道反应器中在0.1‑5MPa下共聚反应1‑3h至反应结束后,经分离、洗涤、干燥,得C4‑C8α‑单烯烃与马来酸酐的共聚物;其中,整个过程的温度控制在50‑100℃,共混溶液在微通道反应器内的流速为5‑20ml/min。该方法通过使用含有静止元件的混合器结合微通道反应器进行共聚反应,可显著提高反应效率,且不会堵塞微通道反应器。
Description
技术领域
本发明涉及高分子材料制备技术领域,具体涉及一种C4-C8α-单烯烃与马来酸酐的共聚方法。
背景技术
C4至C8的α-烯烃马来酸酐共聚物,是一种用途广泛的化工产品,共聚物中的酸酐基团可以发生酯化、酰胺化、亚胺化和离子化等反应,得到的产物可进一步拓展其应用范围。例如异丁烯马来酸酐共聚物中的酸酐基团,通过一系列反应得到的不同分子量、不同功能基团(酰胺-氨型、酰亚胺型、交联型、水解型、离子型等)的衍生产品的用途也是不同的。低分子量异丁烯马来酸酐共聚物可作为阻垢剂、分散剂、水泥浆的减水剂使用,中高分子量异丁烯马来酸酐共聚物可作为木材和纸加工用粘接剂、乳液聚合稳定剂等使用。氨化后的异丁烯马来酸酐共聚物可作为黏合剂、水性涂料等使用,亚胺改性后的异丁烯马来酸酐共聚物可作为聚合稳定剂、粘接用乳胶使用,交联后的异丁烯马来酸酐共聚物可用做吸水性树脂使用,应用广泛。因此,C4至C8的α-烯烃马来酸酐共聚物性能优异,具有重要的应用前景。
现有的C4至C8的α-烯烃马来酸酐共聚物的制备方法主要采用沉淀聚合的方法合成,通常采用的方式是将C4-C8α-单烯烃直接加入到马来酸酐溶液中进行共聚反应,如:中国专利文献CN111285968A公开了一种高交替性可控分子量顺酐异丁烯共聚物的制备方法,具体包括以下步骤:1)于高压釜中,在无氧条件下,将顺酐与溶剂搅拌混合;2)向高压釜中通入异丁烯气体和溶有引发剂的溶剂进行反应;3)将反应取得的混合体系过滤,取滤饼以极性有机溶剂、水洗涤,干燥得顺酐异丁烯共聚物。中国专利文献CN102690393A公开了一种C5共混溶液-马来酸酐制备的含有功能性基团的共聚物及制备方法,具体是在氮气保护的条件下,将单体马来酸酐和引发剂偶氮二异丁腈(AIBN)加入到酯类介质中充分溶解后,再加入C5共混溶液于体系中溶解,得到C5与马来酸酐共聚物的乳白色的稳定的固液分散体系,经离心分离,真空干燥,得到白色粉末状C5与马来酸酐高度交联的共聚物,其中,C5共混溶液中烯烃和二烯烃均与马来酸酐发生反应。中国专利文献CN107722177A公开了一种混合碳四利用的方法和装置,装置具体包括聚合设备、气液分离器、裂解设备和液固分离器。通过共聚反应和蒸汽裂解反应相结合,使混合碳四充分得到利用,提供的含有马来酸酐官能团的聚合物,可以进一步作为功能材料的原料进行应用。
上述文献中公开的方法均存在C4-C8α-单烯烃溶解时间较长,利用效率较低的问题。因此,如何缩短C4-C8α-单烯烃溶解时间,进而提高C4-C8α-单烯烃与马来酸酐共聚反应效率、缩短反应时间是目前亟待解决的技术问题。
微通道反应器具有较大的换热比表面积、优质的传质传热特性、无放大效应、生产灵活且安全性能高等优势,但是其存在管路内径狭小易堵塞的问题。采用微通道反应器制备C4-C8α-单烯烃—马来酸酐极性共聚物易导致管路内径堵塞,反应无法进行。
发明内容
因此,本发明要解决的技术问题是克服现有技术中C4-C8α-单烯烃与马来酸酐极性共聚物的制备方法存在C4-C8α-单烯烃与马来酸酐共聚反应效率低、反应时间长,采用微通道反应器易堵塞的缺陷,从而提供一种C4-C8α-单烯烃与马来酸酐的共聚方法。
为此,本发明提供如下技术方案:
一种C4-C8α-单烯烃与马来酸酐的共聚方法,包括以下步骤:
(1)在惰性氛围中,将C4-C8α-单烯烃与含有引发剂的马来酸酐溶液在含有静止元件的反应器中停留5-20s进行混合,得共混溶液;
(2)将步骤(1)得到的所述共混溶液通入至少2个并联的微通道反应器中在0.1-5MPa下共聚反应1-3h至反应结束后,经分离、洗涤、干燥,得所述C4-C8α-单烯烃与马来酸酐的共聚物;
其中,整个制备过程的温度控制在50-100℃;
所述共混溶液在所述微通道反应器内的流速为5-20ml/min。
如果更换混合方式,比如将引发剂与C4-C8α-单烯烃在溶剂中混合后,再与马来酸酐溶液一起在含有静止元件的反应器中混合;或者是将C4-C8α-单烯烃和马来酸酐先溶于溶剂中,然后再与引发剂一起在含有静止元件的反应器中混合,会延长C4-C8α-单烯烃的溶解时间,降低C4-C8α-单烯烃与马来酸酐的共聚物的产率。
可选的,C4-C8α-单烯烃为双键在分子链端部的单烯烃,碳原子数4-8。
可选的,所述惰性氛围为氮气、氦气和氩气等中的任一种,现有的惰性氛围均能满足本发明技术方案的实施,但是出于成本的考虑,一般采用氮气。
可选的,所述微通道反应器内为中空螺旋盘管结构;优选地,盘管的长度为3-6m,盘管的内径为1-1.5mm。
可选的,所述微通道反应器上设有压力控制阀,所述压力控制阀的压力控制范围为0-10MPa。
可选的,所述含有静止元件的反应器为静态混合器,所述静态混合器的两端至少含有2个进口和2个出口;优选地,所述C4-C8α-单烯烃与含有引发剂的马来酸酐溶液分别从不同的进口进入所述静态混合器。
其中,C4-C8α-单烯烃从其中一个进口进入静态混合器,含有引发剂的马来酸酐溶液从另一个进口进入静态混合器,其中一个出口用于将未融入马来酸酐溶液中的C4-C8α-单烯烃(挥发的C4-C8α-单烯烃)排出并返回静态混合器进行循环利用,另一个出口排出的液体为含有C4-C8α-单烯烃、引发剂和马来酸酐的共混溶液。
优选地,步骤(1)中,在惰性氛围中,将50-100℃的C4-C8α-单烯烃与50-100℃的含有引发剂的马来酸酐溶液在含有静止元件的混合器中停留5-20s进行混合,并在混合的同时完成初步共聚反应,得共混溶液。
可选的,所述静态混合器选自SV型静态混合器、SX型静态混合器和SK型静态混合器中的任一种,优选地,所述静态混合器的长度为20-70cm,内孔直径为3-20cm,所述静止元件之间等距间隔,间隔距离为0.1-0.5cm。
可选的,所述C4-C8α-单烯烃与含有引发剂的马来酸酐溶液在静态混合器中可以层流、过渡流或紊流的方式进行共混。
可选地,所述静态混合器中用于排出含有C4-C8α-单烯烃、引发剂和马来酸酐的共混溶液的出口与所述微通道反应器的入口连通,优选地,所述静态混合器中用于排出含有C4-C8α-单烯烃、引发剂和马来酸酐的共混溶液的出口通过缓冲罐、计量泵和分流泵与所述微通道反应器的入口连通。
可选的,步骤(2)中分离得到的液体中含有过量的未反应的C4-C8α-单烯烃。
可选的,步骤(1)中,所述混合的压力为0.1-1MPa;
步骤(1)中,所述C4-C8α-单烯烃与所述含有引发剂的马来酸酐溶液的质量比为1:(5-55)。
可选的,步骤(1)中,所述C4-C8α-单烯烃与马来酸酐的质量比为(0.2-5):1,优选地,质量比为(0.6-3):1;
步骤(1)中,所述引发剂与马来酸酐的质量比为(0.01-0.20):1;
步骤(1)中,所述含有引发剂的马来酸酐溶液中所述马来酸酐的浓度为3wt%-25wt%。
可选的,所述引发剂为热分解型引发剂,优选地,所述引发剂选用过氧化二苯甲酰、过氧化二异丙苯、过氧化二特丁基、过氧化十二酰、过氧化苯甲酸特丁酯、过氧化二碳酸二异丙基酯、过氧化二碳二环己酯、偶氮二异丁腈和偶氮二异庚腈中的至少一种;
所述含有引发剂的马来酸酐溶液中的溶剂为有机酸烷基酯、烷烃和芳香烃中的至少一种。
所述有机酸烷基酯可选自乙酸异戊酯、乙酸乙酯和乙酸丙酯等中的任一种;
所述烷烃可选自C5-C16直链或支链的液态烷烃,如戊烷、己烷、庚烷等中的任一种;
所述芳香烃可选自如甲苯、苯等中的任一种。
可选的,步骤(2)中,所述分离的方式为过滤或离心,分离后的液相为有机溶剂,可回收利用。
可选的,步骤(2)中,采用醇类进行洗涤,如乙醇、甲醇、异丙醇等。
可选的,步骤(2)中,所述干燥为烘干,干燥温度为60-100℃。
与现有技术相比,本发明具有以下有益效果:
1、本发明提供的C4-C8α-单烯烃与马来酸酐的共聚方法,通过将马来酸酐和C4-C8α-单烯烃先在静态混合器中进行初步共混,利用静态混合器内部特殊结构阻隔住杂物(静态混合器内部结构较为特殊,且内径更大,只需定期清理即可,不会引起堵塞),结合共混溶液在微通道反应器内的流速和反应温度、时间,不仅能够避免微通道反应器内管路的堵塞,使反应顺利进行,而且最终生产出均匀的C4-C8α-单烯烃马来酸酐共聚物,并且能够有效提高共聚物的产率。此外,通过将静态混合器与微通道反应器一起引入到极性共聚反应中,相较于常规的只带有搅拌装置的反应釜、反应管等,微通道反应器不仅压力控制更精准,安全性更高,而且能够实现反应热的有效去除,精确控制反应温度,使得外部加热条件更宽松,有效节约能耗的同时精准控制反应物料的停留时间。
2、本发明提供的C4-C8α-单烯烃与马来酸酐的共聚方法,通过使用含有静止元件的混合器并限定停留时间,可使C4-C8α-单烯烃与含有引发剂的马来酸酐溶液充分且快速的互溶,并完成初步的极性共聚反应,同时大幅节约能耗,结合后续将共混溶液通入至少2个并联的微通道反应器进行共聚反应,并限定共混溶液在微通道反应器内的流速为5-20ml/min,各参数及装置之间相互配合,可显著降低C4-C8α-单烯烃溶解时间以及制备过程的温度,实现高效共聚反应,大幅节约能耗,提高反应效率、缩短反应时间,且通过含有静止元件的混合器与微通道反应器结合的方式,可以实现连续进料,连续出料的效果,可不停机连续操作,效率更高。
3、针对C4-C8α-单烯烃与马来酸酐反应的特点,将过程强化设备静态混合器引入到极性共聚反应中,静态混合器可增强C4-C8α-单烯烃传质效率、提高C4-C8α-单烯烃溶解程度,提升了C4-C8α-单烯烃反应效率,同时静态混合器中不含动态元件,使极性反应更加节能环保高效。
4、针对C4-C8α-单烯烃与马来酸酐反应的特点,在极性共聚反应中,将至少两个微通道反应器并联进行极性共聚反应。并联反应方式相较于两个微通道反应器串联、采用一个体积更大的微通道反应器、或两个并联的常规反应釜来说,能有效的去除极性共聚反应的聚合热,较好的控制聚合反应温度;提供必要的物料混合条件,保证反应器内浓度分布较为均匀;操作费用较低,且大幅增加了聚合物的产量反应效率以及反应量将大幅提升,有利于产品工业化生产。
5、本发明提供了一种新的C4-C8α-单烯烃极性共聚的方法,通过静态混合器加并联微通道反应器的方式使C4-C8α-单烯烃与马来酸酐在极短的时间内充分共混,结合控制极性共聚反应的时间及温度等参数,不仅仅提升了传质效率,也增大了操作的连续性,大大减少了反应过程中的能量流失,降低了极性反应成本,提高了反应物的生成率;为高效生产C4-C8α-单烯烃极性共聚物提供了更可行的方法。
附图说明
图1为本发明实施例1中α-单烯烃与马来酸酐的共聚方法的流程示意图;
图2为实施例4-1制得的α-单烯烃与马来酸酐共聚物的红外色谱图;
图3为实施例11制得的α-单烯烃与马来酸酐共聚物的红外色谱图。
具体实施方式
以下对本发明的实施例作详细说明:本实施例在以本发明技术方案为前提下进行实施,给出了详细的实施方式和过程,但本发明的保护范围不限于下述的实施例,下列实施例中未注明具体条件的实验方法,通常按照常规条件。
实施例1
如图1所示,为C4-C8α-单烯烃与马来酸酐的共聚方法的流程示意图,具体如下:
(1)氮气吹扫静态混合器后,将4.7g偶氮二易丁腈和294g马来酸酐溶于2.1L乙酸异戊酯中得到含引发剂的马来酸酐溶液(溶液A),该溶液A换热至60℃后,通过计量泵计量后经静态混合器的入口进入静态混合器,α-单烯烃(异丁烯)换热至60℃后,通过计量泵计量后经静态混合器的入口进入静态混合器,α-单烯烃和溶液A在静态混合器内的质量比为1:12,α-单烯烃和溶液A在静态混合器内充分混合并进行初步反应,得到共混溶液。其中,静态混合器的内孔直径为10cm,静止元件之间等距间隔,间隔距离为0.3cm,操作压力为0.6Mpa。
(2)将步骤(1)得到的共混溶液通过缓冲罐和计量泵、分流泵后分别通入到两个并列的微通道反应器中继续进行共聚反应,共混溶液在2个微通道反应器内的流速均为10ml/min,反应温度均为60℃,反应压力均为1MPa,反应时间均为3h;然后将得到的液固共混物进行过滤分离,得到的固相用无水乙醇进行洗涤、70℃烘干,得到α-单烯烃与马来酸酐的共聚物,其中,两个微通道反应器内均为中空螺旋盘管结构,盘管的长度为5m,盘管的内径为1.5mm。
下表1中为按照上述的试验条件,改变静态混合器长度以及α-单烯烃和溶液A在静态混合器中的停留时间,最终得到的共聚物的产量及数均分子量。
表1
静态混合器长度 | 停留时间 | 共聚物质量 | 共聚物数均分子量 | |
实施例1-1 | 70cm | 20s | 434g | 104000 |
实施例1-2 | 20cm | 5s | 390g | 84000 |
实施例2
实施例2与实施例1-1相似,区别仅在于步骤(1)中α-单烯烃和溶液A在静态混合器内的质量比不同,实施例2的步骤(1)中α-单烯烃和溶液A在静态混合器内的质量比及共聚物的质量和数据分子量具体见下表所示。
表2
实施例3
实施例3与实施例1-1相似,区别仅在于步骤(1)中静态混合器的操作压力不同,实施例3的步骤(1)中静态混合器的操作压力及共聚物的质量和数据分子量具体见下表所示。
表3
静态混合器的操作压力 | 共聚物质量 | 共聚物数均分子量 | |
实施例3-1 | 0.1Mpa | 390g | 92000 |
实施例3-2 | 1Mpa | 440g | 100000 |
实施例4
实施例4与实施例1-1相似,区别仅在于步骤(1)中α-单烯烃和溶液A换热后的温度不同,实施例4的步骤(1)中α-单烯烃和溶液A换热后的温度相同,具体换热后的温度及共聚物的质量和数据分子量具体见下表所示。
表4
如图2所示,为实施例4-1制得的α-单烯烃与马来酸酐共聚物的红外谱图,其中,1770.28cm-1和1852.74cm-1为酸酐的C=O伸缩振动吸收峰,2900cm-1附近为甲基和亚甲基的伸缩振动吸收峰。
实施例5
实施例5与实施例4-1相似,区别仅在于步骤(2)的反应温度不同,
实施例5的步骤(2)中的反应温度及共聚物的质量和数据分子量具体见下表所示。
表5
反应温度 | 共聚物质量 | 共聚物数均分子量 | |
实施例5-1 | 70℃ | 447g | 103000 |
实施例5-2 | 90℃ | 442g | 74000 |
实施例6
实施例6与实施例5-1相似,区别仅在于,步骤(2)中反应压力不同,实施例11-12的步骤(2)中的反应压力及共聚物的质量和数据分子量具体见下表所示。
表6
反应压力 | 共聚物质量 | 共聚物数均分子量 | |
实施例6-1 | 0.2Mpa | 420g | 84000 |
实施例6-2 | 3Mpa | 438g | 89000 |
实施例7
实施例7与实施例5-1相似,区别仅在于,步骤(1)中引发剂用量不同,实施例7的步骤(1)中的引发剂用量及共聚物的质量和数据分子量具体见下表所示。
表8
引发剂质量 | 共聚物质量 | 共聚物数均分子量 | |
实施例7-1 | 23g | 440g | 60000 |
实施例7-2 | 50g | 450g | 43000 |
实施例8
实施例8与实施例5-1相似,区别仅在于,步骤(1)中马来酸酐用量不同,实施例15-16的步骤(1)中的马来酸酐用量及共聚物的质量和数据分子量具体见下表所示。
表8
马来酸酐用量 | 共聚物质量 | 共聚物数均分子量 | |
实施例8-1 | 98g | 138g | 59000 |
实施例8-2 | 525g | 443g | 88000 |
实施例9-12
实施例9-12与实施例5-1相似,区别仅在于,步骤(1)中α-单烯烃的种类以及α-单烯烃与溶液A的质量比不同,实施例9-12的步骤(1)中的α-单烯烃的种类,α-单烯烃与溶液A的质量比及共聚物的质量和数据分子量具体见下表所示。
表9
如图3所示,为实施例11制得的共聚物的红外谱图,1771.99cm-1和1856.31cm-1为酸酐的C=O伸缩振动吸收峰,2900cm-1附近为甲基和亚甲基的伸缩振动吸收峰。
对比例1
将4.7g偶氮二易丁腈、294g马来酸酐溶于2.1L乙酸异戊酯中得到含引发剂的马来酸酐溶液(溶液A),该溶液A换热至70℃后,α-单烯烃(异丁烯)换热至70℃后,α-单烯烃和溶液A按照质量比为1:12分别通过缓冲罐和计量泵、分流泵后分别通入到两个并联的微通道反应器中继续进行共聚反应,物料在2个微通道反应器内的流速均为10ml/min,反应温度均为70℃,反应压力均为1MPa,反应时间为3h;然后将得到的液固共混物进行过滤分离,得到的固相用无水乙醇进行洗涤、70℃烘干,得到α-单烯烃与马来酸酐共聚物。其中,两个微通道反应器内均为中空螺旋盘管结构,盘管的长度为5m,盘管的内径为1.5mm。
该对比例制得的白色异丁烯与马来酸酐共聚物350g,数均分子量为70000。
由该对比例与实施例5-1相比可知,其他条件相同,只是省略在静态混合器进行充分共混和初步反应的条件下,最终得到的异丁烯与马来酸酐共聚物产率降低。
对比例2
(1)氮气吹扫静态混合器后,将4.7g偶氮二易丁腈、294g马来酸酐溶于2.1L乙酸异戊酯中得到含引发剂的马来酸酐溶液(溶液A),该溶液A换热至70℃后,通过计量泵计量后经静态混合器的入口进入静态混合器,α-单烯烃(异丁烯)换热至70℃后,通过计量泵计量后经静态混合器的入口进入静态混合器,α-单烯烃和溶液A在静态混合器内的质量比为1:12,α-单烯烃和溶液A在静态混合器内充分混合并进行初步反应(停留时间为20s),得到共混溶液。其中,静态混合器的内孔直径为10cm,静止元件之间等距间隔,间隔距离为0.3cm,长度为70cm,内孔直径为10cm,操作压力为0.6Mpa。
(2)将步骤(1)得到的共混溶液通入一个微通道反应器中继续进行共聚反应,共混溶液在微通道反应器内的流速为10ml/min,反应温度为70℃,反应压力为1MPa,反应时间为3h;然后将得到的液固共混物进行过滤分离,得到的固相用无水乙醇进行洗涤、70℃烘干,得到α-单烯烃与马来酸酐共聚物,其中微通道反应器内部为中空螺旋盘管结构,盘管的长度为5m,盘管的内径为1.5mm。
该对比例制得的异丁烯与马来酸酐共聚物362g,数均分子量为77000。
由该对比例与实施例5-1相比可知,其他条件相同,只是将两个并列的微通道反应器调换成一个微通道反应器的条件下,最终得到的异丁烯与马来酸酐共聚物产率降低。
对比例3
(1)氮气吹扫静态混合器后,将4.7g偶氮二易丁腈、294g马来酸酐溶于2.1L乙酸异戊酯中得到含引发剂的马来酸酐溶液(溶液A),该溶液A换热至70℃后,通过计量泵计量后经静态混合器的入口进入静态混合器,α-单烯烃(异丁烯)换热至70℃后,通过计量泵计量后经静态混合器的入口进入静态混合器,α-单烯烃和溶液A在静态混合器内的质量比为1:12,α-单烯烃和溶液A在静态混合器内充分混合并进行初步反应(停留时间为20s),得到共混溶液。其中,静态混合器的长度为70cm,内孔直径为10cm,静止元件之间等距间隔,间隔距离为0.3cm,操作压力为0.6Mpa。
(2)将步骤(1)得到的共混溶液通过缓冲罐和计量泵、分流泵分别通入到两个并联的常规反应釜(内部只含搅拌器)中继续进行共聚反应,搅拌速率为500r/min,反应温度为70℃,反应压力为1MPa,反应时间为3h;然后将得到的液固共混物进行过滤分离,得到的固相用乙醇进行洗涤、70℃烘干,得到α-单烯烃与马来酸酐共聚物。
该对比例制得的白色异丁烯与马来酸酐共聚物365g,数均分子量为90000。
由该对比例与实施例5-1相比可知,在其他条件相同,只是将两个微通道反应器调换成2个常规的只带搅拌的反应釜的条件下,最终得到的异丁烯与马来酸酐共聚物产率降低。
当然,本发明还可有其它多种实施例,在不背离本发明精神及其实质的情况下,熟悉本领域的技术人员可根据本发明作出各种相应的改变和变形,但这些相应的改变和变形都应属于本发明的保护范围。
Claims (10)
1.一种C4-C8α-单烯烃与马来酸酐的共聚方法,其特征在于,包括以下步骤:
(1)在惰性氛围中,将C4-C8α-单烯烃与含有引发剂的马来酸酐溶液在含有静止元件的反应器中停留5-20s进行混合,得共混溶液;
(2)将步骤(1)得到的所述共混溶液通入至少2个并联的微通道反应器中在0.1-5MPa下共聚反应1-3h至反应结束后,经分离、洗涤、干燥,得C4-C8α-单烯烃与马来酸酐的共聚物;
其中,整个过程的温度控制在50-100℃;
所述共混溶液在所述微通道反应器内的流速为5-20ml/min。
2.如权利要求1所述的共聚方法,其特征在于,所述微通道反应器内为中空螺旋盘管结构。
3.根据权利要求1所述的共聚方法,其特征在于,所述微通道反应器上设有压力控制阀,所述压力控制阀的压力控制范围为0-10MPa。
4.根据权利要求1所述的共聚方法,其特征在于,所述含有静止元件的反应器为静态混合器,所述静态混合器的两端至少含有2个进口和2个出口。
5.根据权利要求4所述的共聚方法,其特征在于,所述静态混合器选自SV型静态混合器、SX型静态混合器和SK型静态混合器中的任一种。
6.根据权利要求1所述的共聚方法,其特征在于,步骤(1)中,所述混合的压力为0.1-1MPa。
7.根据权利要求1所述的共聚方法,其特征在于,步骤(1)中,所述C4-C8α-单烯烃与所述含有引发剂的马来酸酐溶液的质量比为1:(5-55)。
8. 根据权利要求1所述的共聚方法,其特征在于,步骤(1)中,所述C4-C8α-单烯烃与马来酸酐的质量比为(0.2-5):1。
9.根据权利要求1所述的共聚方法,其特征在于,步骤(1)中,所述引发剂与马来酸酐的质量比为(0.01-0.20):1;和/或
步骤(1)中,所述含有引发剂的马来酸酐溶液中所述马来酸酐的浓度为3wt%-25wt%。
10.根据权利要求1所述的共聚方法,其特征在于,所述引发剂为热分解型引发剂;和/或
所述含有引发剂的马来酸酐溶液中的溶剂为有机酸烷基酯、烷烃和芳香烃中的至少一种。